CN109749181A - 一种耐压绝缘材料 - Google Patents

一种耐压绝缘材料 Download PDF

Info

Publication number
CN109749181A
CN109749181A CN201711051238.7A CN201711051238A CN109749181A CN 109749181 A CN109749181 A CN 109749181A CN 201711051238 A CN201711051238 A CN 201711051238A CN 109749181 A CN109749181 A CN 109749181A
Authority
CN
China
Prior art keywords
parts
insulating materials
pressure
cooled
cosolvent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711051238.7A
Other languages
English (en)
Inventor
王云华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Danyang Boya New Material Technology Services Ltd
Original Assignee
Danyang Boya New Material Technology Services Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Danyang Boya New Material Technology Services Ltd filed Critical Danyang Boya New Material Technology Services Ltd
Priority to CN201711051238.7A priority Critical patent/CN109749181A/zh
Publication of CN109749181A publication Critical patent/CN109749181A/zh
Withdrawn legal-status Critical Current

Abstract

本发明涉及一种耐压绝缘材料，所述耐压绝缘材料的组分按照重量份如下所示：丁苯橡胶20‑25份,异戊橡胶15‑20份，聚乙烯蜡20‑25份，三甘醇二异辛酸酯5‑10份，聚丁二烯环氧树脂15‑20份，纳米二氧化硅2‑5份，偶氮二异丁腈2‑4份，助溶剂5‑8份，增稠剂1‑3份，固化剂0.5‑0.8份。本发明制作工艺简单，原料易于购买，制作成本低廉，绝缘效果好，且耐压性能好具有广阔的应用前景。

Description

一种耐压绝缘材料
技术领域
本发明涉及绝缘材料技术领域，尤其涉及一种耐压绝缘材料。
背景技术
现有技术中绝缘子材料一般选择绝缘玻璃或者陶瓷，但是陶瓷是脆性材料，而且陶瓷表面光滑度没有绝缘玻璃好，为了提高绝缘子耐污闪性能，采用表面光洁度高的耐压玻璃效果会相对好，但是高压电线用绝缘子使用时间长以后，会出现局部闪络现象，所以增加耐压玻璃表面的机械强度，增加其耐冲击性，防止绝缘子表面泄露电流增大，产生局部电弧和出现闪络现象。
发明内容
为解决上述问题，本发明提供了一种耐压绝缘材料。
本发明的技术方案如下：
一种耐压绝缘材料，其特征在于：所述耐压绝缘材料的组分按照重量份如下所示：丁苯橡胶20-25份,异戊橡胶15-20份，聚乙烯蜡20-25份，三甘醇二异辛酸酯5-10份，聚丁二烯环氧树脂15-20份，纳米二氧化硅2-5份，偶氮二异丁腈2-4份，助溶剂5-8份，增稠剂1-3份，固化剂0.5-0.8份。
进一步的，所述助溶剂为尿素，菸酰胺和乙酰胺中的一种。
进一步的，所述增稠剂为羧甲基纤维素钠、藻酸丙二醇酯和卡拉胶中的一种。
进一步的，所述固化剂为二氨基二苯基砜、联苯胺中的一种。
更进一步的，一种耐压绝缘材料制备方法，其特征在于：
S1：将丁苯橡胶，异戊橡胶，聚乙烯蜡，三甘醇二异辛酸酯，聚丁二烯环氧树脂，偶氮二异丁腈，增稠剂放入反应釜内，于120-140℃条件下高速搅拌30min；
S2：在反应釜中加入纳米二氧化硅和助溶剂，高速搅拌15min后降温至80℃，低速搅拌8h；
S3：将反应釜冷却降温至40-60℃加入固化剂低速搅拌30min；
S4：将反应釜冷却至室温，静置1h后即可得到成品。
借由上述方案，本发明至少具有如下优点：
本发明制作工艺简单，原料易于购买，制作成本低廉，绝缘效果好，且耐压性能好具有广阔的应用前景。
具体实施方式
下面结合实施例对本发明的技术方案作如下详细说明。
实施例1
一种耐压绝缘材料，其特征在于：所述耐压绝缘材料的组分按照重量份如下所示：丁苯橡胶21份,异戊橡胶19份，聚乙烯蜡24份，三甘醇二异辛酸酯6份，聚丁二烯环氧树脂15份，纳米二氧化硅3份，偶氮二异丁腈2份，菸酰胺5份，藻酸丙二醇酯1份，二氨基二苯基砜0.5份。
其制备方法为：
S1：将丁苯橡胶，异戊橡胶，聚乙烯蜡，三甘醇二异辛酸酯，聚丁二烯环氧树脂，偶氮二异丁腈，增稠剂放入反应釜内，于120-140℃条件下高速搅拌30min；
S2：在反应釜中加入纳米二氧化硅和助溶剂，高速搅拌15min后降温至80℃，低速搅拌8h；
S3：将反应釜冷却降温至40-60℃加入固化剂低速搅拌30min；
S4：将反应釜冷却至室温，静置1h后即可得到成品。
实施例2
一种耐压绝缘材料，其特征在于：所述耐压绝缘材料的组分按照重量份如下所示：丁苯橡胶22份,异戊橡胶18份，聚乙烯蜡25份，三甘醇二异辛酸酯5份，聚丁二烯环氧树脂17份，纳米二氧化硅3份，偶氮二异丁腈4份，尿素8份，卡拉胶3份，二氨基二苯基砜0.8份。
其制备方法为：
S1：将丁苯橡胶，异戊橡胶，聚乙烯蜡，三甘醇二异辛酸酯，聚丁二烯环氧树脂，偶氮二异丁腈，增稠剂放入反应釜内，于120-140℃条件下高速搅拌30min；
S2：在反应釜中加入纳米二氧化硅和助溶剂，高速搅拌15min后降温至80℃，低速搅拌8h；
S3：将反应釜冷却降温至40-60℃加入固化剂低速搅拌30min；
S4：将反应釜冷却至室温，静置1h后即可得到成品。
实施例3
一种耐压绝缘材料，其特征在于：所述耐压绝缘材料的组分按照重量份如下所示：丁苯橡胶23份,异戊橡胶18份，聚乙烯蜡22份，三甘醇二异辛酸酯8份，聚丁二烯环氧树脂17份，纳米二氧化硅2份，偶氮二异丁腈2-4份，乙酰胺6份，羧甲基纤维素钠2份，联苯胺0.7份。
其制备方法为：
S1：将丁苯橡胶，异戊橡胶，聚乙烯蜡，三甘醇二异辛酸酯，聚丁二烯环氧树脂，偶氮二异丁腈，增稠剂放入反应釜内，于120-140℃条件下高速搅拌30min；
S2：在反应釜中加入纳米二氧化硅和助溶剂，高速搅拌15min后降温至80℃，低速搅拌8h；
S3：将反应釜冷却降温至40-60℃加入固化剂低速搅拌30min；
S4：将反应釜冷却至室温，静置1h后即可得到成品。
以上所述仅是本发明的优选实施方式，并不用于限制本发明，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和变型，这些改进和变型也应视为本发明的保护范围。

Claims (5)

1.一种耐压绝缘材料，其特征在于：所述耐压绝缘材料的组分按照重量份如下所示：丁苯橡胶20-25份,异戊橡胶15-20份，聚乙烯蜡20-25份，三甘醇二异辛酸酯5-10份，聚丁二烯环氧树脂15-20份，纳米二氧化硅2-5份，偶氮二异丁腈2-4份，助溶剂5-8份，增稠剂1-3份，固化剂0.5-0.8份。
2.根据权利要求1所述的一种耐压绝缘材料，其特征在于：所述助溶剂为尿素，菸酰胺和乙酰胺中的一种。
3.根据权利要求1所述的一种耐压绝缘材料，其特征在于：所述增稠剂为羧甲基纤维素钠、藻酸丙二醇酯和卡拉胶中的一种。
4.根据权利要求1所述的一种耐压绝缘材料，其特征在于：所述固化剂为二氨基二苯基砜、联苯胺中的一种。
5.根据权利要求1所述的一种耐压绝缘材料制备方法，其特征在于：
S1：将丁苯橡胶，异戊橡胶，聚乙烯蜡，三甘醇二异辛酸酯，聚丁二烯环氧树脂，偶氮二异丁腈，增稠剂放入反应釜内，于120-140℃条件下高速搅拌30min；
S2：在反应釜中加入纳米二氧化硅和助溶剂，高速搅拌15min后降温至80℃，低速搅拌8h；
S3：将反应釜冷却降温至40-60℃加入固化剂低速搅拌30min；
S4：将反应釜冷却至室温，静置1h后即可得到成品。
CN201711051238.7A 2017-11-01 2017-11-01 一种耐压绝缘材料 Withdrawn CN109749181A (zh)