CN109972268A - A kind of cooling ventilating fabric - Google Patents
A kind of cooling ventilating fabric Download PDFInfo
- Publication number
- CN109972268A CN109972268A CN201910300275.XA CN201910300275A CN109972268A CN 109972268 A CN109972268 A CN 109972268A CN 201910300275 A CN201910300275 A CN 201910300275A CN 109972268 A CN109972268 A CN 109972268A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- fiber
- weft
- warp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of cooling ventilating fabric, including warp and weft, warp includes the flax fiber of 20-27 parts by weight, the bamboo fiber of 10-20 parts by weight, the china-hemp fibers of 30-33 parts by weight, the tencel fiber of 3-7 parts by weight and the polypropylene fibre of 28-35 parts by weight, weft includes the cotton fiber of 20-25 parts by weight, the More of 35-40 parts by weight is for fiber, the polypropylene fibre of 32-38 parts by weight and the mint fibers of 8-13 parts by weight, compared with prior art, the present invention has following the utility model has the advantages that by by flax fiber, bamboo fiber, china-hemp fibers, tencel fiber and polypropylene fibre mixing, and by cotton fiber, More is for fiber, polypropylene fibre and mint fibers mixing, it is woven into and radiates with moisture absorption, the fabric of cooling ventilating, it mentions The comfort of height dress.
Description
Technical field
The present invention is a kind of cooling ventilating fabric, belongs to fabric field.
Background technique
With the improvement of material living standards, requirement of the people to textile is no longer limited to keep warm, is comfortable etc. and is original
Fundamental characteristics.Therefore, dress materials are to adapt to trend, need to become diversification, multifunction.Currently, clothes material in the market
Material is functional homogenous material, is not suitable as dress materials and adapts to trend.Currently, general chemical & blended fabric is due to hygroscopicity
Difference, snugness of fit be not high.
Summary of the invention
In view of the deficienciess of the prior art, it is an object of the present invention to provide a kind of cooling ventilating fabric, to solve above-mentioned back
The problem of being proposed in scape technology.
To achieve the goals above, the present invention is to realize by the following technical solutions: a kind of cooling ventilating fabric, packet
Warp and weft are included, the warp includes the flax fiber of 20-27 parts by weight, the bamboo fiber of 10-20 parts by weight, 30-33 weight
The china-hemp fibers, the tencel fiber of 3-7 parts by weight and the polypropylene fibre of 28-35 parts by weight of part are measured, the weft includes 20-
The cotton fibers of 25 parts by weight, 35-40 parts by weight More for fiber, the polypropylene fibre of 32-38 parts by weight and 8-13 weight
The mint fibers of part.
A kind of cooling ventilating fabric, is prepared by the following steps:
Step 1: the Chinese fiber crops of the flax fiber of 20-27 parts by weight, the bamboo fiber of 10-20 parts by weight, 30-33 parts by weight are fine
The polypropylene fibre of dimension, the tencel fiber of 3-7 parts by weight and 28-35 parts by weight is added to the mixer, and is added into mixing machine
Enter 3-5g/L softening agent, 60-65 DEG C of temperature, mixes 30-40 minutes, warp blended product is made, the cotton of 20-25 parts by weight is fine
It ties up, the More of 35-40 parts by weight adds for the mint fibers of fiber, the polypropylene fibre of 32-38 parts by weight and 8-13 parts by weight
Enter in mixing machine, and 3-5g/L softening agent is added into mixing machine, 60-65 DEG C of temperature, mixes 30-40 minutes, it is mixed that weft is made
Spun articles；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 190~200 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 10-15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
Further, the softening agent is a kind of ester based quaternary ammonium salt.
Beneficial effects of the present invention: a kind of cooling ventilating fabric of the invention, because the present invention passes through flax fiber, bamboo original
Fiber, china-hemp fibers, tencel fiber and polypropylene fibre mixing, and by cotton fiber, More for fiber, polypropylene fibre with
And mint fibers mixing, it is woven into the fabric with moisture absorption heat dissipation, cooling ventilating, improves the comfort of dress.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
The present invention provides a kind of technical solution: a kind of cooling ventilating fabric, including warp and weft, warp include 20-27
The flax fiber of parts by weight, the bamboo fiber of 10-20 parts by weight, the china-hemp fibers of 30-33 parts by weight, 3-7 parts by weight tencel
The polypropylene fibre of fiber and 28-35 parts by weight, weft include the More of the cotton fiber of 20-25 parts by weight, 35-40 parts by weight
For the mint fibers of fiber, the polypropylene fibre of 32-38 parts by weight and 8-13 parts by weight.
A kind of cooling ventilating fabric, is prepared by the following steps:
Step 1: the Chinese fiber crops of the flax fiber of 20-27 parts by weight, the bamboo fiber of 10-20 parts by weight, 30-33 parts by weight are fine
The polypropylene fibre of dimension, the tencel fiber of 3-7 parts by weight and 28-35 parts by weight is added to the mixer, and is added into mixing machine
Enter 3-5g/L softening agent, 60-65 DEG C of temperature, mixes 30-40 minutes, warp blended product is made, the cotton of 20-25 parts by weight is fine
It ties up, the More of 35-40 parts by weight adds for the mint fibers of fiber, the polypropylene fibre of 32-38 parts by weight and 8-13 parts by weight
Enter in mixing machine, and 3-5g/L softening agent is added into mixing machine, 60-65 DEG C of temperature, mixes 30-40 minutes, it is mixed that weft is made
Spun articles；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 190~200 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 10-15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
Softening agent is a kind of ester based quaternary ammonium salt.
Embodiment 1: warp include the flax fiber of 22 parts by weight, the bamboo fiber of 13 parts by weight, 31 parts by weight the Chinese fiber crops
The polypropylene fibre of fiber, the tencel fiber of 4 parts by weight and 30 parts by weight, weft include the cotton fiber of 21 parts by weight, 36 weights
Measure the mint fibers of the More for fiber, the polypropylene fibre of 32 parts by weight and 11 parts by weight of part；
Preparation step:
Step 1: by the flax fiber of 22 parts by weight, the bamboo fiber of 13 parts by weight, the china-hemp fibers of 31 parts by weight, 4 parts by weight
Tencel fiber and the polypropylene fibres of 30 parts by weight be added to the mixer, and 5g/L softening agent is added into mixing machine, temperature
Degree 65 DEG C, mix 40 minutes, be made warp blended product, by the cotton fiber of 21 parts by weight, 36 parts by weight More for fiber, 32
The polypropylene fibre of parts by weight and the mint fibers of 11 parts by weight are added to the mixer, and 5g/L softness is added into mixing machine
Agent 65 DEG C of temperature, mixes 40 minutes, weft blended product is made；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 200 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
Embodiment 2:
Warp includes the flax fiber of 25 parts by weight, the bamboo fiber of 11 parts by weight, the china-hemp fibers of 30 parts by weight, 6 parts by weight
Tencel fiber and 28 parts by weight polypropylene fibre, weft includes More's generation of the cotton fiber of 20 parts by weight, 35 parts by weight
The mint fibers of fiber, the polypropylene fibre of 36 parts by weight and 9 parts by weight；
Preparation step:
Step 1: by the flax fiber of 25 parts by weight, the bamboo fiber of 11 parts by weight, the china-hemp fibers of 30 parts by weight, 6 parts by weight
Tencel fiber and the polypropylene fibres of 28 parts by weight be added to the mixer, and 4g/L softening agent is added into mixing machine, temperature
Degree 60 DEG C, mix 30 minutes, be made warp blended product, by the cotton fiber of 20 parts by weight, 35 parts by weight More for fiber, 36
The polypropylene fibre of parts by weight and the mint fibers of 9 parts by weight are added to the mixer, and 4g/L softness is added into mixing machine
Agent, temperature 60 C mix 30 minutes, and weft blended product is made；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 190 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
Embodiment 3: warp include the flax fiber of 23 parts by weight, the bamboo fiber of 12 parts by weight, 33 parts by weight china-hemp fibers,
The polypropylene fibre of the tencel fiber of 3 parts by weight and 29 parts by weight, weft include the cotton fiber of 25 parts by weight, 35 parts by weight
Mint fibers of the More for fiber, the polypropylene fibre of 32 parts by weight and 8 parts by weight；
Preparation step:
Step 1: by the flax fiber of 23 parts by weight, the bamboo fiber of 12 parts by weight, the china-hemp fibers of 33 parts by weight, 3 parts by weight
Tencel fiber and the polypropylene fibres of 29 parts by weight be added to the mixer, and 5g/L softening agent is added into mixing machine, temperature
Degree 60 DEG C, mix 40 minutes, be made warp blended product, by the cotton fiber of 25 parts by weight, 35 parts by weight More for fiber, 32
The polypropylene fibre of parts by weight and the mint fibers of 8 parts by weight are added to the mixer, and 5g/L softness is added into mixing machine
Agent, temperature 60 C mix 40 minutes, and weft blended product is made；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 200 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
Embodiment 4: warp include the flax fiber of 20 parts by weight, the bamboo fiber of 15 parts by weight, 30 parts by weight china-hemp fibers,
The polypropylene fibre of the tencel fiber of 7 parts by weight and 28 parts by weight, weft include the cotton fiber of 22 parts by weight, 37 parts by weight
Mint fibers of the More for fiber, the polypropylene fibre of 32 parts by weight and 9 parts by weight；
Preparation step:
Step 1: by warp include the flax fiber of 20 parts by weight, the bamboo fiber of 15 parts by weight, 30 parts by weight china-hemp fibers,
The tencel fiber of 7 parts by weight and the polypropylene fibre of 28 parts by weight are added to the mixer, and addition 5g/L is soft into mixing machine
Soft dose, temperature 60 C mixes 30 minutes, warp blended product is made, by the cotton fiber of 22 parts by weight, More's generation of 37 parts by weight
The mint fibers of fiber, the polypropylene fibre of 32 parts by weight and 9 parts by weight are added to the mixer, and are added into mixing machine
5g/L softening agent, temperature 60 C mix 30 minutes, and weft blended product is made；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 200 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention, for those skilled in the art
For member, it is clear that invention is not limited to the details of the above exemplary embodiments, and without departing substantially from spirit of the invention or substantially
In the case where feature, the present invention can be realized in other specific forms.Therefore, in all respects, should all will implement
Example regards exemplary as, and is non-limiting, and the scope of the present invention is by appended claims rather than above description limits
It is fixed, it is intended that including all changes that fall within the meaning and scope of the equivalent elements of the claims in the present invention.
In addition, it should be understood that although this specification is described in terms of embodiments, but not each embodiment is only wrapped
Containing an independent technical solution, this description of the specification is merely for the sake of clarity, and those skilled in the art should
It considers the specification as a whole, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
The other embodiments being understood that.
Claims (3)
1. a kind of cooling ventilating fabric, including warp and weft, it is characterised in that: the warp includes the Asia of 20-27 parts by weight
Flaxen fiber, the bamboo fiber of 10-20 parts by weight, the china-hemp fibers of 30-33 parts by weight, 3-7 parts by weight tencel fiber and 28-
The polypropylene fibre of 35 parts by weight, the weft include the cotton fiber of 20-25 parts by weight, 35-40 parts by weight More for fiber,
The polypropylene fibre of 32-38 parts by weight and the mint fibers of 8-13 parts by weight.
2. a kind of cooling ventilating fabric according to claim 1, it is characterised in that: be prepared by the following steps:
Step 1: the Chinese fiber crops of the flax fiber of 20-27 parts by weight, the bamboo fiber of 10-20 parts by weight, 30-33 parts by weight are fine
The polypropylene fibre of dimension, the tencel fiber of 3-7 parts by weight and 28-35 parts by weight is added to the mixer, and is added into mixing machine
Enter 3-5g/L softening agent, 60-65 DEG C of temperature, mixes 30-40 minutes, warp blended product is made, the cotton of 20-25 parts by weight is fine
It ties up, the More of 35-40 parts by weight adds for the mint fibers of fiber, the polypropylene fibre of 32-38 parts by weight and 8-13 parts by weight
Enter in mixing machine, and 3-5g/L softening agent is added into mixing machine, 60-65 DEG C of temperature, mixes 30-40 minutes, it is mixed that weft is made
Spun articles；
Step 2: after the warp blended product generated in step 1 and weft blended product are woven into warp and weft respectively, adopting
Warp and weft are woven into cloth with air-jet loom；
Step 3: within the temperature range of 190~200 DEG C, making cloth circulation colouring incessantly in continuous 12 hours in dye vat；
Step 4: cloth after dyeing being taken out, with 90 DEG C of warm water repeated flushing 10-15min, is drained；
Step 5: the cloth drained in step 4 is subjected to high-temperature shaping in the case where temperature is greater than 130 DEG C with forming machine.
3. a kind of cooling ventilating fabric according to claim 2, it is characterised in that: the softening agent is a kind of ester group quaternary ammonium
Salt.