CN109811559A - The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric - Google Patents
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric Download PDFInfo
- Publication number
- CN109811559A CN109811559A CN201910004980.5A CN201910004980A CN109811559A CN 109811559 A CN109811559 A CN 109811559A CN 201910004980 A CN201910004980 A CN 201910004980A CN 109811559 A CN109811559 A CN 109811559A
- Authority
- CN
- China
- Prior art keywords
- fabric
- imitative
- spins
- knitted fabric
- fibre spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the production methods that a kind of pyrus nivalis spins imitative bast fibre spinning knitted fabric, belong to technical field of textile fabric.The production method that pyrus nivalis of the invention spins imitative bast fibre spinning knitted fabric includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → pre-treatment refining → washing → heating dyeing → heat preservation → cooling row pressure → to sample → reduction cleaning → soft treatment → cloth outputting → dehydration → shaping and drying → moisture absorbable and breathable finishing → antistatic finish → inspection → finished product, wherein the fabric is the fabric that terylene and modified dacron (CDP) interweave, heating rate when dyeing is 0.8-1.2 DEG C/min, dyeing temperature is 118-122 DEG C, keeps the temperature 18-22min.Pyrus nivalis produced by the present invention spins the shortcomings that imitative bast fibre spinning knitted fabric overcomes coarse feel existing for natural ramie fiber fabric, poor color fastness, creases easily simultaneously, and properties reach even better than natural ramie fiber fabric.
Description
Technical field
The invention belongs to technical field of textile fabric, and in particular to a kind of production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric.
Background technique
The advantage that flaxen fiber has other fibers to hardly match, such as have good moisture absorption dissipate drenched airway dysfunction, feel nice and cool it is well-pressed,
Quality is light, electrostatic is few, fabric is not easy to pollute, tone is soft generous, rough, but there is also following disadvantages: feel is coarse, wears not
It is smooth, comfort is poor has prodding and itching feeling, creases easily, poor color fastness, while flaxen fiber cost of material itself is high, and dyeing and finishing technology is multiple
Miscellaneous, expensive, finished product cloth price is also more expensive, therefore market in urgent need is cheap, and appearance and wears performance can be replaced
For the imitative ramie product of natural ramie fiber fabric.
Summary of the invention
A kind of production side of imitative bast fibre spinning knitted fabric of pyrus nivalis spinning is provided the purpose of the present invention is overcome the deficiencies in the prior art
Method, the pyrus nivalis spin the characteristic that imitative bast fibre spinning knitted fabric not only has natural ramie fiber, also have good flexibility and color fastness.
The present invention adopts the following technical scheme:
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → preceding place
Reason refining → washing → heating dyeing → heat preservation → cooling row pressure → to sample → reduction cleaning → soft treatment → cloth outputting → dehydration
→ shaping and drying → moisture absorbable and breathable finishing → antistatic finish → inspection → finished product, wherein the fabric is terylene and modified dacron
(CDP) fabric to interweave, heating rate when dyeing are 0.8-1.2 DEG C/min, and dyeing temperature is 118-122 DEG C, keep the temperature 18-
22min。
Further, during the reduction cleaning, be added according to watermeter following component: sodium hydrosulfite 3-5g/L,
Soda ash 0.5-0.85g/L, detergent 2-15g/L.
Further, dye liquor includes following component according to fabric weight meter when the dyeing: disperse dyes 1-5%,
Dye of positive ion 1-3%, anhydrous sodium sulphate 0.5-3%, Disperse Leveler 0.5-3% contaminate on warm type disperse dyes in dyeing
Dye polyester, using dye modified dacron dyestuff on the dye of positive ion.
Further, the following component according to fabric weight meter: amino silicone softener is added when the soft treatment
0.5-5%.
Further, the amino silicone softener is amino silicone softener TF-402.
Further, the following component according to fabric weight meter is added when the moisture absorbable and breathable finishing: moisture absorbing and sweat releasing is whole
Manage agent 1-3%.
Further, the moisture control agent is moisture control agent TF-620.
Further, the following component according to fabric weight meter: antistatic agent is added in the antistatic finish step
0.5-3%.
Further, the antistatic agent is non-ionic antistatic agent TF-480.
Further, the rate of temperature fall when cooling row pressure is 0.7-0.9 DEG C/min.
The present invention, as fabric raw material, utilizes two kinds using cheap modified dacron (CDP) and terylene intertexture fabric
The larger feature of fiber dyeing performance difference, by dye selection, dyeing and finishing technology improve, assign article in two kinds of fibers not
Same form and aspect, make cloth cover random color point occur, and appearance seems to achieve the effect that natural ramie fiber textile.Simultaneously by soft
Soft, moisture absorbing and sweat releasing, antistatic final finishing make fabric of the present invention rich in distinctive ventilative, the nice and cool, antistatic performance of linen, also
Overcome coarse feel existing for flaxen fiber fabric, prodding and itching feeling, poor color fastness, the shortcomings that creasing easily, thus make it is of the invention at
The natural linen fabric of the substitution that product cloth can mix the spurious with the genuine in appearance, it is fine that inherent properties reach even better than natural fiber crops
Fabric is tieed up, it, can be very since the garment material appearance of the imitative Ramie Noil Products of pyrus nivalis of the present invention spinning is beautiful, feel is unique, comfortable and easy to wear
The good needs for meeting client are suitable for high-grade men and women's summer clothes, housing, easy dress, trousering etc., in market by client's
Favor extensively.
There is colorful point effect to reach cloth cover, raw material need to select the biggish double conjugate fibers of dyeability difference,
So that occurring two kinds of tones after two kinds of stock-dyes, to obtain beautiful natural point effect.Double groups provided in the market
There are many fabric that condensating fiber interweaves, and only terylene/modified dacron (CDP) intertexture fabric can achieve said effect, the reason is as follows that:
First, two kinds of fiber dyeing performance difference are larger, and polyester fiber obtains dark coloured light, modified polyester fibre with disperse dyeing
Only to paint to the dye of positive ion, the dye of positive ion obtains that color ratio is more bright-coloured, as the light color for setting off dominant hue in two-color effect, with
The terylene tone of disperse dyes is contrasted, and cloth cover is easy to produce the unique random color point effect of color flaxen fiber.Second, Modified Polyester
The surface area of synthetic fibre is small and concave-convex sense is strong, and the fabric cloth cover sense after interweaving with terylene is coarse and has the distinctive rough well-pressed wind of flaxen fiber
Lattice.
In addition, the improvement of dyeing is also more crucial, it is necessary first to consider the dyestuff for being suitble to two kinds of fibers to dye simultaneously,
Modified dacron is contaminated on the CD dye of positive ion can ensure the color fastness after bright in colour and dye, considered when dye polyester select for
Modified dacron is protected not to be hydrolyzed, therefore dyeing temperature should be controlled at 118-122 DEG C, therefore using middle warm nature disperse dyes as terylene
Dyestuff can obtain deeper color in the sufficiently upper dye of 120 DEG C of temperature, also can protect well crossed fiber not by high-temperature water
Solution.
The sufficiently upper dye of dyestuff to ensure two kinds of crossed fibers, it is necessary to extend the heating-up time, with the liter of 0.8-1.2 DEG C/min
Warm rate can fully ensure that the different upper dye temperature of two kinds of fibers and longer upper dye time, obtain uniform cloth face color.Together
When be the damage for preventing high temperature to modified polyester fibre, therefore holding temperature is 118-122 DEG C, soaking time 18-22min.
Since the fiber rigidity of intertexture fabric of the invention is strong, two kinds of fiber heat-shrinkable difference are big, to prevent fast cooling from generating
Cloth cover gauffer, therefore rate of temperature fall need to be reduced to 0.7-0.9 DEG C/min.
After the completion of dyeing, then final finishing is carried out to fabric, to reach higher dyefastness, needs to carry out after dyeing thorough
Reduction cleaning carries out reduction cleaning using sodium hydrosulfite, soda ash, detergent, thoroughly to wash away cloth cover loose colour, so that fabric is each
Item fastness reaches 3-4 grades, and some fastness can reach 4 or more, much higher than the fastness after natural ramie fiber dyeing；Reduction cleaning is dry
Amino silicone soft finish is carried out after net, assigns the feel of cloth cover soft comfortable, and moisture absorbing and sweat releasing is carried out when being formed after drying and is resisted quiet
Electricity arranges, and the fabric that makes that treated is provided with the unique moisture absorption of natural ramie fiber and dissipates that wet, ventilative, not personal and dress of perspiring is nice and cool
Comfortable characteristic.By the research and development of above-mentioned technique, the pyrus nivalis that can produce the high-quality for being enough to mix the spurious with the genuine spins imitative flax spinning
Fabric.
Compared with the prior art, the present invention has the following beneficial effects:
First: the present invention is refined using terylene and modified dacron intertexture fabric by fabric debatching → cloth feeding → pre-treatment
→ washing → dyeing → heat preservation → cooling row pressure → to sample → reduction cleaning → soft treatment → cloth outputting → dehydration → shaping and drying
The techniques such as → moisture absorbable and breathable finishing → antistatic finish, make fabric cloth cover random color point occur, and appearance reaches natural ramie fiber spinning
The effect of fabric；
Second: pyrus nivalis produced by the present invention spins imitative bast fibre spinning knitted fabric and overcomes feel existing for natural ramie fiber fabric simultaneously
Coarse, poor color fastness, the shortcomings that creasing easily, properties reach even better than natural ramie fiber fabric, fastness to soaping and reach
Reach 3-4 grades of (GB/T8427-2008), dry fastnesses to 3-4 grades (GB/T3921-2008), color fastness to light and reaches 3-4
Grade, fastness to wet rubbing reach 3-4 grades, water absorption rate reaches 100% (GB/T21655.1-2008), evaporation rate is greater than 0.2g/h
(GB/T21655.1-2008)。
Specific embodiment
Below by specific embodiment, invention is further described in detail, but those skilled in the art will manage
Solution, the following example is merely to illustrate the present invention, and should not be taken as limiting the scope of the invention.
Embodiment 1
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → preceding place
Reason refining → washing → heating dyeing (dye liquor includes the following component according to fabric weight meter when dyeing: disperse dyes 3.5%,
The dye of positive ion 1.5%, anhydrous sodium sulphate 2.2%, Disperse Leveler 1.5% contaminate terylene on warm type disperse dyes in dyeing
Dyestuff, using modified dacron dyestuff is contaminated on the dye of positive ion, heating rate when dyeing is 1 DEG C/min, dyeing temperature 120
DEG C, keep the temperature 20min.) → heat preservation → cooling row pressure (rate of temperature fall is controlled in 0.8 DEG C/min) → to (reduction of sample → reduction cleaning
In cleaning process, the following component according to watermeter: sodium hydrosulfite 4g/L, soda ash 0.7g/L, detergent 10g/L is added) → soft
Processing (the following component according to fabric weight meter: amino silicone softener TF-402 2.5% is added when soft treatment) → cloth outputting →
(the following component according to fabric weight meter: moisture absorption is added in dehydration → shaping and drying → moisture absorbable and breathable finishing when moisture absorbable and breathable finishing
Absorbable and breathable finishing agent TF-620 1.5%.(antistatic finish step is added according to fabric weight meter such as the following group for) → antistatic finish
Point: non-ionic antistatic agent TF-480 1.5%.) → inspection → finished product, wherein the fabric is terylene and modified dacron (CDP)
The fabric of intertexture.
The fastness to soaping that pyrus nivalis obtained by the present embodiment spins imitative bast fibre spinning knitted fabric finished product reaches 3-4 grades of (GB/T3921-
2008), color fastness to light reach 3-4 grades (GB/T8427-2008), dry fastness reach 3-4 grades, fastness to wet rubbing reach 3-
4 grades, water absorption rate reach 100% (GB/T21655.1-2008), evaporation rate be greater than 0.2g/h (GB/T21655.1-2008).
Embodiment 2
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → preceding place
Reason refining → washing → heating dyeing (dye liquor includes the following component according to fabric weight meter when dyeing: disperse dyes 4.5%,
The dye of positive ion 2.5%, anhydrous sodium sulphate 1.7%, Disperse Leveler 2.5% contaminate terylene on warm type disperse dyes in dyeing
Dyestuff, using modified dacron dyestuff is contaminated on the dye of positive ion, heating rate when dyeing is 1.1 DEG C/min, dyeing temperature 119
DEG C, keep the temperature 19min.) → heat preservation → cooling row pressure (rate of temperature fall is controlled in 0.7-0.9 DEG C/min) → to sample → reduction cleaning
(during reduction cleaning, the following component according to watermeter: sodium hydrosulfite 3.5g/L, soda ash 0.6g/L, detergent 3g/L is added)
→ soft treatment (the following component according to fabric weight meter: amino silicone softener TF-402 1.5% is added when soft treatment) →
Cloth outputting → dehydration → shaping and drying → moisture absorbable and breathable finishing (is added according to fabric weight meter when moisture absorbable and breathable finishing such as the following group
Point: moisture control agent TF-620 2%.(antistatic finish step is added according to fabric weight meter for) → antistatic finish
Following component: non-ionic antistatic agent TF-480 2%.) → inspection → finished product, wherein the fabric is terylene and modified dacron
(CDP) fabric to interweave.
The fastness to soaping that pyrus nivalis obtained by the present embodiment spins imitative bast fibre spinning knitted fabric finished product reaches 3-4 grades of (GB/T3921-
2008), color fastness to light reach 3-4 grades (GB/T8427-2008), dry fastness reach 3-4 grades, fastness to wet rubbing reach 3-
4 grades, water absorption rate reach 100% (GB/T21655.1-2008), evaporation rate be greater than 0.2g/h (GB/T21655.1-2008).
Embodiment 3
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → preceding place
Managing refining → washing → heating dyeing, (dye liquor includes the following component according to fabric weight meter when dyeing: disperse dyes 1%, sun
Ionic dye 1%, anhydrous sodium sulphate 0.5%, Disperse Leveler 0.5% contaminate dye polyester on warm type disperse dyes in dyeing,
Using modified dacron dyestuff is contaminated on the dye of positive ion, heating rate when dyeing is 0.8 DEG C/min, and dyeing temperature is 118 DEG C, is protected
Warm 22min.) → heat preservation → cooling row pressure (rate of temperature fall is controlled in 0.7 DEG C/min) → to sample → reduction cleaning (reduction cleaning mistake
The following component according to watermeter: sodium hydrosulfite 3g/L, soda ash 0.5g/L, detergent 2g/L is added in Cheng Zhong) → soft treatment is (soft
The following component according to fabric weight meter: amino silicone softener TF-402 0.5% is added when supple-settlement) → cloth outputting → dehydration →
(the following component according to fabric weight meter is added when moisture absorbable and breathable finishing: moisture absorbing and sweat releasing is whole for shaping and drying → moisture absorbable and breathable finishing
Manage agent TF-620 1%.) → antistatic finish (antistatic finish step be added according to fabric weight meter following component: it is non-from
Sub- antistatic agent TF-4800.5%.) → inspection → finished product, wherein the fabric is the base that terylene and modified dacron (CDP) interweave
Cloth.
The fastness to soaping that pyrus nivalis obtained by the present embodiment spins imitative bast fibre spinning knitted fabric finished product reaches 3-4 grades of (GB/T3921-
2008), color fastness to light reach 3-4 grades (GB/T8427-2008), dry fastness reach 3-4 grades, fastness to wet rubbing reach 3-
4 grades, water absorption rate reach 100% (GB/T21655.1-2008), evaporation rate be greater than 0.2g/h (GB/T21655.1-2008).
Embodiment 4
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → preceding place
Managing refining → washing → heating dyeing, (dye liquor includes the following component according to fabric weight meter when dyeing: disperse dyes 5%, sun
Ionic dye 3%, anhydrous sodium sulphate 3%, Disperse Leveler 3% contaminate dye polyester on warm type disperse dyes in dyeing, use
Modified dacron dyestuff is contaminated on the dye of positive ion, heating rate when dyeing is 1.2 DEG C/min, and dyeing temperature is 122 DEG C, heat preservation
18min.) → heat preservation → cooling row pressure (rate of temperature fall is controlled in 0.9 DEG C/min) → to sample → reduction cleaning (reduction cleaning process
In, the following component according to watermeter: sodium hydrosulfite 5g/L, soda ash 0.85g/L, detergent 15g/L is added) → soft treatment is (soft
The following component according to fabric weight meter: amino silicone softener TF-402 5% is added when supple-settlement) → cloth outputting → dehydration → fixed
(the following component according to fabric weight meter: moisture absorbable and breathable finishing is added in type drying → moisture absorbable and breathable finishing when moisture absorbable and breathable finishing
Agent TF-620 3%.(the following component according to fabric weight meter: nonionic is added in antistatic finish step for) → antistatic finish
Antistatic agent TF-4803%.) → inspection → finished product, wherein the fabric is the fabric that terylene and modified dacron (CDP) interweave.
The fastness to soaping that pyrus nivalis obtained by the present embodiment spins imitative bast fibre spinning knitted fabric finished product reaches 3-4 grades of (GB/T3921-
2008), color fastness to light reach 3-4 grades (GB/T8427-2008), dry fastness reach 3-4 grades, fastness to wet rubbing reach 3-
4 grades, water absorption rate reach 100% (GB/T21655.1-2008), evaporation rate be greater than 0.2g/h (GB/T21655.1-2008).
Embodiment 5
The production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, includes the following steps: fabric debatching → overflow dyeing machine cloth feeding → preceding place
Reason refining → washing → heating dyeing (dye liquor includes the following component according to fabric weight meter when dyeing: disperse dyes 5.1%,
The dye of positive ion 0.9%, anhydrous sodium sulphate 3.3%, Disperse Leveler 3.3% contaminate terylene on warm type disperse dyes in dyeing
Dyestuff, using modified dacron dyestuff is contaminated on the dye of positive ion, heating rate when dyeing is 0.7 DEG C/min, dyeing temperature 120
DEG C, keep the temperature 23min.) → heat preservation → cooling row pressure (rate of temperature fall is controlled in 0.8 DEG C/min) → to (reduction of sample → reduction cleaning
In cleaning process, the following component according to watermeter: sodium hydrosulfite 2.8g/L, soda ash 0.49g/L, detergent 14g/L is added) → soft
Supple-settlement (the following component according to fabric weight meter: amino silicone softener TF-402 0.4% is added when soft treatment) → cloth outputting
→ dehydration → shaping and drying → moisture absorbable and breathable finishing (is added the following component according to fabric weight meter: inhaling when moisture absorbable and breathable finishing
Wet absorbable and breathable finishing agent TF-620 0.8%.(antistatic finish step is added according to the as follows of fabric weight meter for) → antistatic finish
Component: non-ionic antistatic agent TF-480 3.1%.) → inspection → finished product, wherein the fabric is terylene and modified dacron
(CDP) fabric to interweave.
The fastness to soaping that pyrus nivalis obtained by the present embodiment spins imitative bast fibre spinning knitted fabric finished product reaches 3-4 grades of (GB/T3921-
2008), color fastness to light reach 3-4 grades (GB/T8427-2008), dry fastness reach 3-4 grades, fastness to wet rubbing reach 3-
4 grades, water absorption rate reach 100% (GB/T21655.1-2008), evaporation rate be greater than 0.2g/h (GB/T21655.1-2008).
Claims (10)
1. the production method that pyrus nivalis spins imitative bast fibre spinning knitted fabric, which comprises the steps of: fabric debatching → cloth feeding → preceding
Handle refining → washing → dyeing → heat preservation → cooling row pressure → to sample → reduction cleaning → soft treatment → cloth outputting → dehydration →
Shaping and drying → moisture absorbable and breathable finishing → antistatic finish → inspection → finished product, wherein the fabric is that terylene and modified dacron are handed over
The fabric knitted, heating rate when dyeing are 0.8-1.2 DEG C/min, and dyeing temperature is 118-122 DEG C, keep the temperature 18-22min.
2. the production method that pyrus nivalis according to claim 1 spins imitative bast fibre spinning knitted fabric, which is characterized in that the reduction cleaning
In the process, the following component according to watermeter: sodium hydrosulfite 3-5g/L, soda ash 0.5-0.85g/L, detergent 2-15g/L is added.
3. the production method that pyrus nivalis according to claim 1 spins imitative bast fibre spinning knitted fabric, which is characterized in that contaminated when the dyeing
Liquid includes the following component according to fabric weight meter: disperse dyes 1-5%, dye of positive ion 1-3%, anhydrous sodium sulphate 0.5-3%, being divided
Dissipate levelling agent 0.5-3%.
4. the production method that pyrus nivalis according to claim 1 spins imitative bast fibre spinning knitted fabric, which is characterized in that the soft treatment
When be added according to fabric weight meter following component: amino silicone softener 0.5-5%.
5. the production method that pyrus nivalis according to claim 4 spins imitative bast fibre spinning knitted fabric, which is characterized in that the amino silicone is soft
Soft dose is amino silicone softener TF-402.
6. the production method that pyrus nivalis according to claim 1 spins imitative bast fibre spinning knitted fabric, which is characterized in that the moisture absorbing and sweat releasing
The following component according to fabric weight meter: moisture control agent 1-3% is added when arrangement.
7. the production method that pyrus nivalis according to claim 6 spins imitative bast fibre spinning knitted fabric, which is characterized in that the moisture absorbing and sweat releasing
Finishing agent is moisture control agent TF-620.
8. the production method that pyrus nivalis according to claim 1 spins imitative bast fibre spinning knitted fabric, which is characterized in that described antistatic whole
Step addition is managed according to the following component of fabric weight meter: antistatic agent 0.5-3%.
9. the production method that pyrus nivalis according to claim 8 spins imitative bast fibre spinning knitted fabric, which is characterized in that the antistatic agent
For non-ionic antistatic agent TF-480.
10. the production method that pyrus nivalis according to claim 1 spins imitative bast fibre spinning knitted fabric, which is characterized in that the cooling row
Rate of temperature fall when pressure is 0.7-0.9 DEG C/min.