CN110055004A - A kind of aqueous PP faces patch and its manufacture craft directly - Google Patents
A kind of aqueous PP faces patch and its manufacture craft directly Download PDFInfo
- Publication number
- CN110055004A CN110055004A CN201910332065.9A CN201910332065A CN110055004A CN 110055004 A CN110055004 A CN 110055004A CN 201910332065 A CN201910332065 A CN 201910332065A CN 110055004 A CN110055004 A CN 110055004A
- Authority
- CN
- China
- Prior art keywords
- glue
- aqueous
- coating
- added
- release paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of aqueous PP to face patch and its manufacture craft directly, it includes substrate, coating, glue, bottom and release paper that the aqueous PP, which faces patch directly, the coating uniform is coated on substrate lower surface, the bottom fits in the another side of coating, the another side stacking of bottom is coated with glue and forms glue layer, and release paper is bonded with glue layer.The present invention improves the performance for facing patch directly, prepared face directly pastes close structure between not only each layer by improving to the formula and production method of facing patch directly, loose deformation is not susceptible to when use, and glue layer stickiness is excellent, and when use, is not easily to fall off, to have a vast market space.
Description
Technical field
The present invention relates to patch technical field is faced directly, specifically a kind of aqueous PP faces patch and its manufacture craft directly.
Background technique
Decorative paster by bottom off-style paper layer and is pasted function paper layer on it and is constituted, which is characterized in that function paper layer by
Fabric is white PVC and the compound composition of black PVC heat, is evenly equipped with regularly arranged aperture on function paper layer, forms net
Trellis.The aperture is round hole, and other shapes can also be used certainly.Decorative paster using the above structure has cost opposite
It is lower and can single sided perspective.
Existing patch of facing directly is due to loosely organized between each layer, and easily deformation occurs in use, to influence
It faces the using effect of patch directly, and then influences to face directly the economic benefit of patch producer.
Summary of the invention
The purpose of the present invention is to provide a kind of aqueous PP to face patch directly, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of aqueous PP faces patch, including substrate, coating, glue, bottom and release paper directly, and the coating uniform is coated under substrate
Surface, the bottom fit in the another side of coating, and the another side stacking of bottom is coated with glue and forms glue layer, release paper
It is bonded with glue layer.
As further scheme of the invention: the substrate is to add release paper to be bonded by PP.
As further scheme of the invention: the coating is mixed by following raw material: brightening agent 0.277g, PVA
Micelle 9g, I 0.016g of defoaming agent, wetting agent 0.016g, II 0.024g of defoaming agent, silica 3g.
As the present invention further scheme: the bottom includes following raw material: lotion 0.75g, curing agent 0.243g,
III 0.002g of wetting agent 0.009g and defoaming agent.
As further scheme of the invention: the release paper includes following raw material: white spirit 3.1g, silicone oil
0.385g, curing agent 0.0057g and remover 0.0057g.
As further scheme of the invention: the manufacture craft of the glue, comprising the following steps:
11) above-mentioned raw materials are weighed by quality；
12) pure water 1988kg is added first into reaction pot, brightening agent 13.85kg and BP-17 micelle 450kg is then added,
5-10min is stirred with speed of agitator 30-60r/min；
13) 120min is kept the temperature after being warming up to 84 degree, adjusting mixing speed at this time is 40r/min；
14) 712kg pure water and 150kg silica are taken, is dispersed in dispersion machine, and turns stirring 30 minutes in revolving speed 40r/min,
Then filtered by 200 mesh filter screens；
15) reaction pot is cooled to 60 degree, filtered silica dispersions stirring 40-90min is then added；
16) glue is put after being cooled to 45 degree, after placing 48 hours, wetting agent 100g amount is added by every 100kg glue, storing container is added
Middle stirring 30 minutes, places 4 hours and uses on the machine.
As further scheme of the invention: the manufacture craft of the bottom, comprising the following steps:
21) above-mentioned raw materials are weighed by quality；
22) 5min is stirred after sequentially adding water, lotion and curing agent into reaction kettle, defoaming agent and wetting agent is then added, then
Stir 10-30min, mixing speed 800r/min.
As further scheme of the invention: the manufacture craft of the release paper:
31) above-mentioned raw materials are weighed by quality；
32) white spirit and silicone oil, pneumatic stirring 5-10min are added into reaction vessel；
33) curing agent is added and stirs 10min, add remover and stirs 10-30min；
34) it is filtered using 400 mesh filter screens.
The aqueous PP faces the manufacture craft of patch directly, comprising the following steps:
S1, above-mentioned raw materials are weighed by weight, ink is stamped by required pattern by printing machine on substrate；
S2, glue is prepared；
S3, bottoming is carried out in substrate lower surface Coating, and to bottom；
S4, the another side that bottom is fitted in coating using coating machine, the another side stacking coating glue of bottom simultaneously form glue
Layer is put into the drying box that temperature is 60-75 DEG C and is dried, and last chill roll is compound；
S5, release paper is attached on glue layer；
S6, bundling warehousing finished products.
As further scheme of the invention: in step S2, the curing degree of glue is 40%-50%.
Compared with prior art, the beneficial effects of the present invention are:
1, for the present invention by improving to the formula and production method of facing patch directly, the performance of patch is faced in improvement directly, prepared
Face patch not only close structure between each layer directly, when use is not susceptible to loose deformation, and glue layer stickiness is excellent, when use not
It is easy to fall off, to have a vast market space；
2, aqueous PP produced by the present invention, which faces patch directly, has the effect of that environmentally friendly, color saturation is high, beautiful in colour and rapid-curing cutback, solves
PP embrittlement, cannot directly paste problem, product not cissing, not alice, it is indeformable the problems such as, dry doubling, wet combining choose at random, operation letter
Singly, conveniently, efficiently, it is suitable for various small area groove surfaces, such as particle unevenness iron plate, bulky grain bumps vessel, rough earth, wall
Furring tile, stair, trolley roof ditch, vehicle door handle, vehicle body radian etc..
Specific embodiment
Technical solution of the present invention is described in more detail With reference to embodiment.
Embodiment 1
A kind of aqueous PP faces patch, including substrate, coating, glue, bottom and release paper directly, and the coating uniform is coated under substrate
Surface, the bottom fit in the another side of coating, and the another side stacking of bottom is coated with glue and forms glue layer, release paper
It is bonded with glue layer.
Specifically, the substrate is to add release paper to be bonded by PP in the present embodiment.
Specifically, the coating is mixed by following raw material in the present embodiment: brightening agent 0.277g, PVA micelle 9g,
I 0.016g of defoaming agent, wetting agent 0.016g, II 0.024g of defoaming agent, silica 3g.
Specifically, the bottom includes following raw material in the present embodiment: lotion 0.75g, curing agent 0.243g, wetting agent
III 0.002g of 0.009g and defoaming agent.
Specifically, the release paper includes following raw material in the present embodiment: white spirit 3.1g, silicone oil 0.385g, curing agent
0.0057g and remover 0.0057g.
Specifically, in the present embodiment, the manufacture craft of the glue, comprising the following steps:
11) above-mentioned raw materials are weighed by quality；
12) pure water 1988kg is added first into reaction pot, brightening agent 13.85kg and BP-17 micelle 450kg is then added,
5min is stirred with speed of agitator 30r/min；
13) 120min is kept the temperature after being warming up to 84 degree, adjusting mixing speed at this time is 40r/min；
14) 712kg pure water and 150kg silica are taken, is dispersed in dispersion machine, and turns stirring 30 minutes in revolving speed 40r/min,
Then filtered by 200 mesh filter screens；
15) reaction pot is cooled to 60 degree, filtered silica dispersions stirring 40min is then added；
16) glue is put after being cooled to 45 degree, after placing 48 hours, wetting agent 100g amount is added by every 100kg glue, storing container is added
Middle stirring 30 minutes, places 4 hours and uses on the machine.
Specifically, in the present embodiment, the manufacture craft of the bottom, comprising the following steps:
21) above-mentioned raw materials are weighed by quality；
22) 5min is stirred after sequentially adding water, lotion and curing agent into reaction kettle, defoaming agent and wetting agent is then added, then
Stir 10min, mixing speed 800r/min.
Specifically, in the present embodiment, the manufacture craft of the release paper:
31) above-mentioned raw materials are weighed by quality；
32) white spirit and silicone oil, pneumatic stirring 5min are added into reaction vessel；
33) curing agent is added and stirs 10min, add remover and stirs 10min；
34) it is filtered using 400 mesh filter screens.
The aqueous PP faces the manufacture craft of patch directly, comprising the following steps:
S1, above-mentioned raw materials are weighed by weight, ink is stamped by required pattern by printing machine on substrate；
S2, glue is prepared；
S3, bottoming is carried out in substrate lower surface Coating, and to bottom；
S4, the another side that bottom is fitted in coating using coating machine, the another side stacking coating glue of bottom simultaneously form glue
Layer is put into the drying box that temperature is 60 DEG C and is dried, and last chill roll is compound；
S5, release paper is attached on glue layer；
S6, bundling warehousing finished products.
Specifically, in step S2, the curing degree of glue is 40% in the present embodiment.
Embodiment 2
A kind of aqueous PP faces patch, including substrate, coating, glue, bottom and release paper directly, and the coating uniform is coated under substrate
Surface, the bottom fit in the another side of coating, and the another side stacking of bottom is coated with glue and forms glue layer, release paper
It is bonded with glue layer.
Specifically, the substrate is to add release paper to be bonded by PP in the present embodiment.
Specifically, the coating is mixed by following raw material in the present embodiment: brightening agent 0.277g, PVA micelle 9g,
I 0.016g of defoaming agent, wetting agent 0.016g, II 0.024g of defoaming agent, silica 3g.
Specifically, the bottom includes following raw material in the present embodiment: lotion 0.75g, curing agent 0.243g, wetting agent
III 0.002g of 0.009g and defoaming agent.
Specifically, the release paper includes following raw material in the present embodiment: white spirit 3.1g, silicone oil 0.385g, curing agent
0.0057g and remover 0.0057g.
Specifically, in the present embodiment, the manufacture craft of the glue, comprising the following steps:
11) above-mentioned raw materials are weighed by quality；
12) pure water 1988kg is added first into reaction pot, brightening agent 13.85kg and BP-17 micelle 450kg is then added,
10min is stirred with speed of agitator 60r/min；
13) 120min is kept the temperature after being warming up to 84 degree, adjusting mixing speed at this time is 40r/min；
14) 712kg pure water and 150kg silica are taken, is dispersed in dispersion machine, and turns stirring 30 minutes in revolving speed 40r/min,
Then filtered by 200 mesh filter screens；
15) reaction pot is cooled to 60 degree, filtered silica dispersions stirring 90min is then added；
16) glue is put after being cooled to 45 degree, after placing 48 hours, wetting agent 100g amount is added by every 100kg glue, storing container is added
Middle stirring 30 minutes, places 4 hours and uses on the machine.
Specifically, in the present embodiment, the manufacture craft of the bottom, comprising the following steps:
21) above-mentioned raw materials are weighed by quality；
22) 5min is stirred after sequentially adding water, lotion and curing agent into reaction kettle, defoaming agent and wetting agent is then added, then
Stir 30min, mixing speed 800r/min.
Specifically, in the present embodiment, the manufacture craft of the release paper:
31) above-mentioned raw materials are weighed by quality；
32) white spirit and silicone oil, pneumatic stirring 10min are added into reaction vessel；
33) curing agent is added and stirs 10min, add remover and stirs 30min；
34) it is filtered using 400 mesh filter screens.
The aqueous PP faces the manufacture craft of patch directly, comprising the following steps:
S1, above-mentioned raw materials are weighed by weight, ink is stamped by required pattern by printing machine on substrate；
S2, glue is prepared；
S3, bottoming is carried out in substrate lower surface Coating, and to bottom；
S4, the another side that bottom is fitted in coating using coating machine, the another side stacking coating glue of bottom simultaneously form glue
Layer is put into the drying box that temperature is 75 DEG C and is dried, and last chill roll is compound；
S5, release paper is attached on glue layer；
S6, bundling warehousing finished products.
Specifically, in step S2, the curing degree of glue is 50% in the present embodiment.
Embodiment 3
A kind of aqueous PP faces patch, including substrate, coating, glue, bottom and release paper directly, and the coating uniform is coated under substrate
Surface, the bottom fit in the another side of coating, and the another side stacking of bottom is coated with glue and forms glue layer, release paper
It is bonded with glue layer.
Specifically, the substrate is to add release paper to be bonded by PP in the present embodiment.
Specifically, the coating is mixed by following raw material in the present embodiment: brightening agent 0.277g, PVA micelle 9g,
I 0.016g of defoaming agent, wetting agent 0.016g, II 0.024g of defoaming agent, silica 3g.
Specifically, the bottom includes following raw material in the present embodiment: lotion 0.75g, curing agent 0.243g, wetting agent
III 0.002g of 0.009g and defoaming agent.
Specifically, the release paper includes following raw material in the present embodiment: white spirit 3.1g, silicone oil 0.385g, curing agent
0.0057g and remover 0.0057g.
Specifically, in the present embodiment, the manufacture craft of the glue, comprising the following steps:
11) above-mentioned raw materials are weighed by quality；
12) pure water 1988kg is added first into reaction pot, brightening agent 13.85kg and BP-17 micelle 450kg is then added,
5min is stirred with speed of agitator 40r/min；
13) 120min is kept the temperature after being warming up to 84 degree, adjusting mixing speed at this time is 40r/min；
14) 712kg pure water and 150kg silica are taken, is dispersed in dispersion machine, and turns stirring 30 minutes in revolving speed 40r/min,
Then filtered by 200 mesh filter screens；
15) reaction pot is cooled to 60 degree, filtered silica dispersions stirring 60min is then added；
16) glue is put after being cooled to 45 degree, after placing 48 hours, wetting agent 100g amount is added by every 100kg glue, storing container is added
Middle stirring 30 minutes, places 4 hours and uses on the machine.
Specifically, in the present embodiment, the manufacture craft of the bottom, comprising the following steps:
21) above-mentioned raw materials are weighed by quality；
22) 5min is stirred after sequentially adding water, lotion and curing agent into reaction kettle, defoaming agent and wetting agent is then added, then
Stir 20min, mixing speed 800r/min.
Specifically, in the present embodiment, the manufacture craft of the release paper:
31) above-mentioned raw materials are weighed by quality；
32) white spirit and silicone oil, pneumatic stirring 5min are added into reaction vessel；
33) curing agent is added and stirs 10min, add remover and stirs 15min；
34) it is filtered using 400 mesh filter screens.
The aqueous PP faces the manufacture craft of patch directly, comprising the following steps:
S1, above-mentioned raw materials are weighed by weight, ink is stamped by required pattern by printing machine on substrate；
S2, glue is prepared；
S3, bottoming is carried out in substrate lower surface Coating, and to bottom；
S4, the another side that bottom is fitted in coating using coating machine, the another side stacking coating glue of bottom simultaneously form glue
Layer is put into the drying box that temperature is 70 DEG C and is dried, and last chill roll is compound；
S5, release paper is attached on glue layer；
S6, bundling warehousing finished products.
Specifically, in step S2, the curing degree of glue is 45% in the present embodiment.
Better embodiment of the invention is explained in detail above, but the present invention is not limited to above-mentioned embodiment party
Formula within the knowledge of one of ordinary skill in the art can also be without departing from the purpose of the present invention
Various changes can be made.
Claims (10)
1. a kind of aqueous PP faces patch directly, which is characterized in that including substrate, coating, glue, bottom and release paper, the coating is equal
Even to be coated on substrate lower surface, the bottom fits in the another side of coating, and the another side stacking of bottom is coated with glue and shape
At glue layer, release paper is bonded with glue layer.
2. aqueous PP according to claim 1 faces patch directly, which is characterized in that the substrate be added by PP release paper be bonded and
At.
3. aqueous PP according to claim 2 faces patch directly, which is characterized in that the coating is mixed by following raw material:
Brightening agent 0.277g, PVA micelle 9g, I 0.016g of defoaming agent, wetting agent 0.016g, II 0.024g of defoaming agent, silica 3g.
4. aqueous PP according to claim 3 faces patch directly, which is characterized in that the bottom includes following raw material: lotion
0.75g, III 0.002g of curing agent 0.243g, wetting agent 0.009g and defoaming agent.
5. aqueous PP according to claim 4 faces patch directly, which is characterized in that the release paper includes following raw material: white appliances
Oily 3.1g, silicone oil 0.385g, curing agent 0.0057g and remover 0.0057g.
6. aqueous PP according to claim 1 faces patch directly, which is characterized in that the manufacture craft of the glue, including it is following
Step:
11) above-mentioned raw materials are weighed by quality；
12) pure water 1988kg is added first into reaction pot, brightening agent 13.85kg and BP-17 micelle 450kg is then added,
5-10min is stirred with speed of agitator 30-60r/min；
13) 120min is kept the temperature after being warming up to 84 degree, adjusting mixing speed at this time is 40r/min；
14) 712kg pure water and 150kg silica are taken, is dispersed in dispersion machine, and turns stirring 30 minutes in revolving speed 40r/min,
Then filtered by 200 mesh filter screens；
15) reaction pot is cooled to 60 degree, filtered silica dispersions stirring 40-90min is then added；
16) glue is put after being cooled to 45 degree, after placing 48 hours, wetting agent 100g amount is added by every 100kg glue, storing container is added
Middle stirring 30 minutes, places 4 hours and uses on the machine.
7. aqueous PP according to claim 4 faces patch directly, which is characterized in that the manufacture craft of the bottom, including it is following
Step:
21) above-mentioned raw materials are weighed by quality；
22) 5min is stirred after sequentially adding water, lotion and curing agent into reaction kettle, defoaming agent and wetting agent is then added, then
Stir 10-30min, mixing speed 800r/min.
8. aqueous PP according to claim 5 faces patch directly, which is characterized in that the manufacture craft of the release paper:
31) above-mentioned raw materials are weighed by quality；
32) white spirit and silicone oil, pneumatic stirring 5-10min are added into reaction vessel；
33) curing agent is added and stirs 10min, add remover and stirs 10-30min；
34) it is filtered using 400 mesh filter screens.
9. the manufacture craft that a kind of aqueous PP a method as claimed in any one of claims 1-8 faces patch directly, which is characterized in that including following step
It is rapid:
S1, above-mentioned raw materials are weighed by weight, ink is stamped by required pattern by printing machine on substrate；
S2, glue is prepared；
S3, bottoming is carried out in substrate lower surface Coating, and to bottom；
S4, the another side that bottom is fitted in coating using coating machine, the another side stacking coating glue of bottom simultaneously form glue
Layer is put into the drying box that temperature is 60-75 DEG C and is dried, and last chill roll is compound；
S5, release paper is attached on glue layer；
S6, bundling warehousing finished products.
10. the manufacture craft that aqueous PP according to claim 9 faces patch directly, which is characterized in that in step S2, glue is consolidated
Rate is 40%-50%.