CN109896786A - A kind of light building wall thermal insulation material - Google Patents
A kind of light building wall thermal insulation material Download PDFInfo
- Publication number
- CN109896786A CN109896786A CN201711304978.7A CN201711304978A CN109896786A CN 109896786 A CN109896786 A CN 109896786A CN 201711304978 A CN201711304978 A CN 201711304978A CN 109896786 A CN109896786 A CN 109896786A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- thermal insulation
- building wall
- insulation material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of light building wall thermal insulation materials, are prepared by the component of following parts by weight: cement 35-55 parts by weight, aluminium oxide tailing 20-45 parts by weight, epoxy resin 5-10 parts by weight, cinder 12-25 parts by weight, foam 8-25 parts by weight, fire retardant 15-28 parts by weight, dibutyl tin dilaurate 2-4 parts by weight, aluminosilicate fiber cotton 5-10 parts by weight, modification infusorial earth 10-30 parts by weight, foaming agent 2-5 parts by weight, wood fibre 5-12 parts by weight, expanded perlite 5-10 parts by weight.Light building wall thermal insulation material of the present invention, raw material sources used by the preparation method of light heat-insulation wall material are extensive, low in cost, preparation process is simple, easily operated, low energy consumption, and discharges without " three wastes ", has good popularization and application foreground.
Description
Technical field
The invention belongs to the field of building materials, more particularly, to a kind of light building wall thermal insulation material.
Background technique
With the continuous social and economic development, living standards of the people have also obtained certain raising, in such society's back
Under scape, we also have higher requirement architectural engineering.In recent years, people increasingly focus on environmental protection, energy conservation in life,
Also gradually energy-saving and environment-friendly theory is dissolved into architectural engineering, construction material as environment protection architecture engineering important content it
One, people are even more to require its performance.
External-wall heat-insulation material refers exclusively to a kind of thermal insulation material for construction wall, according to using position that can be divided into: exterior wall is protected
Adiabator, heat insulating inner wall material, roofing heat insulating material;Can be divided into according to the inherent ingredient of thermal insulation material: inorganic heat insulation material and
Organic insulation material.Light insulating wall have many advantages, such as high-performance, high quality, energy conservation and environmental protection and closed extensively by people in the industry
Note.It is low but there is also intensity in use process, the disadvantages of heat insulation effect is poor.
Summary of the invention
In view of this, the present invention is directed to propose a kind of light building wall thermal insulation material, is able to solve the above problem.
In order to achieve the above objectives, the technical scheme of the present invention is realized as follows:
A kind of light building wall thermal insulation material, is prepared by the component of following parts by weight:
Cement 35-55 parts by weight,
Aluminium oxide tailing 20-45 parts by weight,
Epoxy resin 5-10 parts by weight,
Cinder 12-25 parts by weight,
Foam 8-25 parts by weight,
Fire retardant 15-28 parts by weight,
Dibutyl tin dilaurate 2-4 parts by weight,
Aluminosilicate fiber cotton 5-10 parts by weight,
Modification infusorial earth 10-30 parts by weight,
Foaming agent 2-5 parts by weight,
Wood fibre 5-12 parts by weight,
Expanded perlite 5-10 parts by weight.
Further, the component by following parts by weight is prepared:
Cement 40-55 parts by weight,
Aluminium oxide tailing 25-45 parts by weight,
Epoxy resin 5-10 parts by weight,
Cinder 15-25 parts by weight,
Foam 10-25 parts by weight,
Fire retardant 20-28 parts by weight,
Dibutyl tin dilaurate 2-4 parts by weight,
Aluminosilicate fiber cotton 5-10 parts by weight,
Modification infusorial earth 15-30 parts by weight,
Foaming agent 2-5 parts by weight,
Wood fibre 5-12 parts by weight,
Expanded perlite 5-10 parts by weight.
Further, the component by following parts by weight is prepared:
40 parts by weight of cement,
25 parts by weight of aluminium oxide tailing,
5 parts by weight of epoxy resin,
15 parts by weight of cinder,
10 parts by weight of foam,
20 parts by weight of fire retardant,
2 parts by weight of dibutyl tin dilaurate,
5 parts by weight of aluminosilicate fiber cotton,
15 parts by weight of modification infusorial earth,
2 parts by weight of foaming agent,
5 parts by weight of wood fibre,
5 parts by weight of expanded perlite.
Further, the component by following parts by weight is prepared:
45 parts by weight of cement,
30 parts by weight of aluminium oxide tailing,
8 parts by weight of epoxy resin,
18 parts by weight of cinder,
20 parts by weight of foam,
26 parts by weight of fire retardant,
3 parts by weight of dibutyl tin dilaurate,
6 parts by weight of aluminosilicate fiber cotton,
22 parts by weight of modification infusorial earth,
4 parts by weight of foaming agent,
8 parts by weight of wood fibre,
8 parts by weight of expanded perlite.
Further, the component by following parts by weight is prepared:
55 parts by weight of cement,
45 parts by weight of aluminium oxide tailing,
10 parts by weight of epoxy resin,
25 parts by weight of cinder,
25 parts by weight of foam,
28 parts by weight of fire retardant,
4 parts by weight of dibutyl tin dilaurate,
10 parts by weight of aluminosilicate fiber cotton,
30 parts by weight of modification infusorial earth,
5 parts by weight of foaming agent,
12 parts by weight of wood fibre,
10 parts by weight of expanded perlite.
Further, the preparation method includes the following steps:
Step 1: cement, aluminium oxide tailing, cinder, modification infusorial earth are first mixed, asphalt mixtures modified by epoxy resin is then sequentially placed into
Rouge, foam, fire retardant, foaming agent, expanded perlite, the stir process 20-30min at 80-85 DEG C, after mixing evenly, then put
Enter dibutyl tin dilaurate, aluminosilicate fiber cotton, wood fibre to stir evenly, carry out ultrasonic treatment 1.5-2.5h, is made mixed
Close material;
Step 2: mixed material is placed in building materials panel moulding apparatus, and building thermal insulation wall body material is made.
Compared with the existing technology, light building wall thermal insulation material of the present invention has the advantage that
Light building wall thermal insulation material of the present invention, original used by the preparation method of light heat-insulation wall material
Expect from a wealth of sources, low in cost, preparation process is simple, easily operated, low energy consumption, and discharges without " three wastes ", has good
Popularization and application foreground.
Specific embodiment
Below with reference to embodiment, the present invention will be described in detail.
Embodiment 1
A kind of light building wall thermal insulation material, preparation method include the following steps:
Step 1: by 40 parts by weight of cement, 25 parts by weight of aluminium oxide tailing, 15 parts by weight of cinder, 15 weight of modification infusorial earth
Amount part is first mixed, and 5 parts by weight of epoxy resin, 10 parts by weight of foam, 20 parts by weight of fire retardant, foaming agent are then sequentially placed into
2 parts by weight, 5 parts by weight of expanded perlite, the stir process 25min at 80 DEG C place into two fourth of tin dilaurate after mixing evenly
2 parts by weight of base tin, 5 parts by weight of aluminosilicate fiber cotton, 5 parts by weight of wood fibre stir evenly, and carry out ultrasonic treatment 2h, are made mixed
Close material;
Step 2: mixed material is placed in building materials panel moulding apparatus, and building thermal insulation wall body material is made.High anti bending strength:
0.4MPa/50mm thickness, compression strength are high: 1.5Mpa, good heat insulating.
Embodiment 2
A kind of light building wall thermal insulation material, preparation method include the following steps:
Step 1: by 45 parts by weight of cement, 30 parts by weight of aluminium oxide tailing, 18 parts by weight of cinder, 22 weight of modification infusorial earth
Amount part is first mixed, and 8 parts by weight of epoxy resin, 20 parts by weight of foam, 26 parts by weight of fire retardant, foaming agent are then sequentially placed into
4 parts by weight, 8 parts by weight of expanded perlite, the stir process 25min at 80 DEG C place into two fourth of tin dilaurate after mixing evenly
3 parts by weight of base tin, 6 parts by weight of aluminosilicate fiber cotton, 8 parts by weight of wood fibre stir evenly, and carry out ultrasonic treatment 2h, are made mixed
Close material;
Step 2: mixed material is placed in building materials panel moulding apparatus, and building thermal insulation wall body material is made.High anti bending strength:
0.4MPa/50mm thickness, compression strength are high: 1.5Mpa, good heat insulating.
Embodiment 3
A kind of light building wall thermal insulation material, preparation method include the following steps:
Step 1: by 55 parts by weight of cement, 45 parts by weight of aluminium oxide tailing, 25 parts by weight of cinder, 30 weight of modification infusorial earth
Amount part is first mixed, and 10 parts by weight of epoxy resin, 25 parts by weight of foam, 28 parts by weight of fire retardant, foaming are then sequentially placed into
5 parts by weight of agent, 10 parts by weight of expanded perlite, stir process 25min places into tin dilaurate after mixing evenly at 80 DEG C
4 parts by weight of dibutyl tin, 10 parts by weight of aluminosilicate fiber cotton, 12 parts by weight of wood fibre stir evenly, and carry out ultrasonic treatment 2h,
Mixed material is made;
Step 2: mixed material is placed in building materials panel moulding apparatus, and building thermal insulation wall body material is made.High anti bending strength:
0.4MPa/50mm thickness, compression strength are high: 1.5Mpa, good heat insulating.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (6)
1. a kind of light building wall thermal insulation material, it is characterised in that: be prepared by the component of following parts by weight:
Cement 35-55 parts by weight,
Aluminium oxide tailing 20-45 parts by weight,
Epoxy resin 5-10 parts by weight,
Cinder 12-25 parts by weight,
Foam 8-25 parts by weight,
Fire retardant 15-28 parts by weight,
Dibutyl tin dilaurate 2-4 parts by weight,
Aluminosilicate fiber cotton 5-10 parts by weight,
Modification infusorial earth 10-30 parts by weight,
Foaming agent 2-5 parts by weight,
Wood fibre 5-12 parts by weight,
Expanded perlite 5-10 parts by weight.
2. light building wall thermal insulation material according to claim 1, it is characterised in that: by the component of following parts by weight
It is prepared:
Cement 40-55 parts by weight,
Aluminium oxide tailing 25-45 parts by weight,
Epoxy resin 5-10 parts by weight,
Cinder 15-25 parts by weight,
Foam 10-25 parts by weight,
Fire retardant 20-28 parts by weight,
Dibutyl tin dilaurate 2-4 parts by weight,
Aluminosilicate fiber cotton 5-10 parts by weight,
Modification infusorial earth 15-30 parts by weight,
Foaming agent 2-5 parts by weight,
Wood fibre 5-12 parts by weight,
Expanded perlite 5-10 parts by weight.
3. light building wall thermal insulation material according to claim 1, it is characterised in that: by the component of following parts by weight
It is prepared:
40 parts by weight of cement,
25 parts by weight of aluminium oxide tailing,
5 parts by weight of epoxy resin,
15 parts by weight of cinder,
10 parts by weight of foam,
20 parts by weight of fire retardant,
2 parts by weight of dibutyl tin dilaurate,
5 parts by weight of aluminosilicate fiber cotton,
15 parts by weight of modification infusorial earth,
2 parts by weight of foaming agent,
5 parts by weight of wood fibre,
5 parts by weight of expanded perlite.
4. light building wall thermal insulation material according to claim 1, it is characterised in that: by the component of following parts by weight
It is prepared:
45 parts by weight of cement,
30 parts by weight of aluminium oxide tailing,
8 parts by weight of epoxy resin,
18 parts by weight of cinder,
20 parts by weight of foam,
26 parts by weight of fire retardant,
3 parts by weight of dibutyl tin dilaurate,
6 parts by weight of aluminosilicate fiber cotton,
22 parts by weight of modification infusorial earth,
4 parts by weight of foaming agent,
8 parts by weight of wood fibre,
8 parts by weight of expanded perlite.
5. light building wall thermal insulation material according to claim 1, it is characterised in that: by the component of following parts by weight
It is prepared:
55 parts by weight of cement,
45 parts by weight of aluminium oxide tailing,
10 parts by weight of epoxy resin,
25 parts by weight of cinder,
25 parts by weight of foam,
28 parts by weight of fire retardant,
4 parts by weight of dibutyl tin dilaurate,
10 parts by weight of aluminosilicate fiber cotton,
30 parts by weight of modification infusorial earth,
5 parts by weight of foaming agent,
12 parts by weight of wood fibre,
10 parts by weight of expanded perlite.
6. light building wall thermal insulation material according to claim 1-5, it is characterised in that: preparation method includes
Following steps:
Step 1: cement, aluminium oxide tailing, cinder, modification infusorial earth are first mixed, be then sequentially placed into epoxy resin,
Foam, fire retardant, foaming agent, expanded perlite, stir process 20-30min places into two after mixing evenly at 80-85 DEG C
Dibutyl tin laurate, aluminosilicate fiber cotton, wood fibre stir evenly, and carry out ultrasonic treatment 1.5-2.5h, and mixture is made
Material;
Step 2: mixed material is placed in building materials panel moulding apparatus, and building thermal insulation wall body material is made.