CN109987904A - A kind of fabricating technology of brick setting material - Google Patents
A kind of fabricating technology of brick setting material Download PDFInfo
- Publication number
- CN109987904A CN109987904A CN201910372689.3A CN201910372689A CN109987904A CN 109987904 A CN109987904 A CN 109987904A CN 201910372689 A CN201910372689 A CN 201910372689A CN 109987904 A CN109987904 A CN 109987904A
- Authority
- CN
- China
- Prior art keywords
- brick setting
- cement
- fabricating technology
- setting material
- cellulose ether
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of fabricating technologies of brick setting material of brick setting technical field of material, and the material specific formula is by mass are as follows: heavy calcium carbonate: 2.5~15.5；S105 slag powders: 10~35；Flyash: 5~25；Cement: 10~30；Expanded perlite: 5~20；Cellulose ether: 0.1~0.5；Water: 10~30, by being mixed, it is packed into mold vibration molding, forms product by maintenance, this technology of preparing simple production process, raw materials are at low cost, function admirable, have environment protection significance.
Description
Technical field
The present invention relates to brick setting technical field of material, specially a kind of fabricating technology of brick setting material.
Background technique
Current organic wall heat insulation material is there are some drawbacks, such as complicated construction technique, easy firing, inorganic material with have
Machine material cannot form one very well, meet high temperature and be easy to peel off, and current thermal insulation material majority is polyurethane foam slabs
Insulating wall material is formed, high temperature resistance is low, at high cost.For this purpose, it is proposed that a kind of preparation process of brick setting material
Technology.
Summary of the invention
The purpose of the present invention is to provide a kind of fabricating technologies of brick setting material, to solve in above-mentioned background technique
The problem of proposition.
To achieve the above object, the invention provides the following technical scheme: a kind of fabricating technology of brick setting material, is somebody's turn to do
Material specific formula is by mass are as follows:
Further, the heavy calcium carbonate is the powder that calcite, marble and lime stone are formed after broken.
Further, the S105 slag powders are the powder that is formed after crushing of metallurgy industry waste residue, main oxides at
It is divided into calcium oxide and silica, aluminium oxide and a small amount of iron oxide, density 2.6g/cm3。
Further, the cement be portland slag cement, including ordinary portland cement, portland slag cement,
Portland fly ash cement and portland-pozzolan cement.
Further, the expanded perlite is natural acidic glassy lava, white, hardness 5.7, density 2-
2.2g/cm3, granularity 1-3 mesh, 3-6 mesh, 6-8 mesh.
Further, the cellulose ether is ether structure high-molecular compound, mainly includes methyl cellulose ether, hydroxypropyl
Methyl cellulose ether and TYLOSE 30000.
Further, the water is tap water.
Further, a kind of fabricating technology of brick setting material, preparation method have following steps:
1, mixing is weighed
Following raw material are weighed up by mass parts, it is spare.Heavy calcium carbonate 2.5~15.5, S105 slag powders: 10~
35, flyash 5~25, cement 10~30.
2, the material in step 1 is put into blender, is carried out mechanical stirring 10~12 minutes.
3,0.1~0.5 part of cellulose ether is poured into 10~30 parts of water, stirring sufficiently, dissolves in cellulose ether in water.
4, the raw material prepared in step 2 and step 3 and aqueous solution are stirred 10~15 points in concrete mixer
Clock, for use.
5, the mixture being stirred in step 4 is fitted into mold, vibration moulding, time of vibration be 5~10s, 24 hours
After demould.
6, after the brick setting idiosome formed in step 5 being put into standard curing room maintenance 28 days, existing product.
Compared with prior art, the beneficial effects of the present invention are:
1. main raw material(s) used in the present invention is expanded perlite, flyash, slag, calcium carbonate and cement, water is utilized
Mud, slag and flyash are as binder, and expanded perlite is as the main aggregate for protecting building material, and light, intensity is high, resistance to
Fire can effectively mitigate the self weight of building material, and as insulating wall material, raw material cost is low, simple production process, formation
Building material high comprehensive performance, promotional value with higher；
2. the present invention utilizes S105 slag powder, flyash, the industrial residues such as expanded perlite or natural material are brick
Body main raw material(s) provides good industrial resources approach for the above industrial residue, has environment protection significance, and it is negative to mitigate environment
Lotus.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
The present invention provides a kind of technical solution: a kind of fabricating technology of brick setting material, the material specific formula are pressed
Quality is calculated as:
Heavy calcium carbonate is the powder that calcite, marble and lime stone are formed after broken, and main component is carbon
Sour calcium；
S105 slag powders are the powder that is formed after crushing of metallurgy industry waste residue, major oxide constituents be calcium oxide and
Silica, aluminium oxide and a small amount of iron oxide, density 2.6g/cm3, performance meets the standard of S105 slag；
Cement is portland slag cement, including ordinary portland cement, portland slag cement, fly ash silicate water
Mud and portland-pozzolan cement, essential mineral group become tricalcium silicate and dicalcium silicate, containing a small amount of tricalcium aluminate and
Tetra calcium aluminoferrite；
Expanded perlite is natural acidic glassy lava, white, hardness 5.7, density 2-2.2g/cm3, granularity 1-
3 mesh, 3-6 mesh, 6-8 mesh, thermal coefficient is small, has good heat insulation effect；
Cellulose ether is ether structure high-molecular compound, mainly includes methyl cellulose ether, hydroxypropyl methyl cellulose ether
And TYLOSE 30000, it is dissolved in water and alkaline solution.
A kind of fabricating technology of brick setting material, preparation method have following steps:
1, mixing is weighed
Following raw material are weighed up by mass parts, it is spare.Heavy calcium carbonate 2.5~15.5, S105 slag powders: 10~
35, flyash 5~25, cement 10~30.
2, the material in step 1 is put into blender, is carried out mechanical stirring 10~12 minutes.
3,0.1~0.5 part of cellulose ether is poured into 10~30 parts of water, stirring sufficiently, dissolves in cellulose ether in water.
4, the raw material prepared in step 2 and step 3 and aqueous solution are stirred 10~15 points in concrete mixer
Clock, for use.
5, the mixture being stirred in step 4 is fitted into mold, vibration moulding, time of vibration be 5~10s, 24 hours
After demould.
6, after the brick setting idiosome formed in step 5 being put into standard curing room maintenance 28 days, existing product.
Embodiment
A kind of fabricating technology of brick setting material, the production method have following steps:
1, mixing is weighed
Following raw material are weighed up by mass parts, it is spare.10 parts of heavy calcium carbonate, 20 parts of S105 slag powders, flyash
15 parts, 25 parts of cement.
2, the material in step 1 is put into blender, is carried out mechanical stirring 10 minutes.
3,0.3 part of part cellulose ether is poured into 30 parts of water, stirring sufficiently, dissolves in cellulose ether in water.
4, the raw material prepared in step 2 and step 3 and aqueous solution are stirred 12 minutes in concrete mixer, to
With.
5, the mixture being stirred in step 4 is fitted into mold, vibration moulding, time of vibration 8s, is taken off after 24 hours
Mould.
6, after the brick setting idiosome formed in step 5 being put into standard curing room maintenance 28 days, existing product.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of fabricating technology of brick setting material, it is characterised in that: the material specific formula is by mass are as follows:
。
2. a kind of fabricating technology of brick setting material according to claim 1, it is characterised in that: the heavy carbonic acid
Calcium powder is the powder that calcite, marble and lime stone are formed after broken.
3. a kind of fabricating technology of brick setting material according to claim 1, it is characterised in that: the S105 slag
Powder is the powder that is formed after crushing of metallurgy industry waste residue, and major oxide constituents are calcium oxide and silica, aluminium oxide and few
The iron oxide of amount, density 2.6g/cm3。
4. a kind of fabricating technology of brick setting material according to claim 1, it is characterised in that: the cement is mine
Slag portland cement, including ordinary portland cement, portland slag cement, Portland fly ash cement and volcanic ash silicic acid
Salt cement.
5. a kind of fabricating technology of brick setting material according to claim 1, it is characterised in that: the expanded pearlite
Rock is natural acidic glassy lava, white, hardness 5.7, density 2-2.2g/cm3, granularity 1-3 mesh, 3-6 mesh, 6-8 mesh.
6. a kind of fabricating technology of brick setting material according to claim 1, it is characterised in that: the cellulose ether
It mainly include methyl cellulose ether, hydroxypropyl methyl cellulose ether and TYLOSE 30000 for ether structure high-molecular compound.
7. a kind of fabricating technology of brick setting material according to claim 1, it is characterised in that: the water is originally
Water.
8. a kind of fabricating technology of brick setting material, it is characterised in that: preparation method has following steps:
1, mixing is weighed
Following raw material are weighed up by mass parts, it is spare.Heavy calcium carbonate 2.5~15.5, S105 slag powders: 10~35, powder
Coal ash 5~25, cement 10~30.
2, the material in step 1 is put into blender, is carried out mechanical stirring 10~12 minutes.
3,0.1~0.5 part of cellulose ether is poured into 10~30 parts of water, stirring sufficiently, dissolves in cellulose ether in water.
4, the raw material prepared in step 2 and step 3 and aqueous solution are stirred 10~15 minutes in concrete mixer, to
With.
5, the mixture being stirred in step 4 is fitted into mold, vibration moulding, time of vibration is 5~10s, is taken off after 24 hours
Mould.
6, after the brick setting idiosome formed in step 5 being put into standard curing room maintenance 28 days, existing product.