CN109721725A - A kind of synthetic method of the extraordinary silane-modified STP resin of high adhesiveness energy - Google Patents
A kind of synthetic method of the extraordinary silane-modified STP resin of high adhesiveness energy Download PDFInfo
- Publication number
- CN109721725A CN109721725A CN201811623885.5A CN201811623885A CN109721725A CN 109721725 A CN109721725 A CN 109721725A CN 201811623885 A CN201811623885 A CN 201811623885A CN 109721725 A CN109721725 A CN 109721725A
- Authority
- CN
- China
- Prior art keywords
- resin
- stp
- silane
- extraordinary
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of synthetic methods of extraordinary silane-modified STP resin of high adhesiveness energy, belong to chemical technology field;During isophorone diisocyanate is added in 500ml glass reaction kettle, meanwhile, starting stirring;Silane coupling agent KH540, normal-temperature reaction are added dropwise into reaction kettle, time for adding is 3h or so, and system keeps original temperature;Extraordinary silane reaction is completed after curing 1h;Then STP resin, stirring half an hour or so are added into reaction kettle, i.e., generation high adhesiveness can extraordinary silane-modified STP resin.Simple process, easy to operate, resulting modified STP resin has preferable adhesive property, and adhesion strength is high, is applicable to the fields such as building, industry and assembling product.
Description
Technical field
The present invention relates to a kind of synthetic methods of extraordinary silane-modified STP resin of high adhesiveness energy, belong to Chemical Engineering Technology neck
Domain.
Background technique
Silane modified polyether (STP) have health environment-friendly, pollution-free, adhesive property is good, good weatherability, can cover with paint, lacquer, colour wash, etc.;Extensively
For building, industry and assembling product field.
Although existing market silane modified polyether does not need silane coupling agent can reach good adhesive property, but such viscous
Connect the requirement that client is often not achieved in intensity.
Summary of the invention
In view of the defects and deficiencies of the prior art, the present invention intends to provide it is a kind of design it is reasonable, easy to operate
The synthetic method of the extraordinary silane-modified STP resin of high adhesiveness energy.
To achieve the above object, the technical solution adopted by the present invention is that: the step of synthetic method, is as follows:
Step 1: during 100 parts of isophorone diisocyanate is added in 500ml glass reaction kettle, meanwhile, starting
Stirring, revolving speed 200rpm;
Step 2: 200 parts of silane coupling agent KH540, normal-temperature reaction are added dropwise into reaction kettle, time for adding is 3h or so,
System keeps original temperature, that is, does not need heating and cooling;
Step 3: extraordinary silane reaction is completed after curing 1h;
Step 4: leaving 1~5 part of extraordinary silane in a kettle, 95~99 parts of STP is then added into reaction kettle
Resin, or so stirring half an hour, the i.e. extraordinary silane-modified STP resin of generation high adhesiveness energy, discharging.
Preferably, the isophorone diisocyanate and the ratio of silane coupling agent KH540 are about 1:2.
Preferably, temperature control is at 25-40 DEG C when stirring in the step 1.
Preferably, extraordinary silane is 2~3 parts in the step 4, STP resin is 96~99 parts.
The isophorone diisocyanate abbreviation IPDI is hydroxyl needed for the polyurethane binder of composite propellant
The curing agent of based prepolymers (i.e. glycol polypropylene).
The molecular structural formula of the silane coupling agent is general are as follows: Y-R-Si (OR) 3 (mono- organic functional base of Y, SiOR mono- in formula
Siloxy).Siloxy has reactivity to inorganic matter, and organic functional base has reactivity or compatibility to organic matter.Cause
This, when silane coupling agent between inorganic between organic interface, organic matrix-silane coupling agent-inorganic matrix knot can be formed
Close layer.
Typical silane coupling agent have A151 (vinyltriethoxysilane), A171 (vinyltrimethoxysilane),
A172 (vinyl three (beta-methoxy ethyoxyl) silane).Silane coupling agent KH540 of the invention is 3- aminopropyl trimethoxy.
The present invention makes the synthesis of extraordinary silane first, is then added to extraordinary silane in the system of resin STP, thus
Obtain modified STP resin.
After adopting the above structure, the invention has the following beneficial effects: a kind of extraordinary silane of high adhesiveness energy of the present invention changes
Property STP resin synthetic method, simple process is easy to operate, resulting modified STP resin have preferable adhesive property, and
Adhesion strength is high, is applicable to the fields such as building, industry and assembling product, in addition, the present invention has design rationally, cost of manufacture
Low advantage.
Specific embodiment
The synthetic method of present embodiment is:
During 100 parts of isophorone diisocyanate is added in 500ml glass reaction kettle, meanwhile, starting stirring turns
Fast 200rpm, temperature control is at 25-40 DEG C when stirring;200 parts of silane coupling agent KH540 is added dropwise into reaction kettle, room temperature is anti-
It answers, time for adding is 3h or so, and system keeps original temperature, that is, does not need heating and cooling;Extraordinary silane reaction after curing 1h
It completes;1~5 part of extraordinary silane is left in a kettle, and 95~99 parts of STP resin, stirring are then added into reaction kettle
Or so half an hour, i.e. generation high adhesiveness can extraordinary silane-modified STP resins.
Wherein, the isophorone diisocyanate and the ratio of silane coupling agent KH540 are about 1:2.The special type silicon
Alkane is 2~3 parts, and STP resin is 96~99 parts.Silane coupling agent KH540 is 3- aminopropyl trimethoxy.
In addition, silane coupling agent KH540, technical grade, Nanjing join silication work;
Isoflurane chalcone diisocyanate, technical grade, Bayer chemistry;
STP resin RISUN 30000T, technical grade, self-control.
DF-101S heat collecting type constant-temperature heating magnetic stirring apparatus, Yu Hua Instrument Ltd., Gongyi City;
JB series blender, Shanghai Sample Model Factory.
Embodiment:
Modified STP resin is made into sealant and carries out cohesive force test
Tensile shear strength testing standard: GB 7124-86 adhesive tensile shear test method
Substrate 1: stainless steel-stainless steel
Substrate 2: aluminium alloy-aluminium alloy
Embodiment one:
The formula of sealant is as follows: 100 parts of modified STP (1 part of extraordinary silane, 99 parts of STP resin), 80 parts of DINP increase
Mould agent, 1 part of vinyltrimethoxysilane, 100 parts of TAKEHARA precipitated calcium carbonates, 100 parts of OMYACARB powdered whitings, 50
Part titanium dioxide, 4 parts of silane coupling agent KH792,1 part of DBDTL catalyst;
Embodiment two:
The formula of sealant is as follows: 100 parts of modified STP (2 parts of extraordinary silane, 98 parts of STP resin), 80 parts of DINP increase
Mould agent, 1 part of vinyltrimethoxysilane, 100 parts of TAKEHARA precipitated calcium carbonates, 100 parts of OMYACARB powdered whitings, 50
Part titanium dioxide, 4 parts of silane coupling agent KH792,1 part of DBDTL catalyst;
Embodiment three:
The formula of sealant is as follows: 100 parts of modified STP (3 parts of extraordinary silane, 97 parts of STP resin), 80 parts of DINP increase
Mould agent, 1 part of vinyltrimethoxysilane, 100 parts of TAKEHARA precipitated calcium carbonates, 100 parts of OMYACARB powdered whitings, 50
Part titanium dioxide, 4 parts of silane coupling agent KH792,1 part of DBDTL catalyst;
Example IV:
The formula of sealant is as follows: 100 parts of modified STP (4 parts of extraordinary silane, 96 parts of STP resin), 80 parts of DINP increase
Mould agent, 1 part of vinyltrimethoxysilane, 100 parts of TAKEHARA precipitated calcium carbonates, 100 parts of OMYACARB powdered whitings, 50
Part titanium dioxide, 4 parts of silane coupling agent KH792,1 part of DBDTL catalyst;
Referring to table 1, the resulting modified STP resin of the present invention has preferable adhesive property, and adhesion strength is high, is applicable in model
It encloses wide.
Table 1: aforementioned four embodiment and the shear strength of existing STP compare.
The above is only used to illustrate the technical scheme of the present invention and not to limit it, and those of ordinary skill in the art are to this hair
The other modifications or equivalent replacement that bright technical solution is made, as long as it does not depart from the spirit and scope of the technical scheme of the present invention,
It is intended to be within the scope of the claims of the invention.
Claims (5)
1. a kind of synthetic method of the extraordinary silane-modified STP resin of high adhesiveness energy, it is characterised in that: the step of the synthetic method
It is rapid as follows:
(step 1): during 100 parts of isophorone diisocyanate is added in 500ml glass reaction kettle, meanwhile, starting is stirred
It mixes, revolving speed 200rpm;
(step 2): 200 parts of silane coupling agent KH540, normal-temperature reaction being added dropwise into reaction kettle, and time for adding is 3h or so, body
System keeps original temperature, that is, does not need heating and cooling;
(step 3): extraordinary silane reaction is completed after curing 1h;
(step 4): leaving 1~5 part of extraordinary silane in a kettle, and 95~99 parts of STP tree is then added into reaction kettle
Rouge, or so stirring half an hour, the i.e. extraordinary silane-modified STP resin of generation high adhesiveness energy, discharging.
2. a kind of synthetic method of extraordinary silane-modified STP resin of high adhesiveness energy according to claim 1, feature exist
In: isophorone diisocyanate and the ratio of silane coupling agent KH540 are about 1:2 in the (step 1).
3. a kind of synthetic method of extraordinary silane-modified STP resin of high adhesiveness energy according to claim 1, feature exist
In: temperature control is at 25-40 DEG C when stirring in the (step 1).
4. a kind of synthetic method of extraordinary silane-modified STP resin of high adhesiveness energy according to claim 1, feature exist
In: extraordinary silane is 2~3 parts in the (step 4), and STP resin is 96~99 parts.
5. a kind of synthetic method of extraordinary silane-modified STP resin of high adhesiveness energy according to claim 1, feature exist
In: the synthetic method makes the synthesis of extraordinary silane first, is then added to extraordinary silane in the system of resin STP,
To obtain modified STP resin.