CN109943154A - The preparation method of environment-friendly type appliance finishes - Google Patents
The preparation method of environment-friendly type appliance finishes Download PDFInfo
- Publication number
- CN109943154A CN109943154A CN201711391913.0A CN201711391913A CN109943154A CN 109943154 A CN109943154 A CN 109943154A CN 201711391913 A CN201711391913 A CN 201711391913A CN 109943154 A CN109943154 A CN 109943154A
- Authority
- CN
- China
- Prior art keywords
- polyisoprene
- mixed solvent
- tributyl phosphate
- environment
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to technical field of coatings, especially a kind of preparation method of environment-friendly type appliance finishes.The coating is made of following mass parts: alkylolamides 15-40, polyisoprene 10-40, tributyl phosphate 10-30, plasticizer 20-40, mixed solvent 5-25, mica powder 5-20, curing agent 1-5；With base alkylolamides, polyisoprene, tributyl phosphate, mixed solvent is raw material, at a certain temperature, through miscible copolyreaction, clout is then added in the product that above-mentioned copolyreaction obtains, filler material carries out mix, then is dispersed grinding manufactured goods, discharging.The present invention is had excellent performance, and for the external coating of household electrical appliances, complies fully with environmental requirement.
Description
Technical field
The present invention relates to technical field of coatings, especially a kind of preparation method of environment-friendly type appliance finishes.
Background technique
It is in electric industrial circle, coating has the double action of protection and decoration as household electrical appliances coat, and some also have
Certain function.Functionalization intelligent development also increasingly shows the environment protection requirement for using material and coating, family to today
Electrocoat requires nontoxic, safety, reduces Volatile organic emissions, is one of effective means using water paint.These are wanted
Ask the technological progress for having driven aqueous industrial coating substantively.But there is also urgent needs in environmental protection for current appliance finishes
It solves the problems, such as.
Summary of the invention
In order to overcome the shortcomings of existing powdery paints, the present invention provides a kind of preparation sides of environment-friendly type appliance finishes
Method.
The technical solution adopted by the present invention to solve the technical problems is: a kind of preparation method of environment-friendly type appliance finishes,
The coating is made of following mass parts: alkylolamides 15-40, polyisoprene 10-40, tributyl phosphate 10-30, plasticising
Agent 20-40, mixed solvent 5-25, mica powder 5-20, curing agent 1-5；With base alkylolamides, polyisoprene, tributyl phosphate is mixed
Bonding solvent is raw material, at a certain temperature, through miscible copolyreaction, then in the product that above-mentioned copolyreaction obtains more than addition
Material, filler material carry out mix, then are dispersed grinding manufactured goods, discharging.
It according to another embodiment of the invention, further comprise that the coating is made of following mass parts: alkylol acyl
Amine 15, polyisoprene 10, tributyl phosphate 10, plasticizer 20, mixed solvent 5, mica powder 5, curing agent 1.
It according to another embodiment of the invention, further comprise that the coating is made of following mass parts: alkylol acyl
Amine 40, polyisoprene 40, tributyl phosphate 30, plasticizer 40, mixed solvent 25, mica powder 20, curing agent 5.
It according to another embodiment of the invention, further comprise that the coating is made of following mass parts: alkylol acyl
Amine 25, polyisoprene 15, tributyl phosphate 20, plasticizer 35, mixed solvent 15, mica powder 18, curing agent 2.
The invention has the advantages that the present invention is had excellent performance, for the external coating of household electrical appliances, complies fully with environmental protection and want
It asks.
Specific embodiment
A kind of preparation method of environment-friendly type appliance finishes, the coating are made of following mass parts: alkylolamides 15-
40, polyisoprene 10-40, tributyl phosphate 10-30, plasticizer 20-40, mixed solvent 5-25, mica powder 5-20, curing agent
1-5；With base alkylolamides, polyisoprene, tributyl phosphate, mixed solvent is raw material, at a certain temperature, anti-through miscible copolymerization
It answers, clout is then added in the product that above-mentioned copolyreaction obtains, filler material carries out mix, then is dispersed grinding manufactured goods,
Discharging.
It according to another embodiment of the invention, further comprise that the coating is made of following mass parts: alkylol acyl
Amine 15, polyisoprene 10, tributyl phosphate 10, plasticizer 20, mixed solvent 5, mica powder 5, curing agent 1.
It according to another embodiment of the invention, further comprise that the coating is made of following mass parts: alkylol acyl
Amine 40, polyisoprene 40, tributyl phosphate 30, plasticizer 40, mixed solvent 25, mica powder 20, curing agent 5.
It according to another embodiment of the invention, further comprise that the coating is made of following mass parts: alkylol acyl
Amine 25, polyisoprene 15, tributyl phosphate 20, plasticizer 35, mixed solvent 15, mica powder 18, curing agent 2.
Claims (4)
1. a kind of preparation method of environment-friendly type appliance finishes, characterized in that the coating is made of following mass parts: alkylol acyl
Amine 15-40, polyisoprene 10-40, tributyl phosphate 10-30, plasticizer 20-40, mixed solvent 5-25, mica powder 5-20,
Curing agent 1-5；With base alkylolamides, polyisoprene, tributyl phosphate, mixed solvent is raw material, at a certain temperature, through miscible
Then clout is added in copolyreaction in the product that above-mentioned copolyreaction obtains, filler material carries out mix, then is dispersed grinding system
Finished product, discharging.
2. the preparation method of environment-friendly type appliance finishes according to claim 1, characterized in that the coating is by following quality
Part composition: alkylolamides 15, polyisoprene 10, tributyl phosphate 10, plasticizer 20, mixed solvent 5, mica powder 5, solidification
Agent 1.
3. the preparation method of environment-friendly type appliance finishes according to claim 1, characterized in that the coating is by following quality
Part composition: alkylolamides 40, polyisoprene 40, tributyl phosphate 30, plasticizer 40, mixed solvent 25, mica powder 20, Gu
Agent 5.
4. the preparation method of environment-friendly type appliance finishes according to claim 1, characterized in that the coating is by following quality
Part composition: alkylolamides 25, polyisoprene 15, tributyl phosphate 20, plasticizer 35, mixed solvent 15, mica powder 18, Gu
Agent 2.