CN109762410A - A kind of production method of top grade nano-antibacterial emulsion paint - Google Patents
A kind of production method of top grade nano-antibacterial emulsion paint Download PDFInfo
- Publication number
- CN109762410A CN109762410A CN201811264000.7A CN201811264000A CN109762410A CN 109762410 A CN109762410 A CN 109762410A CN 201811264000 A CN201811264000 A CN 201811264000A CN 109762410 A CN109762410 A CN 109762410A
- Authority
- CN
- China
- Prior art keywords
- kilogram
- kilograms
- emulsion paint
- antibacterial
- grade nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-grade nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint is mainly prepared from the following materials: polyvinyl acetate emulsion, ethylene glycol, calgon, ammonium hydroxide, tbp, sodium bentonite, rutile-type phthalein white powder and silver ion antimicrobial agent;By selecting the high-quality lotion of high-purity and high-quality raw material to blend with advanced technique, comply fully with national standard, the volatilization of itself zero VOC, product harmful gas emission is negligible, can effectively be purified the air of a room quality, there is extremely strong inhibiting effect for the growth and breeding for each quasi-microorganism being detrimental to health, antibiotic rate reaches 99% or more, and safety and environmental protection, the characteristic and construction technology of coating itself are not influenced, and then achieve the purpose that cleaning ambient, its production technology is uncomplicated, it is easy to operate practical, stable product quality, the present invention has dual antibacterial bacteriostatic, it is long-acting nontoxic, the advantages of persistent.
Description
Technical field
The invention belongs to emulsion paint preparation technical fields, and in particular to a kind of producer of top grade nano-antibacterial emulsion paint
Method.
Background technique
High-grade nano-antibacterial emulsion paint is mainly film forming matter, coalescing agent, filler material, filler, pigment, defoaming agent, resists
Microbial inoculum composition, use polyvinyl acetate emulsion for film forming matter come improve film have scrub performance, ethylene glycol be coalescing agent,
Rutile-type phthalein white powder is filler material, sodium bentonite is filler, tbp is defoaming agent, preferably resolves cream
The problem of shellac varnish viscosity is low, difference of hardness, enhances the crack resistance and glossiness of emulsion paint.Using silver ion antimicrobial agent, pass through silver
Ion and the incidental opposite charge principle of bacterium, therefore be adsorbed to together, so that bacterium is lost mobility, to reach
The purpose of antibiotic health care.
In conventional liquid coating, existing water, and germy grain, it is easy to be contaminated by bacterial, go bad in order to prevent,
Adding preservative agent, and powdery emulsion paint no bacteria pollution problem, are not required to preservative, it is therefore desirable to a kind of strong for harmful to human
The growth and breeding of each quasi-microorganism of health has extremely strong inhibiting effect, and antibiotic rate reaches 99% or more, and the painting of safety and environmental protection
Material.
Summary of the invention
The purpose of the present invention is to provide a kind of production methods of high-grade nano-antibacterial emulsion paint, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the invention provides the following technical scheme: a kind of top grade nano-antibacterial emulsion paint, the height
Shelves nano-antibacterial emulsion paint is mainly prepared from the following materials: polyvinyl acetate emulsion, ethylene glycol, calgon, ammonia
Water, tbp, sodium bentonite, rutile-type phthalein white powder and silver ion antimicrobial agent.
Preferably, the raw material for preparing is calculated by weight: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, six are partially
0.35 kilogram of sodium phosphate, 0.05 kilogram of tbp, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver from
Son does 0.02 kilogram of microbial inoculum, 5 kilograms of water and appropriate ammonium hydroxide.
A kind of production method of top grade nano-antibacterial emulsion paint, including a kind of high described in any one of preparation this paper
The production method of shelves nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint comprises the steps of:
S1, choose following raw material: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, 0.35 kilogram of calgon,
It is public that 0.05 kilogram of tbp, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion do microbial inoculum 0.02
Jin, 5 kilograms of water and appropriate ammonium hydroxide;
S2, in advance with water by sodium bentonite impregnate 24 hours it is spare;
S3, calgon is dissolved with hot water, is added to the water of formula ratio in agitator tank;
S4, soaked sodium base bentonite is added in agitator tank, and stirred evenly;
S5, rutile-type phthalein white powder then is sequentially added, silver ion does microbial inoculum, tbp, and stirs evenly;
S6, will grind in the above-mentioned mixed raw material injection grinder of institute or in colloidal film it is careful;
S7, it ph value is carried out to mixed liquor with spare appropriate ammonium hydroxide is adjusted, be adjusted to 7;
S8, polyvinyl acetate emulsion and ethylene glycol sequentially added again;
S9, it is stirred uniformly, can discharge packaging after filtering.
Compared with prior art, the beneficial effects of the present invention are: by selecting the high-quality lotion of high-purity and high-quality raw material
It is blended with advanced technique, complies fully with national standard, itself zero VOC volatilization, product harmful gas emission can be ignored
Disregard, can effectively purify the air of a room quality, and decomposition occupies indoor furniture peculiar smell, absorb pernicious gas, effectively remove formaldehyde,
Toluene can effectively cover fine cracks, achieve the effect that beautiful and modification wall, enhance service life, have both beautiful and anti-
Collarium protects practicability, reduces harm of the microorganism to human body, and nano-antibacterial emulsion paint is in outer architectural latex coating and nano combined builds
On the basis of building the application study status of emulsion paint, the new approaches using nano-powder antibacterial (interior) wall emulsion paint are proposed, are
Have studied the external wall emulsion paint weatherability of the factors such as type, additive amount, the dispersing mode of nano-powder material, washability to system
Property, the influence of performances such as water-alkali resistance and these factors are to interiro wall latex paint antibiotic and sterilizing, degradation harmful organic substance etc.
The influence of performance successfully develops nano modification external wall and interiro wall latex paint product, and common interior wall is added in antibacterial powder
Nano-antibacterial interiro wall latex paint is made in emulsion paint, it is new can to assign interiro wall latex paint on the basis of keeping its original function
Function, the both harmful organic substances such as catalytic degradation formaldehyde, restraining and sterilizing bacteria etc., the life for each quasi-microorganism being detrimental to health
Long breeding has extremely strong inhibiting effect, and antibiotic rate reaches 99% or more, and safety and environmental protection, does not influence the characteristic of coating itself
And construction technology, and then achieving the purpose that cleaning ambient, production technology is uncomplicated, and easy to operate practical, product quality is steady
The advantages of fixed, the present invention has dual antibacterial bacteriostatic, long-acting nontoxic, persistent.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical solution in the embodiment of the present invention is clearly and completely retouched
It states, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on the present invention
In embodiment, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment 1
A kind of top grade nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint are mainly prepared from the following materials:
Polyvinyl acetate emulsion, ethylene glycol, calgon, ammonium hydroxide, tbp, sodium bentonite, rutile-type phthalein white powder and
Silver ion antimicrobial agent, the raw material for preparing are calculated by weight: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, six inclined phosphorus
0.35 kilogram of sour sodium, 0.05 kilogram of tbp, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion
Do 0.02 kilogram of microbial inoculum, 5 kilograms of water and appropriate ammonium hydroxide.
A kind of production method of top grade nano-antibacterial emulsion paint, including a kind of high described in any one of preparation this paper
The production method of shelves nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint comprises the steps of:
S1, choose following raw material: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, 0.35 kilogram of calgon,
It is public that 0.05 kilogram of tbp, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion do microbial inoculum 0.02
Jin, 5 kilograms of water and appropriate ammonium hydroxide;
S2, in advance with water by sodium bentonite impregnate 24 hours it is spare;
S3, calgon is dissolved with hot water, is added to the water of formula ratio in agitator tank;
S4, soaked sodium base bentonite is added in agitator tank, and stirred evenly;
S5, rutile-type phthalein white powder then is sequentially added, silver ion does microbial inoculum, tbp, and stirs evenly;
S6, will grind in the above-mentioned mixed raw material injection grinder of institute or in colloidal film it is careful;
S7, it ph value is carried out to mixed liquor with spare appropriate ammonium hydroxide is adjusted, be adjusted to 7;
S8, polyvinyl acetate emulsion and ethylene glycol sequentially added again;
S9, it is stirred uniformly, can discharge packaging after filtering.
Embodiment 2
A kind of top grade nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint are mainly prepared from the following materials:
Polyvinyl acetate emulsion, ethylene glycol, calgon, ammonium hydroxide, tbp, sodium bentonite, rutile-type phthalein white powder and
Silver ion antimicrobial agent, the raw material for preparing are calculated by weight: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, six inclined phosphorus
0.35 kilogram of sour sodium, 0.05 kilogram of tbp, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion
Do 0.02 kilogram of microbial inoculum, 5 kilograms of water and appropriate ammonium hydroxide.
A kind of production method of top grade nano-antibacterial emulsion paint, including a kind of high described in any one of preparation this paper
The production method of shelves nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint comprises the steps of:
S1, following raw material: 66.5 kilograms of polyvinyl acetate emulsion, 3.8 kilograms of ethylene glycol, calgon 0.315 is chosen
Kilogram, 0.0475 kilogram of tbp, 0.95 kilogram of sodium bentonite, 19 kilograms of rutile-type phthalein white powder, silver ion do bacterium
0.019 kilogram of agent, 4.6 kilograms of water and appropriate ammonium hydroxide;
S2, in advance with water by sodium bentonite impregnate 24 hours it is spare;
S3, calgon is dissolved with hot water, is added to the water of formula ratio in agitator tank;
S4, soaked sodium base bentonite is added in agitator tank, and stirred evenly;
S5, rutile-type phthalein white powder then is sequentially added, silver ion does microbial inoculum, tbp, and stirs evenly;
S6, will grind in the above-mentioned mixed raw material injection grinder of institute or in colloidal film it is careful;
S7, it ph value is carried out to mixed liquor with spare appropriate ammonium hydroxide is adjusted, be adjusted to 7;
S8, polyvinyl acetate emulsion and ethylene glycol sequentially added again;
S9, it is stirred uniformly, can discharge packaging after filtering.
Embodiment 3
A kind of top grade nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint are mainly prepared from the following materials:
Polyvinyl acetate emulsion, ethylene glycol, calgon, ammonium hydroxide, tbp, sodium bentonite, rutile-type phthalein white powder and
Silver ion antimicrobial agent, the raw material for preparing are calculated by weight: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, six inclined phosphorus
0.35 kilogram of sour sodium, 0.05 kilogram of tbp, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion
Do 0.02 kilogram of microbial inoculum, 5 kilograms of water and appropriate ammonium hydroxide.
A kind of production method of top grade nano-antibacterial emulsion paint, including a kind of high described in any one of preparation this paper
The production method of shelves nano-antibacterial emulsion paint, the top grade nano-antibacterial emulsion paint comprises the steps of:
S1, choose following raw material: 63 kilograms of polyvinyl acetate emulsion, 3.6 kilograms of ethylene glycol, calgon 0.315 are public
Jin, 0.045 kilogram of tbp, 0.9 kilogram of sodium bentonite, 18 kilograms of rutile-type phthalein white powder, silver ion do microbial inoculum
0.018 kilogram, 4.5 kilograms of water and appropriate ammonium hydroxide;
S2, in advance with water by sodium bentonite impregnate 24 hours it is spare;
S3, calgon is dissolved with hot water, is added to the water of formula ratio in agitator tank;
S4, soaked sodium base bentonite is added in agitator tank, and stirred evenly;
S5, rutile-type phthalein white powder then is sequentially added, silver ion does microbial inoculum, tbp, and stirs evenly;
S6, will grind in the above-mentioned mixed raw material injection grinder of institute or in colloidal film it is careful;
S7, it ph value is carried out to mixed liquor with spare appropriate ammonium hydroxide is adjusted, be adjusted to 7;
S8, polyvinyl acetate emulsion and ethylene glycol sequentially added again;
S9, it is stirred uniformly, can discharge packaging after filtering.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (3)
1. a kind of top grade nano-antibacterial emulsion paint, it is characterised in that: the top grade nano-antibacterial emulsion paint is mainly by following raw material
It is prepared: polyvinyl acetate emulsion, ethylene glycol, calgon, ammonium hydroxide, tbp, sodium bentonite, rutile-type
Phthalein white powder and silver ion antimicrobial agent.
2. a kind of high-grade nano-antibacterial emulsion paint according to claim 1, it is characterised in that: described to prepare raw material by weight
Calculate: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, 0.35 kilogram of calgon, 0.05 kilogram of tbp,
1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion do 0.02 kilogram of microbial inoculum, 5 kilograms of water and appropriate ammonium hydroxide.
3. a kind of production method of top grade nano-antibacterial emulsion paint, including described in any one of preparation claim 1-2 one
Kind of high-grade nano-antibacterial emulsion paint, it is characterized by: the production method of the top grade nano-antibacterial emulsion paint includes following step
It is rapid:
S1, following raw material: 70 kilograms of polyvinyl acetate emulsion, 4 kilograms of ethylene glycol, 0.35 kilogram of calgon, phosphoric acid is chosen
0.05 kilogram of tri butyl ester, 1 kilogram of sodium bentonite, 20 kilograms of rutile-type phthalein white powder, silver ion do 0.02 kilogram of microbial inoculum, water 5
Kilogram and appropriate ammonium hydroxide;
S2, in advance with water by sodium bentonite impregnate 24 hours it is spare;
S3, calgon is dissolved with hot water, is added to the water of formula ratio in agitator tank;
S4, soaked sodium base bentonite is added in agitator tank, and stirred evenly;
S5, rutile-type phthalein white powder then is sequentially added, silver ion does microbial inoculum, tbp, and stirs evenly;
S6, will grind in the above-mentioned mixed raw material injection grinder of institute or in colloidal film it is careful;
S7, it ph value is carried out to mixed liquor with spare appropriate ammonium hydroxide is adjusted, be adjusted to 7;
S8, polyvinyl acetate emulsion and ethylene glycol sequentially added again;
S9, it is stirred uniformly, can discharge packaging after filtering.