CN109749399A - 一种汽车轮胎用橡胶材料 - Google Patents
一种汽车轮胎用橡胶材料 Download PDFInfo
- Publication number
- CN109749399A CN109749399A CN201711066975.4A CN201711066975A CN109749399A CN 109749399 A CN109749399 A CN 109749399A CN 201711066975 A CN201711066975 A CN 201711066975A CN 109749399 A CN109749399 A CN 109749399A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- rubber
- automobile tire
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种汽车轮胎用橡胶材料,主要由以质量份数计的以下成分组成:聚氨酯橡胶50‑80份、炭黑0.5‑4份、氯丁橡胶20‑30份、丙烯酸酯橡胶5‑8份、补强剂0.4‑0.8份、防老剂0.05‑0.15份、促进剂0.1‑0.3份、硫化剂0.4‑0.8份、增塑剂1‑2份、偶联剂0.5‑1.2份、改性蛭石粉3‑5份、轻钙粉4‑12份。本发明的橡胶材料通过增大炭黑的比例与改性蛭石粉的添加能够大大提高其耐磨性能及抓地力,特别适合作为汽车轮胎材料。
Description
技术领域
本发明涉及高分子材料制备技术领域,尤其涉及一种汽车轮胎用橡胶材料。
背景技术
汽车轮胎多采用橡胶制成,这就对橡胶的耐磨性能做出了非常高的要求,既要兼顾抓地力又要兼顾耐磨性,现有的橡胶轮胎的使用寿命在3年左右。
发明内容
为了解决上述技术问题,提供一种汽车轮胎专用的橡胶材料,本发明提供以下技术方案:
一种汽车轮胎用橡胶材料,由以质量份数计的以下成分组成:聚氨酯橡胶50-80份、炭黑0.5-4份、氯丁橡胶20-30份、丙烯酸酯橡胶5-8份、补强剂0.4-0.8份、防老剂0.05-0.15份、促进剂0.1-0.3份、硫化剂0.4-0.8份、增塑剂1-2份、偶联剂0.5-1.2份、改性蛭石粉3-5份、轻钙粉4-12份。
进一步的,由以质量份数计的以下成分组成:聚氨酯橡胶65份、炭黑2.2份、氯丁橡胶25份、丙烯酸酯橡胶6.5份、补强剂0.6份、防老剂0.1份、促进剂0.2份、硫化剂0.6份、增塑剂1.5份、偶联剂0.8份、改性蛭石粉4份、轻钙粉8份。
进一步的,由以质量份数计的以下成分组成:聚氨酯橡胶50份、炭黑0.5份、氯丁橡胶20份、丙烯酸酯橡胶5份、补强剂0.4份、防老剂0.05份、促进剂0.1份、硫化剂0.4份、增塑剂1份、偶联剂0.5份、改性蛭石粉3份、轻钙粉4份。
进一步的,由以质量份数计的以下成分组成:聚氨酯橡胶80份、炭黑4份、氯丁橡胶30份、丙烯酸酯橡胶8份、补强剂0.8份、防老剂0.15份、促进剂0.3份、硫化剂0.8份、增塑剂2份、偶联剂1.2份、改性蛭石粉5份、轻钙粉12份。
本发明的有益效果在于:通过增大炭黑的比例与改性蛭石粉的添加能够大大提高其耐磨性能及抓地力,特别适合作为汽车轮胎材料。
具体实施方式
实施例1、
一种汽车轮胎用橡胶材料,聚氨酯橡胶65份、炭黑2.2份、氯丁橡胶25份、丙烯酸酯橡胶6.5份、补强剂0.6份、防老剂0.1份、促进剂0.2份、硫化剂0.6份、增塑剂1.5份、偶联剂0.8份、改性蛭石粉4份、轻钙粉8份。实施例2、
一种汽车轮胎用橡胶材料,由以质量份数计的以下成分组成:聚氨酯橡胶50份、炭黑0.5份、氯丁橡胶20份、丙烯酸酯橡胶5份、补强剂0.4份、防老剂0.05份、促进剂0.1份、硫化剂0.4份、增塑剂1份、偶联剂0.5份、改性蛭石粉3份、轻钙粉4份。
实施例3、
一种汽车轮胎用橡胶材料,由以质量份数计的以下成分组成:聚氨酯橡胶80份、炭黑4份、氯丁橡胶30份、丙烯酸酯橡胶8份、补强剂0.8份、防老剂0.15份、促进剂0.3份、硫化剂0.8份、增塑剂2份、偶联剂1.2份、改性蛭石粉5份、轻钙粉12份。
以上述依据本发明理想实施例为启示,通过上述的说明内容,相关工作人员完全可以在不偏离本项发明技术思想的范围内,进行多样的变更以及修改。本项发明的技术性范围并不局限于说明书上的内容,必须要根据权利要求范围来确定其技术性范围。
Claims (4)
1.一种汽车轮胎用橡胶材料,其特征在于:由以质量份数计的以下成分组成:聚氨酯橡胶50-80份、炭黑0.5-4份、氯丁橡胶20-30份、丙烯酸酯橡胶5-8份、补强剂0.4-0.8份、防老剂0.05-0.15份、促进剂0.1-0.3份、硫化剂0.4-0.8份、增塑剂1-2份、偶联剂0.5-1.2份、改性蛭石粉3-5份、轻钙粉4-12份。
2.如权利要求1所述的一种汽车轮胎用橡胶材料,其特征在于:由以质量份数计的以下成分组成:聚氨酯橡胶65份、炭黑2.2份、氯丁橡胶25份、丙烯酸酯橡胶6.5份、补强剂0.6份、防老剂0.1份、促进剂0.2份、硫化剂0.6份、增塑剂1.5份、偶联剂0.8份、改性蛭石粉4份、轻钙粉8份。
3.如权利要求1所述的一种汽车轮胎用橡胶材料,其特征在于:由以质量份数计的以下成分组成:聚氨酯橡胶50份、炭黑0.5份、氯丁橡胶20份、丙烯酸酯橡胶5份、补强剂0.4份、防老剂0.05份、促进剂0.1份、硫化剂0.4份、增塑剂1份、偶联剂0.5份、改性蛭石粉3份、轻钙粉4份。
4.如权利要求1所述的一种汽车轮胎用橡胶材料,其特征在于:由以质量份数计的以下成分组成:聚氨酯橡胶80份、炭黑4份、氯丁橡胶30份、丙烯酸酯橡胶8份、补强剂0.8份、防老剂0.15份、促进剂0.3份、硫化剂0.8份、增塑剂2份、偶联剂1.2份、改性蛭石粉5份、轻钙粉12份。