CN110053322A - A kind of warm-keeping composite fabric - Google Patents
A kind of warm-keeping composite fabric Download PDFInfo
- Publication number
- CN110053322A CN110053322A CN201810048343.3A CN201810048343A CN110053322A CN 110053322 A CN110053322 A CN 110053322A CN 201810048343 A CN201810048343 A CN 201810048343A CN 110053322 A CN110053322 A CN 110053322A
- Authority
- CN
- China
- Prior art keywords
- composite material
- fabric
- warm
- solid
- surface layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of warm-keeping composite fabrics.The warm-keeping composite fabric is combined by surface layer and inner layer by the way that solid is dotted, and wherein surface layer is woven fabric, inner layer is that warp knit or circle compile knitted pile fabric, and the adhesion amount of solid is 15~18g/m2, and the heat preservation rate of the composite material is 35~50%.Compared with existing product currently on the market, composite material of the invention has excellent warmth retention property and gas permeability, suitable for production autumn and winter shirt, easy dress etc..
Description
Technical field
The invention belongs to textile fields, and in particular to a kind of warm-keeping composite fabric.
Background technique
Composite material is by one or more layers textile material, non-woven material and other functional materials through made of bonding fitting
A kind of new material.Wherein, can generally consider to be bonded PU film or TPU membrane on fabric to improve the warmth retention property of composite material,
But so the breathable moisture permeability of composite material more or less will receive certain influence.When a large amount of perspirations, sweat vapour has can
It can not can be discharged in time.Moreover, the phenomenon that repeatedly composite material is separated it is easy to appear joint place degumming after washing.
A kind of water proof wind proof vapor-permeable type composite material is disclosed in patent document CN202573157U, including being located at outside
Woven layer and knitted fabric layer positioned inside as lining pass through several hot melt glue points between woven layer and knitted fabric layer
Bonding, and another surface of woven layer is covered with waterproof layer, and another surface of knitted fabric layer is covered with moisture absorption layer, and gained composite material was both
The anti-water repellent of energy, and be conducive to exclude the steam of human body.Such composite material due to waterproof layer that there are feels is partially hard;Separately
Outside, warmth retention property also needs to be further increased.
Summary of the invention
In view of the deficiencies of the prior art, the purpose of the present invention is to provide one kind to have good heat-insulation breathable performance, feel
Soft composite material.
Composite material of the invention is combined by surface layer and inner layer by the way that solid is dotted, wherein surface layer be woven fabric,
Inner layer is warp knit or circle compiles knitted pile fabric, and the adhesion amount of solid is 15~18g/m2, and the heat preservation rate of composite material is 35
~50%.
In the present invention, two shell fabrics are carried out dotted compound by solid in table, be conducive to improve fabric gas permeability with
And soft handle degree.Surface layer uses woven fabric, imparts the excellent stiffness of composite material;Inner layer uses knitted pile fabric, no
It only improves feel, improve snugness of fit, but also impart the better heat insulation effect of composite material.
Specific embodiment
Composite material of the invention is combined by surface layer and inner layer by the way that solid is dotted, wherein surface layer be woven fabric,
Inner layer is warp knit or circle compiles knitted pile fabric, and the adhesion amount of solid is 15~18g/m2, and the heat preservation rate of composite material is 35
~50%.
Wherein, surface layer and inner layer compound tense, compared to the comprehensive complex method of solid, the dotted complex method of solid more has
Conducive to the gas permeability and soft handle degree for improving composite material.And specific solid adhesion amount can improve removing by force simultaneously
Power effectively prevent the generation of the degumming foaming phenomena in dress and washing process.In the present invention, the adhesion amount of solid is less than
15g/m2If, bonding force is too small between surface layer and inner layer, will appear degumming phenomenon in wearing process;And adhesion amount is more than 18g/
m2If, adhesion amount is excessive, and the pliability of composite material reduces, and wearing comfort is poor.Solid used in the present invention is preferably poly-
Urethane resin etc..
Surface layer then imparts the excellent stiffness of composite material using woven fabric;Inner layer is not only improved using knitted pile fabric
Feel improves snugness of fit, and imparts the better heat insulation effect of fabric.
Wherein, knitted fabric used in inner layer, fluffing mode are not particularly limited, and can be sanding, ball woll and shake grain processing side
One of formula or multiple combinations form.The fibrous raw material for forming above-mentioned knitted fabric is not particularly limited, and can carry out as needed
Selection, such as terylene, nylon chemical fibre, the regenerated celulose fibres such as viscose glue, the natural fibers such as cotton, form can be short fibre
Yarn or long filament multifilament, when using spun yarn, fiber number be preferably 10~40 (hereinafter referred to as s);It is fine when using long filament multifilament
Degree is preferably 50~200 Denier (hereinafter referred to as D).
In the process of wearing, the surface layer of composite material readily accesses spot etc., thus in the present invention preferred surface layer water
Drop diffusion time is 0.1~10 second, soil resistance is 4 grades or more.Surface layer fabric can be easy by adding hydrophily in padding or bathing
Drying and shaping is made after detergent.Within water droplet diffusion 10 seconds of surface layer fabric, sweat can be preferably absorbed, and
Quickening discharges it external speed.It pads back number to be selected as needed, can be an immersing and rolling, be also possible to two leachings two
It rolls.The easy detergent of hydrophily used, ingredient are not particularly limited in the present invention, as acrylate copolymer, polyether ester are embedding
Section copolymer etc..
In the present invention, preferably the air penetrability of composite material is 10~20cm3/cm2S.Composite material air penetrability is in this range
It is interior, it not only can guarantee the permeability of fabric, but also the entrance of cool exterior air can be prevented, it is ensured that internal insulation effect.
In the present invention, the separation strength of surface layer and inner layer is 250~400cN/cm preferably in composite material.Separation strength is small
If 250cN/cm, composite material is possible to will appear peeling, influences final product quality;And if being greater than 400cN/cm,
The stiffness of composite material increases, it is possible to influence whether the snugness of fit of finished product.
In the present invention, preferably composite material measures its flat appearance after 0,217 103 method of JIS L continuously washs 20 times
4 grades of degree or more.Repeatedly it ensure that the endurance quality of dress without degumming foaming phenomena after washing.
Below with reference to Examples and Comparative Examples, the present invention will be further described, and protection of the invention can not be limited with this
Range.
The test method of each parameter involved in the present invention is as follows:
(1) heat insulating ability
Using KES method, sample is placed on the test hot plate of certain temperature, test maintains this temperature invariable lost
Heat W(W/m2).Specific experimental condition is as follows:
Test environment: 20 DEG C × 65%RH
Hot plate temperature (BT resin substrate material): 40 DEG C
Hot plate size: 10cm × 10cm
Specimen size: 20cm × 20cm
Wind speed: 0.19m/s
Testing time: indefinite (time that different materials substance keeps constant temperature is indefinite)
< result calculates >
ɑ (%)=(W0-W) * 100/W0
ɑ: heat preservation rate (%)
W: the W value tested when placing sample
W0: the W value tested under no sample conditions.
(2) hydrophily
It is tested according to JIS L1907 7.1.1:2010 " the water imbibition experimental method of fibre ".
(3) anti-pollution
It is tested according to JIS L 1919:2006 " the soil resistance test method of fibre ".
(4) gas permeability
It is tested according to JIS L 1096:2010 8.26.1 A method " measurement of fibre aeration ".
(5) separation strength
It is tested according to JIS L1089:2007 " the peel strength experimental method of fibre ".
(6) washing resistance
It is tested according to 103 method of JIS L 0217:2010 " test of fibre home washings program ".
(7) flat appearance degree
It is tested according to AATCC 124-2014.
(8) stiffness
It is tested according to JIS L 1096:2010 8.21.1 A method " the rigid softness experimental method of fibre ".Note: numerical value
It is bigger, indicate that fabric is harder, flexibility is poorer.
Embodiment 1
Select the grammes per square metre 100g/ m formed by 50D-48f- polyester DTY2, thread count 112*90 root/inch woven fabric conduct
Surface layer fabric selects the grammes per square metre 100g/m formed by 50D-72f- polyester DTY2Fluffing circle braided fabric be used as inner layer fabric, general
Surface layer fabric and inner layer fabric carry out fitting processing by polyurethane resin solid, laminating condition: 120 DEG C of * 10m/min,
The coated weight of solid is 17g/m2, maturation 24 hours under the conditions of 40 DEG C of temperature, humidity 70%, obtain composite surface of the invention
Material.It is specific as shown in table 1.
Embodiment 2
Selecting warp and weft is 50D-48f- polyester DTY woven fabric, is processed by the easy detergent of hydrophily, what drying and shaping was formed
Density 112*90 root/inch, grammes per square metre 100g/m2Conduct surface layer fabric.Remaining is the same as embodiment 1.Specific performance test data
As shown in table 1.
Embodiment 3
Solid coated weight is 16g/m2, remaining obtains composite material of the invention with embodiment 2.It is specific as shown in table 1.
Embodiment 4
Solid coated weight is 18g/m2, remaining obtains composite material of the invention with embodiment 2.It is specific as shown in table 1.
Embodiment 5
The grammes per square metre 140g/m for selecting 75D-72f- polyester DTY to be formed2Fluffing circle braided fabric be used as inner layer fabric, remaining with implementation
Example 2 obtains composite material of the invention.It is specific as shown in table 1.
Embodiment 6
The grammes per square metre for selecting 180D-144f- polyester DTY to be formed is 165g/m2Fluffing circle braided fabric be used as inner layer fabric, remaining together
Embodiment 2 obtains composite material of the invention.It is specific as shown in table 1.
Embodiment 7
Selecting the full cotton staple circle of 30S to compile the grammes per square metre formed is 160g/m2Fluffing circle braided fabric be used as inner layer fabric, remaining with reality
Example 2 is applied, composite material of the invention is obtained.It is specific as shown in table 1.
Embodiment 8
The grammes per square metre for selecting 30S polyester-cotton blend blend spun yarn to be formed is 160g/m2Fluffing circle braided fabric be used as inner layer fabric, remaining together
Embodiment 2 obtains composite material of the invention.It is specific as shown in table 1.
Comparative example 1
The grammes per square metre for selecting 50D-72f- polyester DTY to be formed is 100g/m2Circle braided fabric as inner layer fabric, remaining same embodiment
2, obtain composite material.It is specific as shown in table 1.
Comparative example 2
Solid coated weight is 13g/m2, remaining obtains composite material with embodiment 2.It is specific as shown in table 1.
Comparative example 3
Solid coated weight is 20g/m2, remaining obtains composite material with embodiment 2.It is specific as shown in table 1.
Table 1
As can be seen from Table 1:
(1) by embodiment 2, embodiment 3 and embodiment 4 it is found that under equal conditions, the adhesion amount of solid is more, and heat preservation rate is got over
Height, air penetrability is lower, and separation strength is bigger, and stiffness is also bigger (flexibility is poorer), and flatness is suitable after washing.
(2) by embodiment 2 and embodiment 5 it is found that under equal conditions, by grammes per square metre 100g/m2Fluffing circle compile object as inner
Layer formed composite material with by grammes per square metre 140g/m2Fluffing circle compile the composite material that is formed as inner layer of object and compare, the two
Separation strength and appearanc after laundering flatness are suitable, but the former heat insulating ability, gas permeability and flexibility are slightly not as good as the latter.
(3) by comparative example 1 and embodiment 2 it is found that compiling object under equal conditions as what inner layer was formed by the circle not fluffed and answering
Fabric is closed compared with the circle by fluffing compiles the composite material that object is formed as inner layer, the thermal insulation property of nap fabric, which is much higher than, not to be risen
Wool fabric.
(4) by comparative example 2 and embodiment 3 it is found that solid adhesion amount is 13g/m under equal conditions2Composite material with
Solid adhesion amount is 16g/m2Composite material is compared, and the too low separation strength that will lead to of the adhesion amount of solid is relatively low, is gone out after washing
Existing degumming phenomenon, flatness reduce.
(5) by comparative example 3 and embodiment 4 it is found that solid adhesion amount is 20g/m under equal conditions2Composite material with
Solid adhesion amount is 18g/m2Composite material is compared, and the adhesion amount of solid is excessively high to cause fabric stiffness excessive, dress
Comfort is poor.
Claims (5)
1. a kind of warm-keeping composite fabric, it is characterized in that: the composite material is dotted compound by solid by surface layer and inner layer
At, wherein the surface layer is woven fabric, inner layer is warp knit or circle compiles knitted pile fabric, the adhesion amount of the solid is 15~
18g/m2, and the heat preservation rate of the composite material is 35~50%.
2. warm-keeping composite fabric according to claim 1, it is characterized in that: the water droplet diffusion time on the surface layer is 0.1~10
Second, soil resistance are 4 grades or more.
3. warm-keeping composite fabric according to claim 1 or claim 2, it is characterized in that: the air penetrability of the composite material be 10~
20cm3/cm2S.
4. warm-keeping composite fabric according to claim 1 or claim 2, it is characterized in that: in the composite material, the stripping on surface layer and inner layer
It is 250~400cN/cm from strength.
5. warm-keeping composite fabric according to claim 1 or claim 2, it is characterized in that: the composite material passes through JIS L 0217
103 methods measure 4 grades of its flat appearance degree or more after continuously washing 20 times.