CN109811570A - A kind of technique that paper grade pulp is made as raw material activity legal system using fresh bamboo - Google Patents
A kind of technique that paper grade pulp is made as raw material activity legal system using fresh bamboo Download PDFInfo
- Publication number
- CN109811570A CN109811570A CN201910181008.5A CN201910181008A CN109811570A CN 109811570 A CN109811570 A CN 109811570A CN 201910181008 A CN201910181008 A CN 201910181008A CN 109811570 A CN109811570 A CN 109811570A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- pulp
- bamboo pulp
- squeezes
- pressure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of technique for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, comprising: cuts bamboo;Fragment;Super-pressure classification rolls: bamboo chip being placed in classification in roll rolling and is rolled, classification is rolled to roll including four to six grades, and grinding pressure at different levels is gradually increased;Thread rolling;Primary filtering, which squeezes, obtains initial filter bamboo pulp;Secondary filter squeezes: sequentially carrying out physical filtering and secondary extrusion into initial filter bamboo pulp plus after water after heating stirring again, then is filtered bamboo pulp, squeezes and complete to secondary filter from beginning raw bamboo felling, total time is no more than 72h;Biological enzyme bating relieves.This technique, by itself and bamboo fibre quick separating, facilitates the integrality for keeping bamboo fibre to greatest extent when lignin, amino acid, flavones, protein etc. are also in liquid, and easy to operate, low in cost, energy-saving and environmental protection, green, low-carbon are worthy of popularization.
Description
Technical field
The present invention relates to pulp technology for making paper, particularly relate to a kind of make paper grade pulp by raw material activity legal system of fresh bamboo
Technique.
Background technique
China's bamboo resource is abundant, and the annual output of bamboo occupies the first in the world, and most of bamboo pulping Papermaking Performances are excellent,
Close to broadleaf.However bamboo class raw tissue close structure, medicinal liquid osmosis is difficult, in traditional bamboo digesting technoloy, pulp washing
Black liquor directly send evaporation, is easy to happen silicon obstacle and calcium fouling, there are complex operation, digester cycle is long, production efficiency is low,
It consumes energy the problems such as serious, seriously polluted, does not meet green, environmental protection, low-carbon, energy-efficient production theory that country advocates.Thus state
The interior production to bamboo pulp has carried out maximum limitation, how to improve existing bamboo pulp manufacturing technique, is ensuring compliance with country
While green, environmental protection, low-carbon, production energy-saving theory, bamboo resource is efficiently used, to meet worldwide paper requirements not
Break widened requirement, is the current technical issues that need to address.
Summary of the invention
To solve the above the deficiencies in the prior art, the invention proposes one kind to make paper grade (stock) by raw material activity legal system of fresh bamboo
The technique of paper pulp.
The technical scheme of the present invention is realized as follows:
A kind of technique for making paper grade (stock) bamboo pulp using fresh bamboo as raw material activity legal system, includes the following steps:
(1) it cuts bamboo: bamboo section will be obtained after the cleaning of fresh bamboo wood, cutting;
(2) fragment: bamboo section is subjected to fragment and obtains bamboo chip;
(3) super-pressure classification rolls: bamboo chip being placed in classification in roll rolling and is rolled, classification is rolled grinds including four to six grades
Pressure, grinding pressure at different levels are gradually increased;Classification rolls so that fiber stress is gradually increased, and fiber is avoided to deform because once suppressing
Cause fibrous fracture greatly, the integrality of fiber can be kept to greatest extent;Rolling can be by the wood between fiber also in liquid
Element, protein, amino acid and various flavones etc. first squeeze out most of;
(4) thread rolling: the bamboo fiber bundle that super-pressure classification rolls being placed in thread rolling machine and carries out thread rolling, thread rolling process
In can squeeze out again between fiber also in the lignin of liquid, protein, amino acid and various flavones etc.;
(5) primary filtering squeezes: the bamboo pulp containing a large amount of fibers after thread rolling first being carried out physical filtering and squeezes to obtain again
Initial filter bamboo pulp;
(6) secondary filter squeezes: sequentially carrying out physical filtering and two into initial filter bamboo pulp plus after water after heating stirring again
Secondary extruding, then bamboo pulp is filtered, it squeezes and completes to secondary filter from raw bamboo felling, total time is no more than 72h;Primary filtering squeezes
Finally the lignin of liquid, protein, amino acid and various flavones can be separated with bamboo fibre with secondary filter extruding,
(7) biological enzyme bating relieves, and softening is relieved using the prior art, can specifically refer to Chinese patent: a kind of bamboo is fine
The softening method (application number 201710936614.4, publication No. CN 107639708A) of dimension.
Lignin, amino acid, flavones, protein etc. in liquid are carried out multiple, quick separating with bamboo fibre by this technique,
Facilitate to greatest extent keep bamboo fibre integrality, it is easy to operate, low in cost, will not to environment generate pollution, meet
National green, environmental protection, low-carbon, production energy-saving theory, highly promote and apply.
Preferably, fresh bamboo wood is the fresh bamboo of activity of 3 <bamboo age≤7 and felling time no more than 48h, is grown after cutting bamboo
The bamboo section of 1-4m is spent, obtains the bamboo chip that width is not more than 40mm after fragment.
It is further preferred that classification roll in gap between milling roller at different levels it is as follows: level-one: 4-6mm, second level: 2-
4mm, three-level: 1.5-2mm, level Four: 1-1.5mm, Pyatyi: 0.5-1mm, six grades: 0-0.5mm, rolling roller diameter is 200-
1500mm, rolling speed 8-50m/min.
It is further preferred that the grinding pressure of level-one to Pyatyi is not more than 60MPa, six grades of grinding pressure 70-160MPa.It is more
It is secondary, be gradually increased grinding pressure carry out classification roll, both can be effectively by lignin, protein, the ammonia between fiber also in liquid
Base acid and various flavones squeeze out it is most of, and will not damaged fiber, the integrality of fiber can be kept, then ensure bamboo pulp
Excellent properties.
It is further preferred that the bamboo fiber bundle that classification rolls is placed in thread rolling machine after adding water on one side when thread rolling
Heating carries out thread rolling on one side, and adding the weight percent of bamboo fiber bundle after water is 5-50%, and heating temperature is no more than 90 DEG C.Add water can
So that bamboo fiber bundle it is mutual extruding force it is soft, reduce broken, the fracture of fiber;Heating can promote in bamboo fiber bundle
Lignin, amino acid, protein and various flavones isoreactivity ingredients be quickly dissolved into water;It is of course also possible to which directly addition is hot
Water.
It is further preferred that the grinding pressure that individual fibers are born (is arranged no more than 10N under microscope when thread rolling
The fibre bundle of quantity, then presses, after fibre bundle uniformly divides column, by the pressure of application divided by fiber number it can be learnt that.),
The stroke 100-250mm of effective roller compaction process, obtains the bamboo fibre of diameter 0.03-0.1mm, length 0.5-5mm after thread rolling.
It is further preferred that amount of water is not less than twice of initial filter bamboo pulp weight when secondary filter squeezes, heating temperature is
40-90 DEG C, the mixing time of the over dry initial filter bamboo pulp of every 500Kg is not less than 1.5h.
It is further preferred that the concrete operations that biological enzyme bating relieves are as follows: bamboo pulp will be filtered again and be placed in stainless cylinder of steel and add
Heat to 60-65 DEG C, keep the temperature 1h after be cooled to 40-45 DEG C, by Endocellulase, heat-resistant alpha-amylase, beta-glucosidase,
Polygalacturonase, medium temperature amylase and liquefying amylase, which are added in stainless cylinder of steel, stirs at least 1h, the use of every kind of enzyme
The weight percent of amount and over dry bamboo pulp is respectively 0.32 ‰, 0.45 ‰, 0.35 ‰, 0.40 ‰, 0.67 ‰ and 0.56 ‰;Heating
And when heat preservation, stainless cylinder of steel is lower than 2MPa in the pressure of air-tight state and inside, and in this low pressure range, fiber hydrolization is faster.
More preferably, primary filtering, which squeezes, is first filtered using the stainless steel filter screen of 30-70 mesh, then is squeezed;Two
Secondary filtering, which squeezes, is first filtered using the stainless steel filter screen of 40-60 mesh, then carries out high-pressure extrusion, and the pressure of the high-pressure extrusion is not
Lower than 60MPa.
Highly preferred, the initial filter bamboo pulp water content that primary filtering obtains after squeezing is no more than 55%, and secondary filter squeezes
What is obtained afterwards filters bamboo pulp water content not higher than 42% again.
The present invention, by itself and bamboo fibre quick separating, has when lignin, amino acid, flavones, protein etc. are also in liquid
Help to greatest extent keep bamboo fibre integrality, it is easy to operate, low in cost, will not to environment generate pollution, meet state
Family green, environmental protection, low-carbon, production energy-saving theory, highly promote and apply.
Specific embodiment
Technical solution of the present invention is clearly and completely described below in conjunction with the embodiment of the present invention.Obviously, described
Embodiment is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field
Those of ordinary skill's every other embodiment obtained without creative efforts, belongs to protection of the present invention
Range.
Embodiment 1
A kind of technique for making paper grade (stock) bamboo pulp using fresh bamboo as raw material activity legal system, operating procedure are as follows:
(1) it cuts bamboo: being 4 years by bamboo age and cut down activity fresh bamboo of the time no more than 48h and clean, obtain length 1- after cutting
The bamboo section of 4m;
(2) fragment: bamboo section is subjected to fragment and obtains the bamboo chip that width is not more than 40mm;
(3) super-pressure classification rolls: bamboo chip is placed in roll rolling a point level Four and is rolled, the grinding pressure point of level-one to level Four
Not Wei 30MPa, 40MPa, 50MPa, 60MPa, the gap between milling rollers at different levels is as follows: level-one: 4mm, second level: 4mm, three-level:
1.5mm, level Four: 1.5mm, it is 20m/min that roll roller diameter, which be 200mm, rolling speed,;
(4) thread rolling: the bamboo fiber bundle that super-pressure classification rolls is placed in thread rolling machine plus water makes bamboo fiber bundle
Weight percent be 25%, thread rolling is carried out while heating later;Heating temperature is no more than 90 DEG C;Individual fibers are born
Grinding pressure no more than 10N, effective roller compaction process stroke 250mm, finally obtain diameter 0.03-0.1mm, length 0.5-5mm
Bamboo fibre;
(5) primary filtering squeezes: the bamboo pulp containing a large amount of fibers after thread rolling is first used to the stainless steel filter screen of 40 mesh
Filtering squeezes to obtain the initial filter bamboo pulp that water content is no more than 52% again;
(6) secondary filter squeezes: heating stirring into initial filter bamboo pulp plus after water, and amount of water is the two of initial filter bamboo pulp weight
Times, heating temperature is 50 DEG C, and the mixing time of the over dry initial filter bamboo pulp of every 500Kg is 2h, first uses the stainless steel of 50 mesh later
Filter screen filtration, then high-pressure extrusion is carried out, the pressure of high-pressure extrusion is 70MPa, finally obtains water content again not higher than 39%
Filter bamboo pulp;It squeezes and completes to secondary filter from raw bamboo felling, total time 62h;
(7) biological enzyme bating relieves: will filter bamboo pulp again and be placed in stainless cylinder of steel and be heated to 65 DEG C, and be cooled to after keeping the temperature 1h
45 DEG C, by Endocellulase, heat-resistant alpha-amylase, beta-glucosidase, polygalacturonase, medium temperature amylase and liquid
Change type amylase, which is added in stainless cylinder of steel, stirs 1h, and the weight percent of the dosage and over dry bamboo pulp of every kind of enzyme is respectively
0.32 ‰, 0.45 ‰, 0.35 ‰, 0.40 ‰, 0.67 ‰ and 0.56 ‰;When heating and heat preservation, stainless cylinder of steel in air-tight state and
Internal pressure is 0.8MPa.
After above-mentioned processing is fully completed, product is put into press machine and does drainage processing, while being compressed into a set pattern
The squares of lattice and packing, removal, drying, storage.
Embodiment 2
A kind of technique for making paper grade (stock) bamboo pulp using fresh bamboo as raw material activity legal system, operating procedure are as follows:
(1) it cuts bamboo: being 6 years by bamboo age and cut down activity fresh bamboo of the time no more than 48h and clean, obtain length 1- after cutting
The bamboo section of 4m;
(2) fragment: bamboo section is subjected to fragment and obtains the bamboo chip that width is not more than 40mm;
(3) super-pressure classification rolls: bamboo chip is placed in roll rolling a point Pyatyi and is rolled, the grinding pressure point of level-one to Pyatyi
Not are as follows: 15MPa, 20MPa, 30MPa, 40MPa, 50MPa, the gap between milling rollers at different levels are as follows: level-one: 6mm, second level:
2mm, three-level: 2mm, level Four: 1mm, Pyatyi: 1mm, roll roller diameter be 1500mm, rolling speed 30m/min;
(4) thread rolling: the bamboo fiber bundle that super-pressure classification rolls is placed in thread rolling machine plus water makes bamboo fiber bundle
Weight percent be 50%, thread rolling is carried out while heating later;Heating temperature is no more than 90 DEG C;Individual fibers are born
Grinding pressure no more than 10N, effective roller compaction process stroke 100-250mm, finally obtain diameter 0.03-0.1mm, length 0.5-
The bamboo fibre of 5mm;
(5) primary filtering squeezes: the bamboo pulp containing a large amount of fibers after thread rolling is first used to the stainless steel filter screen of 30 mesh
Filtering squeezes to obtain the initial filter bamboo pulp that water content is no more than 52% again;
(6) secondary filter squeezes: heating stirring into initial filter bamboo pulp plus after water, amount of water is not less than initial filter bamboo pulp weight
Four times, heating temperature is 40 DEG C, and the mixing time of the over dry initial filter bamboo pulp of every 500Kg is 1.5h, first uses 50 purposes not later
Rust steel filter screen filtration, then high-pressure extrusion is carried out, the pressure of high-pressure extrusion is 55MPa, finally obtains filtering again for water content 41%
Bamboo pulp;It squeezes and completes to secondary filter from raw bamboo felling, total time 55h;
(7) biological enzyme bating relieves: will filter bamboo pulp again and be placed in stainless cylinder of steel and be heated to 60 DEG C, and be cooled to after keeping the temperature 1h
40 DEG C, by Endocellulase, heat-resistant alpha-amylase, beta-glucosidase, polygalacturonase, medium temperature amylase and liquid
Change type amylase, which is added in stainless cylinder of steel, stirs 2hh, and the weight percent of the dosage and over dry bamboo pulp of every kind of enzyme is respectively
0.32 ‰, 0.45 ‰, 0.35 ‰, 0.40 ‰, 0.67 ‰ and 0.56 ‰;When heating and heat preservation, stainless cylinder of steel in air-tight state and
Internal pressure is 1MPa.
After above-mentioned processing is fully completed, product is put into press machine and does drainage processing, while being compressed into a set pattern
The squares of lattice and packing, removal, drying, storage.
Embodiment 3
A kind of technique for making paper grade (stock) bamboo pulp using fresh bamboo as raw material activity legal system, operating procedure are as follows:
(1) it cuts bamboo: being 5 years by bamboo age and cut down activity fresh bamboo of the time no more than 48h and clean, obtain length 1- after cutting
The bamboo section of 4m;
(2) fragment: bamboo section is subjected to fragment and obtains the bamboo chip that width is not more than 40mm;
(3) super-pressure classification rolls: bamboo chip is placed in roll rolling points six grades and is rolled, the grinding pressure point of level-one to six grades
Not are as follows: 35MPa, 45MPa, 50MPa, 55MPa, 60MPa, 70MPa, classification roll in gap between milling roller at different levels it is as follows:
Level-one 5mm, second level 3mm, three-level 1.8mm, level Four 1.2mm, Pyatyi 0.5mm, six grades of 0.5mm roll roller diameter and are 800mm, grind
Pressure speed is 50m/min;
(4) thread rolling: the bamboo fiber bundle that super-pressure classification rolls is placed in thread rolling machine plus water makes bamboo fiber bundle
Weight percent be 5%, thread rolling is carried out while heating later;Heating temperature is no more than 90 DEG C;Individual fibers are born
Grinding pressure no more than 10N, effective roller compaction process stroke 100-250mm, finally obtain diameter 0.03-0.1mm, length 0.5-
The bamboo fibre of 5mm;
(5) primary filtering squeezes: the bamboo pulp containing a large amount of fibers after thread rolling is first used to the stainless steel filter screen of 50 mesh
Filtering squeezes to obtain the initial filter bamboo pulp that water content is no more than 50% again;
(6) secondary filter squeezes: heating stirring into initial filter bamboo pulp plus after water, and amount of water is the three of initial filter bamboo pulp weight
Times, heating temperature is 60 DEG C, the mixing time position 2h of the over dry initial filter bamboo pulp of every 500Kg, first uses the stainless steel of 40 mesh later
Filter screen filtration, then high-pressure extrusion is carried out, the pressure of high-pressure extrusion is 65MPa, finally obtains water content again not higher than 39%
Filter bamboo pulp;It squeezes and completes to secondary filter from raw bamboo felling, total time 65h;
(7) biological enzyme bating relieves: will filter bamboo pulp again and be placed in stainless cylinder of steel and be heated to 63 DEG C, and be cooled to after keeping the temperature 1h
42 DEG C, by Endocellulase, heat-resistant alpha-amylase, beta-glucosidase, polygalacturonase, medium temperature amylase and liquid
Change type amylase, which is added in stainless cylinder of steel, stirs 1.5h, and the weight percent of the dosage and over dry bamboo pulp of every kind of enzyme is respectively
0.32 ‰, 0.45 ‰, 0.35 ‰, 0.40 ‰, 0.67 ‰ and 0.56 ‰;When heating and heat preservation, stainless cylinder of steel in air-tight state and
Internal pressure is 1.8MPa.
After above-mentioned processing is fully completed, product is put into press machine and does drainage processing, while being compressed into a set pattern
The squares of lattice and packing, removal, drying, storage.
Embodiment 4
A kind of technique for making paper grade (stock) bamboo pulp using fresh bamboo as raw material activity legal system, operating procedure are as follows:
(1) it cuts bamboo: being 7 years by bamboo age and cut down activity fresh bamboo of the time no more than 48h and clean, obtain length 1- after cutting
The bamboo section of 4m;
(2) fragment: bamboo section is subjected to fragment and obtains the bamboo chip that width is not more than 40mm;
(3) super-pressure classification rolls: bamboo chip is placed in roll rolling points six grades and is rolled, the grinding pressure point of level-one to six grades
Not are as follows: 15MPa, 25MPa, 35MPa, 60MPa, 160MPa, the gap between milling rollers at different levels are as follows: level-one 5mm, second level 4mm,
Three-level 1.8mm, level Four 1mm, Pyatyi 1mm, six grades of 0.3mm, roll roller diameter be 1500mm, rolling speed 40m/min;
(4) thread rolling: the bamboo fiber bundle that super-pressure classification rolls is placed in thread rolling machine plus water makes bamboo fiber bundle
Weight percent be 30%, thread rolling is carried out while heating later;Heating temperature is no more than 90 DEG C;Individual fibers are born
Grinding pressure no more than 10N, effective roller compaction process stroke 100-250mm, finally obtain diameter 0.03-0.1mm, length 0.5-
The bamboo fibre of 5mm;
(5) primary filtering squeezes: the bamboo pulp containing a large amount of fibers after thread rolling is first used to the stainless steel filter screen of 30 mesh
Filtering squeezes to obtain the initial filter bamboo pulp of water content 45% again;
(6) secondary filter squeezes: heating stirring into initial filter bamboo pulp plus after water, and amount of water is the two of initial filter bamboo pulp weight
Times, heating temperature is 90 DEG C, and the mixing time of the over dry initial filter bamboo pulp of every 500Kg is 1.5h, first stainless using 60 purposes later
Steel filter screen filtration, then high-pressure extrusion is carried out, the pressure of high-pressure extrusion is 60MPa, and finally obtain water content 40% filters bamboo again
Slurry;It squeezes and completes to secondary filter from raw bamboo felling, total time 70h;
(7) biological enzyme bating relieves: will filter bamboo pulp again and be placed in stainless cylinder of steel and be heated to 65 DEG C, and be cooled to after keeping the temperature 1h
45 DEG C, by Endocellulase, heat-resistant alpha-amylase, beta-glucosidase, polygalacturonase, medium temperature amylase and liquid
Change type amylase, which is added in stainless cylinder of steel, stirs 1h, and the weight percent of the dosage and over dry bamboo pulp of every kind of enzyme is respectively
0.32 ‰, 0.45 ‰, 0.35 ‰, 0.40 ‰, 0.67 ‰ and 0.56 ‰;When heating and heat preservation, stainless cylinder of steel in air-tight state and
Internal pressure is 1.5MPa.
After above-mentioned processing is fully completed, product is put into press machine and does drainage processing, while being compressed into a set pattern
The squares of lattice and packing, removal, drying, storage.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Within mind and principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (10)
1. a kind of technique for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, characterized by the following steps:
(1) it cuts bamboo: bamboo section will be obtained after the cleaning of fresh bamboo wood, cutting;
(2) fragment: bamboo section is subjected to fragment and obtains bamboo chip;
(3) super-pressure classification rolls: bamboo chip being placed in classification in roll rolling and is rolled, the classification is rolled grinds including four to six grades
Pressure, grinding pressure at different levels are gradually increased;
(4) thread rolling: the bamboo fiber bundle that super-pressure classification rolls is placed in thread rolling machine and carries out thread rolling;
(5) primary filtering squeezes: the bamboo pulp containing a large amount of fibers after thread rolling first being carried out physical filtering and squeezes to obtain initial filter again
Bamboo pulp;
(6) secondary filter squeezes: sequentially carrying out physical filtering into initial filter bamboo pulp plus after water after heating stirring again and secondary squeezes
Pressure, then bamboo pulp is filtered, it squeezes and completes to secondary filter from raw bamboo felling, total time is no more than 72h;
(7) biological enzyme bating relieves.
2. the technique according to claim 1 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: institute
The fresh bamboo of activity that fresh bamboo wood is 3 <bamboo age≤7 and cuts down the time no more than 48h is stated, obtains the bamboo section of length 1-4m after cutting bamboo,
The bamboo chip that width is not more than 40mm is obtained after fragment.
3. the technique according to claim 1 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: institute
State classification roll in gap between milling roller at different levels it is as follows: level-one: 4-6mm, second level: 2-4mm, three-level: 1.5-2mm, level Four:
1-1.5mm, Pyatyi: 0.5-1mm, six grades: 0-0.5mm, it is described roll roller diameter be 200-1500mm, rolling speed 8-50m/
min。
4. the technique according to claim 3 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: one
The grinding pressure of grade to Pyatyi is not more than 60MPa, six grades of grinding pressure 70-160MPa.
5. the technique according to claim 1 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: rub with the hands
When silk, the bamboo fiber bundle that classification rolls is placed in after adding water in thread rolling machine and carries out thread rolling while heating, after adding water
The weight percent of bamboo fiber bundle is 5-50%, and heating temperature is no more than 90 DEG C.
6. the technique according to claim 5 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: rub with the hands
When silk, the grinding pressure that individual fibers are born obtains straight no more than 10N, the stroke 100-250mm of effective roller compaction process after thread rolling
The bamboo fibre of diameter 0.03-0.1mm, length 0.5-5mm.
7. the technique according to claim 1 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: two
When secondary filtering squeezes, amount of water is not less than twice of initial filter bamboo pulp weight, and heating temperature is 40-90 DEG C, at the beginning of the over dry of every 500Kg
The mixing time for filtering bamboo pulp is not less than 1.5h.
8. the technique according to claim 1 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that: raw
The concrete operations that object enzyme bating relieves are as follows: bamboo pulp will be filtered again to be placed in stainless cylinder of steel and be heated to 60-65 DEG C, cooling after heat preservation 1h
To 40-45 DEG C, by Endocellulase, heat-resistant alpha-amylase, beta-glucosidase, polygalacturonase, medium temperature amylase
And liquefying amylase is added in stainless cylinder of steel and stirs at least 1h, the weight percent score of the dosage and over dry bamboo pulp of every kind of enzyme
It Wei 0.32 ‰, 0.45 ‰, 0.35 ‰, 0.40 ‰, 0.67 ‰ and 0.56 ‰;When heating and heat preservation, stainless cylinder of steel is in sealed shape
State and inside pressure be lower than 2MPa.
9. the technique according to claim 1-8 for making paper grade (stock) bamboo pulp using fresh bamboo as raw material activity legal system, special
Sign is: primary filtering, which squeezes, is first filtered using the stainless steel filter screen of 30-70 mesh, then is squeezed;Secondary filter squeezes first
It is filtered using the stainless steel filter screen of 40-60 mesh, then carries out high-pressure extrusion, the pressure of the high-pressure extrusion is not less than 60MPa.
10. the technique according to claim 9 for making paper grade (stock) bamboo pulp as raw material activity legal system using fresh bamboo, it is characterised in that:
The initial filter bamboo pulp water content that primary filtering obtains after squeezing is no more than 55%, and it is aqueous that secondary filter obtained after squeezing filters bamboo pulp again
Amount is not higher than 42%.