CN109836983A - A kind of production method of environmental-protection decoration stone material - Google Patents
A kind of production method of environmental-protection decoration stone material Download PDFInfo
- Publication number
- CN109836983A CN109836983A CN201711186900.XA CN201711186900A CN109836983A CN 109836983 A CN109836983 A CN 109836983A CN 201711186900 A CN201711186900 A CN 201711186900A CN 109836983 A CN109836983 A CN 109836983A
- Authority
- CN
- China
- Prior art keywords
- paint
- color
- synthetic resin
- stone material
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production methods of environmental-protection decoration stone material, mainly include the following steps: step 1: raw material being cut into sheet shape, reach paint best adhesion；Step 2: paint filler technique；Step 3: synthetic resin paint primer technique；Step 4: printing layer pastes article layer or synthetic resin paint colored paint layer process；Step 5: synthetic resin varnish layer applies synthetic resin varnish on synthetic resin paint colored paint layer.Product of the present invention novel appearance is beautiful, and material is solid, impact resistant, wear-resistant；Product processes are simple, easy to operate, at low cost；Simultaneously without using any plasticizer in the formula of artificial synthesis stone, novel composite material is combined by its physical characteristic using several hydrocarbon high-molecular compounds completely, and also exist without any halogen in raw material, fully demonstrates no chlorination theory, it is environment friendly and pollution-free.
Description
Technical field
The present invention relates to Building Decoration Material technical fields, and in particular to a kind of production method of environmental-protection decoration stone material.
Background technique
Currently, all kinds of decorative floors emerge one after another in terms of building trade.With the raising that people require, all kinds of decorations
Just towards more durable, more fashion, healthier direction is developed on floor.Decorative stone (decorative stone) is that have decoration
The building stone of performance, is processed for architectural decoration, it can also be used to furniture decoration plane material.With the development of economy, it builds
It is more and more, to decorative stone with increasingly extensive, exacerbate the exploitation to lithotome.Meanwhile although lithotome
Decorative pattern and lines are unique and quality is very rigid, wear-resisting, but still have tiny crackle and pore, easily quilt after being polished polishing
Pollute photochemical colour fading.
Therefore, for defect present in above-mentioned lithotome, the production and utilization of artificial stone is to lithotome
Supplement, especially with the tailing of lithotome or other commercial recovery waste materials as made of the waste residue in glass or power plant etc.
Artificial stone is used as building decoration materials, not only alleviates the demand for lithotome, but also enrich the kind of construction material
Class.Utilization is designed to artificial stone, both artistic and practical building decoration materials can be become.In Publication No.: CN
1188835A；Patent name are as follows: disclosed in composite masonry slab or natural stone sheet and its Chinese patent of production method
A kind of composite masonry slab or natural stone sheet and its production method, it is characterised in that: composite board or natural stone sheet
It is made of lithotome, reinforcing material, reinforcing material mold and adhesive Y, wherein composite masonry slab contains one or more layers
Play the reinforcing material of humidification to one layer or two layers of pure natural masonry slab, and the composite masonry slab that provides of the invention or
The production method of natural stone sheet, main includes cutting for the first time, enhancing processing, generating pedestal or merging stabilizing mechanism, the
The secondary or second above cutting, be placed in vibrationproof compression-resistant material, one or both sides processing in grooving, remove reinforcing material mold and
The technical process such as adhesive Y, trimming；Its main feature is that having used reinforcing material or reinforcing material mold and adhesive Y, can select respectively
Make one or more layers reinforcing material and one layer or two layers lithotome with the same or similar process of flow chart 39 and its technique
It is firmly combined together between each layer, or lithotome is carried out the enhancing such as to bond using reinforcing material mold and adhesive Y
Treatment process, generate pedestal or merging stabilizing mechanism, second or second of above cutting, two-by-two surface processing, remove enhancing
Material molds and adhesive Y and vibrationproof compression-resistant material can be placed in grooving and effectively prevent lithotome in cutting, surface adds
The processes such as work are shattered or are crushed, to obtain composite masonry slab or natural stone sheet.The invention solves existing stone plate
Material is blocked up and brings preponderance, waste rock material resource, the problems such as transport difficult and difficulty of construction are excessive, and product is suitble to
All building decorations and family property production use.But it is not difficult to find out that, the manufacture craft of the invention is only between multi-layered board
Bonding superposition, although solve existing masonry slab it is blocked up and bring preponderance, waste rock material resource, transport difficult and
The problems such as difficulty of construction is excessive, but do not get a promotion for performances such as itself the structural strengths of plate, therefore be difficult full
The sufficient people requirement increasingly harsh to building decoration.
Summary of the invention
The present invention to solve the above-mentioned problems, provides that a kind of novel appearance, material are solid, i.e., with the color of lithotome
Color and decorative pattern, and there is good wear-resisting property and structural strength height, the production side of the low environmental-protection decoration stone material of production cost
Method.
The present invention adopts the following technical scheme:
A kind of production method of environmental-protection decoration stone material, mainly includes the following steps:
Step 1: being cut into sheet shape for raw material, by automatic sand-blasting machine, needing the level of spray paint coarse
Change processing, degreaser clean surface, and 80 degree of drying chambers dehumidify one hour, allow stone material internal moisture all to volatilize, it is best to reach paint
Adhesive force；
Step 2: the gas phase titanium dioxide that weight ratio is 20%-30% paint filler technique: is added with unsaturated polyester resin
Silicon is tuned into pureed add weight than 5% curing agent, scrapes the thickness for applying and scraping in the level for needing spray paint less than 1 millimeter with cutter painting is scraped,
Painting is scraped the infiltration of Shi Ruoyou bubble and must be thoroughly scraped with scraper, to ensure to have good adhesive force, putty painting is waited to scrape 2-3 hours
Afterwards, it is first polished with belt sander with 120#-180# sand paper polishing surface, is carefully scraped once if any pore with scraper after polishing, wait putty
Confirmation surfacing is primary without thin eye, then with 240#-400# sand paper fine grinding after dry, blows away surface dirt with air gun after fine grinding is good
Surface need to be applied with degreaser wiping again；
Step 3: synthetic resin paint primer technique: first doing dedusting oil removing for the stone material for putty of having polished, and selects and prepares
Polyurethane priming paint is once sprayed, and 60 degree of drying chambers toast one hour, after priming paint is dry, is polished with 600# or more sand paper, it is ensured that
It without depressed particle after prime coat polishing, is wiped with degreaser, deployed polyurethane body color enamel-cover is selected to include white or black
Bottom is sprayed before color or silver color or golden progress colored paint；
Step 4: printing layer pastes article layer or synthetic resin and paints colored paint layer process: sprayed before above-mentioned colored paint bottom if any
Polishing is repeated once background color after defect needs background color dry, as zero defect sprays colored varnish after priming paint stands half an hour；Or special bottom
Colored varnish could be sprayed after color is completely dry, such as color spray paint after printing, blow color spray paint after spending rear color spray paint, Hand drawing, crackle effect
Color spray after color spray paint, spot effect after color spray paint, site effect after color spray paint, ink and wash effect after color spray paint, fragment effect after fruit
Paint；After colored paint spraying after completely dry or 60 degree are toasted and carry out a lower road technique in；
Step 5: synthetic resin varnish layer applies synthetic resin varnish on synthetic resin paint colored paint layer.
As a preferred technical solution of the present invention, the stone material is artificial synthesis stone.
As a preferred technical solution of the present invention, the artificial synthesis stone includes successively pressing from top to bottom
Top plate, stiffening plate and lower plywood, the top plate and lower plywood are identical plate.
As a preferred technical solution of the present invention, the top plate is made of following ingredients by weight: TPU
Stuff and other stuff 20%-30%, ethylene methyl acrylate copolymer 8%-10%, polyhydroxyalkanoate 2%-3%, acrylic acid
Lipin polymer 3%-4%, Petropols 1%-2%, strengthen packing material 50%-60%, antioxidant and light stabilizer
0.2%-3%.
As a preferred technical solution of the present invention, the reinforcing packing material is calcite or kaolin.
As a preferred technical solution of the present invention, the antioxidant is antioxidant 1010, the light stabilizer
It is light stabilizer 1268.
The beneficial effects of the present invention are:
Product appearance novelty of the invention is beautiful, and material is solid, impact resistant, wear-resistant.Product processes are simple, easily grasp
Make, it is at low cost.It compensates for the shortcomings that no color of lithotome and decorative pattern and the easily photochemical colour fading of lithotome and pollution；Together
When in the formula of artificial synthesis stone without any plasticizer is used, press its physics using several hydrocarbon high-molecular compounds completely
Property combination also exists without any halogen at novel composite material, and in raw material, fully demonstrates no chlorination theory, ring
It protects pollution-free.
Specific embodiment
Presently in connection with specific embodiment, the present invention will be described in further detail.
Embodiment 1
A kind of production method of environmental-protection decoration stone material, mainly includes the following steps:
Step 1: being cut into sheet shape for raw material, by automatic sand-blasting machine, needing the level of spray paint coarse
Change processing, degreaser clean surface, and 80 degree of drying chambers dehumidify one hour, allow stone material internal moisture all to volatilize, it is best to reach paint
Adhesive force；
Step 2: the gas phase titanium dioxide that weight ratio is 20%-30% paint filler technique: is added with unsaturated polyester resin
Silicon is tuned into pureed add weight than 5% curing agent, scrapes the thickness for applying and scraping in the level for needing spray paint less than 1 millimeter with cutter painting is scraped,
Painting is scraped the infiltration of Shi Ruoyou bubble and must be thoroughly scraped with scraper, to ensure to have good adhesive force, putty painting is waited to scrape 2-3 hours
Afterwards, it is first polished with belt sander with 120#-180# sand paper polishing surface, is carefully scraped once if any pore with scraper after polishing, wait putty
Confirmation surfacing is primary without thin eye, then with 240#-400# sand paper fine grinding after dry, blows away surface dirt with air gun after fine grinding is good
Surface need to be applied with degreaser wiping again；
Step 3: synthetic resin paint primer technique: first doing dedusting oil removing for the stone material for putty of having polished, and selects and prepares
Polyurethane priming paint is once sprayed, and 60 degree of drying chambers toast one hour, after priming paint is dry, is polished with 600# or more sand paper, it is ensured that
It without depressed particle after prime coat polishing, is wiped with degreaser, deployed polyurethane body color enamel-cover is selected to include white or black
Bottom is sprayed before color or silver color or golden progress colored paint；
Step 4: printing layer pastes article layer or synthetic resin and paints colored paint layer process: sprayed before above-mentioned colored paint bottom if any
Polishing is repeated once background color after defect needs background color dry, as zero defect sprays colored varnish after priming paint stands half an hour；Or special bottom
Colored varnish could be sprayed after color is completely dry, such as color spray paint after printing, blow color spray paint after spending rear color spray paint, Hand drawing, crackle effect
Color spray after color spray paint, spot effect after color spray paint, site effect after color spray paint, ink and wash effect after color spray paint, fragment effect after fruit
Paint；After colored paint spraying after completely dry or 60 degree are toasted and carry out a lower road technique in；
Step 5: synthetic resin varnish layer applies synthetic resin varnish on synthetic resin paint colored paint layer；
Wherein, stone material described in step 1 is artificial synthesis stone；The artificial synthesis stone include from top to bottom according to
Top plate made of secondary pressing, stiffening plate and lower plywood, the top plate and lower plywood are identical plate；
The top plate is made of following ingredients by weight: TPU stuff and other stuff 20%, ethylene methyl acrylate copolymerization
Object 8%, acrylic acid esters co-polymer 4%, Petropols 2%, strengthens packing material 55%, antioxygen at polyhydroxyalkanoate 2%
Agent and light stabilizer 3%；
Wherein, the reinforcing packing material is calcite；The antioxidant is antioxidant 1010, the light stabilizer
It is light stabilizer 1268.
Embodiment 2
A kind of production method of environmental-protection decoration stone material, mainly includes the following steps:
Step 1: being cut into sheet shape for raw material, by automatic sand-blasting machine, needing the level of spray paint coarse
Change processing, degreaser clean surface, and 80 degree of drying chambers dehumidify one hour, allow stone material internal moisture all to volatilize, it is best to reach paint
Adhesive force；
Step 2: the gas phase titanium dioxide that weight ratio is 20%-30% paint filler technique: is added with unsaturated polyester resin
Silicon is tuned into pureed add weight than 5% curing agent, scrapes the thickness for applying and scraping in the level for needing spray paint less than 1 millimeter with cutter painting is scraped,
Painting is scraped the infiltration of Shi Ruoyou bubble and must be thoroughly scraped with scraper, to ensure to have good adhesive force, putty painting is waited to scrape 2-3 hours
Afterwards, it is first polished with belt sander with 120#-180# sand paper polishing surface, is carefully scraped once if any pore with scraper after polishing, wait putty
Confirmation surfacing is primary without thin eye, then with 240#-400# sand paper fine grinding after dry, blows away surface dirt with air gun after fine grinding is good
Surface need to be applied with degreaser wiping again；
Step 3: synthetic resin paint primer technique: first doing dedusting oil removing for the stone material for putty of having polished, and selects and prepares
Polyurethane priming paint is once sprayed, and 60 degree of drying chambers toast one hour, after priming paint is dry, is polished with 600# or more sand paper, it is ensured that
It without depressed particle after prime coat polishing, is wiped with degreaser, deployed polyurethane body color enamel-cover is selected to include white or black
Bottom is sprayed before color or silver color or golden progress colored paint；
Step 4: printing layer pastes article layer or synthetic resin and paints colored paint layer process: sprayed before above-mentioned colored paint bottom if any
Polishing is repeated once background color after defect needs background color dry, as zero defect sprays colored varnish after priming paint stands half an hour；Or special bottom
Colored varnish could be sprayed after color is completely dry, such as color spray paint after printing, blow color spray paint after spending rear color spray paint, Hand drawing, crackle effect
Color spray after color spray paint, spot effect after color spray paint, site effect after color spray paint, ink and wash effect after color spray paint, fragment effect after fruit
Paint；After colored paint spraying after completely dry or 60 degree are toasted and carry out a lower road technique in；
Step 5: synthetic resin varnish layer applies synthetic resin varnish on synthetic resin paint colored paint layer；
Wherein, stone material described in step 1 is artificial synthesis stone；The artificial synthesis stone include from top to bottom according to
Top plate made of secondary pressing, stiffening plate and lower plywood, the top plate and lower plywood are identical plate；
The top plate is made of following ingredients by weight: TPU stuff and other stuff 30%, ethylene methyl acrylate copolymerization
Object 10%, polyhydroxyalkanoate 3%, acrylic acid esters co-polymer 4%, Petropols 1.5%, strengthen packing material 60%,
Antioxidant and light stabilizer 2%.
Wherein, the reinforcing packing material is kaolin, and the antioxidant is antioxidant 1010, the light stabilizer
It is light stabilizer 1268.
Finally, it should be noted that these embodiments are merely to illustrate the present invention and do not limit the scope of the invention.In addition,
To those of ordinary skill in the art, other various forms of variations or change can also be made on the basis of the above description
It is dynamic.There is no necessity and possibility to exhaust all the enbodiments.And the obvious variation or change thus amplified out
It is dynamic to be still in the protection scope of this invention.
Claims (6)
1. a kind of production method of environmental-protection decoration stone material, it is characterised in that: mainly include the following steps:
Step 1: being cut into sheet shape for raw material, by automatic sand-blasting machine, at the level roughening for needing spray paint
Reason, degreaser clean surface, and 80 degree of drying chambers dehumidify one hour, and stone material internal moisture is allowed all to volatilize, and reach the best attachment of paint
Power；
Step 2: the fumed silica tune that weight ratio is 20%-30% paint filler technique: is added with unsaturated polyester resin
At pureed add weight than 5% curing agent, the thickness for applying and scraping in the level for needing spray paint is scraped less than 1 millimeter with cutter painting is scraped, painting is scraped
Shi Ruo has bubble infiltration that must be thoroughly scraped with scraper, to ensure to have good adhesive force, after waiting putty painting to scrape 2-3 hours,
First with 120#-180# sand paper polishing surface, is polished with belt sander, carefully scraped once if any pore with scraper after polishing, wait putty dry
Confirmation surfacing is primary without thin eye, then with 240#-400# sand paper fine grinding afterwards, blows away surface dirt with air gun after fine grinding is good and uses again
Degreaser wiping need to apply surface；
Step 3: synthetic resin paint primer technique: first doing dedusting oil removing for the stone material for putty of having polished, and selects the poly- ammonia prepared
Rouge priming paint is once sprayed, and 60 degree of drying chambers toast one hour, after priming paint is dry, is polished with 600# or more sand paper, it is ensured that priming paint
Layer polishing after without depressed particle, wiped with degreaser, select deployed polyurethane body color enamel-cover include white or black or
Bottom is sprayed before silver color or golden progress colored paint；
Step 4: printing layer pastes article layer or synthetic resin paint colored paint layer process: it is for example defective that bottom is sprayed before above-mentioned colored paint
Polishing is repeated once background color after needing background color dry, as zero defect sprays colored varnish after priming paint stands half an hour；Or special background color is complete
Colored varnish could be sprayed after absolutely dry, such as color spray paint after printing, blown after spending rear color spray paint, Hand drawing after color spray paint, crack effect
Color spray paint after color spray paint, spot effect after color spray paint, site effect after color spray paint, ink and wash effect after color spray paint, fragment effect；Color
After paint spraying after completely dry or 60 degree are toasted and carry out a lower road technique in；
Step 5: synthetic resin varnish layer applies synthetic resin varnish on synthetic resin paint colored paint layer.
2. a kind of production method of environmental-protection decoration stone material according to claim 1, it is characterised in that: the stone material is artificial
Synthesis stone.
3. a kind of production method of environmental-protection decoration stone material according to claim 2, it is characterised in that: the artificial compound stone
Material includes top plate, stiffening plate and lower plywood made of successively pressing from top to bottom, and the top plate and lower plywood are identical
Plate.
4. a kind of production method of environmental-protection decoration stone material according to claim 3, it is characterised in that: the top plate is by weight
Amount part meter is made of following ingredients: TPU stuff and other stuff 20%-30%, ethylene methyl acrylate copolymer 8%-10%, poly- hydroxyl
Aliphatic ester 2%-3%, acrylic acid esters co-polymer 3%-4%, Petropols 1%-2%, strengthen packing material 50%-
60%, antioxidant and light stabilizer 0.2%-3%.
5. a kind of production method of environmental-protection decoration stone material according to claim 4, it is characterised in that: material is filled in the reinforcing
Material is calcite or kaolin.
6. a kind of production method of environmental-protection decoration stone material according to claim 4, it is characterised in that: the antioxidant is
Antioxidant 1010, the light stabilizer are light stabilizers 1268.