CN109763227A - Polyester filament interweaves the production technology of multi-functional bed necessaries fabric - Google Patents
Polyester filament interweaves the production technology of multi-functional bed necessaries fabric Download PDFInfo
- Publication number
- CN109763227A CN109763227A CN201910178687.0A CN201910178687A CN109763227A CN 109763227 A CN109763227 A CN 109763227A CN 201910178687 A CN201910178687 A CN 201910178687A CN 109763227 A CN109763227 A CN 109763227A
- Authority
- CN
- China
- Prior art keywords
- ramuscule
- polyester filament
- filament
- pbt
- paying out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention discloses a kind of polyester filament and interweaves the production technology of multi-functional bed necessaries fabric, the bed necessaries fabric uses thick branch polyester filament, ramuscule polyester filament and PBT blend filament for raw material, which is prepared by the following steps to obtain: raw material selection, coloring, drying, braiding, co-extrusion, weaving and arrangement；It solves after being mixed using PBT or PET particle with dyestuff in traditional processing step, coloring is carried out to particle, master batch is made, utilize master batch and thick branch polyester filament, ramuscule polyester filament co-extrusion on wire drawing machine realizes the coloring that line is knitted to fabric, although such mode can improve the defect that polyester fabric is not easy to paint, but it is unable to reach fabric and knits line in coloring according to specific lines, so that fabric, which knits line itself, can not form specific decorative pattern, and since PBT or PET particle is mode and the thick branch polyester filament by wire drawing machine co-extrusion, ramuscule polyester filament combines.
Description
Technical field
The present invention relates to polyester fabric fields, and in particular to polyester filament interweaves the production technology of multi-functional bed necessaries fabric.
Background technique
Polyester fabric is very more a kind of chemical fiber garment fabrics in daily life.Its biggest advantage is that wrinkle resistance
It is fine with conformality, therefore, it is suitble to make coat garment, all kinds of luggages, bed necessaries fabric and tent etc..Polyester filament is in production bed necessaries
It is needed when fabric by a series of procedure of processing, after being mixed using PBT or PET particle with dyestuff in traditional processing step,
Coloring is carried out to particle, master batch is made, co-extrusion is realized on wire drawing machine using master batch and thick branch polyester filament, ramuscule polyester filament
The coloring of line is knitted to fabric, although such mode can improve the defect that polyester fabric is not easy to paint, and fabric is made to knit line
Integral colouring, but be unable to reach fabric and knit line in coloring according to specific lines so that fabric knit line itself can not shape
At specific decorative pattern, and since PBT or PET particle is that mode and thick branch polyester filament, ramuscule by wire drawing machine co-extrusion is washed
Synthetic fibre long filament combines, so that polyester fabric is highly inconvenient when recycling and needing to fade.
Summary of the invention
Interweave the production technology of multi-functional bed necessaries fabric the purpose of the present invention is to provide polyester filament, solves traditional
After being mixed using PBT or PET particle with dyestuff in processing step, coloring is carried out to particle, master batch is made, utilizes master batch and thick branch
Polyester filament, ramuscule the polyester filament co-extrusion on wire drawing machine, which are realized, knits the coloring of line to fabric, although such mode can
Improve polyester fabric and be not easy the defect painted, and fabric is made to knit line integral colouring, but is unable to reach fabric and knits line in coloring
According to specific lines so that fabric, which knits line itself, can not form specific decorative pattern, and due to PBT or PET particle be through
The mode of wire drawing machine co-extrusion is crossed in conjunction with thick branch polyester filament, ramuscule polyester filament, so that polyester fabric is recycling
And highly inconvenient problem when needing to fade.
The purpose of the present invention can be achieved through the following technical solutions:
Polyester filament interweaves the production technology of multi-functional bed necessaries fabric, which uses thick branch polyester filament, ramuscule terylene
Long filament and PBT blend filament are raw material, which is prepared by the following steps to obtain:
Raw material selection, coloring, drying, braiding, co-extrusion, weaving and arrangement；
It includes choosing using 1100D high strength industrial polyester filament as thick branch polyester filament, ramuscule terylene that the raw material, which is chosen,
Long filament, wherein the quantity ratio of thick branch polyester filament and ramuscule polyester filament is 1:(2-4)；
The coloring is mixed dyestuff and PBT blend filament using blender, is carried out after mixing color matching to PBT blend filament
It is dry；
The drying is dried the PBT blend filament by coloring using drying machine, and the temperature of drying machine is controlled in 200-
250 DEG C, drying time 5-8min, PBT blend filament needs to separate when dry between long filament and long filament, does not knot, does not wind；
The braiding will be woven using braiding apparatus between thick branch polyester filament, ramuscule polyester filament and PBT blend filament
Rub, will according to quantity ratio be 1:(2-4 between thick branch polyester filament and ramuscule polyester filament) rub into female silk, then by female silk with
Line is knitted than being woven into the fabric with lines, color for 2:1 according to quantity between PBT blend filament；
The co-extrusion, which is used, knits line progress wire drawing co-extrusion to fabric for wire drawing machine；
The fabric for completing co-extrusion is knitted line using weaving loom and is woven into fabric finished product by the weaving；
It is described arrange complete weaving fabric finished product trimmed, ironing.
Preferably, the braiding apparatus used during the braiding include end, the driving of ramuscule unwrapping wire, ramuscule paying out reel,
First polyester filament wears axis, thick branch from twister structure, the second polyester filament from twister structure, PBT paying out reel, the driving of PBT unwrapping wire, ramuscule
Unwrapping wire driving, thick branch paying out reel, the end both ends are mounted on ramuscule paying out reel, and ramuscule paying out reel one end is put with ramuscule
Line driving is connected, and the first polyester filament is provided with below the end both ends from twister structure, the second polyester filament from twister structure,
First polyester filament is provided with PBT paying out reel, the PBT from twister structure, the second polyester filament from lower section between twister structure
Paying out reel bottom end is connected with the driving of PBT unwrapping wire, and first polyester filament is equal from twister structure, the second polyester filament from twister structure
It wears axis by several ramuscules to constitute, several described ramuscules are worn and are provided with thick branch paying out reel between axis, the thick branch paying out reel one
End is connected with the driving of thick branch unwrapping wire.
Preferably, the quantity of the ramuscule paying out reel at the end both ends is corresponding with the quantity that ramuscule wears axis, and end two
The quantitative range of the ramuscule paying out reel at end is 2-4.
Preferably, the ramuscule paying out reel corresponds to ramuscule polyester filament unwrapping wire, and the thick branch paying out reel is used for thick Zhi Dilun
Long filament unwrapping wire, and the put ramuscule polyester filament of ramuscule paying out reel is worn across corresponding ramuscule and is rubbed axis and thick branch polyester filament
Winding.
Preferably, the PBT paying out reel corresponds to PBT blend filament unwrapping wire.
Preferably, the ramuscule paying out reel is driven by ramuscule unwrapping wire is rotatablely connected between end, the thick branch unwrapping wire
Axis is driven by thick branch unwrapping wire and ramuscule is worn and is rotatablely connected between axis, and the PBT paying out reel is washed by the driving of PBT unwrapping wire with first
Synthetic fibre long filament is rotatablely connected from twister structure, the second polyester filament between twister structure.
Beneficial effects of the present invention: compared with prior art, the present invention on the basis of traditional polyester fabric production technology,
It is rubbed using braiding will be carried out between thick branch polyester filament, ramuscule polyester filament and PBT blend filament, it is first right before braiding is rubbed
PBT blend filament is dyed, then will be rubbed between thick branch polyester filament and ramuscule polyester filament according to quantity ratio for 1:(2-4)
It at female silk, then will according to quantity ratio be that 2:1 is woven into line between female silk and dyed and PBT blend filament after drying
Road, color fabric knit line, due to being used in traditional processing step after PBT or PET particle mixes with dyestuff, to particle progress
Master batch is made in coloring, and using master batch and thick branch polyester filament, ramuscule polyester filament, co-extrusion realization knits line to fabric on wire drawing machine
Coloring, although such mode can improve the defect that polyester fabric is not easy to paint, and fabric is made to knit line integral colouring,
It is to be unable to reach fabric to knit line in coloring according to specific lines, so that fabric, which knits line itself, can not form specific flower
Line, and since PBT or PET particle is mode by wire drawing machine co-extrusion in conjunction with thick branch polyester filament, ramuscule polyester filament,
So that polyester fabric is highly inconvenient when recycling and needing to fade, and length is blended in PBT provided by the present invention
Silk processing method not only fabric to knit line directly to dye required decorative pattern, lines in dyeing, but also make polyester fabric
PBT blend filament need to only be knitted in line from fabric and be extracted out when recycling needs to fade, the immersion without chemical reagent is faded,
The recycling use that fabric knits line will not be influenced；And make fabric integral strength higher using PBT blend filament, wearability
It can more preferably, to realize the multi-functional of bed necessaries fabric.
By using braiding apparatus, and the quantity of the ramuscule paying out reel at braiding apparatus end both ends and ramuscule wear the number of axis
Measure corresponding, the quantitative range of the ramuscule paying out reel at both ends is 2-4, and ramuscule paying out reel corresponds to ramuscule polyester filament unwrapping wire, slightly
Branch paying out reel be used for thick branch polyester filament unwrapping wire, the put ramuscule polyester filament of ramuscule paying out reel pass through corresponding ramuscule wear axis with slightly
Winding is rubbed between branch polyester filament, PBT paying out reel corresponds to PBT blend filament unwrapping wire, and ramuscule unwrapping wire drives when taking up one's knitting
Ramuscule paying out reel is driven to discharge ramuscule polyester filament, ramuscule polyester filament wears axis and wears axis end release from ramuscule through ramuscule,
Thick branch unwrapping wire driving drives thick branch paying out reel to discharge thick branch polyester filament, between thick branch polyester filament and ramuscule polyester filament according to
Quantity ratio is 1:(2-4) female silk is rubbed into, when the quantity of the ramuscule paying out reel of 1 one end of end is two, the first polyester filament
From the ramuscule of twister structure and the second polyester filament from twister structure wear axis be two and branch polyester filament and ramuscule polyester filament it
Between according to quantity ratio be 1:2 rub into female silk；When the quantity of the ramuscule paying out reel of end one end is three, the first polyester filament
Wearing axis from the ramuscule of twister structure and the second polyester filament from twister structure is three, and thick branch polyester filament and ramuscule polyester filament
Between according to quantity ratio are as follows: rub into female silk, ramuscule polyester filament quantity is more, and the thickness of fabric is bigger, then, PBT unwrapping wire
Axis is discharging the PBT blend filament of coloring and is rubbing between two female silks under the driving that PBT unwrapping wire drives, female silk and PBT are total
Line is knitted than being woven into the fabric with lines, color for 2:1 according to quantity between mixed long filament, when needing that PBT blend filament is made to exist
The fabric that a variety of different lines are capable of forming when rubbing between thick branch polyester filament, ramuscule polyester filament knits line, is put by PBT
The revolving speed of line drive control PBT paying out reel and two buses and PBT blend filament rub the speed of winding, to make
Fabric knit line processing when can directly dye a variety of different decorative patterns, lines.
Detailed description of the invention
In order to illustrate the technical solution of the embodiments of the present invention more clearly, will be described below to embodiment required
Attached drawing is briefly described, it should be apparent that, drawings in the following description are only some embodiments of the invention, for ability
For the those of ordinary skill of domain, without creative efforts, it can also be obtained according to these attached drawings other attached
Figure.
Fig. 1 is braiding apparatus structural schematic diagram of the present invention.
Fig. 2 is first polyester filament of the invention from twister structure structural schematic diagram.
In figure: 1, end；2, ramuscule unwrapping wire drives；3, ramuscule paying out reel；4, the first polyester filament is from twister structure；5, second
Polyester filament is from twister structure；6, PBT paying out reel；7, PBT unwrapping wire drives；8, ramuscule wears axis；9, thick branch unwrapping wire driving；10, thick branch
Paying out reel.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts all other
Embodiment shall fall within the protection scope of the present invention.
As shown in Figs. 1-2, polyester filament interweaves the production technology of multi-functional bed necessaries fabric, which uses thick Zhi Di
Synthetic fibre long filament, ramuscule polyester filament and PBT blend filament are raw material, which is prepared by the following steps to obtain:
Raw material selection, coloring, drying, braiding, co-extrusion, weaving and arrangement；
It includes choosing using 1100D high strength industrial polyester filament as thick branch polyester filament, ramuscule polyester filament that raw material, which is chosen,
Wherein the quantity ratio of thick branch polyester filament and ramuscule polyester filament is 1:(2-4)；
Coloring is mixed dyestuff and PBT blend filament using blender, is done after mixing color matching to PBT blend filament
It is dry；
Dry that the PBT blend filament by coloring is dried using drying machine, the temperature of drying machine is controlled in 200-250
DEG C, drying time 5-8min, PBT blend filament needs to separate when dry between long filament and long filament, does not knot, does not wind；
Braiding will carry out braiding using braiding apparatus and rub between thick branch polyester filament, ramuscule polyester filament and PBT blend filament,
It will be that 1:2-4 rubs into female silk, then female silk is blended with PBT according to quantity ratio between thick branch polyester filament and ramuscule polyester filament
Line is knitted than being woven into the fabric with lines, color for 2:1 according to quantity between long filament；
Co-extrusion, which is used, knits line progress wire drawing co-extrusion to fabric for wire drawing machine；
The fabric for completing co-extrusion is knitted line using weaving loom and is woven into fabric finished product by weaving；
Arrange complete weaving fabric finished product trimmed, ironing.
The braiding apparatus used during braiding includes end 1, the driving of ramuscule unwrapping wire 2, ramuscule paying out reel 3, the first terylene
Long filament is from twister structure 4, the second polyester filament from twister structure 5, PBT paying out reel 6, PBT unwrapping wire driving 7, ramuscule wear axis 8, thick branch is put
Line drives 9, thick branch paying out reel 10, and 1 both ends of end are mounted on ramuscule paying out reel 3, and 3 one end of ramuscule paying out reel and ramuscule unwrapping wire drive
Dynamic 2 are connected, and the first polyester filament are provided with below 1 both ends of end from twister structure 4, the second polyester filament from twister structure 5, and first
Polyester filament is provided with PBT paying out reel 6,6 bottom of PBT paying out reel from twister structure 4, the second polyester filament from lower section between twister structure 5
End is connected with PBT unwrapping wire driving 7, and the first polyester filament is from twister structure 4, the second polyester filament from twister structure 5 by several
Ramuscule wears the composition of axis 8, several ramuscules are worn and are provided with thick branch paying out reel 10 between axis 8, and thick 10 one end of branch paying out reel is put with thick branch
Line driving 9 is connected.
The quantity of the ramuscule paying out reel 3 at 1 both ends of end is corresponding with the quantity that ramuscule wears axis 8, and the ramuscule at 1 both ends of end
The quantitative range of paying out reel 3 is 2-4.Ramuscule paying out reel 3 corresponds to ramuscule polyester filament unwrapping wire, and thick branch paying out reel 10 is used for thick Zhi Di
Synthetic fibre long filament unwrapping wire, and the put ramuscule polyester filament of ramuscule paying out reel 3 is worn axis 8 and thick branch polyester filament across corresponding ramuscule
Winding is rubbed, 2 driving ramuscule paying out reel 3 of ramuscule unwrapping wire driving discharges ramuscule polyester filament when taking up one's knitting, and ramuscule terylene is long
Silk wears axis 8 through ramuscule and wears 8 end release of axis from ramuscule, and the thick 9 thick branch paying out reel 10 of driving of branch unwrapping wire driving discharges thick Zhi Di
Synthetic fibre long filament rubs into female silk according to quantity ratio between thick branch polyester filament and ramuscule polyester filament for 1:(2-4), when end 1 one
When the quantity of the ramuscule paying out reel 3 at end is two, the first polyester filament is from twister structure 4 and the second polyester filament from twister structure 5
It is to rub into female silk according to quantity ratio between two and branch polyester filament and ramuscule polyester filament for 1:2 that ramuscule, which wears axis 8,；When
When the quantity of the ramuscule paying out reel 3 of 1 one end of end is three, the first polyester filament is twisted certainly from twister structure 4 and the second polyester filament
It is three that the ramuscule of mechanism 5, which wears axis 8, and is rubbed between thick branch polyester filament and ramuscule polyester filament according to quantity ratio for 1:3
At female silk, ramuscule polyester filament quantity is more, and the thickness of fabric is bigger.
PBT paying out reel 6 corresponds to PBT blend filament unwrapping wire, and PBT paying out reel 6 discharges under the driving of PBT unwrapping wire driving 7
The PBT blend filament of color is simultaneously rubbed between two female silks, according to quantity ratio is that 2:1 weaves between female silk and PBT blend filament
Line is knitted at the fabric with lines, color.
Ramuscule paying out reel 3 between ramuscule unwrapping wire driving 2 and end 1 by being rotatablely connected, and thick branch paying out reel 10 is by slightly propping up
Unwrapping wire driving 9 and ramuscule are worn and are rotatablely connected between axis 8, and PBT paying out reel 6 is twisted certainly by the driving 7 of PBT unwrapping wire and the first polyester filament
Mechanism 4, the second polyester filament are rotatablely connected between twister structure 5, when need to make PBT blend filament with thick branch polyester filament,
The fabric that a variety of different lines are capable of forming when rubbing between ramuscule polyester filament knits line, passes through 7 control PBT of PBT unwrapping wire driving
The speed for rubbing winding of the revolving speed of paying out reel 6 and two buses and PBT blend filament, exists so that fabric knits line
A variety of different decorative patterns, lines can be directly dyed when processing.
The invention has the benefit that compared with prior art, the present invention is on traditional polyester fabric production technology basis
On, it is rubbed using braiding will be carried out between thick branch polyester filament, ramuscule polyester filament and PBT blend filament, before braiding is rubbed
First PBT blend filament is dyed, then by between thick branch polyester filament and ramuscule polyester filament according to quantity ratio be 1:(2-4)
It rubs into female silk, then will according to quantity ratio be that 2:1 is woven into and has between female silk and dyed and PBT blend filament after drying
Lines, color fabric knit line, due to being used in traditional processing step after PBT or PET particle mixes with dyestuff, to particle into
Master batch is made in row coloring, and using master batch, fabric is knitted in the co-extrusion realization on wire drawing machine with thick branch polyester filament, ramuscule polyester filament
The coloring of line although such mode can improve the defect that polyester fabric is not easy to paint, and makes fabric knit line integral colouring,
But it is unable to reach fabric and knits line in coloring according to specific lines, so that fabric, which knits line itself, can not form specific flower
Line, and since PBT or PET particle is mode by wire drawing machine co-extrusion in conjunction with thick branch polyester filament, ramuscule polyester filament,
So that polyester fabric is highly inconvenient when recycling and needing to fade, and length is blended in PBT provided by the present invention
Silk processing method not only fabric to knit line directly to dye required decorative pattern, lines in dyeing, but also make polyester fabric
PBT blend filament need to only be knitted in line from fabric and be extracted out when recycling needs to fade, the immersion without chemical reagent is faded,
The recycling use that fabric knits line will not be influenced；
By using braiding apparatus, and the quantity of the ramuscule paying out reel 3 at 1 both ends of braiding apparatus end and ramuscule wear the number of axis 8
To measure corresponding, the quantitative range of the ramuscule paying out reel 3 at both ends is 2-4, the corresponding ramuscule polyester filament unwrapping wire of ramuscule paying out reel 3,
Thick branch paying out reel 10 is used for thick branch polyester filament unwrapping wire, and the put ramuscule polyester filament of ramuscule paying out reel 3 passes through corresponding ramuscule and wears
Winding, the corresponding PBT blend filament unwrapping wire of PBT paying out reel 6, the ramuscule when taking up one's knitting are rubbed between axis 8 and thick branch polyester filament
2 driving ramuscule paying out reel 3 of unwrapping wire driving discharges ramuscule polyester filament, and ramuscule polyester filament is worn axis 8 and worn from ramuscule through ramuscule
8 end release of axis, the thick 9 thick branch paying out reel 10 of driving of branch unwrapping wire driving discharge thick branch polyester filament, thick branch polyester filament and ramuscule
Female silk is rubbed into for 1:(2-4) according to quantity ratio between polyester filament, when the quantity of the ramuscule paying out reel 3 of 1 one end of end is two
When, it is two and Zhi Dilun that the ramuscule of the first polyester filament from twister structure 4 and the second polyester filament from twister structure 5, which wears axis 8,
Female silk is rubbed into for 1:2 according to quantity ratio between long filament and ramuscule polyester filament；When the number of the ramuscule paying out reel 3 of 1 one end of end
When amount is three, it is three that the ramuscule of the first polyester filament from twister structure 4 and the second polyester filament from twister structure 5, which wears axis 8, and
Female silk is rubbed into for 1:3 according to quantity ratio between thick branch polyester filament and ramuscule polyester filament, ramuscule polyester filament quantity is more,
The thickness of fabric is bigger, then, PBT paying out reel 6 PBT unwrapping wire driving 7 driving under discharge coloring PBT blend filament and with
It is rubbed between two female silks, according to quantity than being woven into the face with lines, color for 2:1 between female silk and PBT blend filament
Material knits line, a variety of when needing to be capable of forming PBT blend filament when rubbing between thick branch polyester filament, ramuscule polyester filament
The fabric of different lines knits line, is blended by the revolving speed and two buses of 7 control PBT paying out reel 6 of PBT unwrapping wire driving with PBT
The speed for rubbing winding of long filament so that fabric knit line processing when can directly dye a variety of different decorative patterns,
Lines.
The present invention is when in use: the selection of raw material is first carried out, using 1100D high strength industrial polyester filament as thick Zhi Di
Synthetic fibre long filament, ramuscule polyester filament, wherein the quantity ratio of thick branch polyester filament and ramuscule polyester filament is 1:(2-4)；
It is then coloured, is mixed dyestuff and PBT blend filament using blender when coloring, to PBT after mixing color matching
Blend filament is dried；It is dried, the PBT blend filament by coloring is dried using drying machine, drying machine again
Temperature control at 200-250 DEG C, drying time 5-8min, PBT blend filament needs between long filament and long filament point when dry
From not knotting, do not wind；
And then woven, using braiding apparatus by between thick branch polyester filament, ramuscule polyester filament and PBT blend filament into
Row braiding is rubbed, and the quantity of the ramuscule paying out reel 3 at 1 both ends of braiding apparatus end is corresponding with the quantity that ramuscule wears axis 8, both ends
The quantitative range of ramuscule paying out reel 3 is 2-4, and when taking up one's knitting, 2 driving ramuscule paying out reel 3 of ramuscule unwrapping wire driving discharges ramuscule
Polyester filament, ramuscule polyester filament wear axis 8 through ramuscule and wear 8 end release of axis, the thick branch of thick 9 driving of branch unwrapping wire driving from ramuscule
Paying out reel 10 discharges thick branch polyester filament, rubs between thick branch polyester filament and ramuscule polyester filament according to quantity ratio for 1:(2-4)
It is twisted female silk, when the quantity of the ramuscule paying out reel 3 of 1 one end of end is two, the first polyester filament is washed from twister structure 4 with second
The ramuscule of synthetic fibre long filament from twister structure 5 wears axis 8, and to be between two and branch polyester filament and ramuscule polyester filament be according to quantity ratio
1:2 rubs into female silk；When the quantity of the ramuscule paying out reel 3 of 1 one end of end be three when, the first polyester filament from twister structure 4 with
It is three that the ramuscule of second polyester filament from twister structure 5, which wears axis 8, and between thick branch polyester filament and ramuscule polyester filament according to
Quantity ratio is that 1:3 rubs into female silk, and ramuscule polyester filament quantity is more, and the thickness of fabric is bigger, and PBT paying out reel 6 is in PBT unwrapping wire
The PBT blend filament of coloring is discharged under the driving of driving 7 and is rubbed between two female silks, between female silk and PBT blend filament
Knit line than being woven into the fabric with lines, color for 2:1 according to quantity, when need to make PBT blend filament with thick Zhi Dilun
The fabric that a variety of different lines are capable of forming when rubbing between long filament, ramuscule polyester filament knits line, passes through 7 control of PBT unwrapping wire driving
The speed for rubbing winding of the revolving speed of PBT paying out reel 6 processed and two buses and PBT blend filament, so that fabric
A variety of different decorative patterns, lines can directly be dyed in processing by knitting line；
And then, it fabric is knitted into line after completing braiding is put into inside wire drawing machine and carry out co-extrusion；Then utilized using weaving
The fabric for completing co-extrusion is knitted line and is woven into fabric finished product by weaving loom；Finally, arrange complete weaving fabric finished product trimmed,
Ironing.
The above content is just an example and description of the concept of the present invention, affiliated those skilled in the art
It makes various modifications or additions to the described embodiments or is substituted in a similar manner, without departing from invention
Design or beyond the scope defined by this claim, be within the scope of protection of the invention.
Claims (6)
- The production technology of multi-functional bed necessaries fabric 1. polyester filament interweaves, it is characterised in that: the bed necessaries fabric uses thick Zhi Dilun Long filament, ramuscule polyester filament and PBT blend filament are raw material, which is prepared by the following steps to obtain:Raw material selection, coloring, drying, braiding, co-extrusion, weaving and arrangement；It includes choosing using 1100D high strength industrial polyester filament as thick branch polyester filament, ramuscule terylene that the raw material, which is chosen, Long filament, wherein the quantity ratio of thick branch polyester filament and ramuscule polyester filament is 1:(2-4)；The coloring is mixed dyestuff and PBT blend filament using blender, is carried out after mixing color matching to PBT blend filament It is dry；The drying is dried the PBT blend filament by coloring using drying machine, and the temperature of drying machine is controlled in 200- 250 DEG C, drying time 5-8min, PBT blend filament needs to separate when dry between long filament and long filament, does not knot, does not wind；The braiding will be woven using braiding apparatus between thick branch polyester filament, ramuscule polyester filament and PBT blend filament Rub, will according to quantity ratio be 1:(2-4 between thick branch polyester filament and ramuscule polyester filament) rub into female silk, then by female silk with Line is knitted than being woven into the fabric with lines, color for 2:1 according to quantity between PBT blend filament；The co-extrusion, which is used, knits line progress wire drawing co-extrusion to fabric for wire drawing machine；The fabric for completing co-extrusion is knitted line using weaving loom and is woven into fabric finished product by the weaving；It is described arrange complete weaving fabric finished product trimmed, ironing.
- The production technology of multi-functional bed necessaries fabric 2. polyester filament according to claim 1 interweaves, it is characterised in that: described The braiding apparatus used during braiding includes that end (1), ramuscule unwrapping wire driving (2), ramuscule paying out reel (3), the first terylene are long Silk wears axis from twister structure (4), the second polyester filament from twister structure (5), PBT paying out reel (6), PBT unwrapping wire driving (7), ramuscule (8), thick branch unwrapping wire drives (9), thick branch paying out reel (10), and end (1) both ends are mounted on ramuscule paying out reel (3), described Ramuscule paying out reel (3) one end is connected with ramuscule unwrapping wire driving (2), and it is long to be provided with the first terylene below end (1) both ends For silk from twister structure (4), the second polyester filament from twister structure (5), first polyester filament is long from twister structure (4), the second terylene Silk is provided with PBT paying out reel (6) from lower section between twister structure (5), PBT paying out reel (6) bottom end and PBT unwrapping wire driving (7) It is connected, first polyester filament wears axis by several ramuscules from twister structure (4), the second polyester filament from twister structure (5) (8) it constitutes, several described ramuscules are worn and are provided with thick branch paying out reel (10) between axis (8), described thick branch paying out reel (10) one end It is connected with thick branch unwrapping wire driving (9).
- The production technology of multi-functional bed necessaries fabric 3. polyester filament according to claim 2 interweaves, it is characterised in that: described The quantity of the ramuscule paying out reel (3) at end (1) both ends is corresponding with the quantity that ramuscule wears axis (8), and the ramuscule at end (1) both ends The quantitative range of paying out reel (3) is 2-4.
- The production technology of multi-functional bed necessaries fabric 4. polyester filament according to claim 2 interweaves, it is characterised in that: described Ramuscule paying out reel (3) corresponds to ramuscule polyester filament unwrapping wire, and the thick branch paying out reel (10) is used for thick branch polyester filament unwrapping wire, and thin The put ramuscule polyester filament of branch paying out reel (3) is worn across corresponding ramuscule and rubs winding axis (8) and thick branch polyester filament.
- The production technology of multi-functional bed necessaries fabric 5. polyester filament according to claim 2 interweaves, it is characterised in that: described PBT paying out reel (6) corresponds to PBT blend filament unwrapping wire.
- The production technology of multi-functional bed necessaries fabric 6. polyester filament according to claim 2 interweaves, it is characterised in that: described By being rotatablely connected between ramuscule unwrapping wire driving (2) and end (1), the thick branch paying out reel (10) passes through ramuscule paying out reel (3) Thick branch unwrapping wire driving (9) and ramuscule are worn and are rotatablely connected between axis (8), the PBT paying out reel (6) by PBT unwrapping wire driving (7) and First polyester filament is rotatablely connected from twister structure (4), the second polyester filament between twister structure (5).