CN109811108A - 一种含轻稀土金属的孕育剂及其制备方法 - Google Patents
一种含轻稀土金属的孕育剂及其制备方法 Download PDFInfo
- Publication number
- CN109811108A CN109811108A CN201910212032.0A CN201910212032A CN109811108A CN 109811108 A CN109811108 A CN 109811108A CN 201910212032 A CN201910212032 A CN 201910212032A CN 109811108 A CN109811108 A CN 109811108A
- Authority
- CN
- China
- Prior art keywords
- rare earth
- inovulant
- earth metal
- light rare
- containing light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含轻稀土金属的孕育剂及其制备方法,包括重量百分计的硅65‑75%,铈0.8‑5%,锰0.2‑3%,铝0.4‑2.6%,钙0.8‑3%,铁15‑30%。本发明含轻稀土金属的孕育剂通过将铈元素和硅、锰、铝、铁元素复合,发挥各元素自身孕育能力的同时,进一步进行协同作用,中和有害元素的作用,产生稳定的金属间化合物,且对硫和氧有强亲和力,从而生成高度稳定的氧化物、硫化物和硫氧化物。在整个凝固区间内,此类含铈的化合物都有助于改善生核条件,有益于孕育处理过程;能够降低多元合金熔点便于在铁液中扩散和吸收,细化奥氏体枝晶,提高铸铁强度。
Description
技术领域
本发明涉及一种含轻稀土金属的孕育剂及其制备方法,属于铸造技术领域。
背景技术
铸铁是含碳大于2.1%的铁碳合金,它是将铸造生铁(部分炼钢生铁)在炉中重新熔化,并加进铁合金、废钢、回炉铁调整成分而得到。与生铁区别是铸铁是二次加工,大都加工成铸铁件。铸铁件具有优良的铸造性可制成复杂零件,一般有良好的切削加工性。另外具有耐磨性和消震性良好,价格低等特点。
目前,提高灰铸铁的性能,常采取下列几种措施:
(1)化学成分的合理选配
灰铸铁的含碳量大多在2.6%~3.6%,含硅量在1.2%~3.0%,碳硅都是强烈地促进石墨化的元素,可用碳当量CE来说明它们对灰铸铁金相组织和力学性能的影响。提高碳当量促使石墨化变粗,数量增多,强度和硬度下降。降低碳当量可减少石墨数量,细化石墨,增加初析奥氏体枝晶,从而是提高灰铸铁力学性能时常采取的措施。但降低碳当量会导致铸造性能降低,铸件断面敏感性增大,铸件内应力增加,硬度上升加工困难等问题,因此必须辅以其它的措施。
(2)改变炉料组成
灰铸铁的炉料一般由新生铁、废钢、回炉料和铁合金等组成。加入废钢,降低铁液含碳量,可以提高灰铸铁的力学性能,在生不同牌号灰铸铁时将加入不同比例的废钢作为保证材质性能的一个控制指标。近年来由于工业发达国家废钢供应十分充裕,价格也远较新生铁便宜,于是发展了不用新生铁而只用废钢和回炉料,用增碳方法调节碳量的合成铸铁及其冶炼方法。合成铸铁不仅能降低成本,而且在同样的化学成分下能获得更好的力学性能。
(3)、铁液过热处理
温度、化学成分、纯净度是铁液的三项主要冶金指标,而铁液温度的高低又直接影响到成分和纯净度。铁液温度的提高有利于提高流动性、获得健全铸件,降低废品率,而且在一定范围内有利于力学性能的改善。
(4)、铁液孕育处理
孕育处理就是在铁液进入铸件型腔前,把孕育剂附加到铁液中以改变铁液的冶金状态,从而改善铸铁的显微组织和性能,而这些性能的改善并不能由于加入孕育剂后铁液化学成分的变化来解释。随着孕育剂、孕育方法的改进,孕育处理已是现代铸造生产中提高铸铁性能的重要手段。
现有的孕育处理存在如下缺点:1、机械混合的孕育剂成分不均匀,存在成分偏析,生产出的铸件性能不一致;2、混合孕育剂的实际使用效果往往不如单独使用一种孕育剂的效果明显,不能很好的发挥出孕育剂中元素应有的作用;3、较高的钙含量和铝含量对铁水的孕育效果较差,而且钙和铝有强烈的还原作用,与铁水中的硫和氧元素反应形成氧化渣,影响铁水质量。
发明内容
本发明所要解决的技术问题是针对现有技术的不足,提供一种够防止有效元素偏析,有效发挥稀土金属孕育效果的铸铁用孕育剂。
为了解决上述技术问题,本发明采取的技术方案如下:
一种含轻稀土金属的孕育剂,包括以下重量百分比的组分:
硅 65-75%;
铈 0.8-5%;
锰 0.2-3%;
铝 0.4-2.6%;
钙 0.8-3%;
铁 15-30%。
其中,铈作为轻稀土金属,可以中和有害元素的作用,产生稳定的金属间化合物,且对硫和氧有强亲和力,从而生成高度稳定的氧化物、硫化物和硫氧化物。在整个凝固区间内,此类含铈的化合物都有助于改善生核条件,有益于孕育处理过程。
锰锰元素的加入能够降低多元合金熔点便于在铁液中扩散和吸收,细化奥氏体枝晶,提高铸铁强度。
具体地,所述的硅、铁元素来自硅铁合金,其中,硅含量为75~85%,铁含量为20~25%。
所述的铈元素来自金属铈。
所述的锰元素来自金属锰。
所述的铝元素来自金属铝。
所述的钙元素来自金属钙。
本发明还提供上述含轻稀土金属的孕育剂的制备方法,包括如下步骤:
(1)按照比例称取硅铁合金、金属铈、金属锰、金属铝和金属钙,并破碎成小块;
(2)将破碎的原料放入中频感应电炉进行熔炼,熔炼温度为1300-1400℃,时间为15~25min,熔炼过程中需要不断的搅拌,使得原料充分的混合;
(3)熔炼结束后,将料浆浇注至充有惰性保护气体的水冷模型中;
(4)铸锭冷却后破碎制粒即得。
有益效果:
本发明含轻稀土金属的孕育剂通过将铈元素和硅、锰、铝、铁元素复合,发挥各元素自身孕育能力的同时,进一步进行协同作用,中和有害元素的作用,产生稳定的金属间化合物,且对硫和氧有强亲和力,从而生成高度稳定的氧化物、硫化物和硫氧化物。在整个凝固区间内,此类含铈的化合物都有助于改善生核条件,有益于孕育处理过程;能够降低多元合金熔点便于在铁液中扩散和吸收,细化奥氏体枝晶,提高铸铁强度。
具体实施方式
根据下述实施例,可以更好地理解本发明。
实施例1
该含轻稀土金属的孕育剂包括以下重量百分比的组分:
硅 70%;
铈 2%;
锰 1%;
铝 1.2%;
钙 1%;
铁 24.8%。
通过将硅铁合金(硅含量75~85%,铁含量20~25%)、金属铈、金属锰、金属铝和金属钙,并破碎成小块;然后放入中频感应电炉进行熔炼,熔炼温度为1300-1400℃,时间为15~25min,熔炼过程中需要不断的搅拌,使得原料充分的混合;熔炼结束后,将料浆浇注至充有惰性保护气体的水冷模型中;铸锭冷却后破碎制粒即得。
实施例2
该含轻稀土金属的孕育剂包括以下重量百分比的组分:
硅 65%;
铈 5%;
锰 3%;
铝 2.6%;
钙 3%;
铁 21.4%。
通过将硅铁合金(硅含量75~85%,铁含量20~25%)、金属铈、金属锰、金属铝和金属钙,并破碎成小块;然后放入中频感应电炉进行熔炼,熔炼温度为1300-1400℃,时间为15~25min,熔炼过程中需要不断的搅拌,使得原料充分的混合;熔炼结束后,将料浆浇注至充有惰性保护气体的水冷模型中;铸锭冷却后破碎制粒即得。
实施例3
该含轻稀土金属的孕育剂包括以下重量百分比的组分:
硅 75%;
铈 0.8%;
锰 0.2%;
铝 0.4%;
钙 0.8%;
铁 22.8%。
通过将硅铁合金(硅含量75~85%,铁含量20~25%)、金属铈、金属锰、金属铝和金属钙,并破碎成小块;然后放入中频感应电炉进行熔炼,熔炼温度为1300-1400℃,时间为15~25min,熔炼过程中需要不断的搅拌,使得原料充分的混合;熔炼结束后,将料浆浇注至充有惰性保护气体的水冷模型中;铸锭冷却后破碎制粒即得。
实施例4
将实施例1~3产品用于铸铁生产中,生产出的铸铁与常规工艺(不加孕育剂)生产的铸铁相比,可有效消除铸件微观疏松,降低硫氧化物,有助于改善生核条件,有益于孕育处理过程,细化奥氏体枝晶,制得的球墨铸铁具有很好的耐高温、耐腐性能,且具有很好的强度和韧性,综合性能好,具体参数见表1。
表1
项目 | 实施例1 | 实施例2 | 实施例3 | 常规工艺 |
珠光体含量% | 95.4 | 94.7 | 94.1 | 76.1 |
抗拉强度MPa | 312 | 305 | 301 | 253 |
硬度HB | 238 | 230 | 231 | 175 |
本发明提供了一种含轻稀土金属的孕育剂及其制备方法的思路及方法,具体实现该技术方案的方法和途径很多,以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。本实施例中未明确的各组成部分均可用现有技术加以实现。
Claims (7)
1.一种含轻稀土金属的孕育剂,其特征在于,包括以下重量百分比的组分:
硅65-75%;
铈0.8-5%;
锰0.2-3%;
铝0.4-2.6%;
钙0.8-3%;
铁15-30%。
2.根据权利要求1所述的含轻稀土金属的孕育剂,其特征在于,所述的硅、铁元素来自硅铁合金,其中,硅含量为75~85%,铁含量为20~25%。
3.根据权利要求1所述的含轻稀土金属的孕育剂,其特征在于,所述的铈元素来自金属铈。
4.根据权利要求1所述的含轻稀土金属的孕育剂,其特征在于,所述的锰元素来自金属锰。
5.根据权利要求1所述的含轻稀土金属的孕育剂,其特征在于,所述的铝元素来自金属铝。
6.根据权利要求1所述的含轻稀土金属的孕育剂,其特征在于,所述的钙元素来自金属钙。
7.权利要求1所述的含轻稀土金属的孕育剂的制备方法,其特征在于,包括如下步骤:
(1)按照比例称取硅铁合金、金属铈、金属锰、金属铝和金属钙,并破碎成小块;
(2)将破碎的原料放入中频感应电炉进行熔炼,熔炼温度为1300-1400℃,时间为15~25min,熔炼过程中需要不断的搅拌,使得原料充分的混合;
(3)熔炼结束后,将料浆浇注至充有惰性保护气体的水冷模型中;
(4)铸锭冷却后破碎制粒即得。