CN109837468A - 一种耐腐蚀合金 - Google Patents

一种耐腐蚀合金 Download PDF

Info

Publication number
CN109837468A
CN109837468A CN201711203539.7A CN201711203539A CN109837468A CN 109837468 A CN109837468 A CN 109837468A CN 201711203539 A CN201711203539 A CN 201711203539A CN 109837468 A CN109837468 A CN 109837468A
Authority
CN
China
Prior art keywords
alloy
chromium
corrosion
nickel
corrosion resisting
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711203539.7A
Other languages
English (en)
Inventor
李双哲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Golden Long Pipeline Engineering Co Ltd
Original Assignee
Tianjin Golden Long Pipeline Engineering Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tianjin Golden Long Pipeline Engineering Co Ltd filed Critical Tianjin Golden Long Pipeline Engineering Co Ltd
Priority to CN201711203539.7A priority Critical patent/CN109837468A/zh
Publication of CN109837468A publication Critical patent/CN109837468A/zh
Pending legal-status Critical Current

Abstract

一种耐腐蚀合金,所述合金由质量为以下百分比的各组分组成:铬:11%~15%,镍:3%~5%,锰:7%~13%,硅:12%~15%,钴:1%~4%,余量为铁。本发明的有益之处在于:本发明制成的产品耐蚀性优异,在长期使用过程中不易生锈。本发明合金的铬含量,大大低于传统304不锈钢18%‑20%铬含量,本合金在铬含量远远低于常规水平的基础上,其防锈性能达到了较高的水准。

Description

一种耐腐蚀合金
技术领域
本发明涉及一种合金材料,特别是涉及一种耐腐蚀合金。
背景技术
金属抗腐蚀材料,相对非金属耐腐蚀材料而言,金属抗腐蚀材料主要有铁基合金(耐腐蚀不锈钢);镍基合金(Ni-Cr合金,Ni-Cr-Mo合金,Ni-Cu合金等);活性金属。
耐腐蚀不锈钢主要是指普通的耐大气或海水等腐蚀的300系列不锈钢304,316L,317L等;较强抗腐蚀能力的奥氏体不锈钢904L,254SMO;双相钢2205,2507等;含Cu的耐腐蚀合金20合金等;
镍基耐蚀合金主要是哈氏合金以及Ni-Cu合金等,由于金属Ni本身是面心立方结构,晶体学上的稳定性使得它能够比Fe能够容纳更多的合金元素,如Cr,Mo等,从而达到抵抗各种环境的能力;同时镍本身就具有一定的抗腐蚀能力,尤其是抗氯离子引起的应力腐蚀能力。在强还原性腐蚀环境,复杂的混合酸环境,含有卤素离子的溶液中,以哈氏合金为代表的镍基耐蚀合金相对铁基的不锈钢具有绝对的优势。
活性金属也具有很好的抗腐蚀能力,典型代表是Ti;Zr;Ta等;其中最典型的代表是Ti;钛材有着广泛的应用,主要用在一些不锈钢无法适应的腐蚀环境。钛材耐腐蚀原理:在氧化性气氛中,形成致密的氧化膜来提供保护;所以一般不能用于还原性较强或者密封性那个较高的腐蚀环境中(缺氧环境),与此同时,钛材的应用温度一般小于300摄氏度。特别要注意的是,活性金属都不能用于含氟的环境。(如氢氟酸环境可以选用哈氏C2000,NiCu合金等)。
耐腐蚀合金适合酸、碱、盐等环境使用,或者长期潮湿环境使用。但是现有耐腐蚀合金中一般铬、镍含量较高,尤其是铬价格较高,使得合金生产成本居高不下。现阶段研究一种低成本高性能的耐腐蚀合金十分重要。
发明内容
为了克服现有合金材料的不足之处,本发明提供了一种耐腐蚀合金。
本发明的技术方案是这样实现的。
本方案的一种耐腐蚀合金,所述合金由质量为以下百分比的各组分组成:铬:11%~15%,镍:3%~5%,锰:7%~13%,硅:12%~15%,钴:1%~4%,余量为铁。
所述合金由质量为以下百分比的各组分组成:铬:13%,镍:3%,锰:9%,硅:13%,钴:3%,余量为铁。
所述合金由质量为以下百分比的各组分组成:铬:12%,镍:4%,锰:8%,硅:14%,钴:1%,余量为铁。
所述合金由质量为以下百分比的各组分组成:铬:14%,镍:5%,锰:12%,硅:15%,钴:4%,余量为铁。
本发明的有益之处在于:本发明制成的产品耐蚀性优异,在长期使用过程中不易生锈。本发明合金的铬含量,大大低于传统304不锈钢18%-20%铬含量,本合金在铬含量远远低于常规水平的基础上,其防锈性能达到了较高的水准。
具体实施方式
实施例1
一种耐腐蚀合金,将铬:13kg,镍:3kg,锰:9kg,硅:13kg,钴:3kg,59kg铁混合制成100kg所述材料,本发明制成的产品耐蚀性优异,在长期使用过程中不易生锈。本发明合金的铬含量,大大低于传统304不锈钢18%-20%铬含量,本合金在铬含量远远低于常规水平的基础上,其防锈性能达到了较高的水准。
实施例2
一种耐腐蚀合金,将铬:12kg,镍:4kg,锰:8kg,硅:14kg,钴:1kg,61kg铁混合制成100kg所述材料,本发明制成的产品耐蚀性优异,在长期使用过程中不易生锈。本发明合金的铬含量,大大低于传统304不锈钢18%-20%铬含量,本合金在铬含量远远低于常规水平的基础上,其防锈性能达到了较高的水准。
实施例3
一种耐腐蚀合金,将铬:14kg,镍:5kg,锰:12kg,硅:15kg,钴:4kg,50kg铁混合制成100kg所述材料,本发明制成的产品耐蚀性优异,在长期使用过程中不易生锈。本发明合金的铬含量,大大低于传统304不锈钢18%-20%铬含量,本合金在铬含量远远低于常规水平的基础上,其防锈性能达到了较高的水准。
以上对本发明的一个实施例进行了详细说明,但所述内容仅为本发明的较佳实施例,不能被认为用于限定本发明的实施范围。凡依本发明申请范围所作的均等变化与改进等,均应仍归属于本发明的专利涵盖范围之内。

Claims (4)

1.一种耐腐蚀合金,其特征在于:所述合金由质量为以下百分比的各组分组成:铬:11%~15%,镍:3%~5%,锰:7%~13%,硅:12%~15%,钴:1%~4%,余量为铁。
2.根据权利要求1所述的一种耐腐蚀合金,其特征在于:所述合金由质量为以下百分比的各组分组成:铬:13%,镍:3%,锰:9%,硅:13%,钴:3%,余量为铁。
3.根据权利要求1所述的一种耐腐蚀合金,其特征在于:所述合金由质量为以下百分比的各组分组成:铬:12%,镍:4%,锰:8%,硅:14%,钴:1%,余量为铁。
4.根据权利要求1所述的一种耐腐蚀合金,其特征在于:所述合金由质量为以下百分比的各组分组成:铬:14%,镍:5%,锰:12%,硅:15%,钴:4%,余量为铁。
CN201711203539.7A 2017-11-27 2017-11-27 一种耐腐蚀合金 Pending CN109837468A (zh)