CN109836916A - A kind of plate environment protection oil paint treatment process - Google Patents
A kind of plate environment protection oil paint treatment process Download PDFInfo
- Publication number
- CN109836916A CN109836916A CN201910157536.7A CN201910157536A CN109836916A CN 109836916 A CN109836916 A CN 109836916A CN 201910157536 A CN201910157536 A CN 201910157536A CN 109836916 A CN109836916 A CN 109836916A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- environment protection
- paint
- treatment process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of plate environment protection oil paint treatment process, the tail gas that heater generates mixing composition in the step S1 is neutralized through filter, pigment is color pigments in the step S1, extender pigment and rust resisting pigment, grinding machine revolving speed is 1500-2000r/min in the step S2, cooling water is distilled water in the step S2, revolving speed is 150-230r/min in the step S3, structure of the invention is scientific and reasonable, it is safe and convenient to use, pass through tung oil, linseed oil, soya-bean oil, the film-forming components of fish oil and polyvinyl chloride resin composition paint, improve environmental protection effect, in addition defoaming agent, wetting agent and dispersing agent emulsifier help paint production, and defoaming agent, wetting agent and dispersing agent emulsifier are convenient for storing paint, improve the time of its storage, and And by levelling agent, drier and anti-sagging agent can in order to painting efficiency in the construction process, prevent from painting it is dry and astringent with fall, be eventually adding plasticizer, delustering agent, fire retardant and mould inhibitor, prevent paint from burning and going mouldy.
Description
Technical field
The present invention relates to environmental technology field, specially a kind of plate environment protection oil paint treatment process.
Background technique
Paint be it is a kind of can securely be covered on body surface, the chemistry for playing protection, decoration, mark and other specific uses is mixed
Object coating is closed, belongs to organic chemical industry's macromolecular material, is formed by film and belongs to high-molecular compound type, it is current according to the modern times
Chemical products classification, coating belongs to fine chemical product.Modern coating gradually becomes a kind of multi-functional work
Journey material is an important industry in chemical industry.
But plate environment protection oil paint treatment process currently on the market cannot improve the feature of environmental protection of paint, and cannot improve
The production efficiency of paint, and the mildew in later period cannot be prevented, it causes the quality for painting itself to reduce, is not easy to popularization and use
Problem.
Summary of the invention
The present invention provides a kind of plate environment protection oil paint treatment process, can effectively solve in above-mentioned background technique propose cannot
The feature of environmental protection of paint is improved, and the production efficiency of paint cannot be improved, and the mildew in later period cannot be prevented, causes paint certainly
The quality of body reduces, and is not easy to the problem of promoting the use of.
To achieve the above object, the invention provides the following technical scheme: a kind of plate environment protection oil paint treatment process, including such as
Lower step:
S1, accurately weigh composition by weight be 35-55 parts of polyvinyl chloride resin, 18-25 parts ABS, 10-15 part synthetic resin,
2-4 parts of tung oil, 2-3 parts of linseed oil, 2-3 parts of soya-bean oil and 1.2-2 parts of fish oil and 2-5 parts of defoaming agent, 3-4 parts of profit
Humectant, 1.5-2.2 parts of dispersing agent and 2-4 parts of emulsifier are put into blender, while being warming up to 50-65 degree, high-speed stirred
10-20 minutes, pigment and 1-3 parts of anti-settling agent, 2-5 parts of stabilizer and 3-5 parts of anti skinning agent is then added, continues at the uniform velocity
Stirring 20-30 minutes, obtains mixed component；
S2, mixed component is poured into grinding machine, cooling water is added and is again stirring for；
S3, the mixed component after stirring in step S2 is compared by mill base fineness, prevents color difference；
S4, the paint solution after comparing in step S3 is put into blender, the levelling agent of 0.8-1.5 parts of addition, 2-3 parts
Drier and 1.5-2 parts of anti-sagging agent after continue to stir；
S5,1.3-1.5 parts of plasticizer, 1.4-2.3 parts of delustering agent, 1.2-1.7 parts of fire retardant and 1.5-2.3 is added
Stirring continues stirring 20-30 minutes after the mould inhibitor of part, produces environment protection oil paint；
S6, by being inspected by random samples to environment protection oil paint, carry out packing storage after qualified.
According to the above technical scheme, the step S1 high speed speed of agitator is 1200-1700r/min, described at the uniform velocity to stir
Revolving speed 800-960r/min is mixed, wait paint just liquid solid colour, next step operation can be carried out by being visible by naked eyes color difference.
According to the above technical scheme, during the tail gas that heater generates mixing composition in the step S1 is carried out through filter
With.
According to the above technical scheme, pigment is color pigments, extender pigment and rust resisting pigment in the step S1
According to the above technical scheme, grinding machine revolving speed is 1500-2000r/min in the step S2.
According to the above technical scheme, cooling water is distilled water in the step S2.
According to the above technical scheme, revolving speed is 150-230r/min in the step S3.
According to the above technical scheme, revolving speed is 120-150r/min in the step S5.
According to the above technical scheme, sampling observation rate is 3% in the step S6, and detection project is moisture content, viscosity and formaldehyde
Content.
According to the above technical scheme, by bottle placer that environment protection oil paint is filling to paint kettle in the step S6.
Compared with prior art, beneficial effects of the present invention: structure of the invention is scientific and reasonable, safe and convenient to use, passes through
The film-forming components of tung oil, linseed oil, soya-bean oil, fish oil and polyvinyl chloride resin composition paint, improve environmental protection effect, in addition defoaming agent, profit
Humectant and dispersing agent emulsifier help paint production, and defoaming agent, wetting agent and dispersing agent emulsifier are convenient for paint
It is stored, improves the time of its storage, and can construct in order to paint by levelling agent, drier and anti-sagging agent
Efficiency in the process, prevent from painting it is dry and astringent with fall, be eventually adding plasticizer, delustering agent, fire retardant and mould inhibitor, prevent from painting
Burning and mildew.
Specific embodiment
It should be appreciated that preferred embodiments described herein are only used to illustrate and explain the present invention, it is not used to limit this
Invention.
Embodiment 1: a kind of plate environment protection oil paint treatment process includes the following steps:
S1, composition by weight is accurately weighed as 45 parts of polyvinyl chloride resin, 20 parts of ABS, 13 parts of synthetic resin, 3 parts of paulownia
Oil, 2 parts of linseed oil, 3 parts of soya-bean oil and 1.5 parts of fish oil and 2 parts of defoaming agent, 3 parts of wetting agent, 1.7 parts of dispersing agent
Emulsifier with 2 parts is put into blender, while being warming up to 60 degree, and high-speed stirred 10 minutes, the anti-of pigment and 1 part is then added
Heavy agent, 3 parts of stabilizer and 4 parts of anti skinning agent continue at the uniform velocity to stir 25 minutes, obtain mixed component；
S2, mixed component is poured into grinding machine, cooling water is added and is again stirring for；
S3, the mixed component after stirring in step S2 is compared by mill base fineness, prevents color difference；
S4, by step S3 compare after paint solution be put into blender, be added 1.2 parts levelling agent, 2 parts urge it is dry
Continue to stir after agent and 1.5 parts of anti-sagging agent；
S5, it is stirred after 1.3 parts of plasticizer, 1.4 parts of delustering agent, 1.2 parts of fire retardant and 1.5 parts of mould inhibitor is added
Continue stirring 20 minutes, produces environment protection oil paint；
S6, by being inspected by random samples to environment protection oil paint, carry out packing storage after qualified.
According to the above technical scheme, the step S1 high speed speed of agitator is 1200r/min, the at the uniform velocity speed of agitator
800r/min, wait paint just liquid solid colour, next step operation can be carried out by being visible by naked eyes color difference.
According to the above technical scheme, during the tail gas that heater generates mixing composition in the step S1 is carried out through filter
With.
According to the above technical scheme, pigment is color pigments, extender pigment and rust resisting pigment in the step S1
According to the above technical scheme, grinding machine revolving speed is 1500r/min in the step S2.
According to the above technical scheme, cooling water is distilled water in the step S2.
According to the above technical scheme, revolving speed is 150r/min in the step S3.
According to the above technical scheme, revolving speed is 120r/min in the step S5.
According to the above technical scheme, sampling observation rate is 3% in the step S6, and detection project is moisture content, viscosity and formaldehyde
Content.
According to the above technical scheme, by bottle placer that environment protection oil paint is filling to paint kettle in the step S6.
Embodiment 2: a kind of plate environment protection oil paint treatment process includes the following steps:
S1, composition by weight is accurately weighed as 35 parts of polyvinyl chloride resin, 18 parts of ABS, 10 parts of synthetic resin, 2 parts of paulownia
Oil, 2 parts of linseed oil, 3 parts of soya-bean oil and 2 parts of fish oil and 5 parts of defoaming agent, 4 parts of wetting agent, 2 parts of dispersing agent and 2 parts
Emulsifier be put into blender, while being warming up to 65 degree, high-speed stirred 115 minutes, the anti-settling of pigment and 1 part be then added
Agent, 5 parts of stabilizer and 5 parts of anti skinning agent continue at the uniform velocity to stir 25 minutes, obtain mixed component；
S2, mixed component is poured into grinding machine, cooling water is added and is again stirring for；
S3, the mixed component after stirring in step S2 is compared by mill base fineness, prevents color difference；
S4, the paint solution after comparing in step S3 is put into blender, 1 part of levelling agent, 2 parts of drier is added
Continue to stir with after 1.7 parts of anti-sagging agent；
S5, it is stirred after 1.5 parts of plasticizer, 1.4 parts of delustering agent, 1.2 parts of fire retardant and 1.5 parts of mould inhibitor is added
Continue stirring 20 minutes, produces environment protection oil paint；
S6, by being inspected by random samples to environment protection oil paint, carry out packing storage after qualified.
According to the above technical scheme, the step S1 high speed speed of agitator is 1500r/min, the at the uniform velocity speed of agitator
900r/min, wait paint just liquid solid colour, next step operation can be carried out by being visible by naked eyes color difference.
According to the above technical scheme, during the tail gas that heater generates mixing composition in the step S1 is carried out through filter
With.
According to the above technical scheme, pigment is color pigments, extender pigment and rust resisting pigment in the step S1
According to the above technical scheme, grinding machine revolving speed is 1700r/min in the step S2.
According to the above technical scheme, cooling water is distilled water in the step S2.
According to the above technical scheme, revolving speed is 200r/min in the step S3.
According to the above technical scheme, revolving speed is 130r/min in the step S5.
According to the above technical scheme, sampling observation rate is 3% in the step S6, and detection project is moisture content, viscosity and formaldehyde
Content.
According to the above technical scheme, by bottle placer that environment protection oil paint is filling to paint kettle in the step S6.
Embodiment 3: a kind of plate environment protection oil paint treatment process includes the following steps:
S1, composition by weight is accurately weighed as 55 parts of polyvinyl chloride resin, 25 parts of ABS, 15 parts of synthetic resin, 3 parts of paulownia
Oil, 2 parts of linseed oil, 2 parts of soya-bean oil and 1.8 parts of fish oil and 4 parts of defoaming agent, 3 parts of wetting agent, 1.5 parts of dispersing agent
Emulsifier with 2 parts is put into blender, while being warming up to 65 degree, and high-speed stirred 20 minutes, the anti-of pigment and 3 parts is then added
Heavy agent, 5 parts of stabilizer and 3 parts of anti skinning agent continue at the uniform velocity to stir 30 minutes, obtain mixed component；
S2, mixed component is poured into grinding machine, cooling water is added and is again stirring for；
S3, the mixed component after stirring in step S2 is compared by mill base fineness, prevents color difference；
S4, by step S3 compare after paint solution be put into blender, be added 1 part levelling agent, 2.5 parts urge it is dry
Continue to stir after agent and 1.8 parts of anti-sagging agent；
S5, it is stirred after 1.5 parts of plasticizer, 1.8 parts of delustering agent, 1.5 parts of fire retardant and 1.7 parts of mould inhibitor is added
Continue stirring 30 minutes, produces environment protection oil paint；
S6, by being inspected by random samples to environment protection oil paint, carry out packing storage after qualified.
According to the above technical scheme, the step S1 high speed speed of agitator is 1700r/min, the at the uniform velocity speed of agitator
960r/min, wait paint just liquid solid colour, next step operation can be carried out by being visible by naked eyes color difference.
According to the above technical scheme, during the tail gas that heater generates mixing composition in the step S1 is carried out through filter
With.
According to the above technical scheme, pigment is color pigments, extender pigment and rust resisting pigment in the step S1
According to the above technical scheme, grinding machine revolving speed is 2000r/min in the step S2.
According to the above technical scheme, cooling water is distilled water in the step S2.
According to the above technical scheme, revolving speed is 230r/min in the step S3.
According to the above technical scheme, revolving speed is 150r/min in the step S5.
According to the above technical scheme, sampling observation rate is 3% in the step S6, and detection project is moisture content, viscosity and formaldehyde
Content.
According to the above technical scheme, by bottle placer that environment protection oil paint is filling to paint kettle in the step S6.
By the sampling observation of embodiment 1-3, following table is obtained:
By comparison, the moisture content and content of formaldehyde in discovery embodiment 1 are minimum, and modest viscosity is suitble to promote the use of, peace
Loopful is protected.
Compared with prior art, beneficial effects of the present invention: structure of the invention is scientific and reasonable, safe and convenient to use, passes through
The film-forming components of tung oil, linseed oil, soya-bean oil, fish oil and polyvinyl chloride resin composition paint, improve environmental protection effect, in addition defoaming agent, profit
Humectant and dispersing agent emulsifier help paint production, and defoaming agent, wetting agent and dispersing agent emulsifier are convenient for paint
It is stored, improves the time of its storage, and can construct in order to paint by levelling agent, drier and anti-sagging agent
Efficiency in the process, prevent from painting it is dry and astringent with fall, be eventually adding plasticizer, delustering agent, fire retardant and mould inhibitor, prevent from painting
Burning and mildew.
Finally, it should be noted that being not intended to restrict the invention the foregoing is merely preferred embodiment of the invention, to the greatest extent
Present invention has been described in detail with reference to the aforementioned embodiments for pipe, for those skilled in the art, still can be with
It modifies the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.It is all
Within the spirit and principles in the present invention, any modification, equivalent replacement, improvement and so on should be included in guarantor of the invention
Within the scope of shield.
Claims (10)
1. a kind of plate environment protection oil paint treatment process, characterized by the following steps:
S1, synthetic resin, 2-4 that composition by weight is 35-55 parts of polyvinyl chloride resin, 18-25 parts ABS, 10-15 part are accurately weighed
The tung oil, 2-3 parts of linseed oil, 2-3 parts of soya-bean oil and 1.2-2 parts of fish oil of part and 2-5 parts of defoaming agent, 3-4 parts of wetting
Agent, 1.5-2.2 parts of dispersing agent and 2-4 parts of emulsifier are put into blender, while being warming up to 50-65 degree, high-speed stirred 10-
20 minutes, pigment and 1-3 parts of anti-settling agent, 2-5 parts of stabilizer and 3-5 parts of anti skinning agent is then added, continuation is at the uniform velocity stirred
It mixes 20-30 minutes, obtains mixed component；
S2, mixed component is poured into grinding machine, cooling water is added and is again stirring for；
S3, the mixed component after stirring in step S2 is compared by mill base fineness, prevents color difference；
S4, the paint solution after comparing in step S3 is put into blender, be added 0.8-1.5 parts of levelling agent, 2-3 parts urge
Continue to stir after dry agent and 1.5-2 parts of anti-sagging agent；
S5,1.3-1.5 parts of plasticizer, 1.4-2.3 parts of delustering agent, 1.2-1.7 parts of fire retardant and 1.5-2.3 parts are added
Stirring continues stirring 20-30 minutes after mould inhibitor, produces environment protection oil paint；
S6, by being inspected by random samples to environment protection oil paint, carry out packing storage after qualified.
2. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that the step S1 high speed
Speed of agitator is 1200-1700r/min, the at the uniform velocity speed of agitator 800-960r/min, wait paint just liquid solid colour, no meat
The visible color difference of eye can carry out next step operation.
3. a kind of plate environment protection oil paint treatment process according to claim 2, which is characterized in that heated in the step S1
The tail gas that device generates mixing composition is neutralized through filter.
4. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that pigment in the step S1
For color pigments, extender pigment and rust resisting pigment.
5. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that frosted in the step S2
Machine revolving speed is 1500-2000r/min.
6. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that cooling in the step S2
Water is distilled water.
7. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that revolving speed in the step S3
For 150-230r/min.
8. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that revolving speed in the step S5
For 120-150r/min.
9. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that inspected by random samples in the step S6
Rate is 3%, and detection project is moisture content, viscosity and content of formaldehyde.
10. a kind of plate environment protection oil paint treatment process according to claim 1, which is characterized in that lead in the step S6
Cross bottle placer environment protection oil paint is filling to paint kettle.