CN109852288A - 封口垫片用无蜡弱粘胶及封口垫片 - Google Patents
封口垫片用无蜡弱粘胶及封口垫片 Download PDFInfo
- Publication number
- CN109852288A CN109852288A CN201811486445.XA CN201811486445A CN109852288A CN 109852288 A CN109852288 A CN 109852288A CN 201811486445 A CN201811486445 A CN 201811486445A CN 109852288 A CN109852288 A CN 109852288A
- Authority
- CN
- China
- Prior art keywords
- wax
- back sheet
- seal gasket
- layer
- seal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种封口垫片用无蜡弱粘胶,其组成和重量百分比为:聚乙烯52.8~54.5%、線性低密度聚乙烯12.2~14.6%、乙烯—甲基丙烯酸甲酯共聚物10.6~11.2%、C5石油树脂7.8~8.5%、聚乙烯醇7.5~8.2%、角鲨烷5.7~6.3%。由于本发明使用聚乙烯与線性低密度聚乙烯用于改善操作性,使用乙烯—甲基丙烯酸甲酯共聚物,用于改善质感与气味,使用聚乙烯醇用于调节被粘性、粘结强度。又,由于本发明采用涂一层高分子塑料代替蜡,这一层高分子塑料牢牢粘复在背衬层上,不畏瓶内液体浸泡,起到二次压封的作用,还避免了背衬层吸蜡不干净的问题。
Description
技术领域
本发明涉及化工胶粘剂技术领域,特别是涉及一种封口垫片用无蜡弱粘胶及封口垫片。
背景技术
热熔胶粘剂(Hot Melt Adhesive)简称热熔胶,通常是指在室温下呈固态,加热熔融成液态,涂布,润湿被粘物后,经压合、冷却,在几秒钟内完成粘接的胶粘剂。热熔胶是一类在室温下呈固态,加热熔融后呈液态,涂布于被粘物后,经压合、冷却,在短时间内即可完成粘接的胶粘剂。如图1所示,一种玻璃容器封口垫片,由粘封层、铝塑膜层和背衬层组成,所述铝塑膜层底面和背衬层顶面叠置复合,在铝箔层顶面上设置粘封层。通常的两片式电磁感应封口垫片,采用在铝塑膜上涂一层蜡,再与铝塑膜压合在一起;背衬层与铝塑膜层之间是由一层蜡粘合在一起,封口受热时蜡熔化被背衬层吸收,背衬层与铝塑膜分离。但是当瓶子的口径很大时,垫片中部的蜡往往熔化很慢,难以被纸板吸收,封口后背衬层与铝箔仍有一部分粘连在一起;加之,残留在垫片中部无法有效吸收的蜡,粘附在盖中的背衬层,当盖子拧锁回瓶子,将对瓶中内含物造成递延性污染;加之,纸板背衬层无法阻挡液体浸泡,背衬层受浸泡靡烂,也将对瓶中内含物造成递延性污染。
发明内容
本发明的一个目的在于提供一种封口垫片用无蜡弱粘胶。
本发明的另一个目的在提供一种耐油、耐溶剂且耐水型的封口垫片。
为实现上述目的,本发明的技术解决方案是:
本发明是一种封口垫片用无蜡弱粘胶,其组成和重量百分比为:
聚乙烯 52.8~54.5%
線性低密度聚乙烯 12.2~14.6%
乙烯—甲基丙烯酸甲酯共聚物 10.6~11.2%
C5石油树脂 7.8~8.5%
聚乙烯醇 7.5~8.2%
角鲨烷 5.7~6.3%
本发明是一种封口垫片,由粘封层、铝塑膜层和背衬层组成,所述粘封层、铝塑膜层和背衬层依序叠置复合;所述的粘封层是由上述的无蜡弱粘胶在熔融状态时涂布在铝塑膜层与背衬层间形成的。
采用上述方案后,本发明具有以下优点:
1、由于本发明使用聚乙烯与線性低密度聚乙烯,用于改善操作性。
2、由于本发明使用乙烯—甲基丙烯酸甲酯共聚物,用于改善质感与气味。
3、由于本发明使用C5石油树脂,用于调节与极性或非极性聚合物相容综合性能。
4、由于本发明使用聚乙烯醇,用于调节被粘性、粘结强度。
5、由于本发明使用的角鲨烷,用于提高被粘性、粘结强度、调节热熔胶粉的耐热温度和晾置时间、改善操作性及降低成本。
6、由于本发明采用涂一层高分子塑料代替蜡,这一层高分子塑料牢牢粘复在背衬层上,不畏瓶内液体浸泡,起到二次压封的作用,还避免了背衬层吸蜡不干净的问题。
下面结合附图和具体实施例对本发明作进一步的说明。
附图说明
图1是本发明封口垫片的结构示意图。
具体实施方式
实施例1:
本发明是一种高分子热熔胶,其组成和重量百分比为:
聚乙烯 52.8%
線性低密度聚乙烯 13.6%
乙烯—甲基丙烯酸甲酯共聚物 12.6%
C5石油树脂 7.8%
聚乙烯醇 7.5%
角鲨烷 5.7%
实施例2:
本发明是一种高分子热熔胶,其组成和重量百分比为:
聚乙烯 54.5%
線性低密度聚乙烯 11.3%
乙烯—甲基丙烯酸甲酯共聚物 11.2%
C5石油树脂 8.5%
聚乙烯醇 8.2%
角鲨烷 6.3%
实施例3:
本发明是一种高分子热熔胶,其组成和重量百分比为:
聚乙烯 53.8%
線性低密度聚乙烯 12.2%
乙烯—甲基丙烯酸甲酯共聚物 12%
C5石油树脂 8%
聚乙烯醇 8%
角鲨烷 6%
如图1所示,本发明是一种封口垫片,由粘封层1、铝塑膜层2和背衬层3组成。
所述粘封层1、铝塑膜层2和背衬层3依序叠置复合形成垫片;所述的粘封层1是由上述的无蜡弱粘胶在熔融状态时涂布在铝塑膜层2与背衬层3间形成的。
这一层无蜡弱粘胶(高分子塑料膜)牢牢粘复在背衬层3上,趁热与铝塑膜层2压合在一起;封口后铝塑膜层2粘合在瓶口,旋开盖子时盖子的螺芽卡住纸板或发泡板使背衬层3留在盖子内,而涂在背衬层3上的这层无蜡弱粘胶(高分子塑料膜),不畏瓶内液体浸泡,起到二次压封的作用,还避免了背衬层3吸蜡不干净的问题。
对测试结果﹕
以上所述,仅为本发明较佳实施例而已,故不能以此限定本发明实施的范围,即依本发明申请专利范围及说明书内容所作的等效变化与修饰,皆应仍属本发明专利涵盖的范围内。
Claims (2)
1.一种封口垫片用无蜡弱粘胶,其特征在于:其组成和重量百分比为:
聚乙烯 52.8~54.5%
線性低密度聚乙烯 12.2~14.6%
乙烯—甲基丙烯酸甲酯共聚物 10.6~11.2%
C5石油树脂 7.8~8.5%
聚乙烯醇 7.5~8.2%
角鲨烷 5.7~6.3%。
2.一种封口垫片,由粘封层、铝塑膜层和背衬层组成,所述粘封层、铝塑膜层和背衬层依序叠置复合;其特征在于:所述的粘封层是由如权利要求1所述的无蜡弱粘胶在熔融状态时涂布在铝塑膜层与背衬层间形成的。