CN109763350A - A kind of printing method of clothes lace - Google Patents
A kind of printing method of clothes lace Download PDFInfo
- Publication number
- CN109763350A CN109763350A CN201811442222.3A CN201811442222A CN109763350A CN 109763350 A CN109763350 A CN 109763350A CN 201811442222 A CN201811442222 A CN 201811442222A CN 109763350 A CN109763350 A CN 109763350A
- Authority
- CN
- China
- Prior art keywords
- lace
- mill base
- clothes
- pasting
- printing method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of printing methods of clothes lace, the specific steps are as follows: the suture of lace edge: is sutured with edge of the suture to lace；Modulation mill base: appropriate dyestuff, sodium bicarbonate, cosolvent, rapidogen dye, sodium alginate and hot water are chosen, is placed in blender and is mixed.A kind of printing method of clothes lace of the present invention, edge sealing processing is carried out to lace before lace pasting, be conducive to improve the intensity of lace, durable, it is not tearable, condition is provided for subsequent better progress pasting, graphite fibre yarn and fire-retardant low stretch yarn are added in the component of lace, can increase lace anti-static ability and anti-flaming effect, improve the safety of lace, graphite fibre yarn and fire-retardant low stretch yarn will not influence the colouring and pasting of lace simultaneously, it first dries after stamp and evaporates afterwards, it can first be formed to the lace after pasting, fixation is preferably realized when evaporating, improve the effect of stamp, bring better prospect of the application.
Description
Technical field
The present invention relates to the invention of clothes lace printing method, stamp field traditionally, in particular to a kind of clothes are improved
Fill the printing method of lace.
Background technique
Stamp is the technical process for applying stamp line on textile fabric with dyestuff or pigment, and stamp has textile printing, wool top print
Colored and yarn printing point, and based on textile printing, PRINTED FABRIC is the product rich in artistry, according to the decorative pattern figure of design
Case selects corresponding printing technology, and there are commonly direct printing, resisting printing and three kinds of discharge printing, and direct printing is in white
Or first directly print on light coloured fabrics with dyestuff or pigment, decorative pattern is obtained using the post-processings such as evaporating, process flow is brief, applies
It is most wide.
There are certain drawbacks in processing for the printing method of existing clothes lace, firstly, lace is more loose, to it
Brush and be easy to cause destruction, is easy to tear, condition can not be provided for subsequent better progress pasting, secondly, existing flower
Side does not have antistatic and flame retardant effect, and addition other compositions are easy to influence lace stamp, finally, directly carrying out to it after stamp
It evaporates, cannot achieve and the lace after pasting is carried out shaping, fixation printing effect is bad, for this purpose, it is proposed that a kind of clothes flower
The printing method on side.
Summary of the invention
The main purpose of the present invention is to provide a kind of printing methods of clothes lace, can effectively solve in background technique
The problem of.
To achieve the above object, the technical scheme adopted by the invention is as follows:
A kind of printing method of clothes lace, the specific steps are as follows:
(1) lace edge sutures: being sutured with edge of the suture to lace；
(2) it modulates mill base: choosing appropriate dyestuff, sodium bicarbonate, cosolvent, rapidogen dye, sodium alginate and hot water, be placed on and stir
It mixes in device and is mixed, mill base is made in agitator speed 120-140r/min；
(3) mill base pasting: will be on the lace after edge suture in the mill base coating in step (1) that modulated in step (2)；
(4) it dries: the lace after pasting in step (3) is dried, be used for thermal finalization；
(5) it evaporates: the lace after drying in step (4) being placed in steaming box and is evaporated, temperature is controlled in 150-
175℃；
(6) it soaps, wash: soap boiling is carried out to the lace after evaporating in step (5), the time of soaping is 30-40min, then
It carries out hot water wash and cold water is washed.
Preferably, suture includes fire-retardant low stretch yarn and cotton thread in the step (1), and fire-retardant low stretch yarn: cotton thread 4:
1, lace component includes: nylon 15-25%, spandex 5-15%, cotton thread 30-45%, graphite fibre yarn 10-25%, fire-retardant low bullet
Silk 6-10%.
Preferably, cosolvent is one of urea, nicotinic acid amide and acetamide or a variety of in the step (2).
Preferably, according to mass fraction in the step (2): 10-12 parts of dyestuff, 1-3 parts of sodium bicarbonate, cosolvent 15-20
Part, 5-7 parts of rapidogen dye, 8-10 parts and hot water 25-35 parts of sodium alginate.
Preferably, mill base is uniformly brushed in flower with fine, soft fur brush or scraper during mill base pasting in the step (3)
Bian Shang.
Preferably, drying temperature is 60-80 DEG C in the step (4).
Preferably, the lace after drying is suspended on decatize box bracket in the step (5), push-in cabinet is steamed
Change, for accelerating laking process of the dyestuff in mill base on lace.
Preferably, it soaps in the step (6) for removing the dyestuff low with fiber binding strength in lace, when hot water wash
Between be 10-20min, cold washing time is 15-25min, sufficiently remove cosolvent on lace in the mill base that is coated with, rapidogen dye with
Sodium alginate.
Compared with prior art, the invention has the following beneficial effects:
1, edge sealing processing is carried out to lace before lace pasting, is conducive to the intensity for improving lace, durable is not easy to tear
It splits, provides condition for subsequent better progress pasting；
2, graphite fibre yarn and fire-retardant low stretch yarn are added in the component of lace, can increase the anti-static ability of lace and are prevented
Fuel efficiency fruit improves the safety of lace, while graphite fibre yarn and fire-retardant low stretch yarn will not influence the colouring and pasting of lace；
3, it first dries after stamp and evaporates afterwards, can first be formed to the lace after pasting, fixation is preferably realized when evaporating, is mentioned
The effect of high stamp.
Detailed description of the invention
Fig. 1 is a kind of method flow diagram of the printing method of clothes lace of the present invention.
Specific embodiment
To be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, below with reference to
Specific embodiment, the present invention is further explained.
Embodiment 1
(1) lace edge sutures: being sutured with edge of the suture to lace, suture includes fire-retardant low stretch yarn and cotton
Line, and fire-retardant low stretch yarn: cotton thread 4:1, lace component include: nylon 15%, spandex 5%, cotton thread 30%, graphite fibre yarn
10%, fire-retardant low stretch yarn 6%；
(2) it modulates mill base: appropriate dyestuff, sodium bicarbonate, cosolvent, rapidogen dye, sodium alginate and hot water is chosen, according to quality
Number: 10 parts of dyestuff, 1 part of sodium bicarbonate, 15 parts of cosolvent, 5 parts of rapidogen dye, 8 parts and 25 parts of hot water of sodium alginate are placed on stirring
It is mixed in device, agitator speed 120r/min, mill base is made, cosolvent is one in urea, nicotinic acid amide and acetamide
Kind is a variety of；
(3) mill base pasting: on the lace after edge in the mill base coating in step (1) modulated in step (2) is sutured, color
Mill base is uniformly brushed on lace with fine, soft fur brush or scraper during slurry pasting；
(4) it dries: the lace after pasting in step (3) is dried, drying temperature is 60 DEG C, is used for thermal finalization；
(5) it evaporates: the lace after drying in step (4) being placed in steaming box and is evaporated, by the lace after drying
It being suspended on decatize box bracket, push-in cabinet is evaporated, for accelerating laking process of the dyestuff in mill base on lace, temperature
Degree control is at 150 DEG C；
(6) it soaps, wash: soap boiling is carried out to the lace after evaporating in step (5), the time of soaping is 30min, is then carried out
Hot water wash and cold water are washed, and are soaped for removing the dyestuff low with fiber binding strength in lace, the hot water wash time is 10min, cold
Washing time is 15min, sufficiently removes cosolvent, rapidogen dye and sodium alginate in the mill base being coated on lace.
Embodiment 2
(1) lace edge sutures: being sutured with edge of the suture to lace, suture includes fire-retardant low stretch yarn and cotton
Line, and fire-retardant low stretch yarn: cotton thread 4:1, lace component include: nylon 20%, spandex 10%, cotton thread 38%, graphite fibre yarn
18%, fire-retardant low stretch yarn 8%；
(2) it modulates mill base: appropriate dyestuff, sodium bicarbonate, cosolvent, rapidogen dye, sodium alginate and hot water is chosen, according to quality
Number: 11 parts of dyestuff, 2 parts of sodium bicarbonate, 18 parts of cosolvent, 6 parts of rapidogen dye, 9 parts and 30 parts of hot water of sodium alginate are placed on stirring
It is mixed in device, agitator speed 130r/min, mill base is made, cosolvent is one in urea, nicotinic acid amide and acetamide
Kind is a variety of；
(3) mill base pasting: on the lace after edge in the mill base coating in step (1) modulated in step (2) is sutured, color
Mill base is uniformly brushed on lace with fine, soft fur brush or scraper during slurry pasting；
(4) it dries: the lace after pasting in step (3) is dried, drying temperature is 70 DEG C, is used for thermal finalization；
(5) it evaporates: the lace after drying in step (4) being placed in steaming box and is evaporated, by the lace after drying
It being suspended on decatize box bracket, push-in cabinet is evaporated, for accelerating laking process of the dyestuff in mill base on lace, temperature
Degree control is at 168 DEG C；
(6) it soaps, wash: soap boiling is carried out to the lace after evaporating in step (5), the time of soaping is 35min, is then carried out
Hot water wash and cold water are washed, and are soaped for removing the dyestuff low with fiber binding strength in lace, the hot water wash time is 15min, cold
Washing time is 20min, sufficiently removes cosolvent, rapidogen dye and sodium alginate in the mill base being coated on lace.
Embodiment 3
(1) lace edge sutures: being sutured with edge of the suture to lace, suture includes fire-retardant low stretch yarn and cotton
Line, and fire-retardant low stretch yarn: cotton thread 4:1, lace component include: nylon 25%, spandex 15%, cotton thread 45%, graphite fibre yarn
25%, fire-retardant low stretch yarn 10%；
(2) it modulates mill base: appropriate dyestuff, sodium bicarbonate, cosolvent, rapidogen dye, sodium alginate and hot water is chosen, according to quality
Number: 12 parts of dyestuff, 3 parts of sodium bicarbonate, 20 parts of cosolvent, 7 parts of rapidogen dye, 10 parts and 35 parts of hot water of sodium alginate are placed on and stir
It mixes in device and is mixed, mill base is made in agitator speed 140r/min, and cosolvent is in urea, nicotinic acid amide and acetamide
It is one or more；
(3) mill base pasting: on the lace after edge in the mill base coating in step (1) modulated in step (2) is sutured, color
Mill base is uniformly brushed on lace with fine, soft fur brush or scraper during slurry pasting；
(4) it dries: the lace after pasting in step (3) is dried, drying temperature is 80 DEG C, is used for thermal finalization；
(5) it evaporates: the lace after drying in step (4) being placed in steaming box and is evaporated, by the lace after drying
It being suspended on decatize box bracket, push-in cabinet is evaporated, for accelerating laking process of the dyestuff in mill base on lace, temperature
Degree control is at 175 DEG C；
(6) it soaps, wash: soap boiling is carried out to the lace after evaporating in step (5), the time of soaping is 40min, is then carried out
Hot water wash and cold water are washed, and are soaped for removing the dyestuff low with fiber binding strength in lace, the hot water wash time is 20min, cold
Washing time is 25min, sufficiently removes cosolvent, rapidogen dye and sodium alginate in the mill base being coated on lace.
Table 1 is the comparison of each data and later period printing quality in the printing method of embodiment 1-3 clothes lace, detection knot
Fruit is as follows:
| Graphite fibre yarn % | Fire-retardant low stretch yarn % | Drying temperature DEG C | Evaporate temperature DEG C | Printing quality | |
| Embodiment 1 | 10 | 6 | 60 | 150 | Preferably |
| Embodiment 2 | 18 | 8 | 70 | 168 | Preferably |
| Embodiment 3 | 25 | 10 | 80 | 175 | It is good |
By 1 experimental data of table it is found that carrying out edge sealing processing to lace before lace pasting, be conducive to improve the strong of lace
Degree, durable is not tearable, provides condition for subsequent better progress pasting, adds graphite fibre yarn in the component of lace
With fire-retardant low stretch yarn, can increase lace anti-static ability and anti-flaming effect, improve the safety of lace, while graphite fibre
Yarn and fire-retardant low stretch yarn will not influence the colouring and pasting of lace, first dry after stamp and evaporate afterwards, can be to the lace after pasting
It is first formed, fixation is preferably realized when evaporating, improve the effect of stamp, three groups of embodiments improve clothes flower as shown in Table 1
The printing quality on side, wherein embodiment 3 is optimal selection.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (8)
1. a kind of printing method of clothes lace, it is characterised in that: specific step is as follows:
(1) lace edge sutures: being sutured with edge of the suture to lace；
(2) it modulates mill base: choosing appropriate dyestuff, sodium bicarbonate, cosolvent, rapidogen dye, sodium alginate and hot water, be placed on blender
In mixed, mill base is made in agitator speed 120-140r/min；
(3) mill base pasting: will be on the lace after edge suture in the mill base coating in step (1) that modulated in step (2)；
(4) it dries: the lace after pasting in step (3) is dried, be used for thermal finalization；
(5) it evaporates: the lace after drying in step (4) being placed in steaming box and is evaporated, temperature is controlled in 150-175
℃；
(6) it soaps, wash: soap boiling is carried out to the lace after evaporating in step (5), the time of soaping is 30-40min, is then carried out
Hot water wash and cold water are washed.
2. a kind of printing method of clothes lace according to claim 1, it is characterised in that: suture in the step (1)
Line includes fire-retardant low stretch yarn and cotton thread, and fire-retardant low stretch yarn: cotton thread 4:1, lace component include: nylon 15-25%, spandex 5-
15%, cotton thread 30-45%, graphite fibre yarn 10-25%, fire-retardant low stretch yarn 6-10%.
3. a kind of printing method of clothes lace according to claim 1, it is characterised in that: hydrotropy in the step (2)
Agent is one of urea, nicotinic acid amide and acetamide or a variety of.
4. a kind of printing method of clothes lace according to claim 1, it is characterised in that: in the step (2) according to
Mass fraction: 10-12 parts of dyestuff, 1-3 parts of sodium bicarbonate, 15-20 parts of cosolvent, 5-7 parts of rapidogen dye, 8-10 parts of sodium alginate and heat
25-35 parts of water.
5. a kind of printing method of clothes lace according to claim 1, it is characterised in that: mill base in the step (3)
Mill base is uniformly brushed on lace with fine, soft fur brush or scraper during pasting.
6. a kind of printing method of clothes lace according to claim 1, it is characterised in that: drying in the step (4)
Temperature is 60-80 DEG C.
7. a kind of printing method of clothes lace according to claim 1, it is characterised in that: will be dried in the step (5)
Lace after dry is suspended on decatize box bracket, and push-in cabinet is evaporated, for accelerating the dyestuff in mill base on lace
Laking process.
8. a kind of printing method of clothes lace according to claim 1, it is characterised in that: soap in the step (6)
For removing the dyestuff low with fiber binding strength in lace, the hot water wash time is 10-20min, and cold washing time is 15-
25min sufficiently removes cosolvent, rapidogen dye and sodium alginate in the mill base being coated on lace.