CN110054413A - It is a kind of to remove simultaneously formaldehyde, except the ceramic glaze of toluene and antibacterial - Google Patents
It is a kind of to remove simultaneously formaldehyde, except the ceramic glaze of toluene and antibacterial Download PDFInfo
- Publication number
- CN110054413A CN110054413A CN201910497145.XA CN201910497145A CN110054413A CN 110054413 A CN110054413 A CN 110054413A CN 201910497145 A CN201910497145 A CN 201910497145A CN 110054413 A CN110054413 A CN 110054413A
- Authority
- CN
- China
- Prior art keywords
- except
- glaze
- ceramic glaze
- toluene
- antibacterial
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses one kind can remove formaldehyde simultaneously, except the ceramic glaze of toluene and antibacterial, the ceramic glaze is made of following raw material: frit, feldspar, quartz, kaolin, zirconium silicate, dolomite, burn talcum, zinc oxide, functional powder, CMC and STPP, the ceramic glaze is made of following ratio range: frit: 0-60%, feldspar: 10-50%, quartz: 5-30%, kaolin: 5-20%, zirconium silicate: 0-20%, dolomite: 0-8%, burn talcum: 0-5%, zinc oxide: 0-5%, functional powder: 1-6%, CMC:0.05-0.2% and STPP:0.05-0.5%, the feldspar includes potassium feldspar and albite, structure of the invention is scientific and reasonable, it is safe and convenient to use, by rationally matching It sets, there is the function except formaldehyde, except the function of toluene and the function of antibacterial using the manufactured goods of the ceramic glaze.
Description
Technical field
The present invention relates to ceramic glaze technical fields, specially a kind of to remove simultaneously formaldehyde, except the pottery of toluene and antibacterial
Glaze.
Background technique
Construction sanitary ceramic industry is focused on using advanced glaze technology very much, the country have already appeared it is large quantities of it is professional very
Strong ceramic glaze and preparing ceramic clinker, colorant company, the more and more abundant multiplicity of glaze used in construction sanitary ceramic product, mesh
The glaze product that preceding most pottery enterprises use, classification can be as follows with rough classification with purposes: lead glaze and leadless glaze, raw glaze and frit
Glaze, once-firing or twice firing glaze, ceramic tile, tableware, sanitary ceramics and electroceramics glaze, the leaching glaze divided by enameling method,
Glaze, high-temperature glaze and low temperature glaze, high expansion glaze and Low Thermal Expantion Glaze, firing atmosphere oxidizing flame, neutral flame and reducing flame, face are poured in glaze spraying
Color glaze and colourless glaze, clear frit and opaque glaze, bright glaze, mat glaze, semi-mat glaze or figure glaze etc..
But ceramic glaze currently on the market can not remove formaldehyde, except toluene and antibacterial simultaneously, cause to have in hidden
The risk of hiding.
Summary of the invention
The present invention provides one kind can remove formaldehyde, except the ceramic glaze of toluene and antibacterial simultaneously, can effectively solve above-mentioned
It proposes that ceramic glaze currently on the market can not remove formaldehyde, except toluene and antibacterial simultaneously in background technique, causes to have in
The problem of hiding risk.
To achieve the above object, the invention provides the following technical scheme: one kind can remove formaldehyde, except toluene and antibacterial simultaneously
Ceramic glaze, the ceramic glaze is made of following raw material: frit, feldspar, quartz, kaolin, zirconium silicate, white clouds
Stone burns talcum, zinc oxide, functional powder, CMC and STPP.
According to the above technical scheme, the ceramic glaze is made of following ratio range: frit: 0-60%, feldspar: 10-
50%, quartzy: 5-30%, kaolin: 5-20%, zirconium silicate: 0-20%, dolomite: 0-8%, burning talcum: 0-5%, zinc oxide: 0-5%,
Functional powder: 1-6%, CMC:0.05-0.2% and STPP:0.05-0.5%.
According to the above technical scheme, the ceramic glaze is made of following proportion: feldspar: 44.6%, quartzy: 25%, kaolinite
Soil: 15%, zirconium silicate: 10%, dolomite: 2%, functional powder: 3%, CMC:0.1% and STPP:0.3%.
According to the above technical scheme, the feldspar includes potassium feldspar and albite.
It is a kind of to remove simultaneously formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial, include the following steps:
S1, material is put into ball mill, adds water for ball milling；
S2, it is imposed on above ceramic paste preforms by spraying, drenching technique, after other compound stamps, leaching glaze, glaze spraying technique, is burnt into kiln
Manufactured goods.
According to the above technical scheme, fineness 325, mesh screen residue < 2%, specific gravity: 1.4-2.0, stream are controlled in the step S1
Speed: (Tu Shi glasss) 18-60S.
According to the above technical scheme, firing range in the step S2: 800-1280 degree.
According to the above technical scheme, specifically comprise the following steps: base powder, press-molding, adobe, adobe in the step S2
Dry, leaching overglaze, ink-jet printed, leaching throw glaze, kiln firing, polishing and classification packaging.
According to the above technical scheme, its antibiotic rate of finished product detection, formaldehyde removal rate and benzene removal rate in the step S2；
The antibiotic rate detection staphylococcus glucose bacterium and Escherichia coli.
Compared with prior art, beneficial effects of the present invention: structure of the invention is scientific and reasonable, safe and convenient to use, passes through
Reasonable disposition has the function except formaldehyde, except the function of toluene and the function of antibacterial using the manufactured goods of the ceramic glaze.
Detailed description of the invention
Attached drawing is used to provide further understanding of the present invention, and constitutes part of specification, with reality of the invention
It applies example to be used to explain the present invention together, not be construed as limiting the invention.
In the accompanying drawings:
Fig. 1 is step flow diagram of the invention.
Specific embodiment
Hereinafter, preferred embodiments of the present invention will be described with reference to the accompanying drawings, it should be understood that preferred reality described herein
Apply example only for the purpose of illustrating and explaining the present invention and is not intended to limit the present invention.
Embodiment 1: as shown in Figure 1, the present invention provides technical solution, one kind can remove formaldehyde, except toluene and antibacterial simultaneously
Ceramic glaze, ceramic glaze is made of following raw material: frit, feldspar, quartz, kaolin, zirconium silicate, dolomite,
Burn talcum, zinc oxide, functional powder, CMC and STPP.
According to the above technical scheme, ceramic glaze is made of following proportion: feldspar: 44.6%, quartzy: 25%, kaolin:
15%, zirconium silicate: 10%, dolomite: 2%, functional powder: 3%, CMC:0.1% and STPP:0.3%.
According to the above technical scheme, feldspar includes potassium feldspar and albite.
It is a kind of to remove simultaneously formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial, include the following steps:
S1, material is put into ball mill, adds water for ball milling；
S2, it is imposed on above ceramic paste preforms by spraying, drenching technique, after other compound stamps, leaching glaze, glaze spraying technique, is burnt into kiln
Manufactured goods.
According to the above technical scheme, control fineness 325 in step S1, mesh screen residue < 1%, specific gravity: 1.90, flow velocity: (Tu Shi
Cup) 40S.
According to the above technical scheme, firing range in step S2: 1200 degree.
According to the above technical scheme, specifically comprise the following steps: that base powder, press-molding, adobe, adobe are dry in step S2
Dry, leaching overglaze, ink-jet printed, leaching throw glaze, kiln firing, polishing and classification packaging.
According to the above technical scheme, its antibiotic rate of finished product detection, formaldehyde removal rate and benzene removal rate in step S2；
Antibiotic rate detects staphylococcus glucose bacterium and Escherichia coli.
Embodiment 2: as shown in Figure 1, the present invention provides technical solution, one kind can remove formaldehyde, except toluene and antibacterial simultaneously
Ceramic glaze, ceramic glaze is made of following raw material: frit, feldspar, quartz, kaolin, zirconium silicate, dolomite,
Burn talcum, zinc oxide, functional powder, CMC and STPP.
According to the above technical scheme, ceramic glaze is made of following proportion: frit: 56.6%, feldspar: 18%, quartzy: 6%,
Kaolin: 10%, zirconium silicate: 6%, functional powder: 3%, CMC:0.1% and STPP:0.3%.
According to the above technical scheme, feldspar includes potassium feldspar and albite.
It is a kind of to remove simultaneously formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial, include the following steps:
S1, material is put into ball mill, adds water for ball milling；
S2, it is imposed on above ceramic paste preforms by spraying, drenching technique, after other compound stamps, leaching glaze, glaze spraying technique, is burnt into kiln
Manufactured goods.
According to the above technical scheme, control fineness 325 in step S1, mesh screen residue < 1%, specific gravity: 1.90, flow velocity: (Tu Shi
Cup) 40S.
According to the above technical scheme, firing range in step S2: 1080 degree.
According to the above technical scheme, specifically comprise the following steps: that base powder, press-molding, adobe, adobe are dry in step S2
Dry, leaching overglaze, ink-jet printed, leaching throw glaze, kiln firing, polishing and classification packaging.
According to the above technical scheme, its antibiotic rate of finished product detection, formaldehyde removal rate and benzene removal rate in step S2；
Antibiotic rate detects staphylococcus glucose bacterium and Escherichia coli.
For embodiment 1-2 by detection, the examining report after product is detected by middleization is as follows:
Study testing result:
Compared with prior art, beneficial effects of the present invention: structure of the invention is scientific and reasonable, safe and convenient to use, by reasonable
Configuration has the function except formaldehyde, except the function of toluene and the function of antibacterial using the manufactured goods of the ceramic glaze.
Finally, it should be noted that being not intended to restrict the invention the foregoing is merely preferred embodiment of the invention, to the greatest extent
Present invention has been described in detail with reference to the aforementioned embodiments for pipe, for those skilled in the art, still can be with
It modifies the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.It is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in guarantor of the invention
Within the scope of shield.
Claims (9)
1. one kind can remove simultaneously formaldehyde, except the ceramic glaze of toluene and antibacterial, it is characterised in that: the ceramic glaze is by following
Raw material is made: frit, feldspar, quartz, kaolin, zirconium silicate, dolomite, burn talcum, zinc oxide, functional powder,
CMC and STPP.
2. one kind according to claim 1 can remove simultaneously formaldehyde, except the ceramic glaze of toluene and antibacterial, feature exists
In the ceramic glaze is made of following ratio range: frit: 0-60%, feldspar: 10-50%, quartz: 5-30%, kaolin: 5-
20%, zirconium silicate: 0-20%, dolomite: 0-8%, talcum: 0-5%, zinc oxide: 0-5%, functional powder: 1-6%, CMC is burnt:
0.05-0.2% and STPP:0.05-0.5%.
3. one kind according to claim 1 can remove simultaneously formaldehyde, except the ceramic glaze of toluene and antibacterial, feature exists
In the ceramic glaze is made of following proportion: feldspar: 44.6%, quartzy: 25%, kaolin: 15%, zirconium silicate: 10%, white clouds
Stone: 2%, functional powder: 3%, CMC:0.1% and STPP:0.3%.
4. one kind according to claim 1 can remove simultaneously formaldehyde, except the ceramic glaze of toluene and antibacterial, feature exists
In the feldspar includes potassium feldspar and albite.
5. one kind according to claim 1-4 can remove formaldehyde, except toluene and the ceramic glaze of antibacterial simultaneously
Preparation process, which comprises the steps of:
S1, material is put into ball mill, adds water for ball milling；
S2, it is imposed on above ceramic paste preforms by spraying, drenching technique, after other compound stamps, leaching glaze, glaze spraying technique, is burnt into kiln
Manufactured goods.
6. one kind according to claim 5 can remove formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial simultaneously,
It is characterized in that, controlling fineness 325, mesh screen residue < 2%, specific gravity: 1.4-2.0, flow velocity: (Tu Shi glasss) 18- in the step S1
60S。
7. one kind according to claim 5 can remove formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial simultaneously,
It is characterized in that, firing range in the step S2: 800-1280 degree.
8. one kind according to claim 5 can remove formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial simultaneously,
It is characterized in that, specifically comprising the following steps: base powder, press-molding, adobe, brick bat drying, leaching overglaze, spray in the step S2
Glaze, kiln firing, polishing and classification packaging are thrown in ink-printed, leaching.
9. one kind according to claim 5 can remove formaldehyde, except the preparation process of toluene and the ceramic glaze of antibacterial simultaneously,
It is characterized in that, its antibiotic rate of finished product detection, formaldehyde removal rate and benzene removal rate in the step S2；
The antibiotic rate detection staphylococcus glucose bacterium and Escherichia coli.