CN109929432A - A kind of automobile finish glazing agent - Google Patents
A kind of automobile finish glazing agent Download PDFInfo
- Publication number
- CN109929432A CN109929432A CN201711352666.3A CN201711352666A CN109929432A CN 109929432 A CN109929432 A CN 109929432A CN 201711352666 A CN201711352666 A CN 201711352666A CN 109929432 A CN109929432 A CN 109929432A
- Authority
- CN
- China
- Prior art keywords
- agent
- wax
- automobile finish
- glazing agent
- lacquer painting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile finish glazing agent, glazing agent includes following components (mass percent): natural palm wax 1-2%, microcrystal wax 1-2%, polyester wax 1-3%, silicone resin 5-8%, polyamide 1-2%, polyacrylamide amine emulsifier 2-6%, nonionic emulsifier 1-2%, ultraviolet absorbing agent 0.1-0.3%, antistatic agent 1-2%, essence 0.1-0.2%, solvent 30-50%, deionized water 40-60%.Envelope glaze method of the invention is the following steps are included: 1. check lacquer painting situation, and record；2. automobile finish cleans up；3. spending sludge wipes vehicle；4. rubberizing paper is protected；5. a pair lacquer painting is polished, mirror surface reduction；6. carwash；7. envelope glaze；8. full Che Qingjie.Glazing agent of the invention has the characteristics that high glaze, gloss are lasting, hydrophobicity is strong, is not easy to stain, antiultraviolet, antistatic, resistance to marring are good.
Description
Technical field
The present invention relates to a kind of lacquer painting brightening protecting agents, in particular to automobile finish glazing agent.
Background technique
Automobile finish beauty maintenance is waxed to lacquer painting earliest, decades has been applied in China, since people are to paint
Face protection requires to be continuously improved, and is no longer satisfied a part of car owner, the especially requirement of luxury car car owner to vehicle waxing merely.
Then nearly ten years, referred to as automobile finish beauty maintenance " second generation product " envelope glaze comes into being.Compared with waxing, envelope glaze has
Many advantages, for example, gloss is higher, hydrophobicity is stronger, be not easy to stain, antiultraviolet, antistatic, resistance to marring are more preferable, effect more
Persistently, it is two to three times of the common in-vehicle wax duration.
Automobile finish envelope glaze principle is that glazing agent is pressed into deeply repeatedly in vehicle paint texture using shake throwing technology, forms a kind of spy
Different reticular protection film, allows surface of vehicle as ceramic surface, thus " envelope glaze " title is also got.Glazing agent is different from biography
System vehicle wax ingredient, it, which contains, to form one layer of firm lasting protection film component in lacquer painting, more have similar to the hydrophobic of teflon
Oleophobic ingredient.
Summary of the invention
The purpose of the present invention is to provide a kind of automobile finish glazing agents, and by using glazing agent of the invention, cooperation is originally
The envelope glaze method of disclosure of the invention can form one layer of firm lasting protective film to new car on lacquer painting, make new car beautiful colorful
Lacquer painting is persistently kept；The scratch for having no priming paint on lacquer painting can be removed to used car, make lacquer painting smooth, shine newborn and energy again persistently
It keeps.
The manufacturing method of glazing agent of the present invention is adopted the technical scheme that.
Automobile finish glazing agent of the present invention includes following components: natural palm wax, polyester wax, silicone resin, gathers microcrystal wax
Amide resin, polyacrylamide amine emulsifier, nonionic emulsifier, ultraviolet absorbing agent, antistatic agent, essence, petroleum solvent,
Water.
A kind of automobile finish glazing agent, including natural palm wax 1-2%, microcrystal wax 1-2%, polyester wax 1-3%, silicone resin
5-8%, polyamide 1-2%, polyacrylamide amine emulsifier 2-6%, nonionic emulsifier 1-2%, ultraviolet absorbing agent 0.1-
0.3%, antistatic agent 1-2%, essence 0.1-0.2%, petroleum solvent 30-50%, deionized water 40-60%.
The production method of automobile finish glazing agent of the present invention are as follows: all components in addition to deionized water are A phase, deionization
Water be B phase, A is mixed be heated uniformly to 80-100 DEG C it is spare, by B heat phase to 60-80 DEG C high speed disperser stirring under
It is slowly added into A, insulated and stirred 10-30 minutes, cooling packing was to get product of the present invention.
Specific embodiment
The present invention will be described in detail combined with specific embodiments below.
For the better implementation present invention, following example explanation is now lifted, but embodiment is not limitation of the present invention.
Embodiment 1
A kind of automobile finish glazing agent, each component mass percent are as follows: 2% microcrystal wax of natural palm wax, 1% polyester wax, 2% silicon
2% ultraviolet absorbing agent of resin 6% polyamide, 2% polyacrylamide amine emulsifier, 2% nonionic emulsifier, 0.6% antistatic agent
1.3% essence, 0.2% petroleum solvent, 33% deionized water 44.9%.
Specific implementation method are as follows: all components in addition to deionized water are A phase, and deionized water is B phase, and A is mixed
Be heated uniformly to 80-100 DEG C it is spare, by B heat phase to 60-80 DEG C high speed disperser stirring under be slowly added into A, heat preservation is stirred
It mixes 10-30 minutes, cooling packing is to get product of the present invention.
Embodiment 2
A kind of automobile finish glazing agent, each component mass percent are as follows: 1% microcrystal wax of natural palm wax, 2% polyester wax, 2% silicon
2% ultraviolet absorbing agent of resin 3% polyamide, 2% polyacrylamide amine emulsifier, 6% nonionic emulsifier, 0.2% antistatic agent 2%
0.13% petroleum solvent of essence, 32% deionized water 46.53%.
Specific implementation method are as follows: all components in addition to deionized water are A phase, and deionized water is B phase, and A is mixed
Be heated uniformly to 80-100 DEG C it is spare, by B heat phase to 60-80 DEG C high speed disperser stirring under be slowly added into A, protect
Temperature stirring 10-30 minutes, cooling packing is to get product of the present invention.
Claims (1)
1. a kind of automobile finish glazing agent, it is characterised in that it includes following components (mass percent): natural palm wax 1-2%,
Microcrystal wax 1-2%, polyester wax 1-3%, silicone resin 5-8%, polyamide 1-2%, polyacrylamide amine emulsifier 2-6%, nonionic
Emulsifier 1-2%, ultraviolet absorbing agent 0.1-0.3%, antistatic agent 1-2%, essence 0.1-0.2%, petroleum solvent 30-50%, go from
Sub- water 40-60%.