CN109978120A - A kind of preparation method of frosted card - Google Patents
A kind of preparation method of frosted card Download PDFInfo
- Publication number
- CN109978120A CN109978120A CN201910103118.XA CN201910103118A CN109978120A CN 109978120 A CN109978120 A CN 109978120A CN 201910103118 A CN201910103118 A CN 201910103118A CN 109978120 A CN109978120 A CN 109978120A
- Authority
- CN
- China
- Prior art keywords
- frosted
- card
- preparation
- printing layer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses the present invention to provide a kind of preparation method of frosted card, comprising the following steps: printing, bookbinding and lamination step.The lamination step is that the sense of touch film with frosted finish effect is covered on card body front protecting film, is 2.5MPa-7MPa in pressure, temperature is then to be cold-pressed at 5-25 DEG C hot pressing 2-20 minutes at 100-130 DEG C, that is, prepare the frosted card.Preparation method preparation process of the present invention is simple, and especially hot pressing temperature is low, energy conservation, the frosted card comfortable feel being prepared, and the frosting wearability for the frosted card being especially prepared is good.
Description
Technical field
The invention belongs to card preparation field, in particular to a kind of preparation method of frosted card.
Background technique
Card particular with store up stored magnetic card in people's lives using more and more common.Thus in order to
Increasing the beauty of card, people start to make frosted finish effect on card, the effect of frosted card comfortable feel is not only acted as, and
And since card face has frosted lines, the coefficient of friction of card face is increased, is lost so that card is not easy to slide.It is existing
Frosted card is prepared in technology usually using printing plate, such as patent CN103448396A, preparation process is complicated, and grinds imprinting out
Temperature when sand effect is excessively high (150-180 DEG C), not only bad for energy conservation and environmental protection and also temperature it is excessively high also high to equipment requirement, nothing
Doubting will increase cost of manufacture.
Therefore it provides a kind of preparation process is simple, preparation temperature is low, energy conservation, the preparation method of frosted card at low cost
It is necessary to.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of preparation method of frosted card.It is prepared by the preparation method
Journey is simple, and hot pressing temperature is low, energy conservation, and whole production cost is low.
In order to achieve the object of the present invention, the present invention provides a kind of preparation method of frosted card, comprising the following steps:
(1) (method of printing image-text belongs to those skilled in the art commonly side of printing to printing image-text in two sheets
Method), it is spare；
(2) it binds: using two sheet materials of step (1) preparation as upper printing layer and lower printing layer from upper and lower both direction
Element layer is clamped, layer protecting film (referred to as front protecting film) is then placed in upper printing layer and (new material stock is believed by Jiangsu China
Part Co., Ltd provides) (protective film as mass fraction containing 80% or more polyvinyl chloride, surplus is aqueous binder
Agent), lower printing surface surface also place one layer have magnetic stripe protective film (referred to as back protection film), then by front protecting film,
Upper printing layer, element layer, lower printing layer, back protection film are bound, and card body is prepared；
(3) it is laminated: the sense of touch film with frosted finish effect (is provided, product type by Guangdong Bai Jiate Industrial Co., Ltd.
It is covered on card body front protecting film for CZBJ20181028), is 2.5MPa-7MPa in pressure, temperature is 100-130 DEG C (excellent
Select 110-120 DEG C) under hot pressing 2-20 minutes (preferably 5-15 minutes), be then cold-pressed at 5-25 DEG C, finally by sense of touch film
It is separated with card body, that is, prepares the frosted card.
Further include step (4) after step (3), i.e., after the frosted card of step (3) preparation being stood 2-4 hours, is cut into
The card body for the size that meets the requirements of the customers.
A kind of frosted card is prepared by the preparation method of frosted card of the present invention.
The frosted card includes front protecting film, upper printing layer, element layer, lower printing layer, back protection film from top to bottom.
Preferably, the front protecting film with a thickness of 0.05-0.1mm (preferably 0.08mm)；The thickness of the upper printing layer
Degree is 0.1-0.2mm (preferably 0.17mm)；The element layer with a thickness of 0.25-0.40mm (preferably 0.34mm)；The lower print
Brush layer with a thickness of 0.1-0.2mm (preferably 0.17mm)；The back protection film with a thickness of 0.05-0.1mm (preferably
0.08mm)。
Preferably, step (1) sheet material is PVC (polyvinyl chloride) sheet material or paper web.
The picture and text printed in step (1) are that (such as the picture and text requirement provided according to client) prints according to actual needs
Brush, UV ink can be also possible to right and wrong UV ink by printing ink used, if UV ink, then after step (1) printing image-text also
It need to be solidified with conventional UV curing mode.
Element layer described in step (2) for memory card information data and plays the work with extraneous induction containing chip
With.
Preferably, the bookbinding in step (2) be under 140 DEG C -180 DEG C (preferably 140-160 DEG C) using hot melt by the way of
It is bound, is 2-5 seconds the time required to bookbinding.Forwarding is without using adhesion agents such as glue.
The protective film with magnetic stripe is by the magnetic stripe bought from Shanghai Li Jin Information technology Co., Ltd and the Congjiang in step (2)
The protective film of Su Huaxin new material limited liability company purchase mounts magnetic stripe on protective film at 200 ± 20 DEG C.
Preferably, the cold pressing in step (3) 1-10MPa temperature be 5-25 DEG C at be cold-pressed 5-20 minutes (preferably 8-15 divide
Clock).Pass through cooling water temperature to 5-25 DEG C after the completion of the hot pressing, is then cold-pressed.
Sense of touch film described in step (3) can be recycled.
Preferably, the frosted card with a thickness of 0.78-0.84mm.
Compared with the existing technology, beneficial effects of the present invention are as follows:
Preparation method preparation process of the present invention is simple, and especially hot pressing temperature is low, energy conservation, the frosted card being prepared
Comfortable feel, appearance are good.In addition, the frosting wearability for the frosted card that the present invention is prepared is good.
Detailed description of the invention
Fig. 1 is frosted card prepared by the embodiment of the present invention 2；Wherein 1 indicate front protecting film, 2 indicate upper printing layer, 3 tables
Show element layer, 4 indicate lower printing layer, and 5 indicate back protection film, and front protecting film surface has frosted finish effect.
Specific embodiment
In order to further allow the clear technical solution of the present invention of those skilled in the art, following embodiment is now enumerated
It is illustrated.It should be noted that following embodiment does not constitute a limitation effect to protection scope of the present invention.
Embodiment 1
A kind of preparation method of frosted card, comprising the following steps:
(1) printing image-text in two sheets, it is spare；
(2) it binds: using two sheet materials of step (1) preparation as upper printing layer and lower printing layer from upper and lower both direction
Element layer is clamped, layer protecting film (referred to as front protecting film) is then placed in upper printing layer and (new material stock is believed by Jiangsu China
Part Co., Ltd provides), one layer of protective film (referred to as back protection film) for having magnetic stripe is also placed on lower printing surface surface, then will
Front protecting film, upper printing layer, element layer, lower printing layer, back protection film are bound, and card body is prepared；
(3) it is laminated: the sense of touch film with frosted finish effect is covered on card body front protecting film, be 2.5MPa- in pressure
7MPa, temperature are then to be cold-pressed at 20 DEG C hot pressing 2 minutes at 100 DEG C, finally separate sense of touch film with card body, that is, make
The standby frosted card.
Step (1) sheet material is PVC (polyvinyl chloride) sheet material.
Element layer described in step (2) contains chip, for memory card information data and plays the work with extraneous induction
With.
Bookbinding in step (2) is bound by the way of hot melt at 140 DEG C, is 2 seconds the time required to bookbinding.Dress
Process is ordered without using adhesion agents such as glue.
Cold pressing in step (3) is cold-pressed 5 minutes at being 20 DEG C in 2MPa temperature.
The frosted card includes front protecting film, upper printing layer, element layer, lower printing layer, back protection film from top to bottom.
The front protecting film with a thickness of 0.05mm；The upper printing layer with a thickness of 0.1mm；The thickness of the element layer
Degree is 0.25mm；The lower printing layer with a thickness of 0.1mm；The back protection film with a thickness of 0.05mm.
Embodiment 2
A kind of preparation method of frosted card, comprising the following steps:
(1) printing image-text in two sheets, it is spare；
(2) it binds: using two sheet materials of step (1) preparation as upper printing layer and lower printing layer from upper and lower both direction
Element layer is clamped, layer protecting film (referred to as front protecting film) is then placed in upper printing layer and (new material stock is believed by Jiangsu China
Part Co., Ltd provides), one layer of protective film (referred to as back protection film) for having magnetic stripe is also placed on lower printing surface surface, then will
Front protecting film, upper printing layer, element layer, lower printing layer, back protection film are bound, and card body is prepared；
(3) it is laminated: the sense of touch film with frosted finish effect is covered on card body front protecting film, be 3MPa, temperature in pressure
Then degree was cold-pressed at 25 DEG C for hot pressing 10 minutes at 110 DEG C, and was finally separated sense of touch film with card body, that is, prepare described in
Frosted card.
Step (1) sheet material is PVC sheet.
Bookbinding in step (2) is bound by the way of hot melt at 140 DEG C, is 3 seconds the time required to bookbinding.Dress
Process is ordered without using adhesion agents such as glue.
Cold pressing in step (3) is cold-pressed 10 minutes at 3MPa.
The frosted card includes front protecting film, upper printing layer, element layer, lower printing layer, back protection film from top to bottom.
The front protecting film with a thickness of 0.08mm；The upper printing layer with a thickness of 0.17mm；The element layer
With a thickness of 0.34mm；The lower printing layer with a thickness of 0.17mm；The back protection film with a thickness of 0.08mm.
The structural schematic diagram of frosted card prepared by embodiment 2 is as shown in Figure 1, wherein 1 indicate front protecting film, 2 indicate
Printing layer, 3 indicate element layer, and 4 indicate lower printing layer, and 5 indicate back protection film, and front protecting film surface has frosted finish effect.
Embodiment 3
A kind of preparation method of frosted card, comprising the following steps:
(1) printing image-text in two sheets, it is spare；
(2) it binds: using two sheet materials of step (1) preparation as upper printing layer and lower printing layer from upper and lower both direction
Element layer is clamped, layer protecting film (referred to as front protecting film) is then placed in upper printing layer and (new material stock is believed by Jiangsu China
Part Co., Ltd provides), one layer of protective film (referred to as back protection film) for having magnetic stripe is also placed on lower printing surface surface, then will
Front protecting film, upper printing layer, element layer, lower printing layer, back protection film are bound, and card body is prepared；
(3) it is laminated: the sense of touch film with frosted finish effect is covered on card body front protecting film, be 7MPa, temperature in pressure
Then degree was cold-pressed at 10 DEG C for hot pressing 20 minutes at 130 DEG C, and was finally separated sense of touch film with card body, that is, prepare described in
Frosted card.
Step (1) sheet material is paper web.
Element layer described in step (2) contains chip, for memory card information data and plays the work with extraneous induction
With.
Bookbinding in step (2) is bound by the way of hot melt at 150 DEG C, is 5 seconds the time required to bookbinding.Dress
Process is ordered without using adhesion agents such as glue.
Cold pressing in step (3) is cold-pressed 8 minutes at 8MPa.
The frosted card includes front protecting film, upper printing layer, element layer, lower printing layer, back protection film from top to bottom.
The front protecting film with a thickness of 0.1mm；The upper printing layer with a thickness of 0.2mm；The thickness of the element layer
Degree is 0.40mm；The lower printing layer with a thickness of 0.2mm；The back protection film with a thickness of 0.1mm.
Comparative example 1
Compared with Example 2, the hot pressing temperature in the step (3) in comparative example 1 is 80 DEG C.Remaining preparation process is identical.
Comparative example 2
Compared with Example 3, the pressure of the hot pressing in the step (3) in comparative example 2 is 1MPa.Remaining preparation process phase
Together.
Product measure of merit
Embodiment 1-3 and comparative example the 1-2 product prepared and commercially available frosted are stuck under 0.5Kg pressure and dry grind 1000
It is secondary, the degree of wear (degree of wear is divided into without abrasion, slight, heavier and serious) and feel of the frosting of card is then observed again
(feel is divided into no frosted sense of touch, slight frosted sense of touch and strong frosted sense of touch), the results are shown in Table 1.
Table 1:
As it can be seen from table 1 the Wear Resistance performance of 1-3 of embodiment of the present invention preparation is better than comparative example 1-2 preparation
The wearability performance of product and commercially available frosted card.Particularly, the product of 1-3 of embodiment of the present invention preparation is after wear test
There are also strong frosted senses of touch, it is seen that the product frosted function admirable of 1-3 of embodiment of the present invention preparation, better than comparative example 1-2 preparation
Product and commercially available frosted card.
Claims (9)
1. a kind of preparation method of frosted card, which comprises the following steps:
(1) printing image-text in two sheets, it is spare；
(2) it binds: two sheet materials of step (1) preparation is clamped as upper printing layer and lower printing layer from upper and lower both direction
Then element layer places front protecting film in upper printing layer, place back protection film on lower printing surface surface, then front is protected
Cuticula, upper printing layer, element layer, lower printing layer, back protection film are bound, and card body is prepared；
(3) it is laminated: the sense of touch film with frosted finish effect is covered on card body front protecting film, be 2.5MPa-7MPa in pressure,
Temperature is hot pressing at 100-130 DEG C, is then cold-pressed at 5-25 DEG C, that is, prepares the frosted card.
2. preparation method according to claim 1, which is characterized in that step (1) sheet material is PVC sheet or papery piece
Material.
3. preparation method according to claim 1, which is characterized in that the bookbinding in step (2) be at 140-180 DEG C into
Luggage is ordered.
4. preparation method according to claim 1, which is characterized in that the cold pressing in step (3) is cold-pressed 5- at 1-10MPa
20 minutes.
5. preparation method according to claim 1, which is characterized in that the hot pressing time in step (3) is 2-20 minutes.
6. a kind of frosted card, which is characterized in that frosted card preparation method as described in any one of claim 1-5 is prepared into
It arrives.
7. frosted card according to claim 6, which is characterized in that the frosted card successively includes front protecting from top to bottom
Film (1), upper printing layer (2), element layer (3), lower printing layer (4) and back protection film (5).
8. the frosted card according to any one of claim 6-7, which is characterized in that the front protecting film with a thickness of
0.05-0.1mm；The upper printing layer with a thickness of 0.1-0.2mm；The element layer with a thickness of 0.25-0.40mm；Under described
Printing layer with a thickness of 0.1-0.2mm；The back protection film with a thickness of 0.05-0.1mm.
9. the frosted card according to any one of claim 6-7, which is characterized in that the frosted card with a thickness of 0.78-
0.84mm。