CN109873052A - 一种太阳能电池扩散后退火工艺 - Google Patents

一种太阳能电池扩散后退火工艺 Download PDF

Info

Publication number
CN109873052A
CN109873052A CN201910249286.XA CN201910249286A CN109873052A CN 109873052 A CN109873052 A CN 109873052A CN 201910249286 A CN201910249286 A CN 201910249286A CN 109873052 A CN109873052 A CN 109873052A
Authority
CN
China
Prior art keywords
passed
flow
annealing
nitrogen
gases
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201910249286.XA
Other languages
English (en)
Other versions
CN109873052B (zh
Inventor
韩燕旭
杨飞飞
梁玲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Luan Solar Energy Technology Co Ltd
Original Assignee
Shanxi Luan Solar Energy Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Luan Solar Energy Technology Co Ltd filed Critical Shanxi Luan Solar Energy Technology Co Ltd
Priority to CN201910249286.XA priority Critical patent/CN109873052B/zh
Publication of CN109873052A publication Critical patent/CN109873052A/zh
Application granted granted Critical
Publication of CN109873052B publication Critical patent/CN109873052B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及太阳能电池片生产领域。一种太阳能电池扩散后退火工艺，正常温度推进，将石英炉管升温至840℃，以7slm/min的流量通入氮气，以2.5slm/min的流量通入氧气，不通入其它气体，推进7‑9min；降温到810℃同时进行推进和退火，以5℃/min速率降至810℃，以7slm/min的流量通入氮气，不通入其它气体，保持推进和退火5‑7min；将温度降至750℃‑800℃进行变温退火，以2℃/min降温至780℃，同时保持以7slm/min的流量通入氮气，不通入其它气体，然后保温15‑25min。

Description

一种太阳能电池扩散后退火工艺
技术领域
本发明涉及太阳能电池片生产领域，特别涉及太阳能电池扩散后退火领域。
背景技术
扩散作为常规电池工艺关键的工序，其重要作用不言而喻，扩散主要用于制作PN结，目前的扩散采用管式磷源沉积居多。扩散除建立内建电场之外，还有用于吸杂的作用，其原理是利用表面磷硅玻璃与硅本身固溶度的不同，从而在一定温度下实现吸除杂质的目的，但在具体吸杂工艺中，工艺参数的调整比较复杂，关于温度、时间、速率等都需要兼顾考虑各种情况。
发明内容
本发明所要解决的技术问题是：如何通过调整硅片后退火工艺提高硅片性能。
本发明所采用的技术方案是：一种太阳能电池扩散后退火工艺，在太阳能电池扩散后退火过程中按照如下的步骤进行
步骤一、正常温度推进，将石英炉管升温至840℃，以7slm/min的流量通入氮气，以2.5slm/min的流量通入氧气，不通入其它气体，推进7-9min；
步骤二、降温到810℃同时进行推进和退火，以5℃/min速率降至810℃，以7slm/min的流量通入氮气，不通入其它气体，保持推进和退火5-7min；
步骤三、将温度降至750℃-800℃进行变温退火，以2℃/min降温至780℃，同时保持以7slm/min的流量通入氮气，不通入其它气体，然后保温15-25min。
步骤四、补磷源退火，以900sccm/min流量通入三氯氧磷，以750slm/min流量通入氧气，不通入其它气体，以2℃/min降温至650℃。
步骤五、氮气保护退火，以7slm/min的流量通入氮气，不通入其它气体，以2℃/min降温至常温。
本发明的有益效果是：硅片性能可以得到很大改善，开路电压提升明显，对传统电池提效做出很大贡献（效率提升0.07%）。
具体实施方式
首先石英炉管充氮气，然后石英舟以35cm/min的速度进入石英炉管，关闭炉门，以10℃/min的升温速率至780℃，等待2分钟。
通氮气流量7slm/min、氧气流量2slm/min，共持续5分钟。
设置各温区中心温度为810℃，通氮气流量7slm/min、通小氮流量（三氯氧磷）1000sccm/min、氧气流量为800slm/min，开始磷源沉积，时间为7min。
升温至840℃，通氮气流量7slm/min、氧气流量为2.5slm/min，开始推进工艺，推进时间为8min；以5℃/min降温速率降至810℃，通氮气流量7slm/min，维持6min，进行推进和退火。
设置降温速率为2℃/min，通氮气流量7slm/min，由810℃缓慢降温至780℃，维持20min,进行变温退火。
补磷源退火，以900sccm/min流量通入三氯氧磷，以750slm/min流量通入氧气，以2℃/min降温至650℃。
氮气保护退火，以7slm/min的流量通入氮气，不通入其它气体，以2℃/min降温至常温。
正常扩散工艺包括沉积与推进两个过程，在磷源的沉积过程中，温度相对比较低，属于无限源扩散，在硅片表面形成一部分磷源重掺区域；在推进过程中，温度相对较高，属于有限源推进，在热能的驱动下，磷原子扩散到硅片一定深度，形成PN结。扩散退火要注意两个方面，一是过高温度会导致杂质的再分解，二是过快的降温速率会影响杂质的沉淀与吸出。

Claims (3)

1.一种太阳能电池扩散后退火工艺，其特征在于：在太阳能电池扩散后退火过程中按照如下的步骤进行
步骤一、正常温度推进，将石英炉管升温至840℃，以7slm/min的流量通入氮气，以2.5slm/min的流量通入氧气，不通入其它气体，推进7-9min；
步骤二、降温到810℃同时进行推进和退火，以5℃/min速率降至810℃，以7slm/min的流量通入氮气，不通入其它气体，保持推进和退火5-7min；
步骤三、将温度降至750℃-800℃进行变温退火，以2℃/min降温至780℃，同时保持以7slm/min的流量通入氮气，不通入其它气体，然后保温15-25min。
2.根据权利要求1所述的一种太阳能电池扩散后退火工艺，其特征在于：在步骤三后进行如下步骤四
步骤四、补磷源退火，以900sccm/min流量通入三氯氧磷，以750slm/min流量通入氧气，不通入其它气体，以2℃/min降温至650℃。
3.根据权利要求2所述的一种太阳能电池扩散后退火工艺，其特征在于：在步骤四后进行如下步骤五
步骤五、氮气保护退火，以7slm/min的流量通入氮气，不通入其它气体，以2℃/min降温至常温。
CN201910249286.XA 2019-03-29 2019-03-29 一种太阳能电池扩散后退火工艺 Active CN109873052B (zh)