CN110004552A - Anti-flaming viscose and the continuous synthetic fibre long filament coated yarn spinning of the blended cladding of aramid fiber and manufacturing process - Google Patents
Anti-flaming viscose and the continuous synthetic fibre long filament coated yarn spinning of the blended cladding of aramid fiber and manufacturing process Download PDFInfo
- Publication number
- CN110004552A CN110004552A CN201810826208.7A CN201810826208A CN110004552A CN 110004552 A CN110004552 A CN 110004552A CN 201810826208 A CN201810826208 A CN 201810826208A CN 110004552 A CN110004552 A CN 110004552A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- aramid fiber
- spinning
- blended
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of anti-flaming viscose and the blended cladding silk floss synthetic fibre long filament coated yarn spinning of aramid fiber, it is related to technical field of textile production, spinned rove is mixed by white flame retardant viscose fiber 65%, golden yellow aramid fiber F14 fiber 35%, 66 20D long filament of continuous synthetic fibre is coated in spinning process, anti-flaming viscose and the blended cladding of aramid fiber F14 66 long filament of continuous synthetic fibre is made, the count of yarn is 34 covering yarns, and manufacturing technology steps are as follows: cotton cleaning process, carding step, mixing in doubling step, Roving Frames, spinning process, winding procedure；RING SPINNING board installs godet roller additional, filaments in position is swum the side to the left of area's yarn in drawing-off, winding process adds long thin auxiliary magnet, ensure to leak heart yarn and seersucker excision, each process production environment relative humidity is 53% -59% yarn, and hygroscopicity of yarn of the present invention, permeability are good, and flame retardant property is good, comfortable feel does not melt drop phenomenon.
Description
Technical field
The present invention relates to technical field of textile production, specifically a kind of anti-flaming viscose and the continuous synthetic fibre of the blended cladding of aramid fiber are long
Silk coated yarn spinning and manufacturing process.
Background technique
It is right with continuous development and consumer personalized, fashion-orientation and the diversified pursuit to fabric of spinning technique
Fabric Functional Requirement is also higher and higher, and traditional single structure spinning has been unable to satisfy the market demand.For oil plant, petroleum
The fire-entry suit of work, Fight Fire in Forest clothes and flight management clothes, space suit, army's police uniform, special technical soldier's work clothes etc. are to heat resistance, resistance
The requirement of combustion property increasingly improves, and assigns the more flame retardant properties of textile, it is ensured that safety reduces fire, important in inhibiting.Mesh
Preceding domestic fire-retardant textile fabric is mostly pure chemical fiber or pure cotton final finishing, and generally existing wiriness, strength is low, meets the feelings that fire melts drop
Condition.
Summary of the invention
In order to overcome the deficiencies of the prior art, the present invention provides a kind of anti-flaming viscose and the continuous synthetic fibre long filament spinning of the blended cladding of aramid fiber
Covering yarn and manufacturing process, to solve inflaming retarding fabric wiriness, strength is low, meets the problem of fire melts drop.
For achieving the above object, a kind of anti-flaming viscose of the present invention and the continuous synthetic fibre long filament of the blended cladding of aramid fiber spin cored
Yarn, it is characterised in that: spinned by white flame retardant viscose fiber 60%-70%, golden yellow aramid fiber F14 fiber 30%-40% mixing
Rove coats 66 20D long filament of continuous synthetic fibre in spinning process, yellow anti-flaming viscose and the blended cladding of aramid fiber F14 66 long filament of continuous synthetic fibre is made
Covering yarn；The anti-flaming viscose content of the covering yarn resultant yarn accounts for the 57% of mixed yarn total weight, golden yellow aramid fiber F14 and accounts for mixed yarn
The 30% of total weight, continuous 66 20D long filament of synthetic fibre account for the 13% of mixed yarn total weight, and the covering yarn count of yarn is 34.
A kind of manufacturing process of anti-flaming viscose and the continuous synthetic fibre long filament coated yarn spinning of the blended cladding of aramid fiber, it is characterised in that: work
Steps are as follows for skill:
1., cotton cleaning process:
It weighs respectively according to white flame retardant viscose fiber 60%-70%, golden yellow aramid fiber F14 fiber 30%-40% weight, by two kinds of fibres
Dimension raw material is few on the inside of cotton slot according to fiber content, the principle arrangement on the outside of cotton slot more than fiber content, golden yellow aramid fiber
For F14 fiber on the inside of cotton slot, white flame retardant viscose fiber upper slot arrangement, crawl strike on the outside of cotton slot are uniformly mixed and made into volume
Son；Quantification of 370 grams ms of examination paper, using 420 revs/min of kirschner beater revolving speed, comprehensive hired roughneck's revolving speed is 820 revs/min, coiled sieve
Drawing revolving speed is 10 revs/min；
2., carding step:
Examination paper made of two kinds of fibers is made the carded sliver on A186D carding machine, and 20.0 grams/5 meters of weight of card sliver, cylinder revolving speed is
330 revs/min, licker-in revolving speed is 770 revs/min, and cover board linear velocity is 84 millis m/min, and mote knife height is concordant with machine frame, and angle is
90°；
3., mixing in doubling step:
Two kinds of color fibers are further uniformly mixed, and improve strip longitudinal uniformity by drafting using three mixing；Head is simultaneously adopted
It is mixed with 6 carded slivers, quantification of 20.0 grams/5 meters, total draft multiple is 6.02 times, and wherein back zone drafting multiple is 1.87 times, pressure
Roller linear velocity is 260 ms/min, and roller is held away from be 58 millimeters × 62 millimeters, Pendulum Weighting Arm System: preceding × in × it is afterwards 32 kilograms × 38
Kilogram × 38 kilograms；Two and using 8 and and, quantification of 20.3 grams/5 meters, total draft multiple is 7.88 times, wherein back area draft
Multiple is 2.07 times, and pressure roller linear velocity is 260 ms/min, and roller is held away from being 58 millimeters × 62 millimeters, Pendulum Weighting Arm System: preceding × in
× it is afterwards 32 kilograms × 38 kilograms × 38 kilograms；Three and also using 6 and and, quantification of 20.3 grams/5 meters, total draft multiple is
5.52 times, wherein back zone drafting multiple be 1.4 times, pressure roller linear velocity be 350 ms/min, roller hold away from for 56 millimeters × 60 in the least
Rice, Pendulum Weighting Arm System: preceding × in × it is afterwards 32 kilograms × 38 kilograms × 38 kilograms；
4., Roving Frames:
Regular roving feeding is 5.4 grams/10 meters, drafting multiple 7.52, and wherein back zone drafting multiple is 1.312, twist factor 70.5,
Roller is held away from being 58 millimeters × 68 millimeters, and ingot speed is 560 revs/min；
5., spinning process:
By the blended manufactured rove of flame retardant viscose fiber and aramid fiber F14, in the horn mouth after feeding spinning frame, chinlon 66 filament is logical
Conducting wire pole unwinding is crossed, then front leather roller rear is introduced by godet roller, is led to together with flame retardant viscose fiber and the blended yarn of aramid fiber F14
It crosses front leather roller and holds point, twisting cladding forms covering yarn in twist triangle zone；To guarantee that covered effect does not leak silk, filaments in position exists
Drawing-off is swum the side to the left of area's yarn, and closely yarn, is not spaced, and roller is held away from being 55 millimeters × 65 millimeters, spindle speed
At 13000 revs/min -- 14000 revs/min, rings selects 6903 type, 2/0 wire loop using PG1 series, wire loop；
6., winding procedure:
Using automatic winder, speed is 1400 m/min -1500m/min, electric clear technique: cotton knot 400%, short and thick to be
150%-2.5 centimetres, long is slightly 40%-30 centimetres, and long details is -40%--32 centimetres, and length is -28%-60 centimetres of auxiliary magnet thin, it is ensured that
Excision leakage heart yarn, seersucker；
7., above-mentioned each process production environment relative humidity be 53% -59%.
Each process device configuration is as follows:
FA002A automatic plucker --- FA106C opener --- A045B condenser --- FA076C lapper --- A186D
Carding machine --- FA303 drawing frame (head, two) --- RD221C autoleveller draw frame --- A454 fly frame --- FA502
Ring spinning frame --- Autoconer338 type automatic winder.
Compared with prior art, the present invention will be mixed by white flame retardant viscose fiber 65%, golden yellow aramid fiber F14 fiber 35%
The rove spinned coats 66 20D long filament of continuous synthetic fibre in spinning process, and yellow anti-flaming viscose is made and the blended cladding of aramid fiber F14 is continuous
66 filament core-spun yarn of synthetic fibre；It is total that resultant yarn is that anti-flaming viscose content accounts for the 57% of mixed yarn total weight, golden yellow aramid fiber F14 accounts for mixed yarn
The 30% of weight, continuous 66 20D long filament of synthetic fibre account for the 13% of mixed yarn total weight, the covering yarn that the count of yarn is 34.Its main feature is that yarn
Line wearability is good, and flame retardant property is good, and hygroscopicity, permeability are good, comfortable feel, does not melt drop phenomenon.
Specific embodiment
A kind of anti-flaming viscose of the present invention and the continuous synthetic fibre long filament coated yarn spinning of the blended cladding of aramid fiber, by white flame retardant viscose fiber
60%-70%, golden yellow aramid fiber F14 fiber 30%-40% mix spinned rove, coat 66 20D long of continuous synthetic fibre in spinning process
Yellow anti-flaming viscose and the blended cladding of aramid fiber F14 66 filament core-spun yarn of continuous synthetic fibre is made in silk；The anti-flaming viscose of the covering yarn resultant yarn
Content accounts for the 57% of mixed yarn total weight, golden yellow aramid fiber F14 and accounts for the 30% of mixed yarn total weight, and continuous 66 20D long filament of synthetic fibre accounts for blended
The 13% of yarn total weight, the covering yarn count of yarn are 34.Anti-flaming viscose selects fineness for 4000 Nm, length 51mm,
Strength is 1.6CN/dtex；14 fineness of aramid fiber is 6000 Nm, principal length 38mm, is strongly 15.38CN/dtex.
A kind of manufacturing process of anti-flaming viscose and the continuous synthetic fibre long filament coated yarn spinning of the blended cladding of aramid fiber, processing step are as follows:
1., cotton cleaning process:
It weighs respectively according to white flame retardant viscose fiber 60%-70%, golden yellow aramid fiber F14 fiber 30%-40% weight, by two kinds of fibres
Dimension raw material is few on the inside of cotton slot according to fiber content, the principle arrangement on the outside of cotton slot more than fiber content, golden yellow aramid fiber
For F14 fiber on the inside of cotton slot, white flame retardant viscose fiber upper slot arrangement, crawl strike on the outside of cotton slot are uniformly mixed and made into volume
Son；Quantification of 370 grams ms of examination paper, using 420 revs/min of kirschner beater revolving speed, comprehensive hired roughneck's revolving speed is 820 revs/min, coiled sieve
Drawing revolving speed is 10 revs/min；
2., carding step:
Examination paper made of two kinds of fibers is made the carded sliver on A186D carding machine, and 20.0 grams/5 meters of weight of card sliver, cylinder revolving speed is
330 revs/min, licker-in revolving speed is 770 revs/min, and cover board linear velocity is 84 millis m/min, and mote knife height is concordant with machine frame, and angle is
90°；
3., mixing in doubling step:
Two kinds of color fibers are further uniformly mixed, and improve strip longitudinal uniformity by drafting using three mixing；Head is simultaneously adopted
It is mixed with 6 carded slivers, quantification of 20.0 grams/5 meters, total draft multiple is 6.02 times, and wherein back zone drafting multiple is 1.87 times, pressure
Roller linear velocity is 260 ms/min, and roller is held away from be 58 millimeters × 62 millimeters, Pendulum Weighting Arm System: preceding × in × it is afterwards 32 kilograms × 38
Kilogram × 38 kilograms；Two and using 8 and and, quantification of 20.3 grams/5 meters, total draft multiple is 7.88 times, wherein back area draft
Multiple is 2.07 times, and pressure roller linear velocity is 260 ms/min, and roller is held away from being 58 millimeters × 62 millimeters, Pendulum Weighting Arm System: preceding × in
× it is afterwards 32 kilograms × 38 kilograms × 38 kilograms；Three and also using 6 and and, quantification of 20.3 grams/5 meters, total draft multiple is
5.52 times, wherein back zone drafting multiple be 1.4 times, pressure roller linear velocity be 350 ms/min, roller hold away from for 56 millimeters × 60 in the least
Rice, Pendulum Weighting Arm System: preceding × in × it is afterwards 32 kilograms × 38 kilograms × 38 kilograms；
4., Roving Frames:
Regular roving feeding is 5.4 grams/10 meters, drafting multiple 7.52, and wherein back zone drafting multiple is 1.312, twist factor 70.5,
Roller is held away from being 58 millimeters × 68 millimeters, and ingot speed is 560 revs/min；
5., spinning process:
By the blended manufactured rove of flame retardant viscose fiber and aramid fiber F14, in the horn mouth after feeding spinning frame, chinlon 66 filament is logical
Conducting wire pole unwinding is crossed, then front leather roller rear is introduced by godet roller, is led to together with flame retardant viscose fiber and the blended yarn of aramid fiber F14
It crosses front leather roller and holds point, twisting cladding forms covering yarn in twist triangle zone；To guarantee that covered effect does not leak silk, filaments in position exists
Drawing-off is swum the side to the left of area's yarn, and closely yarn, is not spaced, and roller is held away from being 55 millimeters × 65 millimeters, spindle speed
At 13000 revs/min -- 14000 revs/min, rings selects 6903 type, 2/0 wire loop using PG1 series, wire loop；
6., winding procedure:
Using automatic winder, speed is 1400 m/min -1500m/min, electric clear technique: cotton knot 400%, short and thick to be
150%-2.5 centimetres, long is slightly 40%-30 centimetres, and long details is -40%--32 centimetres, and length is -28%-60 centimetres of auxiliary magnet thin, it is ensured that
Excision leakage heart yarn, seersucker；
7., above-mentioned each process production environment relative humidity be 53% -59%.
Each process device configuration is as follows:
FA002A automatic plucker --- FA106C opener --- A045B condenser --- FA076C lapper --- A186D
Carding machine --- FA303 drawing frame (head, two) --- RD221C autoleveller draw frame --- A454 fly frame --- FA502
Ring spinning frame --- Autoconer338 type automatic winder.
The present invention is led using the rove of flame retardant viscose fiber and aramid fiber F14 fiber mixing spinning in RING SPINNING board installation
Silk wheel produces anti-flaming viscose and the blended cladding of aramid fiber F14 66 filament core-spun yarn of continuous synthetic fibre；To guarantee that fabric is solid, wear-resisting property
Good, flame retardant property is good, using 14 fiber of 57% anti-flaming viscose and 30% aramid fiber, while being improvement wearability, keeps its comfortable and easy to wear,
Hygroscopicity, permeability are good, and using 13% 66 long filament of continuous synthetic fibre, to improve cloth style, wearability is good, uses core-spun yarn
Mode reaches this effect.
Godet wheel device is installed additional in conventional spinning frame with the cotton spinning equipment that the present invention uses, it is desirable that godet roller rotation spirit
Living, center alignment draft area yarn is to the left, guarantees chinlon 66 filament covered effect；Winding process adds long thin auxiliary magnet,
Ensure to leak heart yarn and seersucker excision.
Present invention process production content shown in table one for white flame retardant viscose fiber content account for mixed yarn total weight 57%,
14 content of aramid fiber accounts for mixed yarn total weight 30% and chinlon 66 filament accounts for mixed yarn total weight 13%, produces 34 covering yarn tests and surveys
Try data:
Table one
Process weaves demand after data meet in table.
Claims (3)
1. a kind of anti-flaming viscose and the continuous synthetic fibre long filament coated yarn spinning of the blended cladding of aramid fiber, it is characterised in that: by white anti-flaming viscose
Fiber 60%-70%, golden yellow aramid fiber F14 fiber 30%-40% mix spinned rove, coat 66 20D of continuous synthetic fibre in spinning process
Yellow anti-flaming viscose and the blended cladding of aramid fiber F14 66 filament core-spun yarn of continuous synthetic fibre is made in long filament；The fire-retardant of the covering yarn resultant yarn is glued
Glue content accounts for the 57% of mixed yarn total weight, golden yellow aramid fiber F14 and accounts for the 30% of mixed yarn total weight, and continuous 66 20D long filament of synthetic fibre accounts for mixed
The 13% of total weight of spinning, the covering yarn count of yarn are 34.
2. a kind of anti-flaming viscose and the blended manufacturing process for coating continuous synthetic fibre long filament coated yarn spinning of aramid fiber, it is characterised in that: technique
Steps are as follows:
1., cotton cleaning process:
It weighs respectively according to white flame retardant viscose fiber 60%-70%, golden yellow aramid fiber F14 fiber 30%-40% weight, by two kinds of fibres
Dimension raw material is few on the inside of cotton slot according to fiber content, the principle arrangement on the outside of cotton slot more than fiber content, golden yellow aramid fiber
For F14 fiber on the inside of cotton slot, white flame retardant viscose fiber upper slot arrangement, crawl strike on the outside of cotton slot are uniformly mixed and made into volume
Son；Quantification of 370 grams ms of examination paper, using 420 revs/min of kirschner beater revolving speed, comprehensive hired roughneck's revolving speed is 820 revs/min, coiled sieve
Drawing revolving speed is 10 revs/min；
2., carding step:
Examination paper made of two kinds of fibers is made the carded sliver on A186D carding machine, and 20.0 grams/5 meters of weight of card sliver, cylinder revolving speed is
330 revs/min, licker-in revolving speed is 770 revs/min, and cover board linear velocity is 84 millis m/min, and mote knife height is concordant with machine frame, and angle is
90°；
3., mixing in doubling step:
Two kinds of color fibers are further uniformly mixed, and improve strip longitudinal uniformity by drafting using three mixing；Head is simultaneously adopted
It is mixed with 6 carded slivers, quantification of 20.0 grams/5 meters, total draft multiple is 6.02 times, and wherein back zone drafting multiple is 1.87 times, pressure
Roller linear velocity is 260 ms/min, and roller is held away from be 58 millimeters × 62 millimeters, Pendulum Weighting Arm System: preceding × in × it is afterwards 32 kilograms × 38
Kilogram × 38 kilograms；Two and using 8 and and, quantification of 20.3 grams/5 meters, total draft multiple is 7.88 times, wherein back area draft
Multiple is 2.07 times, and pressure roller linear velocity is 260 ms/min, and roller is held away from being 58 millimeters × 62 millimeters, Pendulum Weighting Arm System: preceding × in
× it is afterwards 32 kilograms × 38 kilograms × 38 kilograms；Three and also using 6 and and, quantification of 20.3 grams/5 meters, total draft multiple is
5.52 times, wherein back zone drafting multiple be 1.4 times, pressure roller linear velocity be 350 ms/min, roller hold away from for 56 millimeters × 60 in the least
Rice, Pendulum Weighting Arm System: preceding × in × it is afterwards 32 kilograms × 38 kilograms × 38 kilograms；
4., Roving Frames:
Regular roving feeding is 5.4 grams/10 meters, drafting multiple 7.52, and wherein back zone drafting multiple is 1.312, twist factor 70.5,
Roller is held away from being 58 millimeters × 68 millimeters, and ingot speed is 560 revs/min；
5., spinning process:
By the blended manufactured rove of flame retardant viscose fiber and aramid fiber F14, in the horn mouth after feeding spinning frame, chinlon 66 filament is logical
Conducting wire pole unwinding is crossed, then front leather roller rear is introduced by godet roller, is led to together with flame retardant viscose fiber and the blended yarn of aramid fiber F14
It crosses front leather roller and holds point, twisting cladding forms covering yarn in twist triangle zone；To guarantee that covered effect does not leak silk, filaments in position exists
Drawing-off is swum the side to the left of area's yarn, and closely yarn, is not spaced, and roller is held away from being 55 millimeters × 65 millimeters, spindle speed
At 13000 revs/min -- 14000 revs/min, rings selects 6903 type, 2/0 wire loop using PG1 series, wire loop；
6., winding procedure:
Using automatic winder, speed is 1400 m/min -1500m/min, electric clear technique: cotton knot 400%, short and thick to be
150%-2.5 centimetres, long is slightly 40%-30 centimetres, and long details is -40%--32 centimetres, and length is -28%-60 centimetres of auxiliary magnet thin, it is ensured that
Excision leakage heart yarn, seersucker；
7., above-mentioned each process production environment relative humidity be 53% -59%.
3. a kind of anti-flaming viscose according to claim 2 and the blended manufacture work for coating continuous synthetic fibre long filament coated yarn spinning of aramid fiber
Skill, it is characterised in that: each process device configuration is as follows:
FA002A automatic plucker --- FA106C opener --- A045B condenser --- FA076C lapper --- A186D
Carding machine --- FA303 drawing frame (head, two) --- RD221C autoleveller draw frame --- A454 fly frame --- FA502
Ring spinning frame --- Autoconer338 type automatic winder.