CN109943393A - A kind of intermetallic composite coating emulsion - Google Patents
A kind of intermetallic composite coating emulsion Download PDFInfo
- Publication number
- CN109943393A CN109943393A CN201711390716.7A CN201711390716A CN109943393A CN 109943393 A CN109943393 A CN 109943393A CN 201711390716 A CN201711390716 A CN 201711390716A CN 109943393 A CN109943393 A CN 109943393A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite coating
- intermetallic composite
- coating emulsion
- emulsion according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of intermetallic composite coating emulsion and its preparation process is disclosed, it includes the raw materials of following quality proportioning: 30-80 parts of base oil, 5-10 parts of water, 5-15 parts of dodecenylsuccinic acid, 5-10 parts of calcium mahogany sulfonate, 1-5 parts of alkyl glucoside, 2-8 parts of sulfurized lard, 2-5 parts of chlorinated paraffin.The present invention has excellent stability, can be used as universal metal working fluid substitute mineral oil metalworking fluid, and its processing performance and environmental-protecting performance are better than common mineral oil base working fluid.
Description
Technical field
The invention belongs to field of machining, more particularly, to a kind of intermetallic composite coating emulsion.
Background technique
In general, people generally use oil base working fluid or oil emulsion in process of metal working, oil base working fluid is difficult to clearly
It washes, easily stays spot, environmental pollution is serious；And it needs to stablize within the scope of very high ph-values.
Intermetallic composite coating emulsion is a kind of in process of metal working, for cooling down and lubricating the work of cutter and workpiece
Industry liquid.Intermetallic composite coating emulsion from a variety of super strong functional auxiliary agents through science it is compound with form, be provided simultaneously with good cold
But performance, greasy property, rustless property, oil removing cleaning function, anti-corrosion function, easily dilutable feature overcome traditional soap base emulsification
The difficult dilution of easily smelly, winter in liquid summer, rust-proof effect difference defect, also have no adverse effects to lathe paint
Summary of the invention
In order to achieve the above objectives, the technical scheme of the present invention is realized as follows:
A kind of intermetallic composite coating emulsion proposed according to the present invention includes according to the mass fraction base oil 30-80 parts, water
5-10 parts, 5-15 parts of dodecenylsuccinic acid, 5-10 parts of calcium mahogany sulfonate, 1-5 parts of alkyl glucoside, 2-8 parts of sulfurized lard, chlorine
2-5 parts of fossil waxes.
The object of the invention to solve the technical problems also can be used following technical measures and further realize.
Intermetallic composite coating emulsion above-mentioned, based on quality amount number, include base oil 40-60 parts, 5-8 parts of water, laurylene
10-15 parts of base succinic acid, 5-8 parts of calcium mahogany sulfonate, 1-3 parts of alkyl glucoside, 3-6 parts of sulfurized lard, 2-3 parts of chlorinated paraffin.
Further, the base oil is mineral oil, vegetable oil or synthetic ester.
Meanwhile the invention also provides a kind of preparation processes of intermetallic composite coating emulsion, the specific steps of which are as follows:
(base oil, alkyl glucoside and water are squeezed into blender heating stirring by than column by (1), and intermixture is made；
(2) it is cooled to room temperature for be mixed dose, under the conditions of high-speed stirred, by dodecenylsuccinic acid, calcium mahogany sulfonate, vulcanization
Lard and chlorinated paraffin sequentially add in intermixture, and adjust pH value to 8.5-9.5, continue stirring until and are mixed evenly, by chemically examining
Room is examined, and finished pot preservation is squeezed into after qualified.
Further, whipping temp is 60 DEG C in step (1).
Further, the lasting mixing time in step (2) is 0.5-1 hours.
Compared with the existing technology, intermetallic composite coating emulsion of the present invention has the advantage that
The present invention has excellent lubricity and rust-preventing characteristic；Product stability is preferable, is conducive to long-time storage；It can meet each
Kind of metal working process is asked, and is also had many advantages, such as that volatility is low, nontoxic, recoverable, be can be used as universal intermetallic composite coating
Cutting fluid substitute mineral oil metalworking fluid, and its processing performance and environmental-protecting performance are better than common mineral oil base working fluid.
In conclusion the intermetallic composite coating emulsion of rational proportion preparation of the present invention, has the advantages that above-mentioned many and reality
With value, and there are no in similar product it is similar be related to publishing or use and really belong to innovation, and more existing metal
Working fluid has further antioxidation, is really one thus more suitable for extensive utility value that is practical, and having industry
New and innovative, progressive, practical new invention.
Specific embodiment
In addition to being defined, technical term used in following embodiment has universal with those skilled in the art of the invention
The identical meanings of understanding.Test reagent used in following embodiment is unless otherwise specified conventional biochemical reagent；It is described
Experimental method is unless otherwise specified conventional method.
Embodiment 1
40 parts of vegetable oil, 5 parts of water, 15 parts of dodecenylsuccinic acid, 8 parts of calcium mahogany sulfonate, 1 part of alkyl glucoside, vulcanization
3 parts of lard, 2 parts of chlorinated paraffin.
Vegetable oil, alkyl glucoside and water are stirred by squeezing into blender than column and be warming up to 60 DEG C, intermixture is made；
To be mixed dose is cooled to room temperature, under the conditions of high-speed stirred, by dodecenylsuccinic acid, calcium mahogany sulfonate, vulcanization pig
Oil and chlorinated paraffin sequentially add in intermixture in proportion, and adjust pH value to 8.5-9.5, persistently stir 0.5-1 hour to mixing
With it is uniform, examined by laboratory, finished pot preservation squeezed into after qualified.
Embodiment 2
The present embodiment the difference from embodiment 1 is that, base oil used be mineral oil.
Embodiment 3
The present embodiment the difference from embodiment 1 is that, base oil used be synthetic ester.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of intermetallic composite coating emulsion, which is characterized in that the raw material comprising following quality proportioning: 30-80 parts of base oil, water 5-
10 parts, 5-15 parts of dodecenylsuccinic acid, 5-10 parts of calcium mahogany sulfonate, 1-5 parts of alkyl glucoside, 2-8 parts of sulfurized lard, chlorination
2-5 parts of paraffin.
2. a kind of agricultural machinery intermetallic composite coating emulsion according to claim 1, which is characterized in that include following quality proportioning
Raw material material: 40-60 parts of base oil, 5-8 parts of water, 10-15 parts of dodecenylsuccinic acid, 5-8 parts of calcium mahogany sulfonate, alkyl glucoside
1-3 parts, 3-6 parts of sulfurized lard, 2-3 parts of chlorinated paraffin.
3. a kind of intermetallic composite coating emulsion according to claim 1 or 2, which is characterized in that the base oil be mineral oil,
Vegetable oil or synthetic ester.
4. a kind of preparation process of intermetallic composite coating emulsion according to claim 1 or 2, which is characterized in that comprising as follows
Step:
(1) base oil, alkyl glucoside and water are squeezed into blender heating stirring by than column, intermixture is made；
(2) it is cooled to room temperature for be mixed dose, under the conditions of high-speed stirred, by dodecenylsuccinic acid, calcium mahogany sulfonate, sulfurized lard
It is sequentially added in intermixture with chlorinated paraffin, and adjusts pH value to 8.5-9.5, continued stirring until and be mixed evenly, examined by laboratory
It tests, finished pot preservation is squeezed into after qualified.
5. a kind of preparation process of intermetallic composite coating emulsion according to claim 4, which is characterized in that step is stirred in (1)
Mixing temperature is 60 DEG C.
6. a kind of preparation process of agricultural machinery intermetallic composite coating emulsion according to claim 3, which is characterized in that step (2)
In continue mixing time be 0.5-1 hours.