CN106904843A - A kind of double glazing preparation method of surface with glomerocryst technique - Google Patents
A kind of double glazing preparation method of surface with glomerocryst technique Download PDFInfo
- Publication number
- CN106904843A CN106904843A CN201710083033.0A CN201710083033A CN106904843A CN 106904843 A CN106904843 A CN 106904843A CN 201710083033 A CN201710083033 A CN 201710083033A CN 106904843 A CN106904843 A CN 106904843A
- Authority
- CN
- China
- Prior art keywords
- glomerocryst
- glass
- technique
- double glazing
- adhesive tape
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of double glazing preparation method of surface with glomerocryst technique of glass making process technical field, the surface carries comprising the following steps that for the double glazing preparation method of glomerocryst technique：S1：Glass plate is pre-processed, and makes its any surface finish；S2：Spray-on coating, and drying solidifies it；S3：Carry out spraying lid color；S4：Adhesive tape is placed at glass plate edge；S5：In layer glass plate lumen loading epoxy resin, be integrated into glomerocryst technique in laminated glass by the present invention, the hardness of glass can be improved while glass aesthetics is increased, epoxy resin is filled in laminated glass simultaneously, bonding firmness is high between making layer glass, and glomerocryst technique is by the way of spraying in the present invention, and is sprayed using two-layer, it is difficult to fade, increases adhesive strength of the coating in glass surface.
Description
Technical field
The present invention relates to glass making process technical field, double glazing system of specially a kind of surface with glomerocryst technique
Make method.
Background technology
Polycrystalline glass elegance is beautiful, and texture is better than ceramic.Make flexible and changeable, color, pattern, specification can be made by oneself
It is processed, drills and is fabricated to variously-shaped, and several different colours can be made in same panel, can be also made by hot bending
Into tortuous and semicircular body.Polycrystalline glass foreign popular, be widely used in bathroom, kitchen, windowsill, lines, hall's wall curtain and
The surface of all indoor walls and ground decoration, can also be fabricated to kitchen platform, dining table, furniture, screen, boiler face, sanitary equipment basin platform etc..And
And can be used in mixed way with woodwork, its performance moisture-proof, protection against the tide, antiacid, alkali resistant.Laminated glass（Laminated Glass）Also known as
Be doubling glass, vacuum glass, be by two panels or divided glass, between pressed from both sides one or more layers organic polymer intermediate coat, pass through
Cross special high temperature precompressed（Or vacuumize）And after high-temperature high-pressure craft treatment, make what glass and intermediate coat permanent adhesive were integrated
Compound glass product.Laminated glass often has PVB, SGP, EVA, PU etc., colored intermediate coat laminated glass, SGX classes print with intermediate coat
Brush intermediate coat laminated glass, XIR class LOW-E intermediate coat laminated glass etc. are embedded decoration（Wire netting, metallic plate etc.）Interlayer
Decoration and the functional interlayer glass such as glass, embedded PET material laminated glass.But polycrystalline glass intensity is relatively low, broken, folder
Layer glass hard (HRC65Yi Shang) is high, non-breakable, and glomerocryst technique is attached in laminated glass, can increase while its aesthetics is increased
The hardness of vitreum, therefore, come into operation we have proposed a kind of double glazing preparation method of surface with glomerocryst technique, with
Solve the above problems.
The content of the invention
It is above-mentioned to solve it is an object of the invention to provide a kind of double glazing preparation method of surface with glomerocryst technique
The problem proposed in background technology.
To achieve the above object, the present invention provides following technical scheme：A kind of double glazing of surface with glomerocryst technique
Preparation method, the surface carries comprising the following steps that for the double glazing preparation method of glomerocryst technique：
S1：Well and 2 glass sheets of edging treatment are carried out by use requirement cutting, be then dried dehumidification treatments, and will
Glass surface is cleaned up；
S2：2 glass sheets are placed on the table, the coating spray that will be modulated in advance is placed in spray gun, first in glass table
Face sprays one layer of thin bottom, and the good laggard baking box drying of spray solidifies thin bottom；
S3：Lid color is sprayed on glass coating after hardening again, coating is no more than 3mm, secondary baking is then carried out in an oven
It is dry, harden its coating；
S4：Preprepared adhesive tape is immersed in epoxy resin solution, adhesive tape is softened, wherein a glass sheets surrounding
Adhesive tape is placed, and another glass sheets are covered in adhesive tape top, hole for injecting glue is reserved between 2 glass sheets；
S5：When adhesive tape is Nian Jie with glass plate firm, glass plate is inclined into certain angle, by epoxy from reserved hole for injecting glue
Resin infusion fills cavity in the cavity that 2 glass sheets are formed, and discharges the air of its cavity inside.
Preferably, in the step S1, when glass surface cleaning is carried out, cleaned using industrial alcohol, wiped glass
Vapor in glass plate.
Preferably, in the step S2, coating spray is to hatch mixing for siloxanes, glitter, glomerocryst and glomerocryst diluent
Compound, wherein hatching siloxanes：Glitter：Glomerocryst：Glomerocryst diluent=1:0.9:1.8:0.5.
Preferably, in the step S2, oven temperature is 90 DEG C, 40~45min of baking time.
Preferably, in the step S3, the oven temperature of secondary drying is 110 DEG C, and drying time is 50~55 DEG C.
Preferably, in the step S4, the edge of the edge in glass plate of adhesive tape is maintained on same vertical line, by glue
The part of bar protrusion glass plate edge is cut with knife.
Preferably, in the step S5, the gradient of glass plate is 30~40 °, when injecting glue is carried out, using clear hard
Film is overlapped into funnel-form, in flat insertion hole for injecting glue, carries out encapsulating operation.
Compared with prior art, the beneficial effects of the invention are as follows：Be integrated into glomerocryst technique in laminated glass by the present invention,
The hardness of glass can be improved while increasing glass aesthetics, while filling epoxy resin in laminated glass, makes two-layer glass
Firmness is bonded between glass high, glomerocryst technique is difficult to fade by the way of spraying, and using two-layer spraying in the present invention, increases
Plus coating is in the adhesive strength of glass surface.
Brief description of the drawings
Fig. 1 is workflow diagram of the present invention.
Specific embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
Fig. 1 is referred to, the present invention provides a kind of technical scheme：A kind of double glazing making side of surface with glomerocryst technique
Method, the surface carries comprising the following steps that for the double glazing preparation method of glomerocryst technique：
S1：Well and 2 glass sheets of edging treatment are carried out by use requirement cutting, be then dried dehumidification treatments, and will
Glass surface is cleaned up, and when glass surface cleaning is carried out, is cleaned using industrial alcohol, and the water on erasing glass plate steams
Gas；
S2：2 glass sheets are placed on the table, the coating spray that will be modulated in advance is placed in spray gun, first in glass table
Face sprays one layer of thin bottom, and the good laggard baking box drying of spray solidifies thin bottom, coating spray is hatching siloxanes, glitter, glomerocryst and
The mixture of glomerocryst diluent, wherein hatching siloxanes：Glitter：Glomerocryst：Glomerocryst diluent=1:0.9:1.8:0.5, baking box temperature
It is 90 DEG C to spend, 40~45min of baking time；
S3：Lid color is sprayed on glass coating after hardening again, coating is no more than 3mm, secondary baking is then carried out in an oven
It is dry, its coating is hardened, the oven temperature of secondary drying is 110 DEG C, and drying time is 50~55 DEG C；
S4：Preprepared adhesive tape is immersed in epoxy resin solution, adhesive tape is softened, wherein a glass sheets surrounding
Adhesive tape is placed, and another glass sheets are covered in adhesive tape top, hole for injecting glue is reserved between 2 glass sheets, adhesive tape
The edge that edge is in glass plate is maintained on same vertical line, and the part of adhesive tape protrusion glass plate edge is cut with knife；
S5：When adhesive tape is Nian Jie with glass plate firm, glass plate is inclined into certain angle, by epoxy from reserved hole for injecting glue
Resin infusion fills cavity in the cavity that 2 glass sheets are formed, and discharges the air of its cavity inside, glass plate
Gradient be 30~40 °, when injecting glue is carried out, funnel-form is overlapped into using clear hard film, in flat insertion hole for injecting glue,
Carry out encapsulating operation.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding can carry out various changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (7)
1. a kind of surface carries the double glazing preparation method of glomerocryst technique, it is characterised in that：The surface carries glomerocryst technique
Double glazing preparation method is comprised the following steps that：
S1：Well and 2 glass sheets of edging treatment are carried out by use requirement cutting, be then dried dehumidification treatments, and will
Glass surface is cleaned up；
S2：2 glass sheets are placed on the table, the coating spray that will be modulated in advance is placed in spray gun, first in glass table
Face sprays one layer of thin bottom, and the good laggard baking box drying of spray solidifies thin bottom；
S3：Lid color is sprayed on glass coating after hardening again, coating is no more than 3mm, secondary baking is then carried out in an oven
It is dry, harden its coating；
S4：Preprepared adhesive tape is immersed in epoxy resin solution, adhesive tape is softened, wherein a glass sheets surrounding
Adhesive tape is placed, and another glass sheets are covered in adhesive tape top, hole for injecting glue is reserved between 2 glass sheets；
S5：When adhesive tape is Nian Jie with glass plate firm, glass plate is inclined into certain angle, by epoxy from reserved hole for injecting glue
Resin infusion fills cavity in the cavity that 2 glass sheets are formed, and discharges the air of its cavity inside.
2. a kind of surface according to claim 1 carries the double glazing preparation method of glomerocryst technique, it is characterised in that：Institute
State in step S1, when glass surface cleaning is carried out, cleaned using industrial alcohol, the vapor on erasing glass plate.
3. a kind of surface according to claim 1 carries the double glazing preparation method of glomerocryst technique, it is characterised in that：Institute
State in step S2, coating spray is the mixture for hatching siloxanes, glitter, glomerocryst and glomerocryst diluent, wherein hatching silica
Alkane：Glitter：Glomerocryst：Glomerocryst diluent=1:0.9:1.8:0.5.
4. a kind of surface according to claim 1 carries the double glazing preparation method of glomerocryst technique, it is characterised in that：Institute
State in step S2, oven temperature is 90 DEG C, 40~45min of baking time.
5. a kind of surface according to claim 1 carries the double glazing preparation method of glomerocryst technique, it is characterised in that：Institute
State in step S3, the oven temperature of secondary drying is 110 DEG C, and drying time is 50~55 DEG C.
6. a kind of surface according to claim 1 carries the double glazing preparation method of glomerocryst technique, it is characterised in that：Institute
State in step S4, the edge of the edge in glass plate of adhesive tape is maintained on same vertical line, and adhesive tape is protruded into glass plate edge
Part cut with knife.
7. a kind of surface according to claim 1 carries the double glazing preparation method of glomerocryst technique, it is characterised in that：Institute
State in step S5, the gradient of glass plate is 30~40 °, when injecting glue is carried out, funnel-form is overlapped into using clear hard film,
In flat insertion hole for injecting glue, encapsulating operation is carried out.