CN109943078A - 一种可自修复的硅胶手套的制备方法 - Google Patents

一种可自修复的硅胶手套的制备方法 Download PDF

Info

Publication number
CN109943078A
CN109943078A CN201910145550.5A CN201910145550A CN109943078A CN 109943078 A CN109943078 A CN 109943078A CN 201910145550 A CN201910145550 A CN 201910145550A CN 109943078 A CN109943078 A CN 109943078A
Authority
CN
China
Prior art keywords
parts
silica
selfreparing
fingerprint
gloves
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910145550.5A
Other languages
English (en)
Inventor
桑树军
李民刚
王振山
刘喆
马保军
汪金鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhong Hongpulin Medical Supplies Ltd Co
Original Assignee
Zhong Hongpulin Medical Supplies Ltd Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhong Hongpulin Medical Supplies Ltd Co filed Critical Zhong Hongpulin Medical Supplies Ltd Co
Priority to CN201910145550.5A priority Critical patent/CN109943078A/zh
Publication of CN109943078A publication Critical patent/CN109943078A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种可自修复的硅胶手套的制备方法，它包括以下步骤：第一步，将1份的乙烯基硅氧烷，5‑10份的氢硅氧烷，10‑15的4‑[(烯丙氧基)甲基]‑2‑(4‑乙烯基苯基)‑1,3,2二氧硼杂环戊烷，10‑20份的MQ硅树脂、0.3‑1份的铂催化剂、5‑10份的二氧化硅或二氧化钛混合均匀作为浸渍液；第二步，将手模加热到50℃‑60℃，将手模浸入第一步的混合浸渍液中进行浸渍，在温度为90℃‑150℃的条件下进行硫化处理；第三步，清洗后脱模即得到最终产品。本发明的一种可自修复的硅胶手套的制备方法，利用动态硼酸酯共价键，在湿润条件下实现手套破裂部分的自动修复，实用环保。

Description

一种可自修复的硅胶手套的制备方法
技术领域
本发明涉及手套制备领域，尤其涉及一种可自修复的硅胶手套的制备方法。
背景技术
硅橡胶具有耐高温、耐低温、耐水蒸汽、无毒环保的特点，用其制备的硅胶手套在食品、医疗行业具有广泛应用。硅胶手套相比于普通橡胶手套属于高档品，价格相对较贵。普通硅胶手套一旦被破坏(如刀割)就失去了防护作用，需要废弃，这对资源是一种浪费，经济上也不合算。动态共价键同时具有普通共价键的强度，又能像氢键那样可逆地断裂重组。利用动态共价键制备可修复材料近年来受到广泛关注(Chemical Society Reviews,2008,5,5)，但还没有关于可修复硅胶手套的相关报导。
发明内容
本发明的目的在于针对现有技术的不足而提供一种可自修复的硅胶手套的制备方法，利用动态硼酸酯共价键，在湿润条件下实现手套破裂部分的自动修复，实用环保。
为达到上述目的，本发明通过以下技术方案来实现。
一种可自修复的硅胶手套的制备方法，其特征在于：它包括以下步骤：
第一步，将1份的乙烯基硅氧烷，5-10份的氢硅氧烷，10-15的4-[(烯丙氧基)甲基]-2-(4-乙烯基苯基)-1,3,2二氧硼杂环戊烷，10-20份的MQ硅树脂、0.3-1份的铂催化剂、5-10份的二氧化硅或二氧化钛混合均匀作为浸渍液；
第二步，将手模加热到50℃-60℃，将手模浸入第一步的混合浸渍液中进行浸渍，在温度为90℃-150℃的条件下进行硫化处理；
第三步，清洗后脱模即得到最终产品。
进一步的，所述第一步的浸渍液中加入30-50份的氢呋喃。
进一步的，所述第二步中的硫化处理时间为20-40分钟。
本发明的一种可自修复的硅胶手套的制备方法，利用动态硼酸酯共价键，在湿润条件下实现手套破裂部分的自动修复，实用环保。
具体实施方式
下面结合实施例对本发明做进一步说明，但不局限于说明书上的内容。
一种可自修复的硅胶手套的制备方法，包括以下步骤：
第一步，将1份的乙烯基硅氧烷，5-10份的氢硅氧烷，10-15的4-[(烯丙氧基)甲基]-2-(4-乙烯基苯基)-1,3,2二氧硼杂环戊烷(VPD)，10-20份的MQ硅树脂、0.3-1份的铂催化剂、5-10份的二氧化硅或二氧化钛加入到30-50份的四氢呋喃(THF)中混合均匀作为浸渍液，其中四氢呋喃(THF)为溶剂。
第二步，将手模加热到50℃-60℃，将手模浸入第一步的混合浸渍液中进行浸渍，在温度为90℃-150℃的条件下进行硫化处理，硫化20-40分钟。
第三步，清洗后脱模即得到最终产品。
以上所述份数均是质量份数。
本发明制备的产品的修复原理为：
上述氢硅氧烷中的x,y各自为20-40的自然数。乙烯基硅氧烷中的m,n各自为500-1500的自然数。
下面以具体实施例来说明：
实施例1(手套的制备)
1)将1份乙烯基硅氧烷、5份的氢硅氧烷、15份的VPD、10份的MQ硅树脂、0.3份的铂催化剂、5份的二氧化硅加入到50份的四氢呋喃(THF)中混合均匀作为浸渍液。
其中m,n各自为500-1500的自然数，x,y各自为20-40的自然数。
2)将手模加热到60℃，将手模浸入聚有机硅氧烷混合液中进行浸渍，在温度为90℃的条件下进行硫化处理20分钟。
3)清洗后脱模即得到最终产品。
实施例2(手套的制备)
1)将1份乙烯基硅氧烷、10份的氢硅氧烷、10份的VPD、10份的MQ硅树脂、1份的铂催化剂、10份的二氧化硅加入到40份的四氢呋喃(THF)中混合均匀作为浸渍液。其中m,n各自为500-1500的自然数，x,y各自为20-40的自然数。
2)将手模加热到50℃，将手模浸入聚有机硅氧烷混合液中进行浸渍，在温度为150℃的条件下进行硫化处理30分钟。
3)清洗后脱模即得到最终产品。
实施例3(手套的制备)
1)将1份乙烯基硅氧烷、10份的氢硅氧烷、12份的VPD、10份的MQ硅树脂、0.5份的铂催化剂、10份的二氧化钛加入到30份的四氢呋喃(THF)中混合均匀作为浸渍液。其中m,n各自为500-1500的自然数，x,y各自为20-40的自然数。
2)将手模加热到50℃，将手模浸入聚有机硅氧烷混合液中进行浸渍，在温度为120℃的条件下进行硫化处理40分钟。
3)清洗后脱模即得到最终产品。
实施例4(破裂手套的修复)
将实施例1中制备的手套的手指部分用刀切断，断面用水浸湿后对接，室温下放置12小时后测试拉伸强度，拉伸强度恢复到原来的85％。
本发明的一种可自修复的硅胶手套的制备方法，利用动态硼酸酯共价键，在湿润条件下实现手套破裂部分的自动修复，实用环保。
显然，本发明的上述实施方式仅仅是为清楚地说明本发明所作的举例，而并非是对本发明的实施方式的限定。对于所属领域的普通技术人员来说，在上述说明的基础上还可以做出其它不同形式的变化或变动。这里无法对所有的实施方式予以穷举。凡是属于本发明的技术方案所引伸出的显而易见的变化或变动仍处于本发明的保护范围之列。

Claims (3)

1.一种可自修复的硅胶手套的制备方法，其特征在于：它包括以下步骤：
第一步，将1份的乙烯基硅氧烷，5-10份的氢硅氧烷，10-15的4-[(烯丙氧基)甲基]-2-(4-乙烯基苯基)-1,3,2二氧硼杂环戊烷，10-20份的MQ硅树脂、0.3-1份的铂催化剂、5-10份的二氧化硅或二氧化钛混合均匀作为浸渍液；
第二步，将手模加热到50℃-60℃，将手模浸入第一步的混合浸渍液中进行浸渍，在温度为90℃-150℃的条件下进行硫化处理；
第三步，清洗后脱模即得到最终产品。
2.根据权利要求1所述的一种可自修复的硅胶手套的制备方法，其特征在于：所述第一步的浸渍液中加入30-50份的氢呋喃。
3.根据权利要求1所述的一种可自修复的硅胶手套的制备方法，其特征在于：所述第二步中的硫化处理时间为20-40分钟。
CN201910145550.5A 2019-02-27 2019-02-27 一种可自修复的硅胶手套的制备方法 Pending CN109943078A (zh)