CN110042313B - 高强度铁基合金、其制造方法和由其得到的制品 - Google Patents
高强度铁基合金、其制造方法和由其得到的制品 Download PDFInfo
- Publication number
- CN110042313B CN110042313B CN201910163334.3A CN201910163334A CN110042313B CN 110042313 B CN110042313 B CN 110042313B CN 201910163334 A CN201910163334 A CN 201910163334A CN 110042313 B CN110042313 B CN 110042313B
- Authority
- CN
- China
- Prior art keywords
- austenite
- steel
- carbon
- iron
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Links
- XEEYBQQBJWHFJM-UHFFFAOYSA-N Iron Chemical compound [Fe] XEEYBQQBJWHFJM-UHFFFAOYSA-N 0.000 title claims abstract description 128
- 229910045601 alloy Inorganic materials 0.000 title claims abstract description 116
- 239000000956 alloy Substances 0.000 title claims abstract description 116
- 229910052742 iron Inorganic materials 0.000 title claims abstract description 64
- 238000004519 manufacturing process Methods 0.000 title claims abstract description 9
- 238000000034 method Methods 0.000 claims abstract description 70
- 239000000463 material Substances 0.000 claims abstract description 29
- 238000005260 corrosion Methods 0.000 claims abstract description 27
- 230000007797 corrosion Effects 0.000 claims abstract description 27
- 238000000137 annealing Methods 0.000 claims abstract description 21
- 239000002243 precursor Substances 0.000 claims abstract description 15
- 229910000831 Steel Inorganic materials 0.000 claims description 183
- 239000010959 steel Substances 0.000 claims description 183
- 229910001566 austenite Inorganic materials 0.000 claims description 134
- OKTJSMMVPCPJKN-UHFFFAOYSA-N Carbon Chemical compound [C] OKTJSMMVPCPJKN-UHFFFAOYSA-N 0.000 claims description 82
- 229910052799 carbon Inorganic materials 0.000 claims description 82
- 238000010438 heat treatment Methods 0.000 claims description 63
- OAICVXFJPJFONN-UHFFFAOYSA-N Phosphorus Chemical compound [P] OAICVXFJPJFONN-UHFFFAOYSA-N 0.000 claims description 55
- 229910052698 phosphorus Inorganic materials 0.000 claims description 55
- 239000011574 phosphorus Substances 0.000 claims description 55
- 230000009466 transformation Effects 0.000 claims description 42
- PWHULOQIROXLJO-UHFFFAOYSA-N Manganese Chemical compound [Mn] PWHULOQIROXLJO-UHFFFAOYSA-N 0.000 claims description 36
- 238000001816 cooling Methods 0.000 claims description 36
- 229910052748 manganese Inorganic materials 0.000 claims description 36
- 239000011572 manganese Substances 0.000 claims description 36
- 230000000717 retained effect Effects 0.000 claims description 36
- 229910000859 α-Fe Inorganic materials 0.000 claims description 26
- CWYNVVGOOAEACU-UHFFFAOYSA-N Fe2+ Chemical compound [Fe+2] CWYNVVGOOAEACU-UHFFFAOYSA-N 0.000 claims description 23
- 230000008569 process Effects 0.000 claims description 21
- RYGMFSIKBFXOCR-UHFFFAOYSA-N Copper Chemical compound [Cu] RYGMFSIKBFXOCR-UHFFFAOYSA-N 0.000 claims description 16
- 229910052802 copper Inorganic materials 0.000 claims description 16
- 239000010949 copper Substances 0.000 claims description 16
- 229910001562 pearlite Inorganic materials 0.000 claims description 16
- 150000001247 metal acetylides Chemical class 0.000 claims description 14
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims description 13
- WPBNNNQJVZRUHP-UHFFFAOYSA-L manganese(2+);methyl n-[[2-(methoxycarbonylcarbamothioylamino)phenyl]carbamothioyl]carbamate;n-[2-(sulfidocarbothioylamino)ethyl]carbamodithioate Chemical compound [Mn+2].[S-]C(=S)NCCNC([S-])=S.COC(=O)NC(=S)NC1=CC=CC=C1NC(=S)NC(=O)OC WPBNNNQJVZRUHP-UHFFFAOYSA-L 0.000 claims description 8
- 230000001351 cycling effect Effects 0.000 claims description 7
- 230000000694 effects Effects 0.000 claims description 6
- 238000005382 thermal cycling Methods 0.000 claims description 4
- 125000004122 cyclic group Chemical group 0.000 claims description 2
- 238000001556 precipitation Methods 0.000 claims description 2
- 238000005507 spraying Methods 0.000 claims description 2
- -1 and methods Substances 0.000 abstract description 2
- 230000001747 exhibiting effect Effects 0.000 abstract description 2
- 230000006698 induction Effects 0.000 description 50
- 238000010791 quenching Methods 0.000 description 33
- 229910000734 martensite Inorganic materials 0.000 description 30
- 230000000171 quenching effect Effects 0.000 description 25
- 229910001563 bainite Inorganic materials 0.000 description 23
- 238000003754 machining Methods 0.000 description 19
- 239000000126 substance Substances 0.000 description 18
- 238000012545 processing Methods 0.000 description 17
- 230000004907 flux Effects 0.000 description 14
- 229910000640 Fe alloy Inorganic materials 0.000 description 13
- 238000013508 migration Methods 0.000 description 11
- 230000005012 migration Effects 0.000 description 11
- 239000000047 product Substances 0.000 description 11
- 238000005452 bending Methods 0.000 description 9
- 239000000203 mixture Substances 0.000 description 9
- 229910000975 Carbon steel Inorganic materials 0.000 description 8
- 238000004090 dissolution Methods 0.000 description 8
- 229910052751 metal Inorganic materials 0.000 description 8
- 239000002184 metal Substances 0.000 description 8
- 229910001021 Ferroalloy Inorganic materials 0.000 description 7
- 238000005275 alloying Methods 0.000 description 7
- 238000000265 homogenisation Methods 0.000 description 7
- 230000001965 increasing effect Effects 0.000 description 6
- 150000003839 salts Chemical class 0.000 description 6
- 208000010392 Bone Fractures Diseases 0.000 description 5
- 206010017076 Fracture Diseases 0.000 description 5
- HCHKCACWOHOZIP-UHFFFAOYSA-N Zinc Chemical compound [Zn] HCHKCACWOHOZIP-UHFFFAOYSA-N 0.000 description 5
- 230000008901 benefit Effects 0.000 description 5
- 239000000919 ceramic Substances 0.000 description 5
- 230000001066 destructive effect Effects 0.000 description 5
- 238000005096 rolling process Methods 0.000 description 5
- 238000011282 treatment Methods 0.000 description 5
- 239000011701 zinc Substances 0.000 description 5
- 229910052725 zinc Inorganic materials 0.000 description 5
- PXHVJJICTQNCMI-UHFFFAOYSA-N Nickel Chemical compound [Ni] PXHVJJICTQNCMI-UHFFFAOYSA-N 0.000 description 4
- 238000004458 analytical method Methods 0.000 description 4
- 230000009286 beneficial effect Effects 0.000 description 4
- 238000010276 construction Methods 0.000 description 4
- 238000005336 cracking Methods 0.000 description 4
- 238000013461 design Methods 0.000 description 4
- 238000005246 galvanizing Methods 0.000 description 4
- 238000003672 processing method Methods 0.000 description 4
- 238000012360 testing method Methods 0.000 description 4
- 229910000851 Alloy steel Inorganic materials 0.000 description 3
- 239000011248 coating agent Substances 0.000 description 3
- 238000000576 coating method Methods 0.000 description 3
- 230000007423 decrease Effects 0.000 description 3
- 239000012467 final product Substances 0.000 description 3
- QMQXDJATSGGYDR-UHFFFAOYSA-N methylidyneiron Chemical compound [C].[Fe] QMQXDJATSGGYDR-UHFFFAOYSA-N 0.000 description 3
- 238000012986 modification Methods 0.000 description 3
- 230000004048 modification Effects 0.000 description 3
- 230000036961 partial effect Effects 0.000 description 3
- 230000002093 peripheral effect Effects 0.000 description 3
- 238000011160 research Methods 0.000 description 3
- 238000005496 tempering Methods 0.000 description 3
- 238000009864 tensile test Methods 0.000 description 3
- 230000000930 thermomechanical effect Effects 0.000 description 3
- 229910001209 Low-carbon steel Inorganic materials 0.000 description 2
- 239000003570 air Substances 0.000 description 2
- 239000012080 ambient air Substances 0.000 description 2
- 230000002902 bimodal effect Effects 0.000 description 2
- 230000015572 biosynthetic process Effects 0.000 description 2
- 238000009529 body temperature measurement Methods 0.000 description 2
- 238000006243 chemical reaction Methods 0.000 description 2
- 239000000470 constituent Substances 0.000 description 2
- 238000011161 development Methods 0.000 description 2
- 238000009826 distribution Methods 0.000 description 2
- 230000009977 dual effect Effects 0.000 description 2
- 238000002474 experimental method Methods 0.000 description 2
- 238000000445 field-emission scanning electron microscopy Methods 0.000 description 2
- 239000011159 matrix material Substances 0.000 description 2
- 238000001000 micrograph Methods 0.000 description 2
- 229910052759 nickel Inorganic materials 0.000 description 2
- 238000002161 passivation Methods 0.000 description 2
- 239000002244 precipitate Substances 0.000 description 2
- 230000009467 reduction Effects 0.000 description 2
- 239000007787 solid Substances 0.000 description 2
- 239000006104 solid solution Substances 0.000 description 2
- 238000000638 solvent extraction Methods 0.000 description 2
- 239000010935 stainless steel Substances 0.000 description 2
- 238000009628 steelmaking Methods 0.000 description 2
- 238000012546 transfer Methods 0.000 description 2
- 241000239290 Araneae Species 0.000 description 1
- 238000012935 Averaging Methods 0.000 description 1
- 229910000712 Boron steel Inorganic materials 0.000 description 1
- 229910001339 C alloy Inorganic materials 0.000 description 1
- 229910000677 High-carbon steel Inorganic materials 0.000 description 1
- 229910000954 Medium-carbon steel Inorganic materials 0.000 description 1
- 229910001294 Reinforcing steel Inorganic materials 0.000 description 1
- 239000000654 additive Substances 0.000 description 1
- 230000002411 adverse Effects 0.000 description 1
- 238000013459 approach Methods 0.000 description 1
- 238000005279 austempering Methods 0.000 description 1
- 239000010962 carbon steel Substances 0.000 description 1
- 238000005524 ceramic coating Methods 0.000 description 1
- 230000008859 change Effects 0.000 description 1
- 238000001311 chemical methods and process Methods 0.000 description 1
- 239000013626 chemical specie Substances 0.000 description 1
- 239000012141 concentrate Substances 0.000 description 1
- 239000000498 cooling water Substances 0.000 description 1
- RKTYLMNFRDHKIL-UHFFFAOYSA-N copper;5,10,15,20-tetraphenylporphyrin-22,24-diide Chemical compound [Cu+2].C1=CC(C(=C2C=CC([N-]2)=C(C=2C=CC=CC=2)C=2C=CC(N=2)=C(C=2C=CC=CC=2)C2=CC=C3[N-]2)C=2C=CC=CC=2)=NC1=C3C1=CC=CC=C1 RKTYLMNFRDHKIL-UHFFFAOYSA-N 0.000 description 1
- 230000008878 coupling Effects 0.000 description 1
- 238000010168 coupling process Methods 0.000 description 1
- 238000005859 coupling reaction Methods 0.000 description 1
- 238000000354 decomposition reaction Methods 0.000 description 1
- 230000001627 detrimental effect Effects 0.000 description 1
- 238000010586 diagram Methods 0.000 description 1
- 229910003460 diamond Inorganic materials 0.000 description 1
- 239000010432 diamond Substances 0.000 description 1
- 230000002708 enhancing effect Effects 0.000 description 1
- 229940116007 ferrous phosphate Drugs 0.000 description 1
- 239000012530 fluid Substances 0.000 description 1
- 231100001261 hazardous Toxicity 0.000 description 1
- BHEPBYXIRTUNPN-UHFFFAOYSA-N hydridophosphorus(.) (triplet) Chemical compound [PH] BHEPBYXIRTUNPN-UHFFFAOYSA-N 0.000 description 1
- AOBAVABSFWTQIX-UHFFFAOYSA-L hydrogen phosphate;iron(2+) Chemical compound [Fe+2].OP([O-])([O-])=O AOBAVABSFWTQIX-UHFFFAOYSA-L 0.000 description 1
- 239000012535 impurity Substances 0.000 description 1
- 238000010348 incorporation Methods 0.000 description 1
- 230000001939 inductive effect Effects 0.000 description 1
- 230000000977 initiatory effect Effects 0.000 description 1
- 229910000155 iron(II) phosphate Inorganic materials 0.000 description 1
- SDEKDNPYZOERBP-UHFFFAOYSA-H iron(ii) phosphate Chemical compound [Fe+2].[Fe+2].[Fe+2].[O-]P([O-])([O-])=O.[O-]P([O-])([O-])=O SDEKDNPYZOERBP-UHFFFAOYSA-H 0.000 description 1
- 239000007788 liquid Substances 0.000 description 1
- 230000005426 magnetic field effect Effects 0.000 description 1
- 238000010297 mechanical methods and process Methods 0.000 description 1
- 239000000155 melt Substances 0.000 description 1
- 150000002739 metals Chemical class 0.000 description 1
- 230000003287 optical effect Effects 0.000 description 1
- 238000005457 optimization Methods 0.000 description 1
- 235000012771 pancakes Nutrition 0.000 description 1
- 230000035515 penetration Effects 0.000 description 1
- 125000004437 phosphorous atom Chemical group 0.000 description 1
- 238000007781 pre-processing Methods 0.000 description 1
- 230000000750 progressive effect Effects 0.000 description 1
- 230000005855 radiation Effects 0.000 description 1
- 230000002829 reductive effect Effects 0.000 description 1
- 230000002441 reversible effect Effects 0.000 description 1
- 238000012552 review Methods 0.000 description 1
- 238000013341 scale-up Methods 0.000 description 1
- 238000006748 scratching Methods 0.000 description 1
- 230000002393 scratching effect Effects 0.000 description 1
- 238000000926 separation method Methods 0.000 description 1
- 238000007493 shaping process Methods 0.000 description 1
- 239000000243 solution Substances 0.000 description 1
- 125000006850 spacer group Chemical group 0.000 description 1
- 230000000087 stabilizing effect Effects 0.000 description 1
- 229910001220 stainless steel Inorganic materials 0.000 description 1
- 238000011426 transformation method Methods 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
- 238000009966 trimming Methods 0.000 description 1
- 238000005406 washing Methods 0.000 description 1
- 239000008207 working material Substances 0.000 description 1
Images
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/34—Methods of heating
- C21D1/42—Induction heating
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/18—Hardening; Quenching with or without subsequent tempering
- C21D1/19—Hardening; Quenching with or without subsequent tempering by interrupted quenching
- C21D1/20—Isothermal quenching, e.g. bainitic hardening
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/26—Methods of annealing
- C21D1/32—Soft annealing, e.g. spheroidising
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
- C21D1/62—Quenching devices
- C21D1/673—Quenching devices for die quenching
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
- C21D9/52—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for wires; for strips ; for rods of unlimited length
- C21D9/54—Furnaces for treating strips or wire
- C21D9/56—Continuous furnaces for strip or wire
- C21D9/60—Continuous furnaces for strip or wire with induction heating
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/001—Austenite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/002—Bainite
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
- C21D2211/00—Microstructure comprising significant phases
- C21D2211/008—Martensite
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
- Y02P10/00—Technologies related to metal processing
- Y02P10/25—Process efficiency
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Mechanical Engineering (AREA)
- Materials Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Heat Treatment Of Articles (AREA)
- Heat Treatment Of Steel (AREA)
Applications Claiming Priority (7)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US201462013396P | 2014-06-17 | 2014-06-17 | |
| US62/013,396 | 2014-06-17 | ||
| US201462093731P | 2014-12-18 | 2014-12-18 | |
| US62/093,731 | 2014-12-18 | ||
| US201562100373P | 2015-01-06 | 2015-01-06 | |
| US62/100,373 | 2015-01-06 | ||
| CN201580032939.9A CN106414787B (zh) | 2014-06-17 | 2015-06-17 | 高强度铁基合金、其制造方法和由其得到的制品 |
Related Parent Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CN201580032939.9A Division CN106414787B (zh) | 2014-06-17 | 2015-06-17 | 高强度铁基合金、其制造方法和由其得到的制品 |
Publications (2)
| Publication Number | Publication Date |
|---|---|
| CN110042313A CN110042313A (zh) | 2019-07-23 |
| CN110042313B true CN110042313B (zh) | 2021-11-30 |
Family
ID=54936087
Family Applications (2)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CN201910163334.3A Active CN110042313B (zh) | 2014-06-17 | 2015-06-17 | 高强度铁基合金、其制造方法和由其得到的制品 |
| CN201580032939.9A Active CN106414787B (zh) | 2014-06-17 | 2015-06-17 | 高强度铁基合金、其制造方法和由其得到的制品 |
Family Applications After (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| CN201580032939.9A Active CN106414787B (zh) | 2014-06-17 | 2015-06-17 | 高强度铁基合金、其制造方法和由其得到的制品 |
Country Status (8)
| Country | Link |
|---|---|
| US (1) | US20170145528A1 (enExample) |
| EP (1) | EP3158100A4 (enExample) |
| JP (2) | JP2017524813A (enExample) |
| CN (2) | CN110042313B (enExample) |
| AU (1) | AU2015277142A1 (enExample) |
| CA (1) | CA2952255C (enExample) |
| MX (2) | MX2016016888A (enExample) |
| WO (1) | WO2015195851A1 (enExample) |
Families Citing this family (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| US10961599B2 (en) | 2016-07-20 | 2021-03-30 | Hyundai Motor Company | Lightweight door beam, composition thereof and method of manufacturing the same |
| KR101936478B1 (ko) * | 2016-12-15 | 2019-01-08 | 현대자동차주식회사 | 입체냉각방식 핫 스템핑 공법과 핫 스템핑 시스템 |
| WO2019079763A1 (en) * | 2017-10-19 | 2019-04-25 | Cola Gary M Jr | HIGH STRENGTH STEELS, METHODS OF MANUFACTURE THEREOF AND ARTICLES RESULTING FROM THE SAME |
Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN1316018A (zh) * | 1999-06-30 | 2001-10-03 | 新日本制铁株式会社 | 可冷加工钢棒或钢丝及其生产工艺 |
| CN101029351A (zh) * | 2007-04-02 | 2007-09-05 | 马鞍山钢铁股份有限公司 | 中碳钢形变诱导铁素体超量析出生产方法 |
| CN101845599A (zh) * | 2009-03-24 | 2010-09-29 | 宝山钢铁股份有限公司 | 一种耐候钢及其制造方法 |
| CN102575311A (zh) * | 2009-10-12 | 2012-07-11 | 斯奈克玛 | 矿渣层下再熔后的马氏体不锈钢的热处理 |
| CN103215421A (zh) * | 2012-01-20 | 2013-07-24 | 通用汽车环球科技运作有限责任公司 | 用于制造高强度和延展性的钢板的热处理 |
Family Cites Families (16)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| JPS63115654A (ja) * | 1986-11-05 | 1988-05-20 | Mitsubishi Heavy Ind Ltd | 金属薄板鋳造方法及び装置 |
| US6395108B2 (en) * | 1998-07-08 | 2002-05-28 | Recherche Et Developpement Du Groupe Cockerill Sambre | Flat product, such as sheet, made of steel having a high yield strength and exhibiting good ductility and process for manufacturing this product |
| JP2002363650A (ja) * | 2001-06-07 | 2002-12-18 | Kobe Steel Ltd | シーム溶接性に優れた超高強度冷延鋼板の製造方法 |
| US10174390B2 (en) * | 2006-10-03 | 2019-01-08 | Gary M. Cola, JR. | Microtreatment of iron-based alloy, apparatus and method therefor, and articles resulting therefrom |
| US20100163140A1 (en) * | 2008-06-16 | 2010-07-01 | Cola Jr Gary M | Microtreatment of Iron-Based Alloy, Apparatus and Method Therefor, and Microstructure Resulting Therefrom |
| JP5493986B2 (ja) * | 2009-04-27 | 2014-05-14 | Ｊｆｅスチール株式会社 | 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法 |
| JP4977879B2 (ja) * | 2010-02-26 | 2012-07-18 | Ｊｆｅスチール株式会社 | 曲げ性に優れた超高強度冷延鋼板 |
| JP5466576B2 (ja) * | 2010-05-24 | 2014-04-09 | 株式会社神戸製鋼所 | 曲げ加工性に優れた高強度冷延鋼板 |
| JP5740908B2 (ja) * | 2010-10-20 | 2015-07-01 | 新日鐵住金株式会社 | 冷間鍛造後の急速加熱焼入れ性に優れた中炭素鋼板の焼入れ方法 |
| JP5856002B2 (ja) * | 2011-05-12 | 2016-02-09 | Ｊｆｅスチール株式会社 | 衝突エネルギー吸収能に優れた自動車用衝突エネルギー吸収部材およびその製造方法 |
| CN102828119A (zh) * | 2011-06-14 | 2012-12-19 | 鞍钢股份有限公司 | 高弯曲型980MPa级冷轧双相钢及其制备工艺 |
| JP5825185B2 (ja) * | 2012-04-18 | 2015-12-02 | 新日鐵住金株式会社 | 冷延鋼板およびその製造方法 |
| CA2877175C (en) * | 2012-05-25 | 2023-07-25 | Gary M. Cola | Microtreatment and microstructure of carbide containing iron-based alloy |
| JP5821794B2 (ja) * | 2012-07-18 | 2015-11-24 | 新日鐵住金株式会社 | 焼入れ鋼材およびその製造方法ならびに焼入れ用鋼材 |
| JP5906154B2 (ja) * | 2012-07-20 | 2016-04-20 | 株式会社神戸製鋼所 | 耐遅れ破壊性に優れた高強度鋼板およびその製造方法 |
| JP2016020537A (ja) * | 2014-06-16 | 2016-02-04 | 株式会社神戸製鋼所 | 冷間加工用機械構造用鋼及びその製造方法 |
-
2015
- 2015-06-07 US US15/319,710 patent/US20170145528A1/en not_active Abandoned
- 2015-06-17 WO PCT/US2015/036313 patent/WO2015195851A1/en not_active Ceased
- 2015-06-17 JP JP2016573965A patent/JP2017524813A/ja active Pending
- 2015-06-17 AU AU2015277142A patent/AU2015277142A1/en not_active Abandoned
- 2015-06-17 CA CA2952255A patent/CA2952255C/en active Active
- 2015-06-17 CN CN201910163334.3A patent/CN110042313B/zh active Active
- 2015-06-17 CN CN201580032939.9A patent/CN106414787B/zh active Active
- 2015-06-17 MX MX2016016888A patent/MX2016016888A/es unknown
- 2015-06-17 EP EP15809902.8A patent/EP3158100A4/en not_active Withdrawn
-
2016
- 2016-12-16 MX MX2023007656A patent/MX2023007656A/es unknown
-
2020
- 2020-12-01 JP JP2020199811A patent/JP2021046611A/ja active Pending
Patent Citations (5)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| CN1316018A (zh) * | 1999-06-30 | 2001-10-03 | 新日本制铁株式会社 | 可冷加工钢棒或钢丝及其生产工艺 |
| CN101029351A (zh) * | 2007-04-02 | 2007-09-05 | 马鞍山钢铁股份有限公司 | 中碳钢形变诱导铁素体超量析出生产方法 |
| CN101845599A (zh) * | 2009-03-24 | 2010-09-29 | 宝山钢铁股份有限公司 | 一种耐候钢及其制造方法 |
| CN102575311A (zh) * | 2009-10-12 | 2012-07-11 | 斯奈克玛 | 矿渣层下再熔后的马氏体不锈钢的热处理 |
| CN103215421A (zh) * | 2012-01-20 | 2013-07-24 | 通用汽车环球科技运作有限责任公司 | 用于制造高强度和延展性的钢板的热处理 |
Also Published As
| Publication number | Publication date |
|---|---|
| EP3158100A4 (en) | 2018-02-28 |
| WO2015195851A1 (en) | 2015-12-23 |
| EP3158100A1 (en) | 2017-04-26 |
| JP2017524813A (ja) | 2017-08-31 |
| CA2952255C (en) | 2023-07-25 |
| MX2016016888A (es) | 2017-07-27 |
| AU2015277142A1 (en) | 2017-02-02 |
| CN106414787A (zh) | 2017-02-15 |
| CN106414787B (zh) | 2020-07-14 |
| CA2952255A1 (en) | 2015-12-23 |
| MX2023007656A (es) | 2023-07-07 |
| JP2021046611A (ja) | 2021-03-25 |
| US20170145528A1 (en) | 2017-05-25 |
| CN110042313A (zh) | 2019-07-23 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| CN106011418B (zh) | 用于获得梯度化性能的处理工艺及其构件 | |
| US8518195B2 (en) | Heat treatment for producing steel sheet with high strength and ductility | |
| BRPI0912879A2 (pt) | processo de fabricação de chapas de aços fase dual laminadas a frio com resistência muito elevada e chapas assim produzidas | |
| KR20170106480A (ko) | 핫 스탬핑용 강판, 핫 스탬핑 방법 및 핫 스탬핑된 부품 | |
| US11519050B2 (en) | Method for producing a re-shaped component from a manganese-containing flat steel product and such a component | |
| KR102006963B1 (ko) | 강 반제품의 열간성형에 의해 부품을 생산하기 위한 방법 | |
| CN104641006B (zh) | 含碳化物的铁基合金的微处理和微结构 | |
| CN110042313B (zh) | 高强度铁基合金、其制造方法和由其得到的制品 | |
| RU2722786C1 (ru) | Способ изготовления подвергнутой формованию детали из плоского стального продукта со средним содержанием марганца и такая деталь | |
| KR20170106973A (ko) | 높은 인장 강도의 강철 와이어 | |
| US20100163140A1 (en) | Microtreatment of Iron-Based Alloy, Apparatus and Method Therefor, and Microstructure Resulting Therefrom | |
| JP2017524813A5 (enExample) | ||
| JP5870825B2 (ja) | 合金化溶融亜鉛めっき熱延鋼板およびその製造方法 | |
| JP6068570B2 (ja) | 高強度鋼板の焼きなましプロセス | |
| US20170335418A1 (en) | High strength iron-based alloys, processes for making same, and articles resulting therefrom | |
| JP5682828B2 (ja) | せん断加工部品およびその製造方法 | |
| RU2081182C1 (ru) | Способ термической обработки проката | |
| RU2169198C2 (ru) | Способ термомеханической обработки проката | |
| Pan et al. | Processing and stability of ultrafine grained structures in some microalloy steels | |
| JPH0735537B2 (ja) | 高延性高強度熱延鋼板の製造方法 |
Legal Events
| Date | Code | Title | Description |
|---|---|---|---|
| PB01 | Publication | ||
| PB01 | Publication | ||
| SE01 | Entry into force of request for substantive examination | ||
| SE01 | Entry into force of request for substantive examination | ||
| GR01 | Patent grant | ||
| GR01 | Patent grant |