CN109868098A - A kind of family bathroom space marine glue preparation method - Google Patents
A kind of family bathroom space marine glue preparation method Download PDFInfo
- Publication number
- CN109868098A CN109868098A CN201910051262.3A CN201910051262A CN109868098A CN 109868098 A CN109868098 A CN 109868098A CN 201910051262 A CN201910051262 A CN 201910051262A CN 109868098 A CN109868098 A CN 109868098A
- Authority
- CN
- China
- Prior art keywords
- marine glue
- agent
- film forming
- bathroom space
- dry powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of family bathroom space marine glue preparation method, including main film forming substance, subsidiary film forming matter and auxiliary film forming matter, the main film forming substance is js polymer material, the subsidiary film forming matter is dry powder material, the auxiliary film forming matter is promoter material, the js polymer material is Epoxy-Acrylate Emulsion, and the dry powder material is quartz sand, sericite and talcum powder material, and the promoter material is dispersing agent, defoaming agent, water-reducing agent and plasticizer.The present invention goes out to be used for the lotion of marine glue by the way that multiple material is carried out composite manufacturing, and a variety of dry powder and auxiliary agent is added, effectively marine glue is made to be rapidly achieved waterproof effect, it is able to suppress coating and eliminates the foam generated in production, to make family bathroom space marine glue have the characteristics that several functions, it the features such as effective waterproof durable for increasing family bathroom space marine glue, is re-worked without prying open the floor tile of toilet.
Description
Technical field
The present invention relates to marine glue manufacturing technology field more particularly to a kind of family bathroom space marine glue preparation methods.
Background technique
Toilet is exactly that lavatory, toilet, bathing pool are collectively referred to as.The toilet of house is generally divided into dedicated and public.Specially
Only serve master bedroom；It is common to be connected with public aisle, it is public by other kinsfolks and guest.It can according to layout
It is divided into self, dual-purpose type and three kinds of compromise type.Semi open model, open and closed can be divided into according to form.At present relatively
The popular semi open model for being to discriminate between dry zoning.
However toilet is in use, can't do without the use of water, in high-rise buildings, if the waterproof of toilet is special
Property is not strong, and the depth of water is easy to cause to enter metope bottom, so that resident downstairs is dripped to, however the mending option of seepage in toilet is more multiple
It is miscellaneous, it needs all to pry open floor tile and does water-proofing treatment again, higher cost is constructed complex.
Therefore, invent a kind of family bathroom space solved the above problems with marine glue preparation method it is necessary.
Summary of the invention
The purpose of the present invention is to provide a kind of family bathroom space marine glue preparation methods, are asked with solving above-mentioned technology
Topic.
The present invention using following technical scheme in order to solve the above technical problems, realized: a kind of family bathroom space waterproof
Glue preparation method, including main film forming substance, subsidiary film forming matter and auxiliary film forming matter, the main film forming substance are poly- for js
Object material is closed, the subsidiary film forming matter is dry powder material, and the auxiliary film forming matter is promoter material.
Preferably, the js polymer material is Epoxy-Acrylate Emulsion, and the dry powder material is quartz sand, sericite
With talcum powder material, the promoter material is dispersing agent, defoaming agent, water-reducing agent and plasticizer.
Preferably, the Epoxy-Acrylate Emulsion is by methyl methacrylate, butyl acrylate, acrylic acid-2-ethyl
Own ester, acrylic acid, methacrylic acid antelope ethyl ester, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate material system
At.
Preferably, the quartz sand is powdery setting, and main ingredient is silica, and flint sand diameter is 200 mesh,
The talcum powder diameter is 300 mesh.
Preferably, the proportion between the js polymer material and dry powder material is 2:1 or 1:2.
Based on a kind of above-mentioned family bathroom space marine glue preparation method, comprising the following steps:
S1 prepares Epoxy-Acrylate Emulsion: by methyl methacrylate, butyl acrylate and acrylic acid-2-ethyl caproite
It is mixed, is collected as emulsifier spare, acrylic acid and methacrylic acid antelope ethyl ester are mixed, it is standby as buffer
With, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate is spare as initiator, respectively take a certain amount of emulsification
Agent, buffer carry out mixing pre-emulsification 1h with initiator, and emulsion is prepared, and the emulsion and initiator for respectively taking 30% carry out
It is mixed, and is heated to 78 degree, then heating time 20min slowly uniformly drips remaining emulsion with initiator
It adds in mixed solution, and temperature is heated to 85 degree, keep the temperature 30min, carry out precipitating filtering, be prepared into obtain epoxy acrylic
Ester lotion；
The mixing of S2 level-one: taking a certain amount of Epoxy-Acrylate Emulsion to be added thereto the prepared dry powder material of institute, will
Temperature is heated to 20-30 degree, carries out intermittence and stirs evenly back and forth；
The mixing of S3 second level: auxiliary agent is added by being mixed into the Epoxy-Acrylate Emulsion after dry powder material, the addition of auxiliary agent is suitable
Sequence is that dispersing agent, water-reducing agent, defoaming agent and plasticizer sequentially add, and after auxiliary agent is added completely into, continues to stir 1h；
S4 storage: will be prepared marine glue and be put into inside plastics Object storing drum, Object storing drum is sealed, and be placed on dry cool place
Position in store.
Preferably, the component percentage amounts of sand, sericite and talcum powder are respectively in dry powder material in the step S2
30%, 25%, 45%, total component percentage amounts of dry powder are 100%.
Preferably, the percentage amounts of dispersing agent and plasticising in entire marine glue are respectively in auxiliary agent in the step S3
0.1%-2%, 2%-10%, it is suitable that defoaming agent and water-reducing agent in the auxiliary agent according to moisture content used in marine glue carry out selection
Amount uses.
Preferably, dispersing agent, water-reducing agent, defoaming agent and the plasticising in the step S3 in auxiliary agent is in addition manner, often
A kind of auxiliary agent is added in lotion be stirred 10min after, a kind of auxiliary agent under being added again.
The beneficial effects of the present invention are:
Compared with existing family bathroom space marine glue, multiple material is carried out composite manufacturing and goes out to be used for the present invention by the present invention
The lotion of marine glue, and a variety of dry powder and auxiliary agent is added, effectively make the organic polymeric emulsions dehydration of JS compound water-proof glue
And becoming has cohesiveness and successional layers of elastomeric film, and cement is made to absorb the water in lotion and harden, to make flexible poly-
Compound film layer and hardening of cement body are intertwined and cohere into a firm and flexible waterproof layer securely, and by dry
It is that can increase JS coating intensity, application property and resist saturating that its performance of silica flour, which stablizes acidproof, wear-resisting characteristic and talcum powder, in powder
Aqueous, water-reducing agent can be significant in the features such as coating weatherability, adhesive force, colour retention can be improved in sericite in powder and auxiliary agent
Reduction polymer cement paint stir hourly water consumption, improve film consistency, have strong peptizaiton to cement, can accelerate
The speed of hydrated cementitious, to be rapidly achieved waterproof effect, defoaming agent is able to suppress the bubble that coating is generated in production, construction
Foam can finally eliminate foam, so that family bathroom space marine glue be made to have the characteristics that several functions, effectively increase family
The features such as waterproof durable of use in toilet marine glue, re-works without prying open the floor tile of toilet.
Specific embodiment
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained, and however, the following embodiments are merely preferred embodiments of the present invention, and not all.
Based on the implementation example in the implementation mode, those skilled in the art's obtained other realities without making creative work
Example is applied, protection scope of the present invention is belonged to.Experimental method in following embodiments is unless otherwise specified conventional method,
The materials, reagents and the like used in the following examples is commercially available unless otherwise specified.
Embodiment one:
A kind of family bathroom space marine glue preparation method, including main film forming substance, subsidiary film forming matter and auxiliary at
Membrane substance, the main film forming substance are js polymer material, and the subsidiary film forming matter is dry powder material, the auxiliary film forming
Substance is promoter material.
Preferably, the js polymer material is Epoxy-Acrylate Emulsion, and the dry powder material is quartz sand, sericite
With talcum powder material, the promoter material is dispersing agent, defoaming agent, water-reducing agent and plasticizer.
Preferably, the Epoxy-Acrylate Emulsion is by methyl methacrylate, butyl acrylate, acrylic acid-2-ethyl
Own ester, acrylic acid, methacrylic acid antelope ethyl ester, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate material system
At.
Preferably, the quartz sand is powdery setting, and main ingredient is silica, and flint sand diameter is 200 mesh,
The talcum powder diameter is 300 mesh.
Preferably, the proportion between the js polymer material and dry powder material is 2:1 or 1:2.
Based on a kind of above-mentioned family bathroom space marine glue preparation method, comprising the following steps:
S1 prepares Epoxy-Acrylate Emulsion: by methyl methacrylate, butyl acrylate and acrylic acid-2-ethyl caproite
It is mixed, is collected as emulsifier spare, acrylic acid and methacrylic acid antelope ethyl ester are mixed, it is standby as buffer
With, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate is spare as initiator, respectively take a certain amount of emulsification
Agent, buffer carry out mixing pre-emulsification 1h with initiator, and emulsion is prepared, and the emulsion and initiator for respectively taking 30% carry out
It is mixed, and is heated to 78 degree, then heating time 20min slowly uniformly drips remaining emulsion with initiator
It adds in mixed solution, and temperature is heated to 85 degree, keep the temperature 30min, carry out precipitating filtering, be prepared into obtain epoxy acrylic
Ester lotion；
The mixing of S2 level-one: the Epoxy-Acrylate Emulsion that percentage is 30% is taken to add the dry powder material that percentage is 60%
Enter wherein, temperature is heated to 20-30 degree, carries out intermittence and stir evenly back and forth；
The mixing of S3 second level: auxiliary agent is added by being mixed into the Epoxy-Acrylate Emulsion after dry powder material, the addition of auxiliary agent is suitable
Sequence is that dispersing agent, water-reducing agent, defoaming agent and plasticizer sequentially add, and after auxiliary agent is added completely into, continues to stir 1h；
S4 storage: will be prepared marine glue and be put into inside plastics Object storing drum, Object storing drum is sealed, and be placed on dry cool place
Position in store.
Preferably, the component percentage amounts of sand, sericite and talcum powder are respectively in dry powder material in the step S2
30%, 25%, 45%, total component percentage amounts of dry powder are 100%.
Preferably, the percentage amounts of dispersing agent and plasticising in entire marine glue are respectively in auxiliary agent in the step S3
0.1%-2%, 2%-10%, it is suitable that defoaming agent and water-reducing agent in the auxiliary agent according to moisture content used in marine glue carry out selection
Amount uses.
Preferably, dispersing agent, water-reducing agent, defoaming agent and the plasticising in the step S3 in auxiliary agent is in addition manner, often
A kind of auxiliary agent is added in lotion be stirred 10min after, a kind of auxiliary agent under being added again.
Embodiment two:
A kind of family bathroom space marine glue preparation method, including main film forming substance, subsidiary film forming matter and auxiliary at
Membrane substance, the main film forming substance are js polymer material, and the subsidiary film forming matter is dry powder material, the auxiliary film forming
Substance is promoter material.
Preferably, the js polymer material is Epoxy-Acrylate Emulsion, and the dry powder material is quartz sand, sericite
With talcum powder material, the promoter material is dispersing agent, defoaming agent, water-reducing agent and plasticizer.
Preferably, the Epoxy-Acrylate Emulsion is by methyl methacrylate, butyl acrylate, acrylic acid-2-ethyl
Own ester, acrylic acid, methacrylic acid antelope ethyl ester, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate material system
At.
Preferably, the quartz sand is powdery setting, and main ingredient is silica, and flint sand diameter is 200 mesh,
The talcum powder diameter is 300 mesh.
Preferably, the proportion between the js polymer material and dry powder material is 2:1 or 1:2.
Based on a kind of above-mentioned family bathroom space marine glue preparation method, comprising the following steps:
S1 prepares Epoxy-Acrylate Emulsion: by methyl methacrylate, butyl acrylate and acrylic acid-2-ethyl caproite
It is mixed, is collected as emulsifier spare, acrylic acid and methacrylic acid antelope ethyl ester are mixed, it is standby as buffer
With, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate is spare as initiator, respectively take a certain amount of emulsification
Agent, buffer carry out mixing pre-emulsification 1h with initiator, and emulsion is prepared, and the emulsion and initiator for respectively taking 30% carry out
It is mixed, and is heated to 78 degree, then heating time 20min slowly uniformly drips remaining emulsion with initiator
It adds in mixed solution, and temperature is heated to 85 degree, keep the temperature 30min, carry out precipitating filtering, be prepared into obtain epoxy acrylic
Ester lotion；
The mixing of S2 level-one: the Epoxy-Acrylate Emulsion that percentage is 60% is taken to add the dry powder material that percentage is 30%
Enter wherein, temperature is heated to 20-30 degree, carries out intermittence and stir evenly back and forth；
The mixing of S3 second level: auxiliary agent is added by being mixed into the Epoxy-Acrylate Emulsion after dry powder material, the addition of auxiliary agent is suitable
Sequence is that dispersing agent, water-reducing agent, defoaming agent and plasticizer sequentially add, and after auxiliary agent is added completely into, continues to stir 1h；
S4 storage: will be prepared marine glue and be put into inside plastics Object storing drum, Object storing drum is sealed, and be placed on dry cool place
Position in store.
Preferably, the component percentage amounts of sand, sericite and talcum powder are respectively in dry powder material in the step S2
30%, 25%, 45%, total component percentage amounts of dry powder are 100%.
Preferably, the percentage amounts of dispersing agent and plasticising in entire marine glue are respectively in auxiliary agent in the step S3
0.1%-2%, 2%-10%, it is suitable that defoaming agent and water-reducing agent in the auxiliary agent according to moisture content used in marine glue carry out selection
Amount uses.
Preferably, dispersing agent, water-reducing agent, defoaming agent and the plasticising in the step S3 in auxiliary agent is in addition manner, often
A kind of auxiliary agent is added in lotion be stirred 10min after, a kind of auxiliary agent under being added again.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
For personnel it should be appreciated that the present invention is not limited to the above embodiments, described in the above embodiment and specification is only the present invention
Preference, be not intended to limit the invention, without departing from the spirit and scope of the present invention, the present invention also has various
Changes and improvements, these changes and improvements all fall within the protetion scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (9)
1. a kind of family bathroom space marine glue preparation method, it is characterised in that: including main film forming substance, subsidiary film forming matter
And auxiliary film forming matter, the main film forming substance are js polymer material, the subsidiary film forming matter is dry powder material, described
Auxiliary film forming matter is promoter material.
2. a kind of family bathroom space marine glue preparation method according to claim 1, it is characterised in that: the js polymerization
Object material is Epoxy-Acrylate Emulsion, and the dry powder material is quartz sand, sericite and talcum powder material, the promoter material
For dispersing agent, defoaming agent, water-reducing agent and plasticizer.
3. a kind of family bathroom space marine glue preparation method according to claim 2, it is characterised in that: the epoxy third
Olefin(e) acid ester lotion is by methyl methacrylate, butyl acrylate, acrylic acid-2-ethyl caproite, acrylic acid, methacrylic acid antelope second
Ester, epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate material are made.
4. a kind of family bathroom space marine glue preparation method according to claim 2, it is characterised in that: the quartz sand
For powdery setting, main ingredient is silica, and flint sand diameter is 200 mesh, and the talcum powder diameter is 300 mesh.
5. a kind of family bathroom space marine glue preparation method according to claim 1, it is characterised in that: the js polymerization
Proportion between object material and dry powder material is 2:1 or 1:2.
6. a kind of family bathroom space marine glue preparation method described in -5 according to claim 1, it is characterised in that: including following
Step:
S1 prepares Epoxy-Acrylate Emulsion: methyl methacrylate, butyl acrylate and acrylic acid-2-ethyl caproite are carried out
Mixing, is collected spare as emulsifier, and acrylic acid and methacrylic acid antelope ethyl ester are mixed, spare as buffer, will
Epoxy resin, potassium peroxydisulfate, sodium acetate and lauryl sodium sulfate are spare as initiator, respectively take a certain amount of emulsifier, delay
Electuary carries out mixing pre-emulsification 1h with initiator, and emulsion is prepared, and 30% emulsion is respectively taken to be mixed with initiator
Stirring, and 78 degree are heated to, then remaining emulsion is slowly uniformly added dropwise to by heating time 20min with initiator
In mixed solution, and temperature is heated to 85 degree, keeps the temperature 30min, carry out precipitating filtering, is prepared into obtain epoxy acrylate cream
Liquid；
The mixing of S2 level-one: a certain amount of Epoxy-Acrylate Emulsion is taken to be added thereto the prepared dry powder material of institute, by temperature
It is heated to 20-30 degree, intermittence is carried out and stirs evenly back and forth；
The mixing of S3 second level: auxiliary agent is added by being mixed into the Epoxy-Acrylate Emulsion after dry powder material, the addition sequence of auxiliary agent is
Dispersing agent, water-reducing agent, defoaming agent and plasticizer sequentially add, and after auxiliary agent is added completely into, continue to stir 1h；
S4 storage: will be prepared marine glue and be put into inside plastics Object storing drum, Object storing drum is sealed, and be placed on the position in dry cool place
Set middle storage.
7. a kind of family bathroom space marine glue preparation method according to claim 6, it is characterised in that: the step S2
The component percentage amounts of sand, sericite and talcum powder are respectively 30%, 25%, 45% in middle dry powder material, total component of dry powder
Percentage amounts are 100%.
8. a kind of family bathroom space marine glue preparation method according to claim 6, it is characterised in that: the step S3
Percentage amounts in entire marine glue of dispersing agent and plasticising are respectively 0.1%-2%, 2%-10% in middle auxiliary agent, in the auxiliary agent
Defoaming agent and water-reducing agent selected to use in right amount according to moisture content used in marine glue.
9. a kind of family bathroom space marine glue preparation method according to claim 6, it is characterised in that: the step S3
Dispersing agent, water-reducing agent, defoaming agent and plasticising in middle auxiliary agent are that each auxiliary agent is added in lotion and is stirred in addition manner
After mixing 10min, a kind of auxiliary agent under being added again.