CN109836966A - A kind of aqueous automobile interior trim nylon glass material paint special and preparation method thereof - Google Patents
A kind of aqueous automobile interior trim nylon glass material paint special and preparation method thereof Download PDFInfo
- Publication number
- CN109836966A CN109836966A CN201811622136.0A CN201811622136A CN109836966A CN 109836966 A CN109836966 A CN 109836966A CN 201811622136 A CN201811622136 A CN 201811622136A CN 109836966 A CN109836966 A CN 109836966A
- Authority
- CN
- China
- Prior art keywords
- glass material
- automobile interior
- interior trim
- aqueous
- nylon glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to paint field, a kind of aqueous automobile interior trim nylon glass material paint special and preparation method thereof is disclosed.This aqueous automobile interior trim nylon glass material paint special, including following weight percent composition: aqueous epoxy resins 50-60%；Coalescing agent 10-15%；Deionized water 15-20%；Aqueous pigment 1-10%；High rigidity adhesion promoter 0.1-0.5%；Salt spray resistance auxiliary agent 0.1-0.5%；Thickener 5-10%.Paint special of the present invention possesses preferable paint film richness, hardness and weatherability, can be applied on the nylon glass material of various automobile interior decorations.
Description
Technical field
The present invention relates to paint fields, and in particular to a kind of aqueous automobile interior trim nylon glass material paint special and its preparation side
Method.
Background technique
With the enhancing of environmental consciousness, the limitation mark of volatile organic matter (VOC) discharge has all been worked out in countries in the world in succession
Quasi- and regulation.Water paint has construction environment safety, and the convenient feature of energy conservation and environmental protection, effect has obtained fast in countries in the world
Speed development.Water paint as plus the diluted pure environment-friendly products of clear water, compared with traditional solvent based coating have formaldehydeless, toluene,
The features such as organic solvents such as dimethylbenzene is the environment-friendly products for belonging to a new generation.Because of its safety, energy-saving and environmental protection, will not to human body and
Environmental pollution and pollution, thus receive praises from customers, it is direction and the substitution of oil paint of the following paint industry development
Product.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of aqueous automobile interior trim nylon glass material paint specials, have excellent
Good salt spray resistance, resistance to greasy dirt, solvent resistant, alkali resistance and Corrosion Protection paint film can have been kept under severe oil dirt acid or alkali environment
It is good.
The technical problems to be solved by the invention are achieved by the following technical programs:
A kind of aqueous automobile interior trim nylon glass material paint special, which is characterized in that including following weight percent composition:
Aqueous epoxy resins 50-60%；
Coalescing agent 10-15%；
Deionized water 15-20%；
Aqueous pigment 1-10%；
High rigidity adhesion promoter 0.1-0.5%；
Salt spray resistance auxiliary agent 0.1-0.5%；
Thickener 5-10%.
Further, aqueous automobile interior trim nylon glass material paint special of the invention further includes accounting for paint total weight 0.1-0.5%
PH adjusting agent.
Further, aqueous automobile interior trim nylon glass material paint special of the invention further includes accounting for paint total weight 0.1-0.5%
Dispersing agent.
Further, aqueous automobile interior trim nylon glass material paint special of the invention further includes accounting for paint total weight 0.1-0.5%
Substrate wetting agents.
Further, aqueous automobile interior trim nylon glass material paint special of the invention further includes accounting for paint total weight 0.1-0.5%
Preservative.
Further, high rigidity adhesion promoter is urea ring class wet adhesion promotor WAM, is sweet by allyl glycidyl
The reactions such as oily ether and amine ethylethylene residue urea obtain.
Further, salt spray resistance auxiliary agent is phosphate-molybdate-zinc powder compound corrosion inhibitor W38, is by phosphate-molybdenum
The synthesis such as hydrochlorate-zinc powder.
Further, thickener is silica.
Further, coalescing agent is at least one of butyl, diethylene glycol ether.
A kind of preparation method of aqueous automobile interior trim nylon glass material paint special of the invention, includes the following steps:
Aqueous epoxy resins, coalescing agent are sequentially added in the case where 200-400 per minute turns, and deionized water is added, by pH tune
It to 8.5-9.5, stirs evenly, high rigidity adhesion promoter, salt spray resistance auxiliary agent is then added, in the case where 300-500 per minute turns
It is stirred 10-15 minutes and is slowly added thickener after mixing evenly, so that it is thickened to the cup of salt pan 2 and is measured viscosity 60 seconds and arrive
Between 70 seconds, aqueous pigment is added, 1000-1200 per minute is then carried out and turns stirring 20-30 minutes, finally by inspection, mistake
Filter, weighing packaging.
After adopting the above technical scheme, the invention has the following beneficial effects:
It is aqueous epoxy resins that paint special of the invention, which uses, can be crosslinked at a temperature of toasting 70 °C~80 °C anti-
It answers, forms it into one layer of fine and close coating, make paint film that there is fabulous hardness, good weatherability, excellent wearability is excellent
Acid and alkali-resistance, resistance to gasoline, solvent resistant and moisture resistance properties, very high salt spray resistance and asepsis environment-protecting, environmental sound.Addition
High rigidity adhesion promoter can make paint film have very high hardness and good substrate adhesive force, can be good at preventing
Paint film is scratched, and guarantees the integrality of paint film；The auxiliary agents such as substrate wetting agents are added to, the salt fog resistance of paint film, oil resistant are increased
Dirty, solvent resistant, alkali resistance and Corrosion Protection, paint film can remain intact under severe oil dirt acid or alkali environment；Film forming is added to help
Agent, its main feature is that making paint film that there is good glossiness, richness.
Specific embodiment
The present invention will now be described in detail with reference to examples, and the examples are only preferred embodiments of the present invention,
It is not limitation of the invention.
Embodiment 1
A kind of aqueous automobile interior trim nylon glass material paint special, including following component:
Aqueous epoxy resins 55g；
Diethylene glycol ether 12g；
Deionized water 17.8g%；
Aqueous pigment 5g；
WAM0.5g；
W38 salt spray resistance auxiliary agent 0.5g；
Silica 8g；
Dispersing agent 0.5g；
PH adjusting agent 0.1g；
Substrate wetting agents 0.1g
Essence 0.5g.
Embodiment 2
A kind of aqueous automobile interior trim nylon glass material paint special, including following component:
Aqueous epoxy resins 60g；
Butyl 4g；
Diethylene glycol ether 8g；
Deionized water 12.8g%；
Aqueous pigment 5g；
WAM0.5g；
W38 salt spray resistance auxiliary agent 0.5g；
Silica 8g；
Dispersing agent 0.5g；
PH adjusting agent 0.1g；
Substrate wetting agents 0.1g
Essence 0.5g.
Embodiment 3
A kind of aqueous automobile interior trim nylon glass material paint special, including following component:
Aqueous epoxy resins 50g；
Butyl 15g；
Deionized water 19.8g%；
Aqueous pigment 5g；
WAM0.5g；
W38 salt spray resistance auxiliary agent 0.5g；
Silica 8g；
Dispersing agent 0.5g；
PH adjusting agent 0.1g；
Substrate wetting agents 0.1g
Essence 0.5g.
Embodiment 1-3's the preparation method is as follows:
Low speed sequentially adds aqueous epoxy resins, coalescing agent 12% with 200~400 turns per minute, and deionized water is added,
A small amount of pH adjusting agent is added, pH is adjusted on 8 .5-9, resin is stirred evenly completely, various auxiliary agents are then added low
Speed is stirred 10 minutes under being turned with 300-500 per minute and is slowly added silicon dioxide thickening agents after mixing evenly, its thickening is made
It is measured between viscosity is 60 seconds to 70 seconds to the cup of salt pan 2, sequentially adds and need the aqueous pigment mixed colours and other pigments and fillers,
Specific color is replaced according to the requirement of client, is then carried out 1200 transhipment per minute and is turned 20 minutes, finally by inspection, mistake
Filter, weighing packaging.
In order to further illustrate the present invention, using nylon glass as material, spraying embodiment 1 formed paint film toast 70 °C~
80 °C four hours, be tested for the property again two days later.Test result is as follows:
Due to its excellent paint film richness and hardness, excellent wearability, excellent acid and alkali-resistance, resistance to gasoline, solvent resistant and resistance to
Wet performance and paint film antibacterial and antimildew function, strong covering power, chemical stability is good, does not hydrolyze；Stablize under weak acid and weak base, it is weather-proof
Property is good, can be applied on the nylon glass material of various automobile interior decorations.Customer response works well.
Claims (10)
1. a kind of aqueous automobile interior trim nylon glass material paint special, which is characterized in that including following weight percent composition:
Aqueous epoxy resins 50-60%；
Coalescing agent 10-15%；
Deionized water 15-20%；
Aqueous pigment 1-10%；
High rigidity adhesion promoter 0.1-0.5%；
Salt spray resistance auxiliary agent 0.1-0.5%；
Thickener 5-10%.
2. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that further include that account for Qi total
The pH adjusting agent of weight 0.1-0.5%.
3. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that further include that account for Qi total
The dispersing agent of weight 0.1-0.5%.
4. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that further include that account for Qi total
The substrate wetting agents of weight 0.1-0.5%.
5. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that further include that account for Qi total
The preservative of weight 0.1-0.5%.
6. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that the high rigidity
Adhesion promoter is urea ring class wet adhesion promotor WAM.
7. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that the salt spray resistance
Auxiliary agent is phosphate-molybdate-zinc powder compound corrosion inhibitor.
8. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that the thickener
For silica, water-soluble gelled is used.
9. aqueous automobile interior trim nylon glass material paint special according to claim 1, which is characterized in that the film forming helps
Agent is at least one of butyl, diethylene glycol ether.
10. a kind of preparation method of aqueous automobile interior trim nylon glass material paint special described in any one of claim 1-9,
It is characterized in that, includes the following steps:
Aqueous epoxy resins, coalescing agent are sequentially added in the case where 200-400 per minute turns, and deionized water is added, by pH tune
It to 8.5-9.5, stirs evenly, high rigidity adhesion promoter, salt spray resistance auxiliary agent is then added, in the case where 300-500 per minute turns
It is stirred 10-15 minutes and is slowly added thickener after mixing evenly, so that it is thickened to the cup of salt pan 2 and is measured viscosity 60 seconds and arrive
Between 70 seconds, aqueous pigment is added, 1000-1200 per minute is then carried out and turns stirring 20-30 minutes, finally by inspection, mistake
Filter, weighing packaging.