CN109972294A - A kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging - Google Patents
A kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging Download PDFInfo
- Publication number
- CN109972294A CN109972294A CN201910276048.8A CN201910276048A CN109972294A CN 109972294 A CN109972294 A CN 109972294A CN 201910276048 A CN201910276048 A CN 201910276048A CN 109972294 A CN109972294 A CN 109972294A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- break
- flour packaging
- preparation process
- type non
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation processes of break-resistance tensile type non-woven fabrics flour packaging, including 3s non-woven fabrics, the 3s non-woven fabrics includes polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent, and reinforced modifier, the preparation process of the break-resistance tensile type non-woven fabrics flour packaging include the following steps;By adding polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent in a manufacturing process, and reinforced modifier, the fiber of aramid fiber and high-tenacity terylene degree is also used simultaneously, and in post-production, flour packaging both sides carry out sewing both sides by automatic sewing, so that manufactured non-woven fabrics break-resistance and tensile property are greatly promoted, avoid being damaged in use and caused by rupture, simultaneously when flour is loaded in inside, provided endurance is also improved, and greatly reduces the use limitation of existing non-woven fabrics flour packaging.
Description
Technical field
The invention belongs to field of nonwoven fabric technology, and in particular to a kind of preparation of break-resistance tensile type non-woven fabrics flour packaging
Technique.
Background technique
Non-woven fabrics flour packaging is widely used very early, at present with 2.5kg, 5kg, 10kg metering in supermarket
Based on non-woven fabrics flour packaging, there are also 50kg non-woven fabrics flour packagings.Non-woven fabrics safety and environmental protection, ventilative pole are stored conducive to flour,
It was substituted cloth bag in recent years, woven bag becomes the mainstream of flour packaging.Non-woven fabrics flour packaging is quality-high and inexpensive, is flour packet
The first choice of dress, more suitable for the slightly higher flour packaging of class, wherein the kind to non-woven fabrics is also classified, 3s non-woven fabrics is then
One of model in kind used.
Existing non-woven fabrics flour packaging still has some shortcomings when in use: existing non-woven fabrics flour packaging
In use, it needs to fill the objects such as powder of having one's face covered with, therefore flour packaging made of non-woven fabrics is in bulging state in use, is needed
Biggish Inner extrusion power is provided, while non-woven fabrics is relatively easy to again by various damages such as outside scuffings, so as to cause surface
It ruptures, causes the waste of product, the break-resistance tensile property needs of non-woven fabrics flour packaging are improved.
Summary of the invention
The purpose of the present invention is to provide a kind of preparation processes of break-resistance tensile type non-woven fabrics flour packaging, on solving
State the problem of proposing in background technique.
To achieve the above object, the invention provides the following technical scheme: a kind of break-resistance tensile type non-woven fabrics flour packaging
Preparation process, including 3s non-woven fabrics, the 3s non-woven fabrics include polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softness
Agent and reinforced modifier, the preparation process of the break-resistance tensile type non-woven fabrics flour packaging the following steps are included:
Step 1: by polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, according to one
Certainty ratio is placed in mixing drum, and is mixed uniformly, and high strength fibre is added after mixing, is stirred, dry;
Step 2: the fiber dried in step 1 is sent into opener mixed cotton, and is combed into linearly, fibre web is made
Shape;
Step 3: linearly fibre web is sent into lapping machine, and is mutually laid in 90 degree of intersections;
Step 4: obtained fibre web is sent to drafting machine.
Step 5: under being continuously conveyed of Web forming conveyer belt, continuous fibre web passes through hot-rolling mill.
Step 6: under the rolloff effect of hot-rolling mill, fibre web forms non-woven fabrics.
Step 7: nonwoven surface obtained in step 6 is printed, overlay film, automatic moulding, automatic sewing, is packaged
It examines;
Step 8: flour packaging specification after molding is 0.5,1,1.5,2.5,5,10,25kg.
Preferably, high strength fibre includes the fibers such as aramid fiber and terylene in the step 1.
Preferably, the softening agent is CE either SCM at least one therein.
Preferably, the reinforced modifier is nacrite, calcium carbonate, talcum powder, mica powder, wollastonite, kaolin, hydrogen
Aluminium oxide, magnesium hydroxide at least one therein.
Preferably, the drafting multiple of drafting machine is 2.8~3.7 in the step 4.
Preferably, a length of 3~5 hours when dry in the step 1, temperature is 70~120 DEG C.
Preferably, the polypropylene proportion is 40%~60%, and the nanometer polytetrafluoroethylcomposite proportion is 3%
~5%.
Compared with prior art, the beneficial effects of the present invention are: by adding polypropylene, poly- isobutyl in a manufacturing process
Alkene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, while the fiber of aramid fiber and high-tenacity terylene degree is also used, with
And in post-production, flour packaging both sides carry out sewing both sides by automatic sewing so that manufactured non-woven fabrics break-resistance and
Tensile property is greatly promoted, avoid being damaged in use and caused by rupture, while when flour is loaded in inside,
Provided endurance is also improved, and greatly reduces the use limitation of existing non-woven fabrics flour packaging.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
Embodiment 1
The present invention provides a kind of technical solution: a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging, including
3s non-woven fabrics, 3s non-woven fabrics include polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, are prevented
Rupture tensile type non-woven fabrics flour packaging preparation process the following steps are included:
Step 1: by polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, according to one
Certainty ratio is placed in mixing drum, and is mixed uniformly, and high strength fibre is added after mixing, is stirred, dry;
Step 2: the fiber dried in step 1 is sent into opener mixed cotton, and is combed into linearly, fibre web is made
Shape;
Step 3: linearly fibre web is sent into lapping machine, and is mutually laid in 90 degree of intersections;
Step 4: obtained fibre web is sent to drafting machine.
Step 5: under being continuously conveyed of Web forming conveyer belt, continuous fibre web passes through hot-rolling mill.
Step 6: under the rolloff effect of hot-rolling mill, fibre web forms non-woven fabrics.
Step 7: nonwoven surface obtained in step 6 is printed, overlay film, automatic moulding, automatic sewing, is packaged
It examines;
Step 8: flour packaging specification after molding is 0.5,1,1.5,2.5,5,10,25kg.
In the present embodiment, it is preferred that high strength fibre includes the fibers such as aramid fiber and terylene in step 1.
In the present embodiment, it is preferred that softening agent SCM.
In the present embodiment, it is preferred that reinforced modifier is magnesium hydroxide.
In the present embodiment, it is preferred that the drafting multiple of drafting machine is 2.8 in step 4.
In the present embodiment, it is preferred that a length of 3 hours when dry in step 1, temperature is 70 DEG C.
In the present embodiment, it is preferred that polypropylene proportion is 40%, and nanometer polytetrafluoroethylcomposite proportion is 3%.
Embodiment 2
The present invention provides a kind of technical solution: a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging, including
3s non-woven fabrics, 3s non-woven fabrics include polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, are prevented
Rupture tensile type non-woven fabrics flour packaging preparation process the following steps are included:
Step 1: by polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, according to one
Certainty ratio is placed in mixing drum, and is mixed uniformly, and high strength fibre is added after mixing, is stirred, dry;
Step 2: the fiber dried in step 1 is sent into opener mixed cotton, and is combed into linearly, fibre web is made
Shape;
Step 3: linearly fibre web is sent into lapping machine, and is mutually laid in 90 degree of intersections;
Step 4: obtained fibre web is sent to drafting machine.
Step 5: under being continuously conveyed of Web forming conveyer belt, continuous fibre web passes through hot-rolling mill.
Step 6: under the rolloff effect of hot-rolling mill, fibre web forms non-woven fabrics.
Step 7: nonwoven surface obtained in step 6 is printed, overlay film, automatic moulding, automatic sewing, is packaged
It examines;
Step 8: flour packaging specification after molding is 0.5,1,1.5,2.5,5,10,25kg.
In the present embodiment, it is preferred that high strength fibre includes the fibers such as aramid fiber and terylene in step 1.
In the present embodiment, it is preferred that softening agent CE.
In the present embodiment, it is preferred that reinforced modifier is mica powder.
In the present embodiment, it is preferred that the drafting multiple of drafting machine is 3.4 in step 4.
In the present embodiment, it is preferred that a length of 3.5 hours when dry in step 1, temperature is 80 DEG C.
In the present embodiment, it is preferred that polypropylene proportion is 45%, and nanometer polytetrafluoroethylcomposite proportion is 3.5%.
Embodiment 3
The present invention provides a kind of technical solution: a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging, including
3s non-woven fabrics, 3s non-woven fabrics include polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, are prevented
Rupture tensile type non-woven fabrics flour packaging preparation process the following steps are included:
Step 1: by polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, according to one
Certainty ratio is placed in mixing drum, and is mixed uniformly, and high strength fibre is added after mixing, is stirred, dry;
Step 2: the fiber dried in step 1 is sent into opener mixed cotton, and is combed into linearly, fibre web is made
Shape;
Step 3: linearly fibre web is sent into lapping machine, and is mutually laid in 90 degree of intersections;
Step 4: obtained fibre web is sent to drafting machine.
Step 5: under being continuously conveyed of Web forming conveyer belt, continuous fibre web passes through hot-rolling mill.
Step 6: under the rolloff effect of hot-rolling mill, fibre web forms non-woven fabrics.
Step 7: nonwoven surface obtained in step 6 is printed, overlay film, automatic moulding, automatic sewing, is packaged
It examines;
Step 8: flour packaging specification after molding is 0.5,1,1.5,2.5,5,10,25kg.
In the present embodiment, it is preferred that high strength fibre includes the fibers such as aramid fiber and terylene in step 1.
In the present embodiment, it is preferred that softening agent SCM.
In the present embodiment, it is preferred that reinforced modifier is nacrite.
In the present embodiment, it is preferred that the drafting multiple of drafting machine is 3 in step 4.
In the present embodiment, it is preferred that a length of 4 hours when dry in step 1, temperature is 100 DEG C.
In the present embodiment, it is preferred that polypropylene proportion is 50%, and nanometer polytetrafluoroethylcomposite proportion is 4%.
Embodiment 4
The present invention provides a kind of technical solution: a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging, including
3s non-woven fabrics, 3s non-woven fabrics include polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, are prevented
Rupture tensile type non-woven fabrics flour packaging preparation process the following steps are included:
Step 1: by polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, according to one
Certainty ratio is placed in mixing drum, and is mixed uniformly, and high strength fibre is added after mixing, is stirred, dry;
Step 2: the fiber dried in step 1 is sent into opener mixed cotton, and is combed into linearly, fibre web is made
Shape;
Step 3: linearly fibre web is sent into lapping machine, and is mutually laid in 90 degree of intersections;
Step 4: obtained fibre web is sent to drafting machine.
Step 5: under being continuously conveyed of Web forming conveyer belt, continuous fibre web passes through hot-rolling mill.
Step 6: under the rolloff effect of hot-rolling mill, fibre web forms non-woven fabrics.
Step 7: nonwoven surface obtained in step 6 is printed, overlay film, automatic moulding, automatic sewing, is packaged
It examines;
Step 8: flour packaging specification after molding is 0.5,1,1.5,2.5,5,10,25kg.
In the present embodiment, it is preferred that high strength fibre includes the fibers such as aramid fiber and terylene in step 1.
In the present embodiment, it is preferred that softening agent CE.
In the present embodiment, it is preferred that reinforced modifier is magnesium hydroxide.
In the present embodiment, it is preferred that the drafting multiple of drafting machine is 3.7 in step 4.
In the present embodiment, it is preferred that a length of 5 hours when dry in step 1, temperature is 120 DEG C.
In the present embodiment, it is preferred that polypropylene proportion is 60%, and nanometer polytetrafluoroethylcomposite proportion is 5%.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging, including 3s non-woven fabrics, it is characterised in that: the 3s
Non-woven fabrics includes polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, and the break-resistance is anti-
The preparation process of pull-up non-woven fabrics flour packaging the following steps are included:
Step 1: by polypropylene, polyisobutene, nanometer polytetrafluoroethylcomposite and softening agent and reinforced modifier, according to certain ratio
Example is placed in mixing drum, and is mixed uniformly, and high strength fibre is added after mixing, is stirred, dry;
Step 2: the fiber dried in step 1 is sent into opener mixed cotton, and is combed into linearly, fibre web shape is made;
Step 3: linearly fibre web is sent into lapping machine, and is mutually laid in 90 degree of intersections;
Step 4: obtained fibre web is sent to drafting machine.
Step 5: under being continuously conveyed of Web forming conveyer belt, continuous fibre web passes through hot-rolling mill.
Step 6: under the rolloff effect of hot-rolling mill, fibre web forms non-woven fabrics.
Step 7: nonwoven surface obtained in step 6 is printed, overlay film, automatic moulding, automatic sewing, is packaged inspection
It tests;
Step 8: flour packaging specification after molding is 0.5,1,1.5,2.5,5,10,25kg.
2. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging according to claim 1, it is characterised in that:
High strength fibre includes the fibers such as aramid fiber and terylene in the step 1.
3. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging according to claim 1, it is characterised in that:
The softening agent is CE either SCM at least one therein.
4. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging according to claim 1, it is characterised in that:
The reinforced modifier is nacrite, calcium carbonate, talcum powder, mica powder, wollastonite, kaolin, aluminium hydroxide, magnesium hydroxide
At least one therein.
5. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging according to claim 1, it is characterised in that:
The drafting multiple of drafting machine is 2.8~3.7 in the step 4.
6. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging according to claim 1, it is characterised in that:
A length of 3~5 hours when dry in the step 1, temperature is 70~120 DEG C.
7. a kind of preparation process of break-resistance tensile type non-woven fabrics flour packaging according to claim 1, it is characterised in that:
The polypropylene proportion is 40%~60%, and the nanometer polytetrafluoroethylcomposite proportion is 3%~5%.