CN110042014A - A kind of kitchen pipeline mild dredging agent - Google Patents
A kind of kitchen pipeline mild dredging agent Download PDFInfo
- Publication number
- CN110042014A CN110042014A CN201910135371.3A CN201910135371A CN110042014A CN 110042014 A CN110042014 A CN 110042014A CN 201910135371 A CN201910135371 A CN 201910135371A CN 110042014 A CN110042014 A CN 110042014A
- Authority
- CN
- China
- Prior art keywords
- parts
- dredging
- mixing
- mild
- pipeline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of kitchen pipeline mild dredging agents, belong to duct cleaning technical field.The present invention solves the problems, such as the alkalinity of common pipe-dredging agent itself at present and causes that pipeline local temperature is excessively high and damages pipeline.Ferrous nitrate and ferric nitrate of the invention is generated under alkaline system into nano ferriferrous oxide, plays cooling osmosis to the pipeline of obstruction, and obturator part is cooled and is shunk, and obstruction is hindered to be formed.The present invention is added to containing seleno reagent, can be reacted under low temperature with iron plasma, be generated metal selenide, cooperate subsequent foaming, viscosity reduction effect, it can be rapidly achieved dredging effect, the phosphatide of addition has emulsification, to destroy the blockage structure of the sundries such as grease, dish leaf formation.After gas overflowing, micro-bubble is adsorbable around grease, and cooperation contains carbon dioxide and obtains polyallylamine, with the infiltration to obturator, further functions as viscosity reduction, dredging effect, can avoid damaging the corrosion of pipeline and high temperature.
Description
Technical field
The invention belongs to duct cleaning technical fields, and in particular to a kind of kitchen pipeline mild dredging agent.
Background technique
With the update of technology, unclog the pipe is no longer limited only to using huge tool or drain cleaner etc
Instrument is operated, and can easily solve the problems, such as line clogging using pipe-dredging agent.Domestic pipeline dredging agent, at present
It is broadly divided into liquid-type and solid type two major classes product.Liquid-type product easy-to-leak liquid during transportation, risk is higher, and
Liquid-type product is not too big for blocking more serious pipeline, effect.Solid type product, mostly using caustic alkali as main component,
It may be because the case where moment local temperature rises too high and causes pipeline temperature distortion after contacting with water, it cannot be with pipe in pipeline
The position of pipeline dredging agent contact, cannot also clear up.In the prior art, in order to meet user it is satiny to the feel of paper for daily use,
Be of close texture, it is soft it is flexible, meet water and the demands such as will not fester quickly, it will usually PAE (polyamides is added in paper production
Amine epichlorohydrin resin).Since PAE has positive charge, and easily it is adsorbed on the fiber with negative electrical charge, PART EPOXY
Base and hydroxyl generate ehter bond, form reticular structure in fiber interface, the activity between fiber are limited, to improve the wet of paper
Intensity.In this way, the dry strength of paper is not only increased, can also make paper that there is certain wet strength, in certain journey
Meets the needs of user is to paper on degree.
However, if above-mentioned paper is used as cleaning toilet paper, tissue or the paper that washes one's face etc., higher wet strength, in the wink of water punching
Between be not easy the problem of decomposing completely, line clogging may be caused.Meanwhile it is clean on the market and used in daily life at present
The cleaning supplies such as lavatory treasured, detergent for toilet, toilet-cleaning paste more the effect of tending to disinfection and sterilization, decontamination, deodorization, have ignored toilet bowl, Asiatic water closet pan,
The susceptible to plugging problem of the pipelines such as hand basin, and the phenomenon that leading to line clogging, is commonplace and serious, brings pole to user's life
It is big inconvenient.
Sewer pipe easily deposits the sundries such as hair, grease, dish leaf, meal slag and makes line clogging, brings very to people's life
Big inconvenience.The method of tradition machinery dredging is generallyd use to remove the tamper in sewer, but this method it is time-consuming, it is laborious,
Higher cost, and remove and be not thorough.Sewer line dredging agent is exactly the product for solving the problems, such as this, applied widely, can
Effectively to dredge blockage of sewer caused by a variety of causes such as hair, grease, dish leaf, excrement and papery clast, simultaneously also
It can remove odors, eliminate germ, except roach desinsection, the secondary blocking of prevention pipeline etc., be the good assistant of family kitchen and bath.Currently, being applicable in
Dredging cleaning agent in sewer pipe surface mainly has 3 seed types: cleanser, and primary raw material is dolomite dust or calcite in powder,
Only play mechanical friction, decontamination, the stifled effect of change are poor;Alkali metal type, this dredging agent are stronger to the decomposition of hair,
It is at low cost, but ingredient is more single, and the dosage of alkali is larger, and improper use can cause certain corrosion to pipe surface, to human body
There is potential injury in skin;Without alkali metal type, action temperature and, strong detergency, the line clogging caused by grease have compared with
Good dredging effect, but it is unobvious to line clogging effect caused by hair etc..In view of above-mentioned 3 seed type sewer line dredging agent
Existing advantage and disadvantage develop a kind of potent sewer line dredging agent, to further push the technology in sewer line dredging field
Development.Product passes through effervescent effect energy fast foaming at low temperature, improves the solution rate of product, can make pipe-dredging agent
Rapid dispersion makes tamper dissolution, dispersion, swelling to each position of duct wall, thus unclog the pipe, and kill bacterium.Meanwhile it producing
Product also pass through the steady thermal discharge of effervescent effect, reduce moment local temperature and rise too high bring risk, do not easily cause pipe
Road deformation.
Summary of the invention
The technical problems to be solved by the invention: for the current alkalinity for commonly using pipe-dredging agent itself and pipeline office is caused
Portion's temperature is excessively high and the problem of damaging pipeline, a kind of kitchen pipeline mild dredging agent is provided.
In order to solve the above technical problems, the present invention is using technical solution as described below:
A kind of kitchen pipeline mild dredging agent, including following component: 3 ~ 7 parts of trim,ethylchlorosilanes, 1 ~ 4 part of bentonite, 3 ~ 7 parts
Surfactant, 2 ~ 5 parts of foaming agents, which is characterized in that further include: 25 ~ 40 parts of compound dredging base-materials, 12 ~ 20 parts of composite auxiliary materials.
The preparation method of the compound dredging base-material, includes the following steps:
(1) in 25 ~ 35 DEG C, according to parts by weight, 8 ~ 15 parts of ferrous nitrates, 15 ~ 30 parts of ferric nitrates, 80 ~ 100 parts of water mixing are taken,
PH is adjusted, mixed liquid is obtained, takes mixed liquid that the Tween-80 of the lecithin of mixed liquid quality 3 ~ 7%, mixed liquid quality 5 ~ 8%, constant temperature stirring is added
Mixing, heat preservation is still aging, obtains ageing liquid, takes ageing liquid to be concentrated under reduced pressure, obtains concentrate, take concentrate mist projection granulating, obtain hollow
Nano-beads;
(2) in 1 ~ 4 DEG C, 1:0.04:6 ~ 10 take trash ice, additive, water mixing in mass ratio, obtain trash ice liquid, according to the mass fraction,
Take 40 ~ 60 parts of trash ice liquid, 6 ~ 10 parts of hollow Nano pearls, 10 ~ 15 parts of dehydrated alcohols, 12 ~ 20 parts of polyethylene glycol, 7 ~ 12 parts of citric acids
Solution, 2 ~ 5 parts of auxiliary agents, 8 ~ 14 parts of polymerization material first take trash ice liquid, hollow Nano pearl, dehydrated alcohol, polyethylene glycol mixed in 2 ~ 5 DEG C
Stirring is closed, citric acid solution, auxiliary agent, polymerization material is added, high-speed stirred vacuumizes concentration, refrigerates to get compound dredging base-material.
Additive in the step (2): 1:3 ~ 7 take lactose, mannitol mixing to get additive in mass ratio.
Polymerization material in the step (2): in 28 ~ 40 DEG C, according to parts by weight, 30 ~ 50 parts of acrylic acid, 16 ~ 25 part third
Acrylamide, 0.3 ~ 0.6 part of N, N- methylene-bisacrylamide, 2 ~ 5 parts of castor oil, 7 ~ 14 parts of nonylphenol polyoxyethylene ether, 25 ~ 40
Part NaOH solution mixing, leads to nitrogen protection, and stirring is warming up to 70 ~ 85 DEG C, and the over cure potassium that acrylic acid quality 1 ~ 4% is added mixes
It closes, constant temperature is stirred to react, and discharging is to get polymerization material.
Auxiliary agent in the step (2): 1:2 ~ 4:1 in mass ratio takes microcrystalline wax, magnesium stearate, castor oil mixing, i.e.,
Obtain auxiliary agent.
The preparation of the composite auxiliary material: according to parts by weight, successively take 6 ~ 14 parts containing seleno reagent, 3 ~ 7 parts of benzyl carbinols, 10 ~
20 parts of lauryl alcohols, 8 ~ 15 parts of polyallylamines, 10 ~ 18 parts of fermentation materials, 4 ~ 8 parts of potassium nitrate, 3 ~ 7 parts of sodium nitrites, first 27 ~ 35 DEG C,
It takes lauryl alcohol, polyallylamine to be mixed, is warming up to 40 ~ 55 DEG C, organic selenium, benzyl carbinol, fermentation material, potassium nitrate and nitrous is added
Sour sodium is mixed, and is passed through carbon dioxide gas, boosts, and heat-insulation pressure keeping processing is to get composite auxiliary material.
The seleno reagent that contains: 4 ~ 8:3 in mass ratio takes hexichol selenide, the mixing of two selenium of hexichol to get containing seleno reagent.
The fermentation material: according to the mass fraction, take 6 ~ 10 parts of wormcasts, 5 ~ 8 portions of beef extracts, 7 ~ 12 parts of glucose, 0.1 ~
0.4 part of NaH2PO4, 2 ~ 5 parts of lactobacillus bulgaricus powder, 3 ~ 7 parts of caseins, 300 ~ 500 parts of water mixing, in 28 ~ 32 DEG C, concussion is shaken
Bed fermented and cultured, sterilizes, filtering, collects filtrate to get fermentation material.
The foaming agent: 3 ~ 6:1 in mass ratio takes sodium sulfate of polyethenoxy ether of fatty alcohol, petroleum ether mixing to get foaming
Agent.
The surfactant: 2 ~ 4:1 in mass ratio takes dodecyldimethylammonium hydroxide inner salt, secondary alkyl benzene sulfonic acid sodium salt mixed
It closes to get surfactant.
The present invention is compared with other methods, and advantageous effects are:
(1) for the present invention with the raw materials hollow Nano pearl such as ferrous nitrate, ferric nitrate, ferrous nitrate and ferric nitrate can be in alkaline systems
Lower to generate into nano ferriferrous oxide, ageing generation nano ferriferrous oxide is adsorbable and is scattered in this compound dredging base-material,
Induction promotes moisture quickly to freeze and forms ice crystal, and hollow Nano pearl is under the action ofs polyethylene glycol, additive etc., uniform and stable
Property be maintained, to be conducive to induce and promote to form ice crystal in system, cooling osmosis is played to the pipeline of obstruction, and
So that obturator part is cooled and shrinks, it is convenient for subsequent osmosis, during fermentation material processed, can produce a variety of small molecules
Ingredient rapid dispersion can permeate in the lubricant component of blocking, hinder obstruction to be formed, improve viscosity reducing effect;
(2) present invention is added to containing seleno reagent, can be reacted under low temperature and with iron plasma, and metal selenide is generated,
In process of osmosis, it can be longitudinally formed metal selenide thin film in the pipeline of obstruction, play special adsorption, cooperate subsequent foaming, drop
Viscous effect can reduce the pile-up effect between line clogging object, during used, make in the thermal energy of hot water and the pressure poured into
Under, it can be rapidly achieved dredging effect, the phosphatide of addition has good emulsification, and the polar group in molecular structure can be stretched
It opens up in tamper, plays the role of emulsion dispersion, and phospholipid molecule has more negative electrical charge, can lead to partial charge imbalance,
It is mutually exclusive, to destroy the blockage structure of the sundries such as grease, dish leaf formation, dredging effect is improved, in addition, addition trimethyl chlorine
Silane can cooperate the lecithin with parental type molecular structure again, form organosilicon-phospholipid bilayer lubrication system, improve dredging effect
Fruit;
(3) present invention is polymerize with systems such as acrylic acid, acrylamides and is expected, being scattered in pipeline can first cooperate fermentation material etc. to permeate, with
Grease therein combines, and will be slow expansion, is formed and is squeezed to the structure of dish leaf and grease formation in obstruction pipeline, and polymerize
Material is internal during the preparation process to contain portion gas, and in use, after gas overflowing, micro-bubble is adsorbable in grease week
It encloses, cooperation contains carbon dioxide and obtains polyallylamine, the infiltration with the present invention to obturator, during hot and cold alternation, can allow CO2
Equal gases constantly generate, and further function as viscosity reduction, dredging effect;
(4) low temperature osmotic first is carried out to obstruction pipeline when the present invention uses, lubrication, viscosity reduction adds hot water, with cold and hot thermal gradient energy
Amount effect improves dredging efficiency, avoids common pipe-dredging agent using caustic alkali as main component, meeting is because of moment after contacting with water
The drawbacks of local temperature rises too high and causes pipeline heated and damage can avoid damaging the corrosion of pipeline and high temperature.
Specific embodiment
Auxiliary agent: 1:2 ~ 4:1 in mass ratio takes microcrystalline wax, magnesium stearate, castor oil mixing to get auxiliary agent.
Containing seleno reagent: 4 ~ 8:3 in mass ratio takes hexichol selenide, the mixing of two selenium of hexichol to get containing seleno reagent.
Fermentation material: according to the mass fraction, 6 ~ 10 parts of wormcasts, 5 ~ 8 portions of beef extracts, 7 ~ 12 parts of glucose, 0.1 ~ 0.4 part are taken
NaH2PO4, 2 ~ 5 parts of lactobacillus bulgaricus powder, 3 ~ 7 parts of caseins, 300 ~ 500 parts of water mixed in fermentor, in 28 ~ 32 DEG C, with
180 ~ 220r/min shakes shaker fermentation culture 3 ~ 5 days, and in 100 ~ 110 DEG C of 12 ~ 20min of insulated sterilizing, filtrate is collected in filtering,
Up to fermentation material.
Foaming agent: 3 ~ 6:1 in mass ratio takes sodium sulfate of polyethenoxy ether of fatty alcohol, petroleum ether mixing to get foaming agent.
Surfactant: 2 ~ 4:1 in mass ratio takes dodecyldimethylammonium hydroxide inner salt, the mixing of secondary alkyl benzene sulfonic acid sodium salt, i.e.,
Obtain surfactant.
Polymerization material: in 28 ~ 40 DEG C, according to parts by weight, 30 ~ 50 parts of acrylic acid, 16 ~ 25 parts of acrylamides, 0.3 ~ 0.6 part
N, N- methylene-bisacrylamide, 2 ~ 5 parts of castor oil, 7 ~ 14 parts of nonylphenol polyoxyethylene ether, 25 ~ 40 parts of mass fractions are 20%
NaOH solution mixed in reaction kettle, logical nitrogen protection is warming up to 70 ~ 85 with 400 ~ 700r/min, 35 ~ 60min of magnetic agitation
DEG C, the over cure potassium mixing of acrylic acid quality 1 ~ 4% is added, constant temperature is stirred to react 2 ~ 4h, and discharging is to get polymerization material.
Additive: 1:3 ~ 7 take lactose, mannitol mixing to get additive in mass ratio.
The preparation method of compound dredging base-material, includes the following steps:
(1) in 25 ~ 35 DEG C, according to parts by weight, 8 ~ 15 parts of ferrous nitrates, 15 ~ 30 parts of ferric nitrates, 80 ~ 100 parts of water Yu Fanying are taken
Kettle mixing adjusts pH to 8.0 ~ 8.5 with the sodium hydroxide solution of mass fraction 15%, obtains mixed liquid, take mixed liquid be added mixed liquid quality 3 ~
The Tween-80 of 7% lecithin, mixed liquid quality 5 ~ 8%, constant temperature are stirred 45 ~ 60min, keep the temperature still aging 2 ~ 4h, obtain old
Change liquid, take ageing liquid in 75 ~ 80 DEG C, be concentrated under reduced pressure into the 25 ~ 40% of original volume, obtain concentrate, it is spraying to be delivered to take concentrate
Drier is 90 ~ 100 DEG C in inlet air temperature, and under the conditions of leaving air temp is 75 ~ 85 DEG C, mist projection granulating obtains hollow nano-beads;
(2) in 1 ~ 4 DEG C, 1:0.04:6 ~ 10 take trash ice, additive, the water mixing that partial size is 0.2 ~ 0.5mm in mass ratio, obtain broken
Ice liquid, according to the mass fraction, take 40 ~ 60 parts of trash ice liquid, 6 ~ 10 parts of hollow Nano pearls, 10 ~ 15 parts of dehydrated alcohols, 12 ~ 20 parts it is poly-
Ethylene glycol, the citric acid solution that 7 ~ 12 parts of mass fractions are 20%, 2 ~ 5 parts of auxiliary agents, 8 ~ 14 parts of polymerizations are expected, in 2 ~ 5 DEG C, are first taken broken
Ice liquid, hollow Nano pearl, dehydrated alcohol, polyethylene glycol are mixed in reaction kettle, with 400 ~ 700r/min, 40 ~ 60min of stirring, then plus
Enter citric acid solution, auxiliary agent, polymerization material, with 2000 ~ 3000r/min, 45 ~ 60min of high-speed stirred, vacuumizes and be concentrated into original volume
20 ~ 40%, in 1 ~ 4 DEG C of refrigerator cold-storage to get compound dredging base-material.
The preparation of composite auxiliary material: according to parts by weight, 6 ~ 14 parts are successively taken to contain seleno reagent, 3 ~ 7 parts of benzyl carbinols, 10 ~ 20 parts
Lauryl alcohol, 8 ~ 15 parts of polyallylamines, 10 ~ 18 parts of fermentation materials, 4 ~ 8 parts of potassium nitrate, 3 ~ 7 parts of sodium nitrites, take ten by first 27 ~ 35 DEG C
Glycol, polyallylamine are mixed in reaction kettle, after stirring 2 ~ 5h with 500 ~ 800r/min, are warming up to 40 ~ 55 DEG C, be added organic selenium,
Benzyl carbinol, fermentation material, potassium nitrate and sodium nitrite mixing, after stirring 2 ~ 4h with 1500 ~ 2000r/min, with 100 ~ 130mL/min
Rate is passed through carbon dioxide gas, boosts to 3.2 ~ 4.8MPa, and heat-insulation pressure keeping handles 30 ~ 50min to get composite auxiliary material.
A kind of compound dredging base-material, according to the mass fraction, including following component: 3 ~ 7 parts of tartaric acid, 1 ~ 4 part of bentonite, 3 ~ 7
Part surfactant, 2 ~ 5 parts of foaming agents, 25 ~ 40 parts of compound dredging base-materials, 12 ~ 20 parts of composite auxiliary materials.
A kind of kitchen pipeline preparation method of mild dredging agent, includes the following steps:
(1) according to the mass fraction, 3 ~ 7 parts of trim,ethylchlorosilanes, 1 ~ 4 part of bentonite, 3 ~ 7 parts of surfactants, 2 ~ 5 parts of foaming are taken
Agent, 25 ~ 40 parts of compound dredging base-materials, 12 ~ 20 parts of composite auxiliary materials;
(2) prior to 28 ~ 35 DEG C, surfactant, bentonite, foaming agent, composite auxiliary material is taken to mix in reaction kettle, with 400 ~ 700r/
Min 35 ~ 60min of magnetic agitation is cooled to 3 ~ 7 DEG C, compound dredging base-material, trim,ethylchlorosilane mixing is added, with 500 ~ 800r/
After 40 ~ 60min of min magnetic agitation, in 1 ~ 4 DEG C of refrigerator cold-storage to get pipe-dredging agent.
A kind of application method of kitchen pipeline mild dredging agent: take the pipe-dredging agent of refrigeration by 300 ~ 500g/cm3
Amount (volume of dosage/obstructive position used) pour into the pipeline of obstruction, after standing 6 ~ 10min, pour into pipe-dredging agent used
3 ~ 6 times of quality of 45 ~ 55 DEG C of hot water.
Embodiment 1
Auxiliary agent: 1:2:1 in mass ratio takes microcrystalline wax, magnesium stearate, castor oil mixing to get auxiliary agent.
Containing seleno reagent: 4:3 in mass ratio takes hexichol selenide, the mixing of two selenium of hexichol to get containing seleno reagent.
Fermentation material: according to the mass fraction, 6 parts of wormcasts, 5 portions of beef extracts, 7 parts of glucose, 0.1 part of NaH are taken2PO4, 2 parts protect
Add Leah lactobacillus powder, 3 parts of caseins, 300 parts of water to mix in fermentor, in 28 DEG C, shaker fermentation culture 3 is shaken with 180r/min
It, in 100 DEG C of insulated sterilizing 12min, filtering collects filtrate to get fermentation material.
Foaming agent: 3:1 in mass ratio takes sodium sulfate of polyethenoxy ether of fatty alcohol, petroleum ether mixing to get foaming agent.
Surfactant: 2:1 in mass ratio take dodecyldimethylammonium hydroxide inner salt, secondary alkyl benzene sulfonic acid sodium salt mixing to get
Surfactant.
Polymerization material: in 28 DEG C, according to parts by weight, and 30 parts of acrylic acid, 16 parts of acrylamides, 0.3 part of N, N- di-2-ethylhexylphosphine oxide
The NaOH solution that acrylamide, 2 parts of castor oil, 7 parts of nonylphenol polyoxyethylene ether, 25 parts of mass fractions are 20% is mixed in reaction kettle
It closes, leads to nitrogen protection, with 400r/min magnetic agitation 35min, be warming up to 70 DEG C, the over cure potassium that acrylic acid quality 1% is added is mixed
It closes, constant temperature is stirred to react 2h, and discharging is to get polymerization material.
Additive: 1:3 in mass ratio takes lactose, mannitol mixing to get additive.
The preparation method of compound dredging base-material, includes the following steps:
(1) it in 25 DEG C, according to parts by weight, takes 8 parts of ferrous nitrates, 15 parts of ferric nitrates, 80 parts of water to mix in reaction kettle, uses quality
The sodium hydroxide solution of score 15% adjusts pH to 8.0, obtains mixed liquid, takes mixed liquid that the lecithin of mixed liquid quality 3%, mixed liquid quality is added
5% Tween-80, constant temperature are stirred 45min, keep the temperature still aging 2h, obtain ageing liquid, take ageing liquid in 75 DEG C, depressurize dense
Be reduced to the 25% of original volume, obtain concentrate, take concentrate to be delivered to spray dryer, in inlet air temperature be 90 DEG C, leaving air temp
Under the conditions of 75 DEG C, mist projection granulating obtains hollow nano-beads;
(2) in 1 DEG C, 1:0.04:6 in mass ratio takes trash ice, additive, the water mixing that partial size is 0.2mm, trash ice liquid is obtained, by matter
Number meter is measured, takes 40 parts of trash ice liquid, 6 parts of hollow Nano pearls, 10 parts of dehydrated alcohols, 12 parts of polyethylene glycol, the 7 parts of mass fractions to be
20% citric acid solution, 2 parts of auxiliary agents, 8 parts of polymerization material, in 2 DEG C, first take trash ice liquid, hollow Nano pearl, dehydrated alcohol, poly- second two
Alcohol is mixed in reaction kettle, stirs 40min with 400r/min, citric acid solution, auxiliary agent, polymerization material is added, with 2000r/min high
Speed stirring 45min, vacuumizes and is concentrated into the 20% of original volume, in 1 DEG C of refrigerator cold-storage to get compound dredging base-material.
The preparation of composite auxiliary material: according to parts by weight, 6 parts are successively taken to contain seleno reagent, 3 parts of benzyl carbinols, 10 parts of lauryl alcohols, 8
Part polyallylamine, 10 parts of fermentation materials, 4 parts of potassium nitrate, 3 parts of sodium nitrites, take lauryl alcohol, polyallylamine in reaction kettle by first 27 DEG C
Mixing after stirring 2h with 500r/min, is warming up to 40 DEG C, organic selenium, benzyl carbinol, fermentation material, potassium nitrate and sodium nitrite is added
Mixing is passed through carbon dioxide gas after stirring 2h with 1500r/min with 100mL/min rate, boosts to 3.2MPa, and heat preservation is protected
30min is to get composite auxiliary material for pressure processing.
A kind of compound dredging base-material, according to the mass fraction, including following component: 3 parts of tartaric acid, 1 part of bentonite, 3 parts of surfaces
Activating agent, 2 parts of foaming agents, 25 parts of compound dredging base-materials, 12 parts of composite auxiliary materials.
A kind of kitchen pipeline preparation method of mild dredging agent, includes the following steps:
(1) according to the mass fraction, take 3 parts of trim,ethylchlorosilanes, 1 part of bentonite, 3 parts of surfactants, 2 parts of foaming agents, 25 parts it is multiple
Close dredging base-material, 12 parts of composite auxiliary materials;
(2) prior to 28 DEG C, surfactant, bentonite, foaming agent, composite auxiliary material is taken to mix in reaction kettle, with 400r/min magnetic force
35min is stirred, is cooled to 3 DEG C, compound dredging base-material, trim,ethylchlorosilane mixing is added, with 500r/min magnetic agitation 40min
Afterwards, in 1 DEG C of refrigerator cold-storage to get pipe-dredging agent.
A kind of application method of kitchen pipeline mild dredging agent: take the pipe-dredging agent of refrigeration by 300g/cm3Amount
(volume of dosage/obstructive position used) pours into the pipeline of obstruction, after standing 6min, pours into 3 times of quality of pipe-dredging agent used
45 DEG C of hot water.
Embodiment 2
Auxiliary agent: 1:3:1 in mass ratio takes microcrystalline wax, magnesium stearate, castor oil mixing to get auxiliary agent.
Containing seleno reagent: 6:3 in mass ratio takes hexichol selenide, the mixing of two selenium of hexichol to get containing seleno reagent.
Fermentation material: according to the mass fraction, 8 parts of wormcasts, 6 portions of beef extracts, 10 parts of glucose, 0.3 part of NaH are taken2PO4, 3 parts
Lactobacillus bulgaricus powder, 5 parts of caseins, 400 parts of water are mixed in fermentor, in 30 DEG C, with 200r/min concussion shaker fermentation training
It supports 4 days, in 105 DEG C of insulated sterilizing 16min, filtering collects filtrate to get fermentation material.
Foaming agent: 5:1 in mass ratio takes sodium sulfate of polyethenoxy ether of fatty alcohol, petroleum ether mixing to get foaming agent.
Surfactant: 3:1 in mass ratio take dodecyldimethylammonium hydroxide inner salt, secondary alkyl benzene sulfonic acid sodium salt mixing to get
Surfactant.
Polymerization material: in 35 DEG C, according to parts by weight, and 40 parts of acrylic acid, 20 parts of acrylamides, 0.4 part of N, N- di-2-ethylhexylphosphine oxide
The NaOH solution that acrylamide, 3 parts of castor oil, 10 parts of nonylphenol polyoxyethylene ether, 30 parts of mass fractions are 20% is mixed in reaction kettle
It closes, leads to nitrogen protection, with 550r/min magnetic agitation 50min, be warming up to 75 DEG C, the over cure potassium that acrylic acid quality 2% is added is mixed
It closes, constant temperature is stirred to react 3h, and discharging is to get polymerization material.
Additive: 1:5 in mass ratio takes lactose, mannitol mixing to get additive.
The preparation method of compound dredging base-material, includes the following steps:
(1) it in 30 DEG C, according to parts by weight, takes 11 parts of ferrous nitrates, 22 parts of ferric nitrates, 90 parts of water to mix in reaction kettle, uses matter
The sodium hydroxide solution for measuring score 15% adjusts pH to 8.3, obtains mixed liquid, takes mixed liquid that the lecithin of mixed liquid quality 5%, mixed liquid matter is added
The Tween-80 of amount 7%, constant temperature are stirred 50min, keep the temperature still aging 3h, obtain ageing liquid, take ageing liquid in 77 DEG C, decompression
Be concentrated into the 35% of original volume, obtain concentrate, take concentrate to be delivered to spray dryer, in inlet air temperature be 95 DEG C, wind-warm syndrome out
Under the conditions of degree is 80 DEG C, mist projection granulating obtains hollow nano-beads;
(2) in 3 DEG C, 1:0.04:8 in mass ratio takes trash ice, additive, the water mixing that partial size is 0.3mm, trash ice liquid is obtained, by matter
Number meter is measured, takes 50 parts of trash ice liquid, 8 parts of hollow Nano pearls, 12 parts of dehydrated alcohols, 16 parts of polyethylene glycol, the 10 parts of mass fractions to be
20% citric acid solution, 3 parts of auxiliary agents, 11 parts of polymerization material, in 4 DEG C, first take trash ice liquid, hollow Nano pearl, dehydrated alcohol, poly- second
Glycol is mixed in reaction kettle, stirs 50min with 550r/min, citric acid solution, auxiliary agent, polymerization material is added, with 2500r/min
High-speed stirred 50min is vacuumized and is concentrated into the 30% of original volume, in 3 DEG C of refrigerator cold-storages to get compound dredging base-material.
The preparation of composite auxiliary material: according to parts by weight, successively take 10 parts containing seleno reagent, 5 parts of benzyl carbinols, 15 parts of lauryl alcohols,
11 parts of polyallylamines, 14 parts of fermentation materials, 6 parts of potassium nitrate, 5 parts of sodium nitrites, take lauryl alcohol, polyallylamine in reaction by first 31 DEG C
Kettle mixing after stirring 4h with 650r/min, is warming up to 50 DEG C, organic selenium, benzyl carbinol, fermentation material, potassium nitrate and nitrous acid is added
Sodium mixing is passed through carbon dioxide gas with 115mL/min rate, boosts to 4.0MPa after stirring 3h with 1700r/min, keeps the temperature
Pressure maintaining handles 40min to get composite auxiliary material.
A kind of compound dredging base-material, according to the mass fraction, including following component: 5 parts of tartaric acid, 2 parts of bentonite, 5 parts of surfaces
Activating agent, 4 parts of foaming agents, 30 parts of compound dredging base-materials, 16 parts of composite auxiliary materials.
A kind of kitchen pipeline preparation method of mild dredging agent, includes the following steps:
(1) according to the mass fraction, take 5 parts of trim,ethylchlorosilanes, 3 parts of bentonite, 5 parts of surfactants, 4 parts of foaming agents, 30 parts it is multiple
Close dredging base-material, 16 parts of composite auxiliary materials;
(2) prior to 32 DEG C, surfactant, bentonite, foaming agent, composite auxiliary material is taken to mix in reaction kettle, with 550r/min magnetic force
50min is stirred, is cooled to 5 DEG C, compound dredging base-material, trim,ethylchlorosilane mixing is added, with 650r/min magnetic agitation 50min
Afterwards, in 3 DEG C of refrigerator cold-storages to get pipe-dredging agent.
A kind of application method of kitchen pipeline mild dredging agent: take the pipe-dredging agent of refrigeration by 400g/cm3Amount
(volume of dosage/obstructive position used) pours into the pipeline of obstruction, after standing 8min, pours into 5 times of quality of pipe-dredging agent used
50 DEG C of hot water.
Embodiment 3
Auxiliary agent: 1:4:1 in mass ratio takes microcrystalline wax, magnesium stearate, castor oil mixing to get auxiliary agent.
Containing seleno reagent: 8:3 in mass ratio takes hexichol selenide, the mixing of two selenium of hexichol to get containing seleno reagent.
Fermentation material: according to the mass fraction, 10 parts of wormcasts, 8 portions of beef extracts, 12 parts of glucose, 0.4 part of NaH are taken2PO4, 5 parts
Lactobacillus bulgaricus powder, 7 parts of caseins, 500 parts of water are mixed in fermentor, in 32 DEG C, with 220r/min concussion shaker fermentation training
It supports 5 days, in 110 DEG C of insulated sterilizing 20min, filtering collects filtrate to get fermentation material.
Foaming agent: 6:1 in mass ratio takes sodium sulfate of polyethenoxy ether of fatty alcohol, petroleum ether mixing to get foaming agent.
Surfactant: 4:1 in mass ratio take dodecyldimethylammonium hydroxide inner salt, secondary alkyl benzene sulfonic acid sodium salt mixing to get
Surfactant.
Polymerization material: in 40 DEG C, according to parts by weight, and 50 parts of acrylic acid, 25 parts of acrylamides, 0.6 part of N, N- di-2-ethylhexylphosphine oxide
The NaOH solution that acrylamide, 5 parts of castor oil, 14 parts of nonylphenol polyoxyethylene ether, 40 parts of mass fractions are 20% is mixed in reaction kettle
It closes, leads to nitrogen protection, with 700r/min magnetic agitation 60min, be warming up to 85 DEG C, the over cure potassium that acrylic acid quality 4% is added is mixed
It closes, constant temperature is stirred to react 4h, and discharging is to get polymerization material.
Additive: 1:7 in mass ratio takes lactose, mannitol mixing to get additive.
The preparation method of compound dredging base-material, includes the following steps:
(1) it in 35 DEG C, according to parts by weight, takes 15 parts of ferrous nitrates, 30 parts of ferric nitrates, 100 parts of water to mix in reaction kettle, uses matter
The sodium hydroxide solution for measuring score 15% adjusts pH to 8.5, obtains mixed liquid, takes mixed liquid that the lecithin of mixed liquid quality 7%, mixed liquid matter is added
The Tween-80 of amount 8%, constant temperature are stirred 60min, keep the temperature still aging 4h, obtain ageing liquid, take ageing liquid in 80 DEG C, decompression
Be concentrated into the 40% of original volume, obtain concentrate, take concentrate to be delivered to spray dryer, in inlet air temperature be 100 DEG C, outlet air
Under the conditions of temperature is 85 DEG C, mist projection granulating obtains hollow nano-beads;
(2) in 4 DEG C, 1:0.04:10 in mass ratio takes trash ice, additive, the water mixing that partial size is 0.5mm, trash ice liquid is obtained, by matter
Number meter is measured, takes 60 parts of trash ice liquid, 10 parts of hollow Nano pearls, 15 parts of dehydrated alcohols, 20 parts of polyethylene glycol, the 12 parts of mass fractions to be
20% citric acid solution, 5 parts of auxiliary agents, 14 parts of polymerization material, in 5 DEG C, first take trash ice liquid, hollow Nano pearl, dehydrated alcohol, poly- second
Glycol is mixed in reaction kettle, stirs 60min with 700r/min, citric acid solution, auxiliary agent, polymerization material is added, with 3000r/min
High-speed stirred 60min is vacuumized and is concentrated into the 40% of original volume, in 4 DEG C of refrigerator cold-storages to get compound dredging base-material.
The preparation of composite auxiliary material: according to parts by weight, successively take 14 parts containing seleno reagent, 7 parts of benzyl carbinols, 20 parts of lauryl alcohols,
15 parts of polyallylamines, 18 parts of fermentation materials, 8 parts of potassium nitrate, 7 parts of sodium nitrites, take lauryl alcohol, polyallylamine in reaction by first 35 DEG C
Kettle mixing after stirring 5h with 800r/min, is warming up to 55 DEG C, organic selenium, benzyl carbinol, fermentation material, potassium nitrate and nitrous acid is added
Sodium mixing is passed through carbon dioxide gas with 130mL/min rate, boosts to 4.8MPa after stirring 4h with 2000r/min, keeps the temperature
Pressure maintaining handles 50min to get composite auxiliary material.
A kind of compound dredging base-material, according to the mass fraction, including following component: 7 parts of tartaric acid, 4 parts of bentonite, 7 parts of surfaces
Activating agent, 5 parts of foaming agents, 40 parts of compound dredging base-materials, 20 parts of composite auxiliary materials.
A kind of kitchen pipeline preparation method of mild dredging agent, includes the following steps:
(1) according to the mass fraction, take 7 parts of trim,ethylchlorosilanes, 4 parts of bentonite, 7 parts of surfactants, 5 parts of foaming agents, 40 parts it is multiple
Close dredging base-material, 20 parts of composite auxiliary materials;
(2) prior to 35 DEG C, surfactant, bentonite, foaming agent, composite auxiliary material is taken to mix in reaction kettle, with 700r/min magnetic force
60min is stirred, is cooled to 7 DEG C, compound dredging base-material, trim,ethylchlorosilane mixing is added, with 800r/min magnetic agitation 60min
Afterwards, in 4 DEG C of refrigerator cold-storages to get pipe-dredging agent.
A kind of application method of kitchen pipeline mild dredging agent: take the pipe-dredging agent of refrigeration by 500g/cm3Amount
(volume of dosage/obstructive position used) pours into the pipeline of obstruction, after standing 10min, pours into 6 times of quality of pipe-dredging agent used
55 DEG C of hot water.
Comparative example 1: it is essentially identical with the preparation method of embodiment 1, it has only the difference is that lacking compound dredging base-material.
Comparative example 2: it is essentially identical with the preparation method of embodiment 1, it has only the difference is that lacking composite auxiliary material.
Comparative example 3: the kitchen pipeline mild dredging agent of Yancheng City company production.
By kitchen pipeline obtained by embodiment and comparative example with mild dredging agent according to GB/T13173.2-2000 standard into
Row test, test result are as shown in table 1.
Table 1:
In conclusion present invention gained kitchen pipeline mild dredging agent can be effectively prevented line clogging, compared to commercially available
Product effect is more preferable, is worth promoting.
The foregoing is merely preferred modes of the invention, are not intended to limit the invention, all in spirit and original of the invention
Within then, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of kitchen pipeline mild dredging agent, according to the mass fraction, including following component: 3 ~ 7 parts of trim,ethylchlorosilanes,
1 ~ 4 part of bentonite, 3 ~ 7 parts of surfactants, 2 ~ 5 parts of foaming agents, which is characterized in that further include: 25 ~ 40 parts of compound dredging base-materials,
12 ~ 20 parts of composite auxiliary materials.
2. a kind of kitchen pipeline mild dredging agent according to claim 1, which is characterized in that the compound dredging base-material
Preparation method, include the following steps:
(1) in 25 ~ 35 DEG C, according to parts by weight, 8 ~ 15 parts of ferrous nitrates, 15 ~ 30 parts of ferric nitrates, 80 ~ 100 parts of water mixing are taken,
PH is adjusted, mixed liquid is obtained, takes mixed liquid that the Tween-80 of the lecithin of mixed liquid quality 3 ~ 7%, mixed liquid quality 5 ~ 8%, constant temperature stirring is added
Mixing, heat preservation is still aging, obtains ageing liquid, takes ageing liquid to be concentrated under reduced pressure, obtains concentrate, take concentrate mist projection granulating, obtain hollow
Nano-beads;
(2) in 1 ~ 4 DEG C, 1:0.04:6 ~ 10 take trash ice, additive, water mixing in mass ratio, obtain trash ice liquid, according to the mass fraction,
Take 40 ~ 60 parts of trash ice liquid, 6 ~ 10 parts of hollow Nano pearls, 10 ~ 15 parts of dehydrated alcohols, 12 ~ 20 parts of polyethylene glycol, 7 ~ 12 parts of citric acids
Solution, 2 ~ 5 parts of auxiliary agents, 8 ~ 14 parts of polymerization material first take trash ice liquid, hollow Nano pearl, dehydrated alcohol, polyethylene glycol mixed in 2 ~ 5 DEG C
Stirring is closed, citric acid solution, auxiliary agent, polymerization material is added, high-speed stirred vacuumizes concentration, refrigerates to get compound dredging base-material.
3. a kind of kitchen pipeline mild dredging agent according to claim 2, which is characterized in that in the step (2)
Additive: 1:3 ~ 7 take lactose, mannitol mixing to get additive in mass ratio.
4. a kind of kitchen pipeline mild dredging agent according to claim 2, which is characterized in that in the step (2)
Polymerization material: in 28 ~ 40 DEG C, according to parts by weight, and 30 ~ 50 parts of acrylic acid, 16 ~ 25 parts of acrylamides, 0.3 ~ 0.6 part of N, N- methylene
Base bisacrylamide, 2 ~ 5 parts of castor oil, 7 ~ 14 parts of nonylphenol polyoxyethylene ether, 25 ~ 40 parts of NaOH solution mixing, lead to nitrogen and protect
Shield, stirring, is warming up to 70 ~ 85 DEG C, and the over cure potassium mixing of acrylic acid quality 1 ~ 4% is added, and constant temperature is stirred to react, discharging to get
Polymerization material.
5. a kind of kitchen pipeline mild dredging agent according to claim 2, which is characterized in that in the step (2)
Auxiliary agent: 1:2 ~ 4:1 in mass ratio takes microcrystalline wax, magnesium stearate, castor oil mixing to get auxiliary agent.
6. a kind of kitchen pipeline mild dredging agent according to claim 1, which is characterized in that the system of the composite auxiliary material
It is standby: according to parts by weight, successively to take 6 ~ 14 parts to contain seleno reagent, 3 ~ 7 parts of benzyl carbinols, 10 ~ 20 parts of lauryl alcohols, 8 ~ 15 parts of polyenes third
Amine, 10 ~ 18 parts of fermentation materials, 4 ~ 8 parts of potassium nitrate, 3 ~ 7 parts of sodium nitrites, take lauryl alcohol, polyallylamine mixing to stir by first 27 ~ 35 DEG C
It mixes, is warming up to 40 ~ 55 DEG C, organic selenium, benzyl carbinol, fermentation material, potassium nitrate and sodium nitrite is added and is mixed, is passed through titanium dioxide
Carbon gas, boosting, heat-insulation pressure keeping processing is to get composite auxiliary material.
7. a kind of kitchen pipeline mild dredging agent according to claim 6, which is characterized in that described to contain seleno reagent: to press
4 ~ 8:3 of mass ratio takes hexichol selenide, the mixing of two selenium of hexichol to get containing seleno reagent.
8. a kind of kitchen pipeline mild dredging agent according to claim 6, which is characterized in that the fermentation material: pressing matter
Number meter is measured, 6 ~ 10 parts of wormcasts, 5 ~ 8 portions of beef extracts, 7 ~ 12 parts of glucose, 0.1 ~ 0.4 part of NaH are taken2PO4, 2 ~ 5 parts of Bao Jiali
Sub- lactobacillus powder, 3 ~ 7 parts of caseins, 300 ~ 500 parts of water mixing shake shaker fermentation culture in 28 ~ 32 DEG C, sterilize, filter, receive
Collect filtrate to get fermentation material.
9. a kind of kitchen pipeline mild dredging agent according to claim 1, which is characterized in that the foaming agent: pressing matter
Amount takes sodium sulfate of polyethenoxy ether of fatty alcohol, petroleum ether mixing to get foaming agent than 3 ~ 6:1.
10. a kind of kitchen pipeline mild dredging agent according to claim 1, which is characterized in that the surfactant:
2 ~ 4:1 in mass ratio takes dodecyldimethylammonium hydroxide inner salt, the mixing of secondary alkyl benzene sulfonic acid sodium salt to get surfactant.