CN109731755A - A kind of vacuum cup spray painting improvement technique - Google Patents
A kind of vacuum cup spray painting improvement technique Download PDFInfo
- Publication number
- CN109731755A CN109731755A CN201811478478.XA CN201811478478A CN109731755A CN 109731755 A CN109731755 A CN 109731755A CN 201811478478 A CN201811478478 A CN 201811478478A CN 109731755 A CN109731755 A CN 109731755A
- Authority
- CN
- China
- Prior art keywords
- vacuum cup
- spray
- spray painting
- paint
- curing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to the technical field of producing of cool-bag, specifically disclose a kind of vacuum cup spray painting improvement technique.Comprise the steps of: step 1: material prepares, spray gun, dust removing cloth, sand paper, paint, curing agent, and oven etc. is chosen qualified vacuum cup, dried after cleaning；Step 2: derusting oil removing derusts to vacuum cup surface with dimethylbenzene；Step 3: spray-applied primer；Step 4: essence polishing；Step 5: middle painting is sprayed 1-3 times clockwise with 4-6 grams of floating coating, then is sprayed counterclockwise 1-2 times with Tu paint in 2-3 grams.Step 6: face applies, pure color finishing coat, and aluminium paint is added, and matches curing agent and diluent, ratio 11:2:1:1.Step 7: the product after spraying stands 2-5 hours, and surface is put into drying tunnel after parching；Step 8: waxing forms last protective layer.The present invention proposes that a kind of spray painting of vacuum cup improves technique, and treated, and painting thickness is uniform, and smoothly, without tangerine peel, the defects of bubble, the clear patterns of institute's air brushing are unlikely to deform.
Description
Technical field
The present invention relates to the technical field of producing of cool-bag, are specifically related to a kind of vacuum cup spray painting improvement work
Skill.
Background technique
Vacuum cup is developed from thermos flask, and pot is made into cup for convenience by people, vacuum cup be usually by ceramics or
Shakiness rust steel adds the water container that vacuum layer is made into, and lid is arranged at top, and sealing is tight, and vacuum heat-insulating layer can make in internal water etc.
Liquid delays to radiate, to achieve the purpose that heat preservation.
In the container production process such as cup or bottle, spray painting processing is a kind of common processing method, by container
Paint layer is set on ontology, body body can be prevented to be corroded, is less prone to and gets rusty, degenerates the situations such as discoloration, the service life is longer, together
When, decorative effect can also be played, can satisfy the individual needs of young man, passes through setting different colours, the paint of different pattern
Layer, improves the aesthetics of product.The general layer of paint of the product that current lacquering technologies obtain is in uneven thickness, and paint layer is easy
Abrasion falls off, and influences product beauty, while will lead to product local corrosion, influences normal use.
For the prior art on lacquer spraying technique, it is different that there are painting thickness, and finishing coat is unsmooth easily current mark, wrinkle occurs, tangerine peel,
The defects of bubble such as is mingled at the defect for influencing decorative effect, and the pattern of institute's air brushing has deformation and zigzag is presented.
Summary of the invention
The present invention proposes that a kind of vacuum cup spray painting improves technique primarily directed to the defect of the prior art, spray painting that treated
Thickness is uniform, and smoothly, without tangerine peel, the defects of bubble, the clear patterns of institute's air brushing are unlikely to deform.
For achieving the above object, the present invention takes following technical scheme:
A kind of spray painting of vacuum cup improves technique, and specific step is as follows:
Step 1: material prepares, the cleaning of vacuum cup substrate: preparing spray gun, dust removing cloth, sand paper paints, curing agent, bakes
Case etc. chooses qualified vacuum cup, surface clean is completely dried afterwards；
Step 2: derusting oil removing derusts to vacuum cup surface with dimethylbenzene, is carrying out refine polishing after derusting, then
It is simultaneously dried at once with cleaning cloth with dust removing cloth adhesional wetting degreaser erasing on vacuum cup surface；
Step 3: spray-applied primer, epoxy resin primer, epoxy primer curing agent and corresponding diluent are according to 8:5:3's
Proportion is sprayed；
Step 4: essence polishing, priming paint later polish flat to vacuum cup surface, machine polishing, then fine grinding, carry out after fine grinding
It is micro- to fill out, it dry grinds again after filling up.
Step 5: middle painting is sprayed 1-3 times clockwise with 4-6 grams of floating coating, then is sprayed counterclockwise 1-2 times with Tu paint in 2-3 grams.
Step 6: face applies, pure color finishing coat, and aluminium paint is added, and matches curing agent and diluent, ratio 11:2:1:1.
Step 7: the product after spraying stands 2-5 hours, and surface is put into drying tunnel after parching.
Step 8: waxing carries out polishing grinding to the vacuum cup surface for applying oil wax with sander, forms last protection
Layer.
Preferably, it is dried after spraying the road 1-3 in the step 3.
Preferably, in the step 4 it is micro- fill out selection fill out eye ash, it is micro- to fill out pinprick.
Preferably, clockwise is every all over being separated by 15-20 minutes in the step 5, sprays counterclockwise every all over every 5-10 minutes.
Preferably, face is painted with 2 times in the step 6, and every layer is separated by 10-16 minutes.
Preferably, the step 7 stands 4 hours, and drying tunnel temperature is 80 DEG C and toasts 2 hours.
The invention has the benefit that
The present invention mainly proposes that a kind of vacuum cup spray painting improves technique, when by adjusting priming paint, middle paint and finishing coat spray way
Between, the ratio of baking time and spray painting improves that treated that technique painting thickness is uniform, and smoothly, without tangerine peel, bubble etc. is lacked
It falls into, the clear patterns of institute's air brushing are unlikely to deform.
Specific embodiment
Embodiment 1
A kind of spray painting of vacuum cup improves technique, and specific step is as follows:
Step 1: material prepares, the cleaning of vacuum cup substrate: preparing spray gun, dust removing cloth, sand paper paints, curing agent, bakes
Case etc. chooses qualified vacuum cup, surface clean is completely dried afterwards；
Step 2: derusting oil removing derusts to vacuum cup surface with dimethylbenzene, is carrying out refine polishing after derusting, then
It is simultaneously dried at once with cleaning cloth with dust removing cloth adhesional wetting degreaser erasing on vacuum cup surface；
Step 3: spray-applied primer, epoxy resin primer, epoxy primer curing agent and corresponding diluent are according to 8:5:3's
Proportion is sprayed, and spraying is together；
Step 4: essence polishing, priming paint later polish flat to vacuum cup surface, machine polishing, then fine grinding, carry out after fine grinding
It is micro- to fill out, it is micro- fill out selection fill out eye ash, it is micro- to fill out pinprick, dry grind again after filling up.
Step 5: middle painting is sprayed 1 time clockwise with 4 grams of floating coatings, then is sprayed counterclockwise 1 time with Tu paint in 2 grams.
Step 6: face applies, a pure color finishing coat, and aluminium paint is added, and matches curing agent and diluent, ratio 11:2:1:1.
Step 7: the product after spraying stands 2 hours, and surface is put into 60 DEG C of drying tunnel and toasts 3 hours after parching.
Step 8: waxing carries out polishing grinding to the vacuum cup surface for applying oil wax with sander, forms last protection
Layer.
Embodiment 2
A kind of spray painting of vacuum cup improves technique, and specific step is as follows:
Step 1: material prepares, the cleaning of vacuum cup substrate: preparing spray gun, dust removing cloth, sand paper paints, curing agent, bakes
Case etc. chooses qualified vacuum cup, surface clean is completely dried afterwards；
Step 2: derusting oil removing derusts to vacuum cup surface with dimethylbenzene, is carrying out refine polishing after derusting, then
It is simultaneously dried at once with cleaning cloth with dust removing cloth adhesional wetting degreaser erasing on vacuum cup surface；
Step 3: spray-applied primer, epoxy resin primer, epoxy primer curing agent and corresponding diluent are according to 8:5:3's
Proportion is sprayed；
Step 4: essence polishing, priming paint later polish flat to vacuum cup surface, machine polishing, then fine grinding, carry out after fine grinding
It is micro- to fill out, it is micro- fill out selection fill out eye ash, it is micro- to fill out pinprick, dry grind again after filling up.
Step 5: middle painting is sprayed 3 times clockwise with 6 grams of floating coatings, every all over being separated by 15 minutes then counterclockwise with Tu paint in 3 grams
Spray 2 times, it is every all over every 5 minutes.
Step 6: face is painted with 2 times, and every layer is separated by 10-16 minutes., aluminium paint is added in pure color finishing coat, with curing agent and dilute
Release agent, ratio 11:2:1:1.
Step 7: the product after spraying stands 5 hours, and surface is put into drying tunnel after parching, and temperature is 80 DEG C and toasts 2 hours.
Step 8: waxing carries out polishing grinding to the vacuum cup surface for applying oil wax with sander, forms last protection
Layer.
Embodiment 3
A kind of spray painting of vacuum cup improves technique, and specific step is as follows:
Step 1: material prepares, the cleaning of vacuum cup substrate: preparing spray gun, dust removing cloth, sand paper paints, curing agent, bakes
Case etc. chooses qualified vacuum cup, surface clean is completely dried afterwards；
Step 2: derusting oil removing derusts to vacuum cup surface with dimethylbenzene, is carrying out refine polishing after derusting, then
It is simultaneously dried at once with cleaning cloth with dust removing cloth adhesional wetting degreaser erasing on vacuum cup surface；
Step 3: spray-applied primer, epoxy resin primer, epoxy primer curing agent and corresponding diluent are according to 8:5:3's
Proportion is sprayed, and is dried after spraying 2；
Step 4: essence polishing, priming paint later polish flat to vacuum cup surface, machine polishing, then fine grinding, carry out after fine grinding
It is micro- to fill out, it is micro- fill out selection fill out eye ash, it is micro- to fill out pinprick, dry grind again after filling up.
Step 5: middle painting is sprayed 2 times clockwise with 5 grams of floating coatings, every all over being separated by 20 minutes then counterclockwise with Tu paint in 2 grams
Spray 2 times, it is every all over every 10 minutes.
Step 6: face applies, pure color finishing coat, and aluminium paint is added, and matches curing agent and diluent, ratio 11:2:1:1, and face applies
It is 2 times, every layer is separated by 10-16 minutes.
Step 7: the product after spraying stands 4 hours, and surface is put into drying tunnel after parching, and drying tunnel temperature is 80 DEG C of bakings 2
Hour.
Step 8: waxing carries out polishing grinding to the vacuum cup surface for applying oil wax with sander, forms last protection
Layer.
Clockwise sprays preferably counterclockwise in step 5, embodiment described above in the step 6, only expresses this
Several better embodiments of invention, the description thereof is more specific and detailed, and but it cannot be understood as to the invention patent
The limitation of range.It should be pointed out that for those of ordinary skill in the art, in the premise for not departing from present inventive concept
Under, several modifications and improvements are made, these are all within the scope of protection of the present invention.Therefore, the scope of protection of the patent of the present invention is answered
It is determined by the appended claims.
Claims (6)
1. a kind of vacuum cup spray painting improves technique, which is characterized in that the method includes the steps of:
Step 1: material prepares, the cleaning of vacuum cup substrate: prepare spray gun, dust removing cloth, sand paper paints, curing agent, oven etc.,
Qualified vacuum cup is chosen, surface clean is completely dried afterwards；
Step 2: derusting oil removing derusts to vacuum cup surface with dimethylbenzene, is carrying out refine polishing after derusting, then with removing
Dirt cloth bedews degreaser erasing and is simultaneously dried at once with cleaning cloth on vacuum cup surface；
Step 3: spray-applied primer, epoxy resin primer, epoxy primer curing agent and corresponding diluent according to 8:5:3 proportion
It is sprayed；
Step 4: essence polishing, priming paint later polish flat to vacuum cup surface, machine polishing, then fine grinding, carry out after fine grinding micro-
It fills out, dry grinds again after filling up；
Step 5: middle painting is sprayed 1-3 times clockwise with 4-6 grams of floating coating, then is sprayed counterclockwise 1-2 times with Tu paint in 2-3 grams；
Step 6: face applies, pure color finishing coat, and aluminium paint is added, and matches curing agent and diluent, ratio 11:2:1:1；
Step 7: the product after spraying stands 2-5 hours, and surface is put into drying tunnel after parching；
Step 8: waxing carries out polishing grinding to the vacuum cup surface for applying oil wax with sander, forms last protective layer.
2. a kind of vacuum cup spray painting according to claim 1 improves technique, which is characterized in that spray 1- in the step 3
It is dried after 3.
3. a kind of vacuum cup spray painting according to claim 1 improves technique, which is characterized in that micro- in the step 4 to fill out choosing
It is grey with eye is filled out, it is micro- to fill out pinprick.
4. a kind of vacuum cup spray painting according to claim 1 improves technique, which is characterized in that clockwise in the step 5
It is every all over being separated by 15-20 minute, spray every time counterclockwise every 5-10 minutes.
5. a kind of vacuum cup spray painting according to claim 1 improves technique, which is characterized in that face is painted in the step 6
2 times, every layer is separated by 10-16 minutes.
6. a kind of vacuum cup spray painting according to claim 1 improves technique, which is characterized in that it is small that the step 7 stands 4
When, drying tunnel temperature is 80 DEG C and toasts 2 hours.