CN109912203A - Water flow line style glaze and preparation method thereof - Google Patents
Water flow line style glaze and preparation method thereof Download PDFInfo
- Publication number
- CN109912203A CN109912203A CN201711326450.XA CN201711326450A CN109912203A CN 109912203 A CN109912203 A CN 109912203A CN 201711326450 A CN201711326450 A CN 201711326450A CN 109912203 A CN109912203 A CN 109912203A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- water flow
- flow line
- line style
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water flow line style glaze, the water flow line style glaze ground coat enamel each component and each component quality are as follows: 35 parts~42 parts of feldspar;14 parts~23 parts of dolomite;10 parts~12 parts of talcum;15 parts~18 parts of zinc oxide;6 parts~9 parts of barium carbonate;9 parts~11 parts of kaolin;13 parts~16 parts of zirconium silicate;The each component and each component content of overglaze are as follows: 35 parts~38 parts of soda-lime glass;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;12 parts~15 parts of Jiepai clay;15 parts~16 parts of zinc oxide.The water flow line style glaze is melted by ground coat enamel at high temperature and overglaze, flowing generate such as the fairshaped feeling of waterfall water, therefore in being water flow line style glaze, the glaze can in down-draft kiln steady production 1270 DEG C~1280 DEG C at a temperature of fire, the deep favor by customers.
Description
Technical field
The invention discloses a kind of water flow line style glaze and preparation method thereof.
Background technique
Currently, all kinds of furniture of life, tableware for daily use is all as enthusiasm of the people to ceramic process demand constantly increases
Gradually level off to more special fairly simple beautiful ceramic, which is by ground coat enamel at high temperature and face
Glaze melting, flow generation such as the fairshaped feeling of waterfall water, therefore in being water flow line style glaze, which can stablize life in down-draft kiln
Produce 1270 DEG C~1280 DEG C at a temperature of fire, the deep favor by customers.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies of existing technologies, glazing effect is improved, keeps it more beautiful
It sees, the invention discloses a kind of water flow line style glaze, the water flow line style glaze ground coat enamel each component and each component quality are as follows: feldspar 35
Part~42 parts;14 parts~23 parts of dolomite;10 parts~12 parts of talcum;15 parts~18 parts of zinc oxide;6 parts~9 parts of barium carbonate;It is high
9 parts~11 parts of ridge soil;13 parts~16 parts of zirconium silicate;The each component and each component content of overglaze are as follows: soda-lime glass 35 parts~38
Part;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;12 parts~15 parts of Jiepai clay;Zinc oxide
15 parts~16 parts;.
The step of water flow line style glaze production method, this method, is as follows:
A) water flow line style glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made;
C) clean green body is taken, is dried after upper ground coat enamel, upper overglaze, the upper black glaze outside green body;
D) green body of above-mentioned first-class glaze is burnt into 1270 DEG C of down-draft kiln.
After above-mentioned technical proposal, water flow line style glaze can stablize firing in 1270 DEG C of down-draft kiln, keep it more suitable
It should be deep to be liked by users in volume production.
Specific embodiment
In order that the present invention can be more clearly and readily understood, below according to specific embodiment, to the present invention make into
One step detailed description.
Embodiment one:
The invention discloses a kind of water flow line style glaze, the water flow line style glaze ground coat enamel each component and each component quality are as follows: long
35 parts~42 parts of stone;14 parts~23 parts of dolomite;10 parts~12 parts of talcum;15 parts~18 parts of zinc oxide;Barium carbonate 6 parts~9
Part;9 parts~11 parts of kaolin;13 parts~16 parts of zirconium silicate;The each component and each component content of overglaze are as follows: 35 parts of soda-lime glass~
38 parts;14 parts~16 parts of calcite;10 parts~12 parts of dolomite;4 parts~6 parts of Guizhou clay;8 parts~12 parts of Jiepai clay;Zinc oxide 8
Part~12 parts.
The step of water flow line style glaze production method, this method, is as follows:
A) water flow line style glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made;
C) clean green body is taken, is dried after upper ground coat enamel, upper overglaze, the upper black glaze outside green body;
D) green body of above-mentioned first-class glaze is burnt into 1270 DEG C of down-draft kiln.
Embodiment two:
The invention discloses a kind of water flow line style glaze, the water flow line style glaze ground coat enamel each component and each component quality are as follows: long
35 parts~42 parts of stone;14 parts~23 parts of dolomite;6 parts~8 parts of talcum;15 parts~18 parts of zinc oxide;6 parts~9 parts of barium carbonate;
9 parts~11 parts of kaolin;6 parts~8 parts of zirconium silicate;The each component and each component content of overglaze are as follows: soda-lime glass 35 parts~38
Part;13 parts~15 parts of calcite;12 parts~14 parts of dolomite;4 parts~6 parts of Guizhou clay;12 parts~15 parts of Jiepai clay;Zinc oxide
15 parts~16 parts.
The step of water flow line style glaze production method, this method, is as follows:
A) water flow line style glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made;
C) clean green body is taken, is dried after upper ground coat enamel, upper overglaze, the upper black glaze outside green body;
D) green body of above-mentioned first-class glaze is burnt into 1270 DEG C of down-draft kiln.
Embodiment three:
The invention discloses a kind of water flow line style glaze, the water flow line style glaze ground coat enamel each component and each component quality are as follows: long
35 parts~42 parts of stone;14 parts~23 parts of dolomite;10 parts~12 parts of talcum;15 parts~18 parts of zinc oxide;Barium carbonate 6 parts~9
Part;9 parts~11 parts of kaolin;13 parts~16 parts of zirconium silicate;The each component and each component content of overglaze are as follows: 35 parts of soda-lime glass~
38 parts;10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;12 parts~15 parts of Jiepai clay;Zinc oxide
15 parts~16 parts.
The step of water flow line style glaze production method, this method, is as follows:
A) water flow line style glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts;
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is adjusted
It is stand-by that 51~53 Baume concentration are made;
C) clean green body is taken, is dried after upper ground coat enamel, upper overglaze, the upper black glaze outside green body;
D) green body of above-mentioned first-class glaze is burnt into 1270 DEG C of down-draft kiln.
Conclusion: experiment one: water flow line effect is unobvious.
Experiment two: water flow effects are weaker.
Experiment three: meeting the purpose of this research and development, for the effect in ideal.
In summary 3 points to test three as ideal developmental achievement.
Particular embodiments described above, pair present invention solves the technical problem that, technical scheme and beneficial effects carry out
It is further described, it should be understood that the above is only a specific embodiment of the present invention, is not limited to this
Invention, all within the spirits and principles of the present invention, any modification, equivalent substitution, improvement and etc. done should be included in this hair
Within bright protection scope.
Claims (2)
1. the water flow line style glaze ground coat enamel each component and each component quality are as follows: feldspar the invention discloses a kind of water flow line style glaze
35 parts~42 parts;14 parts~23 parts of dolomite;10 parts~12 parts of talcum;15 parts~18 parts of zinc oxide;6 parts~9 parts of barium carbonate;It is high
9 parts~11 parts of ridge soil;13 parts~16 parts of zirconium silicate;The each component and each component content of overglaze are as follows: 35 parts~38 parts of soda-lime glass;
10 parts~12 parts of calcite;14 parts~16 parts of dolomite;4 parts~6 parts of Guizhou clay;12 parts~15 parts of Jiepai clay;15 parts of zinc oxide
~16 parts.
2. the step of water flow line style glaze glaze production method described in, this method, is as follows:
A) water flow line style glaze ground coat enamel, overglaze are stocked up according to each component and each component mass parts:
B) 1.6 ︰ 0.7 of You Liao ︰ Qiu ︰ water=1 ︰ wet ball grinding 15~17 hours, after the glaze after ball milling crosses 200 meshes, is modulated into
51~53 Baume concentration are stand-by;
C) clean green body is taken, is dried after upper ground coat enamel, upper overglaze, the upper black glaze outside green body.
D) green body of above-mentioned first-class glaze is burnt into 1270 DEG C of down-draft kiln.