CN109810300A - A kind of resistance to dynamic ozone aging tire sidewall glue and preparation method thereof - Google Patents
A kind of resistance to dynamic ozone aging tire sidewall glue and preparation method thereof Download PDFInfo
- Publication number
- CN109810300A CN109810300A CN201910101789.2A CN201910101789A CN109810300A CN 109810300 A CN109810300 A CN 109810300A CN 201910101789 A CN201910101789 A CN 201910101789A CN 109810300 A CN109810300 A CN 109810300A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- aging
- glue
- resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of resistance to dynamic ozone aging sidewall rubbers, the characteristics of being stretched and be easy by ozone aging by flexion for a long time according to tire sidewall, in versatility rubber natural rubber, butadiene rubber, on the basis of butadiene-styrene rubber, the resistance to preferable chlorosulfonated polyethylene rubber of ozone ability is added, the resistance to preferable anti-aging agent 6PPD of the dynamic ozone aging and preferable antioxidant D TPD of suitable resistance to static ozone aging, ultraviolet absorbing agent UV-0 is added in sizing material, product ultraviolet absorbing agent UV-0 cooperation in rubber and chlorosulfonated polyethylene rubber is preferable, while in order to further increase the ozone-resistant aging property of the tire sidewall glue and reduce the cost of sizing material, it joined the high-tenacity butyl with significant ozone-resistant aging property and restore glue.
Description
Technical field
The present invention relates to a kind of tire sealants, and in particular to a kind of resistance to dynamic ozone aging tire sidewall glue and its preparation side
Method belongs to rubber processing techniques field.
Background technique
Ozone is exactly to crack to the erosion results for the rubber product that application centainly strains, these crackles eventually result in
The thorough failure of rubber product.Unlike other rubber products, it bears strength constantly and is constantly moving tire, and takes turns
Tire sidewall rubber is relatively thin, continual by flexion stretching action in motion process, so the present risen year by year in ozone content
It, it is easy to is by dynamic ozone aging.
The prior art is that a large amount of ozone-resistant anti-aging agent is added in tire sidewall glue, and operation in this way easilys lead to tire
During ozone and aging resistance, there is anti-aging agent and tire sidewall surface, especially rubber antioxidant protection wax is precipitated, energy is precipitated
Power is strong, causes tire sidewall to lose original color, influences Appcarance guality of tyres, so cannot go simply to guarantee sidewall
Ozone and aging resistance go that the anti-aging agent of resistance to ozone is largely added.
Summary of the invention
Place to overcome above-mentioned the deficiencies in the prior art, the present invention provides a kind of resistance to dynamic ozone aging tire sidewalls
Glue, it is natural in versatility rubber the characteristics of being stretched and be easy by ozone aging by flexion for a long time according to tire sidewall
On the basis of butadiene-styrene rubber, it is smelly that the preferable chlorosulfonated polyethylene rubber of resistance to ozone ability, resistance to dynamic is added in rubber, butadiene rubber
The preferable anti-aging agent 6PPD of oxygen aging and the preferable antioxidant D TPD of suitable resistance to static ozone aging, two kinds of anti-aging agents are taken
With keeping the aging effect of resistance to dynamic ozone of sizing material more preferable, and cooperate a small amount of protection wax and anti-aging agent TMQ and resistance to ozone ability
Preferably, the high-tenacity butyl that intensity is higher and price is lower restores glue, and rubber is under ultraviolet irradiation, the speed of ozone aging
Degree can more faster, and tellurian uitraviolet intensity is also gradually increasing at present, special thus that ultraviolet light is added in sizing material
Absorbent UV-0, the product ultraviolet absorbing agent UV-0 cooperation in rubber and chlorosulfonated polyethylene rubber preferably, have significant
Ageing-resistant performance.
The present invention is achieved through the following technical solutions: a kind of resistance to dynamic ozone aging tire sidewall glue, feature exist
In: each raw material and its substance number are as follows: natural rubber, 55 parts;Butadiene rubber, 40 parts;Butadiene-styrene rubber, 5 parts;Zinc oxide, 2.8
Part;SA, 2.0 parts;Sulphur, 1.2 parts;Accelerator NS, 1.5 parts;6PPD, 1.5-2 parts of anti-aging agent;TPD, 1-1.5 parts of antioxidant D;
TMQ, 1-2 parts of anti-aging agent;Protection wax, 1 part;Aromatic naphtha, 4.0 parts;Petropols, 3.0 parts;Chlorosulfonated polyethylene rubber, 7-10
Part;UV-0,1.5-2 parts of ultraviolet absorbing agent;N660 carbon black, 30 parts;N330 carbon black, 30 parts;High-tenacity butyl restores glue, 8-10
Part.
The preparation method of the resistance to dynamic ozone aging tire sidewall glue, it is characterised in that:
The preparation of step 1) masterbatch: use X (S) M-1.5L mixer, rotor speed 40r/min, hybrid technique and its add
Material sequence are as follows: natural rubber, butadiene rubber, butadiene-styrene rubber, high-tenacity butyl restore glue, chlorosulfonated polyethylene rubber, anti-aging agent
6PPD, anti-aging agent TMQ, zinc oxide, SA, antioxidant D TPD, protection wax, ultraviolet absorbing agent UV-0 → pressure floating weight (40s) →
N660 carbon black, N330 carbon black → pressure floating weight (100s) → aromatic naphtha, Petropols → pressure floating weight (70s) → dumping, dumping
127 DEG C of temperature;
The preparation of step 2 finished composition: XK-160 open mill, charging sequence are as follows: masterbatch → accelerator NS, sulphur → glue are used
Expect uniformly mixed, thin logical → sizing material slice.
Advantageous effects of the present invention: resistance to dynamic ozone aging tire sidewall glue prepared by the present invention has ageing-resistant performance
Excellent, inexpensive, after 6 months test phases, tire sidewall no cracking, also there is no point types to be cracked.
Specific embodiment
Below with reference to embodiment, the present invention will be further described.
Embodiment 1
A kind of resistance to dynamic ozone aging tire sidewall glue, each raw material and its substance number are as follows: natural rubber, 55 parts;Butadiene rubber,
40 parts;Butadiene-styrene rubber, 5 parts;Zinc oxide, 2.8 parts;SA, 2.0 parts;Sulphur, 1.2 parts;Accelerator NS, 1.5 parts;Anti-aging agent 6PPD,
1.5-2 part;TPD, 1-1.5 parts of antioxidant D;TMQ, 1-2 parts of anti-aging agent;Protection wax, 1 part;Aromatic naphtha, 4.0 parts;Petropols,
3.0 part;Chlorosulfonated polyethylene rubber, 7-10 part;UV-0,1.5-2 parts of ultraviolet absorbing agent;N660 carbon black, 30 parts;N330 charcoal
It is black, 30 parts;High-tenacity butyl restores glue, 8-10 parts.
The preparation method of the resistance to dynamic ozone aging tire sidewall glue:
The preparation of step 1) masterbatch: use X (S) M-1.5L mixer, rotor speed 40r/min, hybrid technique and its add
Material sequence are as follows: natural rubber, butadiene rubber, butadiene-styrene rubber, high-tenacity butyl restore glue, chlorosulfonated polyethylene rubber, zinc oxide,
SA, anti-aging agent 6PPD, anti-aging agent TMQ, protection wax, antioxidant D TPD, ultraviolet absorbing agent UV-0 → pressure floating weight (40s) →
N660 carbon black, N330 carbon black → pressure floating weight (100s) → aromatic naphtha, Petropols → pressure floating weight (70s) → dumping, dumping
127 DEG C of temperature;
The preparation of step 2 finished composition: XK-160 open mill, charging sequence are as follows: masterbatch → accelerator NS, sulphur → glue are used
Expect uniformly mixed, thin logical → sizing material slice.
Above-mentioned high-tenacity butyl restores the performance indicator of glue, as shown in table 1:
The performance indicator of 1 high-tenacity butyl of table recovery glue
The resistance to dynamic ozone aging tire sidewall glue of embodiment preparation, ozone test condition are as follows: 100pphm, 72h, 20% are drawn
It stretches, 50 DEG C;Test piece is intact after test, and the aging phenomena such as no cracking meet resistance to ozone requirement.
Tire is in outdoor carry out ozone test: choosing two 11.2-24-6R1 tires in outdoor carry out installation test, draws
Machine is First Tractor Co., Ltd.'s production, and two tires matching tractor rear-wheel, wherein A tire is normal sidewall rubber wheel
Tire, B tire are to test resistance to dynamic ozone aging tire sidewall rubber tire tire, and tractor is between October in May, 2018-in ozone
The biggish Yangtze River Delta Area of concentration carries out high-intensitive frequent operation, and after 6 months test phases, A tire sidewall goes out point
Type cracking, B tire sidewall no cracking.
Claims (2)
1. a kind of resistance to dynamic ozone aging tire sidewall glue, it is characterised in that: each raw material and its substance number are as follows: natural rubber,
55 parts;Butadiene rubber, 40 parts;Butadiene-styrene rubber, 5 parts;Zinc oxide, 2.8 parts;SA, 2.0 parts;Sulphur, 1.2 parts;Accelerator NS, 1.5
Part;6PPD, 1.5-2 parts of anti-aging agent;TPD, 1-1.5 parts of antioxidant D;TMQ, 1-2 parts of anti-aging agent;Protection wax, 1 part;Aromatic naphtha,
4.0 part;Petropols, 3.0 parts;Chlorosulfonated polyethylene rubber, 7-10 part;UV-0,1.5-2 parts of ultraviolet absorbing agent;N660 charcoal
It is black, 30 parts;N330 carbon black, 30 parts;High-tenacity butyl restores glue, 8-10 parts.
2. a kind of preparation method of resistance to dynamic ozone aging tire sidewall glue as described in claim 1, it is characterised in that:
The preparation of step 1) masterbatch: use X (S) M-1.5L mixer, rotor speed 40r/min, hybrid technique and its add
Material sequence are as follows: natural rubber, butadiene rubber, butadiene-styrene rubber, high-tenacity butyl restore glue, chlorosulfonated polyethylene rubber, anti-aging agent
The small powders such as 6PPD, anti-aging agent TMQ, antioxidant D TPD, ultraviolet absorbing agent UV-0, zinc oxide → pressure floating weight (40s) → N660
Carbon black, N330 carbon black → pressure floating weight (100s) → aromatic naphtha, Petropols → pressure floating weight (70s) → dumping, dump temperature
127℃;
The preparation of step 2 finished composition: XK-160 open mill, charging sequence are as follows: masterbatch → accelerator NS, sulphur → glue are used
Expect uniformly mixed, thin logical → sizing material slice.