CN109719428A - 耐气孔耐预涂漆钢用药芯焊丝 - Google Patents

耐气孔耐预涂漆钢用药芯焊丝 Download PDF

Info

Publication number
CN109719428A
CN109719428A CN201910182410.5A CN201910182410A CN109719428A CN 109719428 A CN109719428 A CN 109719428A CN 201910182410 A CN201910182410 A CN 201910182410A CN 109719428 A CN109719428 A CN 109719428A
Authority
CN
China
Prior art keywords
resistance
fluoride
flux
stomata
cored wire
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201910182410.5A
Other languages
English (en)
Inventor
陈迪
汪春沿
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Nantong Welding Technology Co Ltd
Original Assignee
Jiangsu Nantong Welding Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Nantong Welding Technology Co Ltd filed Critical Jiangsu Nantong Welding Technology Co Ltd
Priority to CN201910182410.5A priority Critical patent/CN109719428A/zh
Publication of CN109719428A publication Critical patent/CN109719428A/zh
Pending legal-status Critical Current

Abstract

本发明公开耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15~30%,硅铁3‑8,氟化钙4‑12%,铝镁合金4‑10%,镁粉6‑10%,金红石22‑38%,铁粉6‑12%,氟化物2‑6%,锰铁2‑6%,其它合金3‑8%;所述氟化物为氟化钾或氟化锂;其它合金为铝、硼、钒、钛、铌和锆的任意比组合;所述药粉重量占所述药芯焊丝重量的12‑15%。本发明提供的耐气孔耐预涂漆钢用药芯焊丝,针对气孔产生的不同机理结合常用的焊接工艺,通过原料的合理添加大大提高焊缝抗气孔能力。

Description

耐气孔耐预涂漆钢用药芯焊丝
技术领域
本发明属于焊丝技术领域,具体涉及一种耐气孔耐预涂漆钢用药芯焊丝。
背景技术
药芯焊丝作为一种高效及自动化程度高焊接材料,比手工焊条在焊接效率、焊缝外观及焊接操控性方面有显著优点,已大量广泛应用于船舶、钻井平台、石油管道、大型桥梁、钢结构、锅炉及压力容器、核电行业等领域。
目前药芯焊丝在焊接预涂漆钢板时,因钢板上的底漆在受热后分解出大量气体,焊接金属结晶过程不能保证气体全部溢出,容易产生气孔及针孔,给结构安全带来很大隐患。
发明内容
本发明的目的在于提供一种耐气孔耐预涂漆钢用药芯焊丝,以解决以上问题。
本发明的技术方案为:耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15~30%,硅铁3-8,氟化钙4-12%,铝镁合金4-10%,镁粉6-10%,金红石22-38%,铁粉6-12%,氟化物2-6%,锰铁2-6%,其它合金3-8%;所述氟化物为氟化钾或氟化锂;其它合金为铝、硼、钒、钛、铌和锆的任意比组合。
优选的,所述药粉重量占所述药芯焊丝重量的12-15%。
优选的,耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15%,硅铁5%,氟化钙10%,铝镁合金5%,镁粉5%,金红石30%,铁粉10%,氟化物6%,锰铁6%,其它合金8%。
优选的,耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金30%,硅铁5,氟化钙6%,铝镁合金5%,镁粉6%,金红石25%,铁粉9%,氟化物6%,锰铁5%,其它合金3%。
优选的,耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金20%,硅铁5,氟化钙6%,铝镁合金8%,镁粉6%,金红石28%,铁粉11%,氟化物6%,锰铁5%,其它合金5%。
有益效果:本发明提供的耐气孔耐预涂漆钢用药芯焊丝,针对气孔产生的不同机理结合常用的焊接工艺,通过原料的合理添加大大提高焊缝抗气孔能力。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15~30%,硅铁3-8,氟化钙4-12%,铝镁合金4-10%,镁粉6-10%,金红石22-38%,铁粉6-12%,氟化物2-6%,锰铁2-6%,其它合金3-8%;所述氟化物为氟化钾或氟化锂;其它合金为铝、硼、钒、钛、铌和锆的任意比组合。
所述药粉重量占所述药芯焊丝重量的12-15%。
实施例1
耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15%,硅铁5%,氟化钙10%,铝镁合金5%,镁粉5%,金红石30%,铁粉10%,氟化物6%,锰铁6%,其它合金8%。
实施例2
耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金30%,硅铁5,氟化钙6%,铝镁合金5%,镁粉6%,金红石25%,铁粉9%,氟化物6%,锰铁5%,其它合金3%。
实施例3
耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金20%,硅铁5,氟化钙6%,铝镁合金8%,镁粉6%,金红石28%,铁粉11%,氟化物6%,锰铁5%,其它合金5%。
药芯焊丝包括外皮和药芯,外皮包裹住药芯;本发明的目的在于对药芯焊丝的药芯组分进行研发,固本发明对外皮不做特别限定说明。
本发明中,合金粉末的粒度为过60-80目。
本发明的的药芯焊丝:屈服强度(Mpa)≥400;抗拉强度(Mpa)490-660;伸长率(%)≥22;-20℃条件下的冲击韧性(J)≥27。

Claims (5)

1.耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15~30%,硅铁3-8,氟化钙4-12%,铝镁合金4-10%,镁粉6-10%,金红石22-38%,铁粉6-12%,氟化物2-6%,锰铁2-6%,其它合金3-8%;所述氟化物为氟化钾或氟化锂;其它合金为铝、硼、钒、钛、铌和锆的任意比组合。
2.根据权利要求1所述的耐气孔耐预涂漆钢用药芯焊丝,其特征在于:所述药粉重量占所述药芯焊丝重量的12-15%。
3.根据权利要求1所述的耐气孔耐预涂漆钢用药芯焊丝,其特征在于:耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金15%,硅铁5%,氟化钙10%,铝镁合金5%,镁粉5%,金红石30%,铁粉10%,氟化物6%,锰铁6%,其它合金8%。
4.根据权利要求1所述的耐气孔耐预涂漆钢用药芯焊丝,其特征在于:耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金30%,硅铁5,氟化钙6%,铝镁合金5%,镁粉6%,金红石25%,铁粉9%,氟化物6%,锰铁5%,其它合金3%。
5.根据权利要求1所述的耐气孔耐预涂漆钢用药芯焊丝,其特征在于:耐气孔耐预涂漆钢用药芯焊丝,其药粉组分质量百分比为:硅锰合金20%,硅铁5,氟化钙6%,铝镁合金8%,镁粉6%,金红石28%,铁粉11%,氟化物6%,锰铁5%,其它合金5%。
CN201910182410.5A 2019-03-12 2019-03-12 耐气孔耐预涂漆钢用药芯焊丝 Pending CN109719428A (zh)