CN109836602A - Plate anti-pollution film and preparation method thereof is built in a kind of room - Google Patents
Plate anti-pollution film and preparation method thereof is built in a kind of room Download PDFInfo
- Publication number
- CN109836602A CN109836602A CN201910053556.XA CN201910053556A CN109836602A CN 109836602 A CN109836602 A CN 109836602A CN 201910053556 A CN201910053556 A CN 201910053556A CN 109836602 A CN109836602 A CN 109836602A
- Authority
- CN
- China
- Prior art keywords
- layer
- built
- cleaning
- self
- bonded
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to building technical field of membrane, plate anti-pollution film and preparation method thereof is built in especially a kind of room, including base, the side of base is bonded with anti-oxidant separation layer, anti-oxidant separation layer is bonded with insulating layer far from the side of base, insulating layer is bonded with fireprotection layer far from the side of anti-oxidant separation layer, and fireprotection layer is bonded with self-cleaning layer far from the side of insulating layer.The present invention also provides the preparation methods that plate anti-pollution film is built in a kind of room.The present invention passes through self-cleaning layer structure, self-cleaning layer is bifluoride cold coating, and bifluoride resin has high intensity, self-cleaning and shock resistance, and there are very high fade resistance and anti-ultraviolet property in extremely harsh and rugged environment, rainwater can make membrane material surface obtain nature cleaning in the case where the surface of film is polymerized to droplet stream, and graphite high temperature anti-oxidation coating can form scleroid coating, antifouling property is good, with very strong wear-resisting property, self-cleaning, structure is simple, is worthy to be popularized.
Description
Technical field
The present invention relates to building technical field of membrane more particularly to a kind of room to build plate anti-pollution film.
Background technique
With the development of society, the material life of people is while being promoted, demand of the people to spiritual this respect is also got over
Come higher, membrane structure is used not only in sports equipment, means of transportation, cultural facility, Landscape Facilities, commercial facility, industrial plants side
Face, it is more and more extensive, it not only the service life it is long, also cost performance it is very high, moulding is also novel, and membrane structure is in building structure
A kind of form that latest development is got up, it inflates using the fabric of function admirable as material, or into film, is supported by air pressure
Film surface, or tightened face using flexible cable or rigidity supporting structure, thus formed have certain rigidity, can cover greatly across
Spend the structural system in space.Since the 1970's, membrane structure is gradually applied to sports building, market, exhibition external
In the long span buildings such as center, transport services facility.
Build film with energy-saving heat-insulating as the main purpose, while also have antiultraviolet and certain security function.This kind of film
Thermal reflecting coating and low-radiation film can be also divided into.Thermal reflecting coating, this film be attached to glass surface make to penetrate in room it is a part of visible
Light and a part of near infrared light reflect and absorb a part of visible light and a part of near infrared light, therefore can allow foot
Enough light enters the room, and the heat of most solar energy is reflected back, so, Indoor Temperature is kept during the broiling summer
Degree will not increase too much, to reduce room conditioning load, reach and save air-conditioning expense and energy-efficient effect.Low-radiation film, this
Kind film can penetrate a certain amount of shortwave solar radiant energy, so that solar radiant heat is entered the room, be absorbed by indoor object；Simultaneously again
The LONG WAVE INFRARED line reflection of 90% or more indoor object radiation can be remained in interior.Low-radiation film can make full use of sunlight
The long-wave radiation energy of radiation and indoor object.Therefore in cold district and heating building using can play heat preservation and energy conservation imitate
Fruit.
Existing building board needs to carry out pad pasting to plate in a pre-installation, so that plate has stronger function, it is existing
Building film pollution resistance wearability it is poor.
Summary of the invention
The purpose of the present invention is to solve one for existing in the prior art the poor disadvantage of pollution resistance wearability, and proposing
Plate anti-pollution film is built in kind room.
To achieve the goals above, present invention employs following technical solutions:
It designs a kind of room and builds plate anti-pollution film, including base, the side of the base is bonded with anti-oxidant separation layer, institute
It states anti-oxidant separation layer and is bonded with insulating layer far from the side of the base, the insulating layer is far from the anti-oxidant separation layer
Side is bonded with fireprotection layer, and the fireprotection layer is bonded with self-cleaning layer far from the side of the insulating layer.
Preferably, the base is that polyester fiber covers layers of polyvinyl chloride films.
Preferably, the anti-oxidant separation layer is graphite high temperature anti-oxidation coating layer.
Preferably, the insulating layer is poly- ammonia dope layer, and the production method of the polyurethane coating is by polyurethane, addition
Adhesive and volatility are put into stirring container after holding agent, stirring container are put into water-bath heater, the temperature of heating water bath
It is 40 DEG C, stirs to liquid.
Preferably, the self-cleaning layer is bifluoride cold coating, is added in the bifluoride cold coating manufacturing process anti-
Aging agent, ultraviolet absorbing agent, stabilizer enhance the weatherability and anti-aging property of film.
The present invention also proposes that the preparation method of plate anti-pollution film is built in a kind of room, includes the following steps:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: anti-oxidant separation layer is coated on the surface of basement membrane, is coated with heat preservation in anti-oxidant insulation surface after illumination curing
Layer, is coated with fireprotection layer in insulation layer surface；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 60-80 DEG C, baking time 2-
8min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 80-
100 DEG C, baking time 6-10min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.
Plate anti-pollution film is built in a kind of room proposed by the present invention, and beneficial effect is: the present invention is by self-cleaning layer structure, certainly
Clean layer is bifluoride cold coating, and bifluoride resin has high-intensitive, corrosion resistant substance, with very strong wear-resisting property, certainly
Clean property and shock resistance, and have very high fade resistance and anti-ultraviolet property in extremely harsh and rugged environment,
Rainwater can make membrane material surface obtain nature cleaning, graphite high temperature anti-oxidation coating can be with shape in the case where the surface of film is polymerized to droplet stream
At scleroid coating, there is good self-healing repair ability to rising-heat contracting-cold, slag-resistant and high temperature sundries corrode and infiltration is invaded
Erosion, material anti-oxidation long service life at high temperature, structure is simple, and antifouling property is good, has very strong wear-resisting property, self-cleaning
Property.
Detailed description of the invention
Fig. 1 is the structural schematic diagram that plate anti-pollution film is built in a kind of room proposed by the present invention.
In figure: base 1, anti-oxidant separation layer 2, insulating layer 3, fireprotection layer 4, self-cleaning layer 5.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Referring to Fig.1, plate anti-pollution film, including base 1 are built in a kind of room, and base 1 is that polyester fiber covers layers of polyvinyl chloride films,
The side of base 1 is bonded with anti-oxidant separation layer 2, and the effect of anti-oxidant separation layer 2 is the antioxygenic property for enhancing film, is pasting
When on plate, it is not easy oxidation by air, anti-oxidant separation layer 2 is graphite high temperature anti-oxidation coating layer, graphite high-temperature oxidation resistant
Coating can form scleroid coating, have good self-healing repair ability to rising-heat contracting-cold, slag-resistant and high temperature sundries are invaded
Erosion and infiltration are corroded, and material anti-oxidation long service life at high temperature is extended, and side of the anti-oxidant separation layer 2 far from base 1 is viscous
It is connected to insulating layer 3, the effect of insulating layer 3 is to enhance the sealing performance of film, and insulating layer 3 is poly- ammonia dope layer.
Insulating layer 3 is bonded with fireprotection layer 4, side of the fireprotection layer 4 far from insulating layer 3 far from the side of anti-oxidant separation layer 2
It is bonded with self-cleaning layer 5, self-cleaning layer 5 is bifluoride cold coating, and bifluoride resin has high intensity, and corrosion resistant substance has
Very strong wear-resisting property, self-cleaning and shock resistance, and have very high anti-colour fading in extremely harsh and rugged environment
Property and anti-ultraviolet property, when rainwater is dropped on plate, rainwater can be such that membrane material surface obtains in the case where the surface of film is polymerized to droplet stream
To cleaning naturally, so that plate has stronger pollution resistance, plate can be with automated cleaning, in bifluoride cold coating manufacturing process
Age resister, ultraviolet absorbing agent, stabilizer is added, enhances the weatherability and anti-aging property of film.
Embodiment 1
The present invention also provides the preparation methods that plate anti-pollution film is built in a kind of room, include the following steps:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: anti-oxidant separation layer is coated on the surface of basement membrane, is coated with heat preservation in anti-oxidant insulation surface after illumination curing
Layer, insulating layer are polyurethane coating, and the production method of polyurethane coating is after polyurethane, addition adhesive and volatility are held agent
Be put into stirring container, stirring container be put into water-bath heater, the temperature of heating water bath is 40 DEG C, stirring to liquid,
Fireprotection layer is coated in insulation layer surface；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 60 DEG C, baking time 2min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 80
DEG C, baking time 6min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.
Embodiment 2
The present invention also provides the preparation methods that plate anti-pollution film is built in a kind of room, include the following steps:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: anti-oxidant separation layer is coated on the surface of basement membrane, is coated with heat preservation in anti-oxidant insulation surface after illumination curing
Layer, insulating layer are polyurethane coating, and the production method of polyurethane coating is after polyurethane, addition adhesive and volatility are held agent
Be put into stirring container, stirring container be put into water-bath heater, the temperature of heating water bath is 40 DEG C, stirring to liquid,
Fireprotection layer is coated in insulation layer surface；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 65 DEG C, baking time 4min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 85
DEG C, baking time 7min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.
Embodiment 3
The present invention also provides the preparation methods that plate anti-pollution film is built in a kind of room, include the following steps:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: anti-oxidant separation layer is coated on the surface of basement membrane, is coated with heat preservation in anti-oxidant insulation surface after illumination curing
Layer, insulating layer are polyurethane coating, and the production method of polyurethane coating is after polyurethane, addition adhesive and volatility are held agent
Be put into stirring container, stirring container be put into water-bath heater, the temperature of heating water bath is 40 DEG C, stirring to liquid,
Fireprotection layer is coated in insulation layer surface；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 70 DEG C, baking time 5min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 90
DEG C, baking time 8min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.
Embodiment 4
The present invention also provides the preparation methods that plate anti-pollution film is built in a kind of room, include the following steps:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: anti-oxidant separation layer is coated on the surface of basement membrane, is coated with heat preservation in anti-oxidant insulation surface after illumination curing
Layer, insulating layer are polyurethane coating, and the production method of polyurethane coating is after polyurethane, addition adhesive and volatility are held agent
Be put into stirring container, stirring container be put into water-bath heater, the temperature of heating water bath is 40 DEG C, stirring to liquid,
Fireprotection layer is coated in insulation layer surface；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 75 DEG C, baking time 7min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 95
DEG C, baking time 9min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.
Embodiment 5
The present invention also provides the preparation methods that plate anti-pollution film is built in a kind of room, include the following steps:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: anti-oxidant separation layer is coated on the surface of basement membrane, is coated with heat preservation in anti-oxidant insulation surface after illumination curing
Layer, insulating layer are polyurethane coating, and the production method of polyurethane coating is after polyurethane, addition adhesive and volatility are held agent
Be put into stirring container, stirring container be put into water-bath heater, the temperature of heating water bath is 40 DEG C, stirring to liquid,
Fireprotection layer is coated in insulation layer surface；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 80 DEG C, baking time 8min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 100
DEG C, baking time 10min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (6)
1. plate anti-pollution film, including base (1) are built in a kind of room, which is characterized in that the side of the base (1) is bonded with antioxygen
Change separation layer (2), the anti-oxidant separation layer (2) is bonded with insulating layer (3), the heat preservation far from the side of the base (1)
Layer (3) is bonded with fireprotection layer (4) far from the side of the anti-oxidant separation layer (2), and the fireprotection layer (4) is far from the insulating layer
(3) side is bonded with self-cleaning layer (5).
2. plate anti-pollution film is built in a kind of room according to claim 1, which is characterized in that the base (1) is that polyester is fine
Dimension covers layers of polyvinyl chloride films.
3. plate anti-pollution film is built in a kind of room according to claim 1, which is characterized in that the anti-oxidant separation layer (2)
For graphite high temperature anti-oxidation coating layer.
4. plate anti-pollution film is built in a kind of room according to claim 1, which is characterized in that the insulating layer (3) is poly- ammonia
Dope layer, the production method of the polyurethane coating are to be put into stirring after polyurethane, addition adhesive and volatility to be held to agent to hold
In device, stirring container is put into water-bath heater, the temperature of heating water bath is 40 DEG C, is stirred to liquid.
5. plate anti-pollution film is built in a kind of room according to claim 1, which is characterized in that the self-cleaning layer (5) is difluoro
Change cold coating, age resister, ultraviolet absorbing agent, stabilizer, enhancing are added in the bifluoride cold coating manufacturing process
The weatherability and anti-aging property of film.
6. the preparation method that plate anti-pollution film is built in a kind of room described in one of -5 according to claim 1, which is characterized in that including such as
Lower step:
S1: preparing material, and basement membrane is lain in and is contained in template, and basement membrane is fixed；
S2: being coated with anti-oxidant separation layer on the surface of basement membrane, be coated with insulating layer in anti-oxidant insulation surface after illumination curing,
Insulation layer surface is coated with fireprotection layer；
S3: will contain template and be put into baking oven, adjust the temperature of baking oven, and stoving temperature is 60-80 DEG C, baking time 2-8min；
S4: template will be contained and taken out, the even spread self-cleaning layer on fireprotection layer is placed again into baking oven, stoving temperature 80-100
DEG C, baking time 6-10min；
S5: taking out and contain template, and cooling takes out basement membrane after drying.