CN107902963A - A kind of preparation method of self-closing polymer cement waterproof paint - Google Patents

A kind of preparation method of self-closing polymer cement waterproof paint Download PDF

Info

Publication number
CN107902963A
CN107902963A CN201711010006.7A CN201711010006A CN107902963A CN 107902963 A CN107902963 A CN 107902963A CN 201711010006 A CN201711010006 A CN 201711010006A CN 107902963 A CN107902963 A CN 107902963A
Authority
CN
China
Prior art keywords
powder
liquid material
parts
preparation
self
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711010006.7A
Other languages
Chinese (zh)
Inventor
王志国
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chengdu Sen Yu Hong Green Engineering Co Ltd
Original Assignee
Chengdu Sen Yu Hong Green Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Sen Yu Hong Green Engineering Co Ltd filed Critical Chengdu Sen Yu Hong Green Engineering Co Ltd
Priority to CN201711010006.7A priority Critical patent/CN107902963A/en
Publication of CN107902963A publication Critical patent/CN107902963A/en
Withdrawn legal-status Critical Current

Abstract

The invention discloses a kind of preparation method of self-closing polymer cement waterproof paint, is made of two kinds of components of powder and liquid material, and the powder and liquid material weight ratio are 1:1, the liquid material is made of acrylic emulsion, wetting agent, plasticizer, defoamer and water;The powder is made of cement, silica flour, talcum powder, active masterbatch FLW, retarder;Specifically include following steps:The preparation of powder component;The preparation of liquid material component;Liquid material and powder are 1 by weight:1 proportioning is packed respectively, and when use, liquid material and powder were mixed evenly again, to obtain the final product.The beneficial effects of the invention are as follows:The present invention has preferable dereism, and can reach higher fracture elongation at the same time.

Description

A kind of preparation method of self-closing polymer cement waterproof paint
Technical field
The present invention relates to building water-proof paint technical field, is that a kind of self-closing polymer cement waterproof applies specifically The preparation method of material.
Background technology
Polymer cement waterproof paint (also known as JS composite water-proof paints) is that a aqueous environment protection of rising in recent years is double Component water-proof material, is generally made of liquid material component and powder component.This kind of coating has the extensibility of polymer coating film concurrently and prevents It is water-based, and hydraulic material intensity is high, the advantages of easily being bonded with wet base, and adjusting can be required according to different engineering positions Pliability and intensity, thus construction method is very flexible.Further, since it is using water as dispersant, overcome tar, pitch, Solvent-type waterproofing paint disadvantage easy to pollute, is conducive to environmental protection.Therefore, this kind of product since the advent of the world has just obtained rapidly Development and extensive use, become the up-and-coming youngster in waterproof coating.
According to newly GB/T23445-2009 national standards are ordered, polymer cement waterproof paint can be divided into I types, II types, III Three kinds of type, wherein, type III polymer cement waterproof paint is a kind of self-closing polymer cement waterproof paint, causes the country Outer insider's concern, its representative products are the PARATEX of Japanese high point Chemical Co., Ltd. invention.
However, above-mentioned commodity need further to improve in terms of tensile strength and adhesion strength, and the country is this kind of Water-repellent paint is fewer and fewer, it would be highly desirable in research and development.
The content of the invention
It is an object of the invention to provide a kind of preparation method of self-closing polymer cement waterproof paint, self-closing's polymerization Thing cement waterproof paint has preferable dereism(Self-healing), and higher fracture elongation can be reached at the same time, become one Flexible waterproof coating of the kind with function of self closing.
The present invention is achieved through the following technical solutions:A kind of self-closing polymer cement waterproof paint, by powder and liquid material Two kinds of component compositions, the powder and liquid material weight ratio are 1:1, the liquid material by acrylic emulsion, wetting agent, plasticizer, Defoamer and water composition, polymer emulsion in the liquid material, wetting agent, plasticizer, defoamer and water content in parts by weight Calculate as follows:
70~90 parts of acrylic emulsion, the acrylic emulsion are modified acrylate emulsion;
0.1~0.5 part of wetting agent,
1~5 part of plasticizer,
0.25 part of softening agent,
10~20 parts of water;
The powder is made of cement, silica flour, talcum powder, active masterbatch FLW, retarder, cement, silica flour in powder, Talcum powder, active masterbatch FLW, retarder, powder defoamer, the content of water-retaining agent are as follows in parts by weight:
25~45 parts of cement,
25~45 parts of silica flour,
Active masterbatch FLW10 ~ 15 part,
20~40 parts of talcum powder,
0.3~0.6 part of retarder,
0.2~0.5 part of powder defoamer,
0.5~0.8 part of water-retaining agent;The water-retaining agent for alkyl biphenyl base ether sulfonate, fatty alcohol polyoxyethylene ether sulfate or Alkyl phenol ether sulfosuccinate ester salt.
In order to further preferably realize the present invention, the wetting agent is polyoxyethylene fatty acid esters, polyethylene glycol oxide One or more in alkyl phenyl ether, polyethylene glycol oxide succinate.
In order to further preferably realize the present invention, the plasticizer is dibutyl phthalate, phthalic acid two One or more kinds of mixtures in monooctyl ester, trimethylpentanediol diisobutyrate.
In order to further preferably realize the present invention, the softening agent is alkyl phenol epoxidised hydrocarbons.
In order to further preferably realize the present invention, the water-retaining agent is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxy Ethene ether sulfate or alkyl phenol ether sulfosuccinate ester salt.
In order to further preferably realize the present invention, the retarder is tartaric acid or citric acid or its esters.
A kind of preparation method of self-closing polymer cement waterproof paint, specifically includes following steps:
Step S1:The preparation of liquid material component;Specifically refer to:
Water, wetting agent, plasticizer, softening agent, defoamer are sequentially added into stirring according to 1000 turns/min in scattered stirring container Speed is mixed, is evenly stirred until no particle, then acrylic emulsion, disperses stirring 15 minutes according to 500 turns/min, until stirring is equal It is even, liquid material is both obtained, discharging packaging is spare;
Step S2:The preparation of powder component;Specifically refer to:
Cement, silica flour, active masterbatch FLW, talcum powder are sequentially added in mixer and stirred, according to 200 turns/min ~ 400 turn/ The mixing speed of min, until stirring evenly;
Step S3:Liquid material and powder are 1 by weight:1 proportioning is packed respectively, liquid material and powder is mixed again during use Uniformly, to obtain the final product.
It is described then to add lye after liquid material stirs evenly in step sl in order to further preferably realize the present invention, The pH value of system is adjusted to 7~9, is stirred evenly.
In order to further preferably realize the present invention, the lye is sodium hydroxide or potassium hydroxide solution.
In order to further preferably realize the present invention, the silica flour is 40~70 mesh quartz sands, 50~100 mesh quartz sands Or 100~200 mesh quartz sand grading.
Compared with prior art, the present invention haing the following advantages and beneficial effect:With preferable dereism(Self-healing Property), and higher fracture elongation can be reached at the same time, become a kind of flexible waterproof coating with function of self closing.
Embodiment
The present invention is described in further detail with reference to embodiment, but the implementation of the present invention is not limited to this.
Embodiment 1:
The present invention is achieved through the following technical solutions, a kind of self-closing polymer cement waterproof paint, by two kinds of powder and liquid material Component forms, and the powder and liquid material weight ratio are 1:1;
The liquid material is made of acrylic emulsion, wetting agent, plasticizer, defoamer and water, polymer emulsion in the liquid material, Wetting agent, plasticizer, the content of defoamer and water are as follows in parts by weight:
70~90 parts of acrylic emulsion, the acrylic emulsion are modified acrylate emulsion;
0.1~0.5 part of wetting agent,
1~5 part of plasticizer,
0.25 part of softening agent,
10~20 parts of water;
The powder is made of cement, silica flour, talcum powder, active masterbatch FLW, retarder, cement, silica flour in powder, Talcum powder, active masterbatch FLW, retarder, powder defoamer, the content of water-retaining agent are as follows in parts by weight:
25~45 parts of cement,
25~45 parts of silica flour,
Active masterbatch FLW10 ~ 15 part,
20~40 parts of talcum powder,
0.3~0.6 part of retarder,
0.2~0.5 part of powder defoamer,
0.5~0.8 part of water-retaining agent;The water-retaining agent for alkyl biphenyl base ether sulfonate, fatty alcohol polyoxyethylene ether sulfate or Alkyl phenol ether sulfosuccinate ester salt.
In order to further preferably realize the present invention, the wetting agent is polyoxyethylene fatty acid esters, polyethylene glycol oxide One or more in alkyl phenyl ether, polyethylene glycol oxide succinate.
In order to further preferably realize the present invention, the plasticizer is dibutyl phthalate, phthalic acid two One or more kinds of mixtures in monooctyl ester, trimethylpentanediol diisobutyrate.
In order to further preferably realize the present invention, the softening agent is alkyl phenol epoxidised hydrocarbons.
In order to further preferably realize the present invention, the water-retaining agent is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxy Ethene ether sulfate or alkyl phenol ether sulfosuccinate ester salt.
Suitable defoamer can be penetrated into foam system, suppressed foam and produced and destroy foam, prevent coating surface shape Into pinprick.
The other parts of the present embodiment are same as the previously described embodiments, and so it will not be repeated.
Embodiment 2:
The present embodiment does further optimization on the basis of above-described embodiment, a kind of self-closing polymer cement waterproof paint, by Two kinds of component compositions of powder and liquid material, the powder and liquid material weight ratio are 1:1,
The liquid material is made of acrylic emulsion, wetting agent, plasticizer, defoamer and water, polymer emulsion in the liquid material, Wetting agent, plasticizer, the content of defoamer and water are as follows in parts by weight:
80 parts of acrylic emulsion,
The acrylic emulsion is modified acrylate emulsion;
.5 parts of wetting agent,
3 parts of plasticizer,
0.25 part of softening agent,
15 parts of water;
The powder is made of cement, silica flour, talcum powder, active masterbatch FLW, retarder, cement, silica flour in powder, Talcum powder, active masterbatch FLW, retarder, powder defoamer, the content of water-retaining agent are as follows in parts by weight:
25 parts of cement,
30 parts of silica flour,
Active masterbatch FLW10 parts;
30 parts of talcum powder,
0.4 part of retarder,
0.3 part of powder defoamer,
0.5 part of water-retaining agent;The water-retaining agent is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxyethylene ether sulfate or alkyl phenol Ether sulfosuccinates salt.
In order to further preferably realize the present invention, the wetting agent is polyoxyethylene fatty acid esters, polyethylene glycol oxide One or more in alkyl phenyl ether, polyethylene glycol oxide succinate.
In order to further preferably realize the present invention, the plasticizer is dibutyl phthalate, phthalic acid two One or more kinds of mixtures in monooctyl ester, trimethylpentanediol diisobutyrate.
In order to further preferably realize the present invention, the softening agent is alkyl phenol epoxidised hydrocarbons.
In order to further preferably realize the present invention, the water-retaining agent is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxy Ethene ether sulfate or alkyl phenol ether sulfosuccinate ester salt.
Suitable defoamer can be penetrated into foam system, suppressed foam and produced and destroy foam, prevent coating surface shape Into pinprick.
The other parts of the present embodiment are same as the previously described embodiments, and so it will not be repeated.
Embodiment 3:
The present embodiment does further optimization on the basis of above-described embodiment, a kind of self-closing polymer cement waterproof paint, by Two kinds of component compositions of powder and liquid material, the powder and liquid material weight ratio are 1:1,
The liquid material is made of acrylic emulsion, wetting agent, plasticizer, defoamer and water, polymer emulsion in the liquid material, Wetting agent, plasticizer, the content of defoamer and water are as follows in parts by weight:
75 parts of acrylic emulsion,
The acrylic emulsion is modified acrylate emulsion;
0.3 part of wetting agent,
2 parts of plasticizer,
0.25 part of softening agent,
20 parts of water;
The powder is made of cement, silica flour, talcum powder, active masterbatch FLW, retarder, cement, silica flour in powder, Talcum powder, active masterbatch FLW, retarder, powder defoamer, the content of water-retaining agent are as follows in parts by weight:
2540 parts of cement,
30 parts of silica flour,
Active masterbatch FLW12 parts,
30 parts of talcum powder,
0.4 part of retarder,
0.5 part of powder defoamer,
0.5 part of water-retaining agent;The water-retaining agent is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxyethylene ether sulfate or alkyl phenol Ether sulfosuccinates salt.
In order to further preferably realize the present invention, the wetting agent is polyoxyethylene fatty acid esters, polyethylene glycol oxide One or more in alkyl phenyl ether, polyethylene glycol oxide succinate.
In order to further preferably realize the present invention, the plasticizer is dibutyl phthalate, phthalic acid two One or more kinds of mixtures in monooctyl ester, trimethylpentanediol diisobutyrate.
In order to further preferably realize the present invention, the softening agent is alkyl phenol epoxidised hydrocarbons.
In order to further preferably realize the present invention, the water-retaining agent is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxy Ethene ether sulfate or alkyl phenol ether sulfosuccinate ester salt.
Suitable defoamer can be penetrated into foam system, suppressed foam and produced and destroy foam, prevent coating surface shape Into pinprick.
The other parts of the present embodiment are same as the previously described embodiments, and so it will not be repeated.
Embodiment 4:
A kind of preparation method of self-closing polymer cement waterproof paint, specifically includes following steps:
Step S1:The preparation of liquid material component;The liquid material constituent content is as follows in parts by weight:
70~90 parts of acrylic emulsion,
0.1~0.5 part of wetting agent,
1~5 part of plasticizer,
0.25 part of softening agent,
10~20 parts of water;
Specifically refer to:
Water, wetting agent, plasticizer, softening agent, defoamer are sequentially added into stirring according to 1000 turns/min in scattered stirring container Speed is mixed, is evenly stirred until no particle, then acrylic emulsion, disperses stirring 15 minutes according to 500 turns/min, until stirring is equal It is even, liquid material is both obtained, discharging packaging is spare;
Step S2:The preparation of powder component;The powder content is as follows in parts by weight:
25~45 parts of cement,
25~45 parts of silica flour,
Active masterbatch FLW10 ~ 15 part,
20~40 parts of talcum powder,
0.3~0.6 part of retarder,
0.2~0.5 part of powder defoamer,
0.5~0.8 part of water-retaining agent;Specifically refer to:
Cement, silica flour, active masterbatch FLW, talcum powder are sequentially added in mixer and stirred, according to 200 turns/min ~ 400 turn/ The mixing speed of min, until stirring evenly;
Step S3:Liquid material and powder are 1 by weight:1 proportioning is packed respectively, liquid material and powder is mixed again during use Uniformly, to obtain the final product.
It is described then to add lye after liquid material stirs evenly in step sl, the pH value of system is adjusted to 7~9, stirring Uniformly.
The lye is sodium hydroxide or potassium hydroxide solution.
Silica flour in the step S1 is 40~70 mesh quartz sands, 50~100 mesh quartz sands or 100~200 mesh are quartzy The grading of sand.
Water-retaining agent in the step S2 is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxyethylene ether sulfate or alkyl Phenolic ether sulfosuccinate ester salt.
A kind of above-mentioned self-closing polymer cement waterproof paint when in use, by weight calculate, by liquid material component with Powder component presses 1:1 proportioning is mixed evenly, knife-coat application.Through according to GB/T23445-2009, " polymer cement waterproof applies Material " standard detection, tensile strength 2.25MPa, elongation at break 103%, when dereism is 5 small.
The other parts of the present embodiment are same as the previously described embodiments, and so it will not be repeated.
The above, is only presently preferred embodiments of the present invention, not does limitation in any form to the present invention, it is every according to Any simply modification, the equivalent variations made according to the technical spirit of the present invention to above example, each fall within the protection of the present invention Within the scope of.

Claims (5)

1. a kind of preparation method of self-closing polymer cement waterproof paint, it is characterised in that specifically include following steps:
Step S1:The preparation of liquid material component;The liquid material constituent content is as follows in parts by weight:
70~90 parts of acrylic emulsion,
0.1~0.5 part of wetting agent,
1~5 part of plasticizer,
0.25 part of softening agent,
10~20 parts of water;Specifically refer to:
Water, wetting agent, plasticizer, softening agent, defoamer are sequentially added into stirring according to 1000 turns/min in scattered stirring container Speed is mixed, is evenly stirred until no particle, then acrylic emulsion, disperses stirring 15 minutes according to 500 turns/min, until stirring is equal It is even, liquid material is both obtained, discharging packaging is spare;
Step S2:The preparation of powder component;The powder content is as follows in parts by weight:
25~45 parts of cement,
25~45 parts of silica flour,
Active masterbatch FLW10 ~ 15 part,
20~40 parts of talcum powder,
0.3~0.6 part of retarder,
0.2~0.5 part of powder defoamer,
0.5~0.8 part of water-retaining agent;Specifically refer to:
Cement, silica flour, active masterbatch FLW, talcum powder are sequentially added in mixer and stirred, according to 200 turns/min ~ 400 turn/ The mixing speed of min, until stirring evenly;
Step S3:Liquid material and powder are 1 by weight:1 proportioning is packed respectively, liquid material and powder is mixed again during use Uniformly, to obtain the final product.
A kind of 2. preparation method of self-closing polymer cement waterproof paint according to claim 1, it is characterised in that:Institute State after liquid material stirs evenly in step sl, then add lye, the pH value of system is adjusted to 7~9, is stirred evenly.
A kind of 3. preparation method of self-closing polymer cement waterproof paint according to claim 2, it is characterised in that:Institute It is sodium hydroxide or potassium hydroxide solution to state lye.
A kind of 4. preparation method of self-closing polymer cement waterproof paint according to claim 1, it is characterised in that:Institute State the grading that the silica flour in step S1 is 40~70 mesh quartz sands, 50~100 mesh quartz sands or 100~200 mesh quartz sands.
A kind of 5. preparation method of self-closing polymer cement waterproof paint according to claim 1, it is characterised in that:Institute It is alkyl biphenyl base ether sulfonate, fatty alcohol polyoxyethylene ether sulfate or alkyl phenol ether sulfo group amber to state the water-retaining agent in step S2 Amber acid esters salt.
CN201711010006.7A 2017-10-25 2017-10-25 A kind of preparation method of self-closing polymer cement waterproof paint Withdrawn CN107902963A (en)