CN110029510A - A kind of preparation method of waterproof warp knit elastic force swimsuit fabric - Google Patents
A kind of preparation method of waterproof warp knit elastic force swimsuit fabric Download PDFInfo
- Publication number
- CN110029510A CN110029510A CN201910261198.1A CN201910261198A CN110029510A CN 110029510 A CN110029510 A CN 110029510A CN 201910261198 A CN201910261198 A CN 201910261198A CN 110029510 A CN110029510 A CN 110029510A
- Authority
- CN
- China
- Prior art keywords
- waterproof
- warp
- fabric
- preparation
- elastic force
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to fabric technical fields, and in particular to a kind of preparation method of waterproof warp knit elastic force swimsuit fabric.Preparation process flow of the invention are as follows: standby base → pre-setting → dyeing → dehydration → finished product sizing, preparation process is simple, and the addition of waterproof agent is in dyeing with setting process, and the addition by controlling auxiliary agent is optimal the waterproof effect of fabric, it is environmentally friendly and using floride-free waterproof agent.The waterproof membrane that swimsuit fabric surface made from preparation method of the present invention is formed, it can prevent moisture content from immersing, with good water-proof function, the discomfort for just entering water can be alleviated, reducing human stimulus to the sense organ, the comfort of swimming is improved, and its original wearability elasticity, feel, conformability etc. will not change.
Description
Technical field
The invention belongs to fabric technical fields, and in particular to a kind of preparation method of waterproof warp knit elastic force swimsuit fabric.
Background technique
Warp knit elastic fabric, because of its good elasticity, elastic recovery, the good taking such as personal feel, is current
The first choice of swimsuit fabric, but existing swimsuit fabric is all without waterproof performance in the market, so people put on swimsuit and are being lauched
When will soon soak, nerve stimulation is obvious, and especially to women and child, this stimulation often generates body not sometimes
It is suitable.
Summary of the invention
The technical problem to be solved in the present invention is that in view of the above problems, providing a kind of waterproof warp knit elastic force swimming
Fill the preparation method of fabric.Swimsuit fabric surface made from preparation method of the present invention, which forms fine and close waterproof membrane, can prevent moisture content
It immerses, there is good water-proof function, and preparation process is simple, it is environmentally friendly using floride-free waterproof agent.
According to technical solution provided by the invention, the preparation method of the waterproof warp knit elastic force swimsuit fabric, including it is as follows
Step:
(1) it standby base: gets out warp-knitted face fabric and shows base；
(2) pre-setting: warp-knitted face fabric is showed into base and carries out pre-setting, pre-setting temperature is 170-195 DEG C, and pre-setting speed is 14-
17m/min；
(3) it dyes: the warp-knitted face fabric after pre-setting being put into the dyeing apparatus for be contained with acid dyes and is dyed, dyeing temperature
90-120 DEG C, dyeing time 35-45min, soaking time 15-25min of degree, fabric goes out the pH of adjusting dyestuff before cylinder after the completion of dyeing
It is worth 4.0-5.5, color fixing agent, waterproof agent 30-50g/L is added, continues to go out cylinder after dyeing 15min-25min；
(4) it is dehydrated: the warp-knitted face fabric after dyeing being put into dewaterer and carries out dehydration 3-6min, revolving speed 1500-1900rpm,
Dewatered moisture content is in 40-70%；
(5) shaping and drying: being added the waterproof agent of 30-50g/L in the forming machine of step (3), controls liquid carrying rate, passes through sizing
Waterproof agent is attached on dewatered warp-knitted face fabric by machine, and is dried by baking oven to get excellent to waterproof performance
Warp-knitted face fabric.
Warp-knitted face fabric in the step (1) is woven by Polyamide Yarns and spandex thread.
The door width of warp-knitted face fabric in the step (1) is 145-160cm, and grammes per square metre is 190-240g/m2。
The Polyamide Yarns is 75D/72F Polyamide Yarns, and the spandex thread is 20D spandex thread.
Waterproof agent in the step (3) is floride-free waterproof agent.
The temperature of forming machine is 110-170 °C in the step (5), sizing speed 10-15m/min.
The dyeing apparatus is the dedicated dye vat of warp-knitted face fabric, other than dye vat task equipment, is attached with one on the outside of dye vat
Special auxiliary agent adds a mixing bowl.
The forming machine uses 10 section cabinet forming machine of Monforts.
Compared with the prior art, the present invention has the following advantages:
(1) waterproof membrane that swimsuit fabric surface made from preparation method of the present invention is formed, can prevent moisture content from immersing, and have good
Water-proof function, the discomfort for just entering water can be alleviated, reducing human stimulus to the sense organ improves the comfort of swimming, its another original clothes
It will not be changed with performance elasticity, feel, conformability etc..
(2) preparation process flow of the invention are as follows: standby base → pre-setting → dyeing → dehydration → finished product sizing, preparation process
Simply, the addition of waterproof agent is in dyeing with setting process, and the addition by controlling auxiliary agent reaches the waterproof effect of fabric
It is environmentally friendly to optimal, and using floride-free waterproof agent.
Further description of the technical solution of the present invention combined with specific embodiments below.
Specific embodiment
Embodiment 1
A kind of preparation method of waterproof warp knit elastic force swimsuit fabric, process flow are as follows: standby base → pre-setting → dyeing → dehydration
The sizing of → finished product, the warp-knitted face fabric bought in the market show base, carry out pre-setting by forming machine, pre-setting temperature is 190 DEG C, in advance
Sizing speed is 14m/min；Warp-knitted face fabric after pre-setting is put into dye vat and is dyed, dyestuff selects acid dyes
Nylosan Blue n-5gl sgr 200, dyes 50min, and keep the temperature 25min at 98 DEG C, and fabric after the completion to be dyed goes out cylinder
Color fixing agent Goon705 2wt.%, waterproof agent Du Pont R3-26791 is added to 4.5 in the preceding pH value for adjusting dye solution with acetic acid
30g/L continues to go out cylinder after dyeing 20min, the warp-knitted face fabric after cylinder out is put into dewaterer and is dehydrated, revolving speed
1500rpm, dewatering time 6min, dewatered moisture content is 50%；Dewatered fabric crosses forming machine drying, to improve warp knit
The waterproof performance of fabric controls liquid carrying rate with the waterproof agent for adding 40g/L in liquid bath in forming machine when shaping and drying,
Waterproof agent is attached on dewatered warp-knitted face fabric, and is dried by baking oven, forming machine temperature is 135 °C, sizing
Speed be 12m/min to get to water-proof function warp knit elastic force swimsuit fabric.
Embodiment 2
A kind of preparation method of waterproof warp knit elastic force swimsuit fabric, process flow are as follows: standby base → pre-setting → dyeing → dehydration
The sizing of → finished product, the warp-knitted face fabric bought in the market show base, carry out pre-setting by forming machine, pre-setting temperature is 195 DEG C, in advance
Sizing speed is 14m/min；Warp-knitted face fabric after pre-setting is put into dye vat and is dyed, dyestuff selects acid dyes
Nylosan Black n-wln, dyes 40min, and keep the temperature 20min at 105 DEG C, and fabric after the completion to be dyed uses vinegar before going out cylinder
Acid adjusts the pH value of dye solution to 4.0, and color fixing agent Goon705 3wt.%, waterproof agent Du Pont R3-26791 35g/L is added,
Continue to go out cylinder after rotating 15min in cylinder, the warp-knitted face fabric after cylinder out is put into dewaterer and is dehydrated, revolving speed
1600rpm, dewatering time 4min, dewatered moisture content is 60%；Dewatered fabric crosses forming machine drying, to improve warp knit
The waterproof performance of fabric controls liquid carrying rate with the waterproof agent for adding 35g/L in liquid bath in forming machine when shaping and drying,
Waterproof agent is attached on dewatered warp-knitted face fabric, and is dried by baking oven, forming machine temperature is 150 °C, sizing
Speed is 13m/min.
Embodiment 3
A kind of preparation method of waterproof warp knit elastic force swimsuit fabric, process flow are as follows: standby base → pre-setting → dyeing → dehydration
The sizing of → finished product, the warp-knitted face fabric bought in the market show base, carry out pre-setting by forming machine, pre-setting temperature is 198 DEG C, in advance
Sizing speed is 16m/min；Warp-knitted face fabric after pre-setting is put into dye vat and is dyed, dyestuff selects acid dyes
Nylosan Rubine n-5bl 200,110 DEG C of dyeing temperature, dyeing time 45min, soaking time 15min, completion to be dyed
Expect to adjust pH value to 5.5 with acetic acid before cylinder out below, color fixing agent Goon705 2wt.%, waterproof agent Du Pont R3-26791 is added
40g/L continues to go out cylinder after rotating 25min in cylinder, the warp-knitted face fabric after cylinder out is put into dewaterer and is dehydrated, revolving speed
1700rpm, dewatering time 3min, dewatered moisture content is 55%；Dewatered fabric crosses forming machine drying, to improve warp knit
The waterproof performance of fabric controls liquid carrying rate with the waterproof agent for adding 30g/L in liquid bath in forming machine when shaping and drying,
Waterproof agent is attached on dewatered warp-knitted face fabric, and is dried by baking oven, forming machine temperature is 160 °C, sizing
Speed 15m/min.
Specific embodiment described above is only to illustrate to the present invention.The technical field of the invention
Technical staff can make various modifications or additions to the described embodiments or be substituted in a similar manner, but
Without departing from the spirit of the invention or going beyond the scope defined by the appended claims.
Claims (8)
1. a kind of preparation method of waterproof warp knit elastic force swimsuit fabric, which comprises the steps of:
(1) it standby base: gets out warp-knitted face fabric and shows base；
(2) pre-setting: warp-knitted face fabric is showed into base and carries out pre-setting, pre-setting temperature is 170-195 DEG C, and pre-setting speed is 12-
17m/min；
(3) it dyes: the warp-knitted face fabric after pre-setting being put into the dyeing apparatus for be contained with acid dyes and is dyed, dyeing temperature
90-120 DEG C, dyeing time 35-45min, soaking time 15-25min of degree, fabric goes out the pH of adjusting dyestuff before cylinder after the completion of dyeing
It is worth 4.0-5.5, color fixing agent, waterproof agent 30-50g/L is added, continues to go out cylinder after dyeing 15min-25min；
(4) it is dehydrated: the warp-knitted face fabric after dyeing being put into dewaterer and carries out dehydration 3-6min, revolving speed 1500-1900rpm,
Dewatered moisture content is in 40-70%；
(5) shaping and drying: being added the waterproof agent of 30-50g/L in the forming machine of step (3), controls liquid carrying rate, passes through sizing
Waterproof agent is attached on dewatered warp-knitted face fabric by machine, and is dried by baking oven to get excellent to waterproof performance
Warp knit elastic force swimsuit fabric.
2. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 1, which is characterized in that the step
(1) warp-knitted face fabric in is woven by Polyamide Yarns and spandex thread.
3. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 1, which is characterized in that the step
(1) the door width of the warp-knitted face fabric in is 145-160cm, and grammes per square metre is 190-240g/m2。
4. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 2, which is characterized in that the polyamide fibre
Silk is 75D/72F Polyamide Yarns, and the spandex thread is 20D spandex thread.
5. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 1, which is characterized in that the step
(3) waterproof agent in is floride-free waterproof agent.
6. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 1, which is characterized in that the step
(5) temperature of forming machine is 110-170 °C in, sizing speed 10-15m/min.
7. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 1, which is characterized in that the dyeing dress
It is set to the dedicated dye vat of warp-knitted face fabric, other than dye vat task equipment, a special auxiliary agent addition a mixing bowl is attached on the outside of dye vat.
8. the preparation method of waterproof warp knit elastic force swimsuit fabric according to claim 1, which is characterized in that the forming machine
Using 10 section cabinet forming machine of Monforts.