CN109795041A - A kind of quartz pushrod cutting technique - Google Patents
A kind of quartz pushrod cutting technique Download PDFInfo
- Publication number
- CN109795041A CN109795041A CN201910073314.7A CN201910073314A CN109795041A CN 109795041 A CN109795041 A CN 109795041A CN 201910073314 A CN201910073314 A CN 201910073314A CN 109795041 A CN109795041 A CN 109795041A
- Authority
- CN
- China
- Prior art keywords
- quartz pushrod
- glutinous agent
- parts
- cutting
- viscous glutinous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of quartz pushrod cutting techniques.The quartz pushrod cutting technique, includes the following steps, the first step, pre-treatment, and quartz pushrod is placed in the hydrofluoric acid that concentration is 5% and is impregnated, later quartz pushrod is taken out, uses pure water rinsing；Second step coats swelling binder on quartz pushrod surface layer；Quartz pushrod is placed in glutinous wax pan by third step, and viscous glutinous agent is poured into glutinous wax pan, is glued glutinous agent and is wrapped up quartz pushrod；The quartz pushrod wrapped up by viscous glutinous agent is stood coagulation forming by the 4th step at normal temperature；5th step, takes out viscous glutinous agent and the quartz pushrod of coagulation forming, carries out integrated cutting to viscous glutinous agent and quartz pushrod using cutting machine；Viscous glutinous agent after cutting is placed in boiling pot by the 6th step with quartz pushrod, carries out boiling the glutinous agent processing of unsticking, the quartz pushrod after must cutting.Quartz pushrod package is glued glutinous agent by the present invention, carries out the case where entirety is fixed, and cutting machine cuts viscous glutinous agent and quartz pushrod one, and quartz pushrod is not in cutting deformation to quartz pushrod by the viscous glutinous agent of coagulation forming.
Description
Technical field
The present invention relates to a kind of for cutting the quartz pushrod technology of manufacture quartz boat, in particular to a kind of quartz pushrod cutter
Skill.
Background technique
During making quartz boat, the first step is exactly to carry out cutting process to former material quartz pushrod, later again to having cut
Quartz pushrod later carries out soldering, obtains the quartz boat of required specification.It is main to use in the cutting process to quartz pushrod
Cutting machine may cause to cut in cutting machine cutting process to quartz pushrod cutting process due to the reason that quartz pushrod shakes
Dip deviation is likely to result in the direct fracture of quartz pushrod if cutting again to the fastening clamp of quartz pushrod both ends, influences
The dimensions of quartz pushrod, to cause the waste of raw material.Therefore, it is necessary to one kind can guarantee and will not go out when cutting quartz pushrod
Now cut the cutting technique of dip deviation.
Summary of the invention
The object of the present invention is to provide it is a kind of it is easy to operate, can guarantee quartz pushrod cutting when without friction and cutting without deformation
Quartz pushrod cutting technique.
In order to achieve the above-mentioned object of the invention, a kind of quartz pushrod cutting technique of the present invention adopts the technical scheme that
A kind of quartz pushrod cutting technique, includes the following steps,
Quartz pushrod is placed in the hydrofluoric acid that concentration is 5% and impregnates 10min by the first step, pre-treatment, and soaking temperature control exists
10-30 DEG C, quartz pushrod is taken out later, uses pure water rinsing 5-10min；The impurity on quartz pushrod surface layer is removed by strong acid,
Guarantee the purity of quartz pushrod.
Second step, quartz pushrod surface layer after flushing coat swelling binder；The presence of swelling binder makes viscous glutinous agent to stone
The viscous glutinous effect of English stick is more preferable.
The quartz pushrod for coating swelling binder drying is placed in glutinous wax pan by third step, and viscous glutinous agent is poured into glutinous wax pan, is glued
Quartz pushrod is wrapped up in glutinous agent；Quartz pushrod is subjected to glutinous Lasaxing Oilfield.
The quartz pushrod wrapped up by viscous glutinous agent is stood 30-40min at normal temperature, it is solidifying to glue glutinous agent package quartz pushrod by the 4th step
Gu molding；Quartz pushrod is fixed using viscous glutinous agent, so that quartz pushrod will not generate relative vibration when cutting.
5th step, takes out viscous glutinous agent and the quartz pushrod of coagulation forming, carries out one to viscous glutinous agent and quartz pushrod using cutting machine
Body cutting；One cutting ensure that the smooth of quartz pushrod cut surface.
Viscous glutinous agent after cutting is placed in boiling pot by the 6th step with quartz pushrod, is carried out boiling the glutinous agent processing of unsticking, must be cut
Quartz pushrod after cutting.
The swelling binder is the mixed solution of copper acetate and alcohol.Facilitate viscous glutinous agent to the viscous glutinous of quartz pushrod.
The viscous glutinous agent is formulated by following component by following parts by weight,
Urethane acrylate: 60-100 parts
Polyamide: 2-5 parts
Rosin: 10-15 parts
Paraffin: 40-75 parts
Triphenol methylmethane triglycidyl ether epoxy resin: 1-2 parts
BHT:2-5 parts
Urethane acrylate adhesion strength with higher, flexibility and high fissility can make excellent viscous glutinous agent matrix.
Polyamide has certain anti acid alkali performance, the quartz pushrod after overpickling also can be carried out viscous glutinous.Rosin and paraffin are made
For the key of viscous glutinous agent stickiness, rosin and the optimal weight of paraffin are 1:5.Triphenol methylmethane three-glycidyl ether ring
Oxygen resin has certain heat-resisting quantity, and urethane acrylate has certain lower temperature resistance, is not easy when ensure that quartz pushrod cutting
The viscous glutinous effect for being influenced by ambient temperature and influencing viscous glutinous agent to quartz pushrod.
The preparation method of the viscous glutinous agent is to be placed in 60-100 parts of urethane acrylates and 2-5 parts of polyamides
It in mixing channel, heats while stirring later, sequentially adds 10-15 parts of rosin, 40-75 parts of paraffin, 1-2 parts of triphenol methylmethanes later
Triglycidyl ether epoxy resin is eventually adding 2-5 parts of BHT, and intermixture is heated to 90-100 DEG C, 30- is mixed
40min must glue glutinous agent, spare.
The quartz pushrod is containing 99.9%SiO2, 0.05%Al2O3, 0.02%Fe2O3, 0.02% nano-TiO2, 0.01%
Li2The quartz pushrod of O.
Compared with prior art, the beneficial effects of the present invention are:
1, the present invention, which glues quartz pushrod package, sticks agent, carries out entirety to quartz pushrod by the viscous glutinous agent of coagulation forming and fixes,
Cutting machine integrally cuts viscous glutinous agent and quartz pushrod, and quartz pushrod will not generate vibration when cutting, from without cutting deformation
The case where.
2, the viscous glutinous agent that the present invention uses has preferable stickiness at normal temperature, and glutinous agent is glued when being boiled to be taken off
It is easy to use from quartz pushrod.
Specific embodiment
With reference to embodiment, the present invention is furture elucidated, it should be understood that these embodiments are merely to illustrate this
It invents rather than limits the scope of the invention, after the present invention has been read, those skilled in the art are to of the invention various
The modification of equivalent form falls within the application range as defined in the appended claims.
A kind of quartz pushrod cutting technique, includes the following steps,
Quartz pushrod is placed in the hydrofluoric acid that concentration is 5% and impregnates 10min by the first step, pre-treatment, and soaking temperature control exists
10-30 DEG C, quartz pushrod is taken out later, uses pure water rinsing 5-10min；
Second step, quartz pushrod surface layer after flushing coat swelling binder, and the viscous glutinous agent is copper acetate and alcohol
Mixed liquor；
The quartz pushrod for coating swelling binder drying is placed in glutinous wax pan by third step, and viscous glutinous agent is poured into glutinous wax pan, is glued
Quartz pushrod is wrapped up in glutinous agent；
The quartz pushrod wrapped up by viscous glutinous agent is stood 30-40min at normal temperature, it is solidifying to glue glutinous agent package quartz pushrod by the 4th step
Gu molding；
5th step, takes out viscous glutinous agent and the quartz pushrod of coagulation forming, carries out one to viscous glutinous agent and quartz pushrod using cutting machine
Body cutting；
Viscous glutinous agent after cutting is placed in boiling pot by the 6th step with quartz pushrod, is carried out boiling the glutinous agent processing of unsticking, must be cut
Quartz pushrod after cutting.
The viscous glutinous agent is formulated by following component by following parts by weight,
Urethane acrylate: 60-100 parts
Polyamide: 2-5 parts
Rosin: 10-15 parts
Paraffin: 40-75 parts
Triphenol methylmethane triglycidyl ether epoxy resin: 1-2 parts
BHT:2-5 parts
The quartz pushrod is containing 99.9%SiO2, 0.05%Al2O3, 0.02%Fe2O3, 0.02% nano-TiO2, 0.01%
Li2The quartz pushrod of O.
Embodiment one
The preparation method of the viscous glutinous agent is that 70 parts of urethane acrylates and 5 parts of polyamides are placed in mixing channel
It is interior, it heats while stirring later, sequentially adds 10 parts of rosin, 40 parts of paraffin, 1 part of triphenol methylmethane three-glycidyl ether ring later
Oxygen resin is eventually adding 2 parts of BHT, and intermixture is heated to 90-100 DEG C, 30-40min is mixed, and must glue glutinous agent, spare.
Embodiment two
The preparation method of the viscous glutinous agent is that 60 parts of urethane acrylates and 3 parts of polyamides are placed in mixing channel
It is interior, it heats while stirring later, sequentially adds 15 parts of rosin, 70 parts of paraffin, 1 part of triphenol methylmethane three-glycidyl ether ring later
Oxygen resin is eventually adding 3 parts of BHT, and intermixture is heated to 90-100 DEG C, 30-40min is mixed, and must glue glutinous agent, spare.
Embodiment three
The preparation method of the viscous glutinous agent is that 100 parts of urethane acrylates and 5 parts of polyamides are placed in mixing channel
It is interior, it heats while stirring later, sequentially adds 15 parts of rosin, 75 parts of paraffin, 2 parts of triphenol methylmethane three-glycidyl ether rings later
Oxygen resin is eventually adding 5 parts of BHT, and intermixture is heated to 90-100 DEG C, 30-40min is mixed, and must glue glutinous agent, spare.
Claims (5)
1. a kind of quartz pushrod cutting technique, it is characterised in that: include the following steps,
Quartz pushrod is placed in the hydrofluoric acid that concentration is 5% and impregnates 10min by the first step, pre-treatment, and soaking temperature is controlled in 10-
30 DEG C, quartz pushrod is taken out later, uses pure water rinsing 5-10min；
Second step, quartz pushrod surface layer after flushing coat swelling binder；
The quartz pushrod for coating swelling binder drying is placed in glutinous wax pan by third step, and viscous glutinous agent is poured into glutinous wax pan, glutinous agent is glued
Wrap up quartz pushrod；
The quartz pushrod wrapped up by viscous glutinous agent is stood 30-40min by the 4th step at normal temperature, and viscous glutinous agent package quartz pushrod is frozen into
Type；
5th step takes out viscous glutinous agent and the quartz pushrod of coagulation forming, is integrally cut to viscous glutinous agent with quartz pushrod using cutting machine
It cuts；
Viscous glutinous agent after cutting is placed in boiling pot by the 6th step with quartz pushrod, carries out boiling the glutinous agent processing of unsticking, after obtaining cutting
Quartz pushrod.
2. quartz pushrod cutting technique according to claim 1, it is characterised in that: the swelling binder is copper acetate and alcohol
Mixed solution.
3. quartz pushrod cutting technique according to claim 1, it is characterised in that: the viscous glutinous agent is by following component by following
Parts by weight are formulated,
Urethane acrylate: 60-100 parts
Polyamide: 2-5 parts
Rosin: 10-15 parts
Paraffin: 40-75 parts
Triphenol methylmethane triglycidyl ether epoxy resin: 1-2 parts
BHT:2-5 parts.
4. quartz pushrod cutting technique according to claim 3, it is characterised in that: the preparation method of the viscous glutinous agent is to incite somebody to action
60-100 parts of urethane acrylates and 2-5 parts of polyamides are placed in mixing channel, are heated while stirring later, later successively
10-15 parts of rosin, 40-75 parts of paraffin, 1-2 parts of triphenol methylmethane triglycidyl ether epoxy resin are added, are eventually adding 2-5 parts
Intermixture is heated to 90-100 DEG C, 30-40min is mixed by BHT, must glue glutinous agent, spare.
5. quartz pushrod cutting technique according to claim 1, it is characterised in that: the quartz pushrod is containing 99.9%SiO2,
0.05%Al2O3, 0.02%Fe2O3, 0.02% nano-TiO2, 0.01%Li2The quartz pushrod of O.