CN109875912B - Hydrogel microsphere for cosmetics and preparation method thereof - Google Patents
Hydrogel microsphere for cosmetics and preparation method thereof Download PDFInfo
- Publication number
- CN109875912B CN109875912B CN201910235211.6A CN201910235211A CN109875912B CN 109875912 B CN109875912 B CN 109875912B CN 201910235211 A CN201910235211 A CN 201910235211A CN 109875912 B CN109875912 B CN 109875912B
- Authority
- CN
- China
- Prior art keywords
- hydrogel
- cosmetics
- cosmetic
- agar
- carrageenan
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a cosmetic hydrogel microsphere and a preparation method thereof, wherein the cosmetic hydrogel microsphere comprises the following components in parts by weight: 0.05 to 1 portion of carrageenan, 0.2 to 1 portion of agar, 0.2 to 1 portion of gellan gum and 0.05 to 1 portion of locust bean gum. The formulation and the process of the hydrogel spheres for cosmetics overcome the problem of instability when the hydrogel spheres are added into cosmetics, so that the hydrogel spheres are suitable for a wider pH value range, a wider electrolyte concentration range and wider applicability of various cosmetic systems, and the stability of the hydrogel spheres for long-term storage is fundamentally solved.
Description
Technical Field
The invention relates to the field of cosmetics, in particular to a hydrogel microsphere for cosmetics and a preparation method thereof.
Background
Currently, hydrogel microspheres used in cosmetics are added into transparent or translucent essence or gel to achieve the effects of carrying active ingredients, increasing the appearance, improving the skin feel after use and the like. The small ball can be made into various colors, and the cosmetics added with the small ball have rich and beautiful appearance and are popular with consumers.
The existing hydrogel beads mostly adopt the principle that a sodium alginate aqueous solution immediately forms transparent gel when meeting calcium ions, and the sodium alginate aqueous solution is dripped into a calcium chloride aqueous solution by a dripping method to form gel beads immediately, and then the gel beads are collected. The obvious disadvantage of this technique is that when the pellets are placed in a cosmetic system that does not contain calcium ions, the calcium ions in the pellets diffuse out of the pellets and the pellets disintegrate and dissolve away, which greatly limits the use of these spherical hydrogels.
Disclosure of Invention
The invention aims to overcome the defects in the prior art and provides a hydrogel microsphere for cosmetics and a preparation method thereof.
In order to achieve the purpose, the invention adopts the technical scheme that: a hydrogel microsphere for cosmetics comprises the following components in parts by weight: 0.05 to 1 portion of carrageenan, 0.2 to 1 portion of agar, 0.2 to 1 portion of gellan gum and 0.05 to 1 portion of locust bean gum.
Compared with the prior art, the hydrogel microsphere for cosmetics has the following advantages: 1. can be stable for a long time in cosmetics with a pH value of 4-9; 2. can be stable for a long time in cosmetics with strong electrolyte system (2% sodium chloride solution); 3. can be stable for a long time in cosmetic systems with or without calcium ions. 4. Can be stable for a long time in a cosmetic system containing a surfactant or an emulsifier; 5. can be stable for a long time in common cosmetic systems such as aqueous solution, hydrogel, cream, emulsion, oil phase and the like; 6. can be stable for a long time in the environment of low temperature (3 ℃) and high temperature (70 ℃); 7. can be squeezed out and pulverized or applied and pulverized by cosmetic small packaging pump head without residue.
As a preferred embodiment of the hydrogel spheres for cosmetics according to the present invention, the following components are included in parts by weight: 0.1-0.5 part of carrageenan, 0.3-0.8 part of agar, 0.3-0.8 part of gellan gum and 0.1-0.5 part of locust bean gum. The hydrogel microspheres prepared by the proportion have better performance and more stable property.
As a preferred embodiment of the hydrogel spheres for cosmetics according to the present invention, the following components are included in parts by weight: 0.3 part of carrageenan, 0.5 part of agar, 0.5 part of gellan gum and 0.3 part of locust bean gum. The hydrogel microspheres prepared by the proportion have the best performance and the most stable property, and can be stored for a long time.
The hydrogel pellet for cosmetics according to the preferred embodiment of the present invention further comprises 0.05 to 0.3 parts by weight of an efficacy additive, wherein the efficacy additive is at least one of yeast extract, astragaloside, sodium hyaluronate, trimethylglycine, polyglutamic acid, and D-mannitol.
The functional additive can exist in the hydrogel spheres stably for a long time, is not easy to deteriorate, and can improve the whitening and moisturizing effects of the hydrogel spheres.
As a preferred embodiment of the hydrogel pellet for cosmetics according to the present invention, the efficacy additive is a mixture of yeast extract, astragaloside, sodium hyaluronate, trimethylglycine, polyglutamic acid, and D-mannitol.
As a preferable embodiment of the hydrogel spheres for cosmetics according to the present invention, the hydrogel spheres for cosmetics further comprise 0.05 to 0.5 parts by weight of jjjj' ma liquid.
As a preferred embodiment of the hydrogel spheres for cosmetics according to the present invention, water is further contained.
As a preferred embodiment of the hydrogel pellet for cosmetics according to the present invention, a colorant is further contained. Coloring or pearlizing agents can be added according to specific requirements.
Another object of the present invention is to provide a method for preparing the hydrogel spheres for cosmetics, the method comprising the steps of:
(1) heating water to boil, sequentially adding carrageenan, agar, gellan gum and locust bean gum, and continuously stirring to completely dissolve;
(2) reducing the temperature to 68-72 ℃, and adding JMPLUS to completely dissolve;
(3) cooling to 58-62 ℃, and adding the functional additive to completely dissolve the functional additive;
(4) preserving heat and defoaming at 58-62 ℃;
(5) and dropping the mixture into a dropping column at the temperature of 58-62 ℃ to form spherical particles, thus obtaining the hydrogel microspheres for cosmetics.
The drop column is a transparent cylindrical column type device filled with an upper oil phase and a lower water phase, and each raw material mixture can form spherical particles in the drop column. The process is simple, and can be used for large-scale industrial production, and the hydrogel spherulites prepared by the process have stable performance and uniform quality.
The invention has the beneficial effects that: the invention provides a hydrogel microsphere for cosmetics and a preparation method thereof. The formulation and the process of the hydrogel spheres for cosmetics overcome the problem of instability when the hydrogel spheres are added into cosmetics, so that the hydrogel spheres are suitable for a wider pH value range, a wider electrolyte concentration range and wider applicability of various cosmetic systems, and the stability of the hydrogel spheres for long-term storage is fundamentally solved.
Drawings
FIG. 1 is a photograph of a hydrogel pellet for cosmetics according to the present invention.
Detailed Description
To better illustrate the objects, aspects and advantages of the present invention, the present invention will be further described with reference to specific examples.
Examples 1 to 6 and comparative examples 1 to 4
The raw material formulation of the hydrogel spheres for cosmetics described in examples 1 to 6 and comparative examples 1 to 4 is shown in table 1, wherein the functional additives have the same components and are a mixture of yeast extract, astragaloside, sodium hyaluronate, trimethylglycine, polyglutamic acid and D-mannitol.
The method for preparing cosmetic hydrogel microspheres described in examples 1 to 6 and comparative examples 1 to 4 comprises the following steps:
(1) heating water to boil, sequentially adding carrageenan, agar, gellan gum and locust bean gum, and continuously stirring to completely dissolve;
(2) cooling to 68-72 ℃, and adding German solution to completely dissolve the German solution;
(3) cooling to 58-62 ℃, and adding the functional additive to completely dissolve the functional additive;
(4) preserving heat and defoaming at 58-62 ℃;
(5) and dripping the mixture into a dripping column at the temperature of 58-62 ℃ to form spherical particles, and screening to obtain the hydrogel microspheres for cosmetics.
Table 1 raw material formulation (wt.%) of hydrogel spherule for cosmetics described in examples 1 to 6 and comparative examples 1 to 4
Example 7
The photographs of the hydrogel spheres obtained in examples 1 to 6 are shown in FIG. 1. The hydrogel microspheres of examples 1 to 6 and comparative examples 1 to 4 were stored in electrolyte solutions at different pH values for 30 days, at different temperatures for 60 days, and for 100 days, respectively, and the stability of the quality was tested, and the test results are shown in table 2.
Table 2 stability test results
Note: the "+" indicates that the shape of the small ball is not changed and the small ball is uniformly twisted and smeared; "-" indicates that the shape of the pellet is changed, or the pellet is dissolved or is not uniformly coated by twisting and smashing.
As can be seen from the test results in Table 2, the hydrogel microspheres of examples 1-6 had pH values ranging from 4 to 9, temperatures ranging from 3 to 70 ℃, 2% NaCl solution and 1% CaCl2The solution can be stored for 30 days, 60 days and 100 days respectively to keep stable quality, and the comparative examples 1-4 can dissolve small spheres to a certain extent and change the appearance along with the increase of the storage timeThe phenomenon of uneven shape or twisting and smearing shows that the components of the formula of the hydrogel spheres are mutually matched, so that the long-term stability of the hydrogel spheres in different solvent systems is ensured, and the defect is that the hydrogel spheres cannot be used.
Finally, it should be noted that the above embodiments are only used for illustrating the technical solutions of the present invention and not for limiting the protection scope of the present invention, and although the present invention is described in detail with reference to the preferred embodiments, it should be understood by those skilled in the art that modifications or equivalent substitutions can be made on the technical solutions of the present invention without departing from the spirit and scope of the technical solutions of the present invention.
Claims (5)
1. The hydrogel microspheres for cosmetics are characterized by comprising the following components in parts by weight based on 100 parts by weight: 0.1-0.5 part of carrageenan, 0.3-0.8 part of agar, 0.3-0.8 part of gellan gum, 0.1-0.5 part of locust bean gum, 0.05-0.3 part of efficacy additive, 0.05-0.5 part of Jima liquid and the balance of water;
the preparation method of the hydrogel spherule for cosmetics comprises the following steps:
(1) heating water to boil, sequentially adding carrageenan, agar, gellan gum and locust bean gum, and continuously stirring to completely dissolve;
(2) cooling to 68-72 ℃, and adding German solution to completely dissolve the German solution;
(3) cooling to 58-62 ℃, and adding the functional additive to completely dissolve the functional additive;
(4) preserving heat and defoaming at 58-62 ℃;
(5) and dropping the mixture into a dropping column at the temperature of 58-62 ℃ to form spherical particles, thus obtaining the hydrogel microspheres for cosmetics.
2. The cosmetic hydrogel microspheres as claimed in claim 1, comprising the following components in parts by weight: 0.3 part of carrageenan, 0.5 part of agar, 0.5 part of gellan gum and 0.3 part of locust bean gum.
3. The cosmetic hydrogel spheroids of claim 1, wherein the efficacy additive is at least one of yeast extract, astragaloside, sodium hyaluronate, trimethylglycine, polyglutamic acid, and D-mannitol.
4. The cosmetic hydrogel spheroids of claim 3, wherein the efficacy additive is a mixture of yeast extract, astragaloside, sodium hyaluronate, trimethylglycine, polyglutamic acid, and D-mannitol.
5. The cosmetic hydrogel spheroids of claim 1, further comprising 0.1 part of a colorant.