CN109747040A - The stirring means of High Strength Non-shrinking Filling Material for duct grouting - Google Patents
The stirring means of High Strength Non-shrinking Filling Material for duct grouting Download PDFInfo
- Publication number
- CN109747040A CN109747040A CN201711091828.2A CN201711091828A CN109747040A CN 109747040 A CN109747040 A CN 109747040A CN 201711091828 A CN201711091828 A CN 201711091828A CN 109747040 A CN109747040 A CN 109747040A
- Authority
- CN
- China
- Prior art keywords
- blender
- high strength
- filling material
- strength non
- swing mechanism
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stirring means of High Strength Non-shrinking Filling Material for duct grouting, this method uses gear speed-changing blender, agitator realizes the rotation with blender opposite direction by swing mechanism, agitator and stirring-head are soaked in advance, water and siccative are simultaneously successively put into agitator by 100:12 by the siccative and moisture of grouting material also known as weight；It opens blender and swing mechanism, swing mechanism is rotated with 28rpm, blender is stirred 1 minute with the low or first gear of 100rpm, is then stirred 3 minutes with the top gear of 400rpm；Blender and swing mechanism are closed, High Strength Non-shrinking Filling Material is obtained.The method ensure that the stirring technique of High Strength Non-shrinking Filling Material, avoids the stirring defect of grouting material, and ensure that duct grouting quality without particular/special requirement to operating personnel.
Description
Technical field
The present invention relates to a kind of stirring means of High Strength Non-shrinking Filling Material for duct grouting.
Background technique
In construction operation process, need to implement cementing operations, the filling to duct after the completion of Precast Pier Columns, bent cap lifting
Slurry generally use High Strength Non-shrinking Filling Material, the grouting material stirring when to water content, very temperature sensitive, to operating personnel's
Skill requirement is higher, usually because the unskilled or carelessness of operating personnel causes grouting material to stir defect, leads to duct grouting matter
It measures unqualified.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of stirring for High Strength Non-shrinking Filling Material for duct grouting
Method is mixed, the method ensure that the stirring technique of High Strength Non-shrinking Filling Material, avoids the stirring defect of grouting material, and to operating personnel
Without particular/special requirement, duct grouting quality ensure that.
In order to solve the above technical problems, stirring means of the present invention for the High Strength Non-shrinking Filling Material of duct grouting include
Following steps:
Step 1: agitator realizes the rotation with blender opposite direction by swing mechanism using gear speed-changing blender, it will
Agitator and stirring-head soak in advance, the siccative and moisture of High Strength Non-shrinking Filling Material also known as weight and by 100:12 successively by water and
Siccative is put into agitator；
Step 2: unlatching blender and swing mechanism, swing mechanism are rotated with 28rpm, blender is stirred with the low or first gear of 100rpm
It mixes 1 minute, is then stirred 3 minutes with the top gear of 400rpm；
Step 3: closing blender and swing mechanism, High Strength Non-shrinking Filling Material is obtained.
Further, the gear speed-changing blender is equipped with mixing timer, and blender is set separately in the mixing timer
The mixing time of low or first gear stirring and top gear stirring.
Further, the blender uses a key control according to the setting of the time of mixing timer, and when use presses starting
Key realization stirs at low speed, high-speed stirred and stopping function.
Further, the swing mechanism includes base rotary-disc, retarder and driving motor, and the driving motor passes through deceleration
Device drives base rotary-disc rotation.
Further, swing mechanism rotates in a counter-clockwise direction in the step 2, and blender bottom gear and top gear are with clockwise
Direction rotates.
Stirring means due to the present invention for the High Strength Non-shrinking Filling Material of duct grouting use above-mentioned technical proposal,
I.e. this method uses gear speed-changing blender, and agitator is realized the rotation with blender opposite direction by swing mechanism, will stirred
It mixes bucket and stirring-head soaks in advance, water and siccative are simultaneously successively put into stirring by 100:12 by the siccative and moisture of grouting material also known as weight
Bucket；It opens blender and swing mechanism, swing mechanism is rotated with 28rpm, blender is stirred 1 minute with the low or first gear of 100rpm,
Then it is stirred 3 minutes with the top gear of 400rpm；Blender and swing mechanism are closed, High Strength Non-shrinking Filling Material is obtained.We
Method ensures the stirring technique of High Strength Non-shrinking Filling Material, avoids the stirring defect of grouting material, and to operating personnel without particular/special requirement,
It ensure that duct grouting quality.
Detailed description of the invention
The present invention will be further described in detail below with reference to the accompanying drawings and embodiments:
Fig. 1 is the present invention for blender schematic diagram in the stirring means of the High Strength Non-shrinking Filling Material of duct grouting.
Specific embodiment
Embodiment is as shown in Figure 1, the stirring means that the present invention is used for the High Strength Non-shrinking Filling Material of duct grouting include such as
Lower step:
Step 1: agitator 2 realizes the rotation with 1 opposite direction of blender by swing mechanism 3 using gear speed-changing blender 1
Turn, agitator 2 and stirring-head 11 soaked in advance, the siccative and moisture of High Strength Non-shrinking Filling Material also known as weight and by 100:12 according to
It is secondary that water and siccative are put into agitator 2；
Step 2: unlatching blender 1 and swing mechanism 3, swing mechanism 3 are rotated with 28rpm, blender 1 is with the low speed of 100rpm
Shelves stirring 1 minute, is then stirred 3 minutes with the top gear of 400rpm；
Step 3: closing blender 1 and swing mechanism 3, High Strength Non-shrinking Filling Material is obtained.
Preferably, the gear speed-changing blender 1 is equipped with mixing timer, and blender is set separately in the mixing timer
The mixing time of low or first gear stirring and top gear stirring.
Preferably, the blender 1 uses a key control according to the setting of the time of mixing timer, and when use presses starting
Key realization stirs at low speed, high-speed stirred and stopping function.
Preferably, the swing mechanism 3 includes base rotary-disc, retarder and driving motor, and the driving motor is by subtracting
Fast device driving base rotary-disc rotation.
Preferably, swing mechanism 3 rotates in a counter-clockwise direction in the step 2,1 bottom gear of blender and top gear with
It is rotated clockwise.
This method makes test block and is detected by being repeatedly stirred test to High Strength Non-shrinking Filling Material, meets
The stirring requirement of the grouting material, and then sum up the siccative of the grouting material and the match ratio of water, agitation phases, mixing speed, stir
Mix the parameters such as time；So that phenomena such as grouting material is not in irregular stirring, excessive agitation, high temperature failure, obtained grouting
Expect that performance is stablized, mixing quality is high.Operating personnel only need to temporally switch the stirring gear of blender simultaneously, to operation
The specialized capability requirement of personnel is low, is more suitable for the grouting material stirring operation of construction site.
Claims (5)
1. a kind of stirring means of the High Strength Non-shrinking Filling Material for duct grouting, it is characterised in that this method includes following step
It is rapid:
Step 1: agitator realizes the rotation with blender opposite direction by swing mechanism using gear speed-changing blender, it will
Agitator and stirring-head soak in advance, the siccative and moisture of High Strength Non-shrinking Filling Material also known as weight and by 100:12 successively by water and
Siccative is put into agitator；
Step 2: unlatching blender and swing mechanism, swing mechanism are rotated with 28rpm, blender is stirred with the low or first gear of 100rpm
It mixes 1 minute, is then stirred 3 minutes with the top gear of 400rpm；
Step 3: closing blender and swing mechanism, High Strength Non-shrinking Filling Material is obtained.
2. the stirring means of the High Strength Non-shrinking Filling Material according to claim 1 for duct grouting, it is characterised in that:
The gear speed-changing blender is equipped with mixing timer, and the stirring of blender low or first gear and high speed is set separately in the mixing timer
The mixing time of shelves stirring.
3. the stirring means of the High Strength Non-shrinking Filling Material according to claim 2 for hole path pressure grouting it is characterized by:
The blender uses a key control according to the setting of the time of mixing timer, when use press start key realization stir at low speed,
High-speed stirred and stopping function.
4. the stirring means of the High Strength Non-shrinking Filling Material according to claim 1,2 or 3 for duct grouting, feature
Be: the swing mechanism includes base rotary-disc, retarder and driving motor, and the driving motor drives pedestal by retarder
Turntable rotation.
5. the stirring means of the High Strength Non-shrinking Filling Material according to claim 4 for hole path pressure grouting, it is characterised in that:
Swing mechanism rotates in a counter-clockwise direction in the step 2, and blender bottom gear and top gear rotate in a clockwise direction.