CN109898361A - A kind of Chemical fiber paper bobbin preparation method - Google Patents
A kind of Chemical fiber paper bobbin preparation method Download PDFInfo
- Publication number
- CN109898361A CN109898361A CN201910113604.XA CN201910113604A CN109898361A CN 109898361 A CN109898361 A CN 109898361A CN 201910113604 A CN201910113604 A CN 201910113604A CN 109898361 A CN109898361 A CN 109898361A
- Authority
- CN
- China
- Prior art keywords
- fibre
- chemical fiber
- bobbin preparation
- chemical
- fiber paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Chemical fiber paper bobbin preparation method, system selects bamboo fibre and removes the impurity in fiber and fibre defect；It after bamboo fibre is blended, is added in other raw materials, is uniformly mixed with the 10-30% of fibre weight part, 30-50%, 50-70% respectively in three times；After mixing is coiled by heat treatment allow fiber fusion together；Hydrolyzed 2 hours at 60 DEG C, precipitating is filtered, washed, dries, processing form paper tube getting the product, obtained in waste acid water can for recycling.The Chemical fiber paper bobbin preparation method, environmental protection processing method is simple, can increase many wearabilities in use, and anti-pressure ability is reinforced.
Description
Technical field
The present invention relates to paper tube preparation technical field, specially a kind of Chemical fiber paper bobbin preparation method.
Background technique
With the development of the society, chemical fibre industry has biggish development, the demand of fiber product is also increasing, therefore
To the production equipment of chemical fibre industry, more stringent requirements are proposed.
It is raw material that chemical fibre, which is with natural polymer or artificial synthesized high-molecular compound, is spun by preparation
The processes such as silk stock solution, the spinning and post-processing fiber obtained with textile performance.
The properties such as length, thickness, whiteness, the gloss of fiber can be adjusted in process of production.And it is respectively provided with resistance to
Light, wear-resisting, easy to wash the advantages that easily doing, not going rotten, be not damaged by insects.It is widely used in manufacture clothing fabric, filter cloth, conveyer belt, the fire hose
Band, rope, fishing net, electric insulated, medical suture, tyre cord and parachute etc..High-molecular compound can be generally made
Solution or melt are extruded from spinning head pore, then form fiber through solidification.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of Chemical fiber paper bobbin preparation method, existing cutting is solved
Device takes time and effort, the unconspicuous problem of cutting effect.
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of Chemical fiber paper bobbin preparation method, packet
Chemical fibre, bamboo fibre are included, system selects bamboo fibre and removes the impurity in fiber and fibre defect；After bamboo fibre is blended, divide three
It is secondary to be added in other raw materials with the 10-30% of fibre weight part, 30- 50%, 50-70% respectively, it is uniformly mixed；It will after mixing is coiled
Heat treatment allow fiber fusion together；It is hydrolyzed 2 hours at 60 DEG C, precipitating is filtered, washed, dries, and processing forms paper tube and obtains
Product, obtained in waste acid water can for recycling.
Further, chemical fibre 20-40%, bamboo fibre 60-80%.
Further, drier is tubular cooler.
Further, finally chemical-fibres filaments are wound.
Further, after paper tube is made, paper layer is added in paper tube synthesis.
Further, the addition paper layer is closely connect with the paper tube ontology.
Compared with prior art, the beneficial effects of the present invention are: the Chemical fiber paper bobbin preparation method, environmental protection processing method letter
It is single, many wearabilities can be increased in use, and anti-pressure ability is reinforced.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
A kind of Chemical fiber paper bobbin preparation method, including chemical fibre, bamboo fibre, system select bamboo fibre and remove the impurity in fiber
And fibre defect；After bamboo fibre is blended, in three times respectively with the 10-30% of fibre weight part, 30- 50%, it is added in 50-70%
In his raw material, it is uniformly mixed；After mixing is coiled by heat treatment allow fiber fusion together；It is hydrolyzed 2 hours at 60 DEG C, precipitating, mistake
Filter, washing, dry, processing forms paper tube getting the product, obtained in waste acid water can be for recycling.
Wherein, chemical fibre 20-40%, bamboo fibre 60-80%.
Wherein, drier is tubular cooler.
Wherein, finally chemical-fibres filaments are wound.
Wherein, after paper tube is made, paper layer is added in paper tube synthesis.
Wherein, the addition paper layer is closely connect with the paper tube ontology.
Moreover, the terms "include", "comprise" or any other variant thereof is intended to cover non-exclusive inclusion, to make
Obtaining the process, method, article or equipment including a series of elements not only includes those elements, but also including not arranging clearly
Other element out, or further include for elements inherent to such a process, method, article, or device.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of Chemical fiber paper bobbin preparation method, including chemical fibre, bamboo fibre, it is characterised in that: system selects bamboo fibre and removes fibre
Impurity and fibre defect in dimension；After bamboo fibre is blended, in three times respectively with the 10-30% of fibre weight part, 30- 50%,
50-70% is added in other raw materials, is uniformly mixed；After mixing is coiled by heat treatment allow fiber fusion together；2 are hydrolyzed at 60 DEG C
Hour, precipitating is filtered, washed, dries, and processing forms paper tube getting the product, obtained in waste acid water can be for repeating benefit
With.
2. a kind of Chemical fiber paper bobbin preparation method according to claim 1, it is characterised in that: chemical fibre 20-40%, bamboo are fine
Tie up 60-80%.
3. a kind of Chemical fiber paper bobbin preparation method according to claim 1, it is characterised in that: drier is tubular cooler.
4. a kind of Chemical fiber paper bobbin preparation method according to claim 1, it is characterised in that: finally receive chemical-fibres filaments
Volume.
5. a kind of Chemical fiber paper bobbin preparation method according to claim 1, it is characterised in that: after paper tube is made, in paper tube
Paper layer is added in synthesis.
6. a kind of Chemical fiber paper bobbin preparation method according to claim 1, it is characterised in that: the addition paper layer and the paper
Cylinder ontology closely connects.