CN109940124A - A kind of lost foam paint and preparation method thereof - Google Patents
A kind of lost foam paint and preparation method thereof Download PDFInfo
- Publication number
- CN109940124A CN109940124A CN201910306278.4A CN201910306278A CN109940124A CN 109940124 A CN109940124 A CN 109940124A CN 201910306278 A CN201910306278 A CN 201910306278A CN 109940124 A CN109940124 A CN 109940124A
- Authority
- CN
- China
- Prior art keywords
- parts
- lost foam
- coating
- foam paint
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 45~55 parts of mullite, 15~25 parts of diatomite, 15~25 parts of attapulgite, 3~7 parts of polyvinyl acetate, 3~7 parts of carboxymethyl cellulose, 48~71 parts of water.Invention additionally discloses a kind of methods for preparing lost foam paint.The present invention, which has, improves the low and high temperature intensity of lost foam paint, resistance to erosion, not easy to crack, higher thixotropy, and can reach azymic, without adding any preservative, being safe from harm to human body, be coated with that number is few, the thin light-weight advantage of coating.
Description
Technical field
The present invention relates to evaporative pattern technical fields more particularly to a kind of lost foam paint and preparation method thereof.
Background technique
Lost foam casting is the cavityless casting that foam mould uses bindless dry sand combination vacuum pumping technology.The country is main
The call wanted has " dry sand cavityless casting ", " vacuum full mold casting ", abbreviation EPC casting;External call mainly has: Lost
Foam Process (U.S.A), P0licastProcess (Italy) etc..Lost foam casting is current casting state-of-the-art in the world
One of technique is made, primary " revolution " being known as in casting history is referred to as 21 century Green foundry both at home and abroad.
Traditional lost foam paint is in order to improve the refractoriness of coating, and refractory aggregate largely uses silica flour, and feature is valence
For the cheap refractoriness height of lattice up to 1750 DEG C, low temperature intensity is high.The disadvantage is that silica flour has phase transformation, volume meeting at 575 DEG C
Increase suddenly.The defects of be easy to causeing flame retardant coating to crack, casting caused to generate burnt-in sand, overlap, crush.Another disadvantage is that thoroughly
Gas performance is poor, no adsorptivity.Most of lost foam casting factory is caused to form nowadays dry in order to increase aeration raising
The granularity of sand.The granularity of dry sand is improved, coating intensity increases again, causes coating layer thickness excessive.Paint thickness increases
Gas permeability is again bad, increases vacuum degree again, forms a poor circulation.Eventually lead to surface roughness height, defect
The appearance for the series of malpractice such as more, yellow area's foam circulation time is long, takes up a large area, and drying chamber mostly energy consumption is big.
Traditional lost foam paint generally uses starch as suspending agent and bonding agent, and feature is cheap suspendability
It is good.The disadvantage is that no thixotropy, the inefficiency that the weak easy drip of adhesive ability causes Bai Mo to hang painting (generally requires and is coated with 3~4
All over) and complicated bubbles model cannot be coated with.Cause variety of moduli weight big due to applying thickness (generally in 1.5~3mm), manually
When being coated with, large labor intensity, foam mold is easy to damage, it is therefore desirable to be divided into smallclothes to be coated with one by one bubbles model, lead to week
It is long to turn the time, and drying chamber quantity is more, and energy consumption is high.The workload of bonding process is increased, and the precision of bonding also proposed very high
It is required that.Another disadvantage is that fermentation is easy when heat in day, gives out acid smell since starch is organic matter.After fermenting simultaneously
Coating suspension performance and adhesive property reduce, and even fail when serious.In order to avoid coating fermentation, can generally be added in coating
The preservatives such as benzoic acid.Long Term Contact may cause adverse effect to human health.
Summary of the invention
Technical problem to be solved by the present invention lies in the low and high temperature for the lost foam paint for how improving the prior art is strong
Degree, resistance to erosion, not easy to crack, higher thixotropy, and azymic can be reached, without adding any preservative, not having to human body
It endangers, be coated with that number is few, and coating is thin light-weight.
The present invention is realized by following technological means solves a kind of above-mentioned technical problem: lost foam paint, including following
The raw material of mass fraction is prepared: 45~55 parts of mullite, 15~25 parts of diatomite, 15~25 parts of attapulgite, poly-vinegar acid
3~7 parts of ethylene, 3~7 parts of carboxymethyl cellulose, 48~71 parts of water.
Preferably, the raw material including following mass fraction is prepared: 50 parts of mullite, 20 parts of diatomite, attapulgite
20 parts, 5 parts of polyvinyl acetate, 5 parts of carboxymethyl cellulose, 60 parts of water.
Invention additionally discloses a kind of methods for preparing above-mentioned lost foam paint, comprising the following steps:
Mullite, diatomite, attapulgite, polyvinyl acetate, carboxymethyl cellulose are added to the water, stirs, impregnate, obtain
To product.
Preferably, the time of stirring is 30~120min.
Preferably, the time of the immersion is not less than 12h.
Preferably, the agitator used that stirs is water-drop-shaped agitator.
Since coating of the invention has good thixotropic property, blender is not closed when in use.It is not using
When close blender.The agitator that this coating uses barrel-shaped preferably water-drop-shaped, blender are placed on the small end of water-drop-shaped, have in this way
Conducive to the coating dead zone reduced when stirring, the coating in bucket can be made uniformly to flow and coating is allowed adequately to be stirred
Mix mixing.Region is coated in the big end of water-drop-shaped, is conducive to the operation of operator in this way.So being not in blender damage
The problem of foam mold.
The present invention has the advantages that
(1) lost foam paint of the invention increases aeration and adsorptivity while guaranteeing refractoriness, and has higher
Low temperature intensity and elevated temperature strength, resistance to erosion is easy to crack.Using Inorganic suspending agent, suspendability is good, there is higher thixotroping
Property, azymic is safe from harm to human body without adding any preservative.It is good to be coated with performance, need to only be coated with one time, the thin weight of coating
Gently (general 0.45~0.8mm of coating layer thickness) can be integrally coated with.Therefore the turnaround time is short, and drying chamber quantity is few, and low energy consumption.It alleviates
The work load of bonding process reduces adhesive reinforcement requirement.Cost performance is high, and with traditional lost foam paint ratio, price is tradition
2.5 times of coating, but 1/3 of dosage less than traditional coating.And production efficiency is significantly improved, is saved a large amount of artificial
With place, the use for reducing drying chamber reduces energy consumption.
(2) present invention with the refractory aggregate mullite through stomata and controls mullite particle diameter distribution by control addition
Section controls gas permeability.If gas permeability is excessively high, the defects of will lead to aluminum liquid filling type excessive velocities, cause volume gas slag.Such as
The defects of fruit gas permeability is too low, and it is excessively slow to will lead to aluminum liquid filling type speed, causes misrun, cold shut, stomata.
(3) present invention controls adsorptivity by adding the diatomite with more penetrability stomatas.Since aluminium alloy pours
Note temperature is about 750~760 DEG C low, and polystyrene foam plastics can largely liquefy, a part gasification.Therefore coating needs have
Liquefied substance is adsorbed the gas hole defect for avoiding that liquefied substance wrapped folder into molten aluminum, is formed to disperse by good adsorptivity in time.
(4) mullite in the present invention and diatomite have the stomata of perforation, therefore thermal insulation property is all very good.So
Heat preservation is solved the problems, such as by both materials.Since aluminium alloy pouring temperature is low, the small-sized casting of heavy wall is unobvious, especially
Medium-and-large-sized casting or thin wall type casting when thermal-insulation coating performance is bad, are easy to appear cold shut and misrun defect.
(5) thixotropy of coating of the present invention is that in stirring, the cotton-shaped variation that generates is realized and and carboxylic by attapulgite
The suspendability of methylcellulose combines the phenomenon that layering occur.For being poured thin-wall complicated aluminium alloy casting
Part, especially casting thinnest part only have 3.5~4mm, there was only the gap 10mm at interlayer minimum.Also, a casting has multiple
Interlayer and functional areas, cavity structure are complicated, and by the oil duct of cast-internal, water channel, air flue and some fabrication holes plus
Strengthening tendons etc. pass through pouring one-step forming.Therefore it needs coating to have and good is coated with performance.Measure the quality master that coating is coated with performance
If thixotropy.In order to obtain with the lubricious of high-quality appearance, in coating use or in the mistake of coating dried/cured
Cheng Zhong needs to keep its sufficient horizontality, to avoid flowing down problems while reducing the generation of coating irregular surface
Occur, should make coating that there is thixotropy.Thixotropy is in coating composition in loosely bound structure its structure quilt after by shearing force
It caused by destruction, after static and restores to the original state, shows on coating, i.e., by stirring or shaking viscosity/dilute, stopping stirring
Or shake viscosity get higher/it is thick, be conducive to foam mold immersion in this way and be coated with operation, simplify technique, reduce labor intensity, improve certainly
Dynamic rate.
(6) lost foam paint of the invention, by control addition with the refractory aggregate mullite and diatom for running through stomata
Soil, Lai Zengjia gas permeability.For diatomite due to more through stomata, its adsorptivity and thermal insulation property is very good.Coating
Thixotropy is that the cotton-shaped variation and carboxymethyl cellulose generated by attapulgite in stirring cooperatively forms.And it is recessed
Convex stick soil can make coating have good elevated temperature strength, and carboxymethyl cellulose makes coating have better suspendability, prevents from applying
Material layering.Polyvinyl acetate can make coating have good low temperature intensity.Meeting lost foam paint, coating is not easy out at normal temperature
It splits, the good not easily to fall off ash of adhesion property;At a high temperature of attapulgite is met in casting, coating is not equally easy to crack, and
And there are enough refractoriness and abrasion resistance.
(7) since coating of the invention uses natural mineral matter as raw material completely, wherein polyvinyl acetate is with water
For decentralized medium carries out emulsion polymerization and obtains, it is a kind of aqueous, environmental protective glue, is widely used in printing, weaving, leather, makes
The industries such as paper, cigarette;Carboxymethyl cellulose is mainly used in food service industry.Therefore the evaporative pattern aluminium alloy coating of my company will not
Personnel are caused to bear with environment.
Detailed description of the invention
Fig. 1 is to be poured in a kind of lost foam paint of the present invention based on the lost foam mould of embodiment 2 and each comparative example
The structural schematic diagram of casting afterwards.
Fig. 2 is the structural schematic diagram of agitator in a kind of lost foam paint of the present invention.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention
And attached drawing, technical scheme in the embodiment of the invention is clearly and completely described.
Embodiment 1
The present embodiment discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 45 parts of mullite,
15 parts of diatomite, 15 parts of attapulgite, 3 parts of polyvinyl acetate, 3 parts of carboxymethyl cellulose, 48 parts of water.
Embodiment 2
The present embodiment discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: including following matter
The raw material of amount number is prepared: 50 parts of mullite, 20 parts of diatomite, 20 parts of attapulgite, 5 parts of polyvinyl acetate, carboxymethyl
60 parts of 5 parts of cellulose, water.
Embodiment 3
The present embodiment discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 55 parts of mullite,
25 parts of diatomite, 25 parts of attapulgite, 7 parts of polyvinyl acetate, 7 parts of carboxymethyl cellulose, 71 parts of water.
Embodiment 4
The present embodiment discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 48 parts of mullite,
22 parts of diatomite, 23 parts of attapulgite, 6 parts of polyvinyl acetate, 4 parts of carboxymethyl cellulose, 62 parts of water.
Embodiment 5
The present embodiment discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 52 parts of mullite,
18 parts of diatomite, 21 parts of attapulgite, 5 parts of polyvinyl acetate, 6 parts of carboxymethyl cellulose, 61 parts of water.
Embodiment 6
A kind of method that lost foam paint for preparing above-mentioned each embodiment is also disclosed in the present embodiment, comprising the following steps:
Comparative example 1
This comparative example discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 55 parts of mica powder,
20 parts of diatomite, 20 parts of attapulgite, 5 parts of polyvinyl acetate, 5 parts of carboxymethyl cellulose, 60 parts of water.
Comparative example 2
This comparative example discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 55 parts of kaolin,
20 parts of diatomite, 20 parts of attapulgite, 5 parts of polyvinyl acetate, 5 parts of carboxymethyl cellulose, 60 parts of water.
Comparative example 3
This comparative example discloses a kind of lost foam paint, and the raw material including following mass fraction is prepared: 55 parts of silica flour,
20 parts of diatomite, 20 parts of attapulgite, 5 parts of polyvinyl acetate, 5 parts of carboxymethyl cellulose, 60 parts of water.
The preparation method of above-mentioned each embodiment and comparative example is also disclosed in the present embodiment: water is added in each dry powder raw material
In, 15h stirring 60min, is impregnated, obtains product.The agitator that stirring uses is preferably water-drop-shaped agitator.
Embodiment 7
Coating property test casting experiment
In order to preferably show coating property, reducing other unfavorable factors influences.Used bubbles model is
One mould is got, and individual difference is reduced to minimum.Opening up for running gate system is from the point of view of influencing each other when reducing casting
, in order to reduce adverse effect when casting, main running channel is preferably insulation fibre running channel, insulation fibre can be aramid fiber 1313 or
Person's asbestos.Preferably, casting is improved into 15cm and forms a running channel nest, can kept away just the lower cold aluminum water of temperature is started down
It opens, and the turbulent flow in casting process can be eliminated more can uniformly to fill type with guarantee test part.Coating passes through before being coated with to be stirred
It mixes and eliminates bubble, be coated with a thickness of 0.55~0.65mm, coating dynamic viscosity is at 1265~1315cP (centipoise).Warp before casting
Adequately drying, the natural sea sand of 40~70 mesh of moulding are crossed, pouring temperature is 759 DEG C, duration of pouring 35s.
The structural schematic diagram of casting after the lost foam mould of 1 lost foam paint of the expression based on embodiment 2 is poured in Fig. 1;2
Indicate the structural schematic diagram of casting after the lost foam mould of the lost foam paint based on comparative example 1 is poured;3 indicate to be based on comparative example
The structural schematic diagram of casting after the lost foam mould casting of 2 lost foam paint;4 indicate the lost foam paint based on comparative example 3
Lost foam mould casting after casting structural schematic diagram.
As shown in Figure 1, the effect of foam mold moulding by casting is preferably the most complete using lost foam paint of the invention.
Using the lost foam paint of comparative example 2, the effect of foam mold moulding by casting in running channel distalmost end preferably only from turning
Misrun at angle.If it is also feasible for being produced in batches using this coating, exactly by being optimized in pouring technology come real
It is existing.But we are the comparative illustrations for passing through embodiment 1 and comparative example 2 in the identical situation of pouring technology here, are being poured
Since running channel proximal end has endlessly, fresh high temperature molten aluminum enters in journey, the good fluidity fltting speed of aluminum water quickly,
But distal end aluminum water temperature gradually decreases, the mobility of aluminum water is deteriorated and also to overcome resistance of the foam in cracking, causes
Running channel proximal end liquid level is high, and running channel distal end liquid level is low, and in casting, cast-internal is formed one and inclined fills type liquid in this way
Bit line.Therefore when coating other performance is identical be coating adsorptivity it is bad in the case where running channel proximal end aluminum water due to temperature
Spend height can by this part foam liquid lysate gasify be discharged, it is some do not come and gasify with not by the foam of paint-absorbable
Lysate just as liquid stream is to distal collection, has no ability to finally inhale so overbrushing material since the aluminum water temperature of distal end is low
Attached foam liquefied substance gasification.The important of paint-absorbable performance can be found out from the two comparisons.
Using the lost foam paint of comparative example 3, the effect of foam mold moulding by casting is less desirable.By according to the analysis, applying
Expect that thermal insulation property is bad along with permeability is high, causes aluminum water cooling rate too fast.Especially into first strand of aluminium of casting
Water, due to the route trip longest that it is walked, and not fresh hot aluminum water is supplemented, and there are no go to foam mold after entering casting
End forms reflux and carrys out additional heat, with regard to rapid cooled and solidified.It is subsequent slowly increased into the aluminum water temperature of casting backward after
It fills type effect or good still overall effect is less desirable.
Using the lost foam paint of comparative example 4, the effect of foam mold moulding by casting is undesirable.Thermal-insulation coating performance is breathed freely
Performance and absorption property are all poor, and the place for only having aluminum water temperature high when filling type can fill type, but it can be seen that have apparent cold
Every.The low place of temperature occurs as soon as large area misrun.
It can be seen that thermal insulation property, permeability and the absorption property in aluminium alloy lost foam cast paint by experiment
Importance.
In conclusion the present invention with the refractory aggregate mullite through stomata and controls mullite grain by control addition
Diameter distributed area controls gas permeability.It if gas permeability is excessively high, will lead to aluminum liquid filling type excessive velocities, volume gas slag etc. caused to lack
It falls into.The defects of if gas permeability is too low, it is excessively slow to will lead to aluminum liquid filling type speed, causes misrun, cold shut, stomata.
The present invention controls adsorptivity by adding the diatomite with more penetrability stomatas.Since aluminium alloy is poured temperature
Low about 750~760 DEG C are spent, polystyrene foam plastics can largely liquefy, a part gasification.Therefore coating needs to have good
Adsorptivity, liquefied substance is adsorbed to the gas hole defect for avoiding that liquefied substance wrapped folder into molten aluminum, is formed to disperse in time.
Mullite and diatomite in the present invention have the stomata of perforation, therefore thermal insulation property is all very good.So logical
Both materials are crossed to solve the problems, such as heat preservation.Since aluminium alloy pouring temperature is low, the small-sized casting of heavy wall is unobvious, especially in
Heavy castings or thin wall type casting when thermal-insulation coating performance is bad, are easy to appear cold shut and misrun defect.
The thixotropy of coating of the present invention be by attapulgite in stirring the cotton-shaped variation that generates realize and with carboxylic first
The suspendability of base cellulose combines the phenomenon that layering occur.For being poured the aluminium alloy casting of thin-wall complicated part
Part, especially casting thinnest part only have 3.5~4mm, there was only the gap 10mm at interlayer minimum.Also, a casting has multiple
Interlayer and functional areas, cavity structure are complicated, and by the oil duct of cast-internal, water channel, air flue and some fabrication holes plus
Strengthening tendons etc. pass through pouring one-step forming.Therefore it needs coating to have and good is coated with performance.Measure the quality master that coating is coated with performance
If thixotropy.In order to obtain with the lubricious of high-quality appearance, in coating use or in the mistake of coating dried/cured
Cheng Zhong needs to keep its sufficient horizontality, to avoid flowing down problems while reducing the generation of coating irregular surface
Occur, makes coating that there is thixotropy.Thixotropy is that in loosely bound structure, its structure is broken after by shearing force in coating composition
Caused by bad, restore to the original state, show on coating again after static, i.e., by stirring or shake viscosity/dilute, stop stirring or
Shake viscosity get higher/it is thick, be conducive to foam mold immersion in this way and be coated with operation, simplify technique, reduce labor intensity, improve automatically
Rate.
Lost foam paint of the invention has refractory aggregate mullite and diatomite through stomata by control addition,
To increase gas permeability.For diatomite due to more through stomata, its adsorptivity and thermal insulation property is very good.The thixotroping of coating
Property be that in stirring, the cotton-shaped variation that generates and carboxymethyl cellulose are cooperatively formed by attapulgite.And concave convex rod
Soil can make coating have good elevated temperature strength, and carboxymethyl cellulose makes coating have better suspendability, prevent coating point
Layer.Polyvinyl acetate can make coating have good low temperature intensity.Meeting lost foam paint, coating is not easy to crack at normal temperature, attached
The good not easily to fall off ash of performance;At a high temperature of attapulgite is met in casting, coating is not equally easy to crack, and has foot
Enough refractoriness and abrasion resistance.
Since coating of the invention uses natural mineral matter as raw material completely, wherein polyvinyl acetate is to be with water
Decentralized medium carry out emulsion polymerization and obtain, be a kind of aqueous, environmental protective glue, be widely used printing, weaving, leather, papermaking,
The industries such as cigarette;Carboxymethyl cellulose is mainly used in food service industry.Therefore the evaporative pattern aluminium alloy coating of my company will not be right
Personnel cause to bear with environment.
The agitator used is stirred in each embodiment of the present invention as water-drop-shaped agitator.Since coating of the invention has
Good thixotropic property, therefore blender 5 is not closed when in use.Blender is closed when not in use.What this coating used stirs
That mixes bucket its groove body 61 is preferably shaped to water-drop-shaped, and blender 5 is placed on the small end of water-drop-shaped, when being conducive to reduce stirring in this way
Coating dead zone can make the coating in bucket uniformly flow and coating is allowed to be sufficiently mixed.It is coated with region
In the big end of water-drop-shaped, be conducive to the operation of operator in this way.So the problem of being not in blender damage foam mold.
It should be noted that, in this document, such as first and second or the like relational terms are used merely to one if it exists
A entity or operation with another entity or operate distinguish, without necessarily requiring or implying these entities or operation it
Between there are any actual relationship or orders.Moreover, the terms "include", "comprise" or its any other variant are intended to
Cover non-exclusive inclusion, so that the process, method, article or equipment for including a series of elements not only includes those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or setting
Standby intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in the process, method, article or apparatus that includes the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features;And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (10)
1. a kind of lost foam paint, which is characterized in that the raw material including following mass fraction is prepared: mullite 45~55
Part, 15~25 parts of diatomite, 15~25 parts of attapulgite, 3~7 parts of polyvinyl acetate, 3~7 parts of carboxymethyl cellulose, water 48~
71 parts.
2. lost foam paint according to claim 1, which is characterized in that the preparation of raw material including following mass fraction and
At: 50 parts of mullite, 20 parts of diatomite, 20 parts of attapulgite, 5 parts of polyvinyl acetate, 5 parts of carboxymethyl cellulose, 60 parts of water.
3. lost foam paint according to claim 1, which is characterized in that the preparation of raw material including following mass fraction and
At: 48 parts of mullite, 22 parts of diatomite, 23 parts of attapulgite, 6 parts of polyvinyl acetate, 4 parts of carboxymethyl cellulose, 62 parts of water.
4. lost foam paint according to claim 1, which is characterized in that the preparation of raw material including following mass fraction and
At: 52 parts of mullite, 18 parts of diatomite, 21 parts of attapulgite, 5 parts of polyvinyl acetate, 6 parts of carboxymethyl cellulose, 61 parts of water.
5. a kind of method for preparing lost foam paint as described in claim 1, comprising the following steps: by mullite, diatomite,
Attapulgite, polyvinyl acetate, carboxymethyl cellulose are added to the water, and stir, impregnate, obtain product.
6. the method according to claim 5 for preparing lost foam paint, which is characterized in that the mass fraction of each raw material
Are as follows: 45~55 parts of mullite, 15~25 parts of diatomite, 15~25 parts of attapulgite, 3~7 parts of polyvinyl acetate, carboxymethyl cellulose
3~7 parts, 48~71 parts of water of element.
7. the method according to claim 5 for preparing lost foam paint, which is characterized in that the mass fraction of each raw material
Are as follows: 50 parts of mullite, 20 parts of diatomite, 20 parts of attapulgite, 5 parts of polyvinyl acetate, 5 parts of carboxymethyl cellulose, 60 parts of water.
8. the method according to claim 5 for preparing lost foam paint, which is characterized in that the time of the stirring be 30~
120min。
9. the method according to claim 5 for preparing lost foam paint, which is characterized in that the time of the immersion is not less than
12h。
10. the method according to claim 5 for preparing lost foam paint, which is characterized in that the stirring that the stirring uses
Bucket is water-drop-shaped agitator.