CN109706725A - A kind of anti-corrosion cloth dye formulation - Google Patents
A kind of anti-corrosion cloth dye formulation Download PDFInfo
- Publication number
- CN109706725A CN109706725A CN201811540156.3A CN201811540156A CN109706725A CN 109706725 A CN109706725 A CN 109706725A CN 201811540156 A CN201811540156 A CN 201811540156A CN 109706725 A CN109706725 A CN 109706725A
- Authority
- CN
- China
- Prior art keywords
- dye formulation
- agent
- cloth
- formulation according
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-corrosion cloth dye formulations, including following constituent and its mass fraction are as follows: calcium carbonate 6-12%, ethyl alcohol 4-9%, polyamide 20-35%, Sodium Polyacrylate 1-5%, deionized water 8-21%, defoaming agent 1-2%, dye leveller 4-8%, pigment 15-25%, glacial acetic acid 1-2%, thickener 1-3%, emulsifier 1-4%, paraffin 3-5%, aluminium powder 5-9%, filler 4-8%, antibacterial agent 1-2%, soda acid agent 2-4%, antioxidant 2-4% and anionic antistatic agents 0.5-1.5%, steps are as follows for the mixed method of the dye formulation: step 1: calcium carbonate 6-12% being added in Xiang Hengwen agitator tank, ethyl alcohol 4-9%, polyamide 20-35%, polyacrylic acid Sodium 1-5% and deionized water 8-21%, controlled at 45-75 degrees Celsius.The addition that the present invention passes through antioxidant, oxidation resistant effect is reached, has avoided the situation of cloth aging easy to oxidize when permanent, to solve the problems, such as that traditional cloth dyestuff does not have corrosion resistance, and then the service life of cloth is extended, it is suitble to promote the use of.
Description
Technical field
The present invention relates to technical field of dye, specially a kind of anti-corrosion cloth dye formulation.
Background technique
Dyestuff, which refers to, can make other substances obtain distinct and securely color a kind of organic compound, due to what is used now
Pigment be all it is artificial synthesized, so also referred to as synthetic dyestuffs.Dyestuff and pigment are typically all itself to have color, and can be with molecule
State or dispersity make other substances obtain distinct and secured color compound.
It selects the various fibers of dyestuff due to nature difference according to fibre property, just needs to select phase when being dyed
The dyestuff of adaptation.Such as when cotton fiber dyeing, due on its molecular structure containing there are many hydrophilic hydroxyls, it is easy to moisture absorption swollen
Change, can with reactive group chemically reactive, and it is more alkaline-resisting, thus may be selected directly, reduction, vulcanization, the dye such as ice dye and activity
Material dyeing.Terylene hydrophobicity is strong, not alkaline-resisting under high temperature, should not select the above dyestuff under normal circumstances, and should select disperse dyes
It is dyed.It selects dyestuff since pollutant purposes is different according to pollutant purposes, therefore the fastness of dyeing product is required also not
Together.The cloth for being used for example as curtain is seldom washed, but will often by solar radiation, therefore when dyeing, should select light fastness compared with
High dyestuff.The light coloured fabrics dyeing worn as underwear and summer, due to often to wash, solarization, so should select washable, resistance to
It shines, the higher dyestuff of color fastness to perspiration.Select dyestuff when selecting dyestuff according to cost of dye, it not only will be from coloured light and fastness
Think, while to consider dyestuff and adjuvant used cost, the source of goods etc..Such as the higher dyestuff of price, should consider as far as possible with can contaminate
Other dyestuffs for obtaining effect same are next alternative, to reduce production cost.The selection of dyestuff selects dye when needing colorant match when colorant match
Material is it should be noted that the performances such as their ingredient, solubility, color fastness, dye-uptake.Since the dyeability of all kinds of dyestuffs is different,
Dyeing effect often is influenced because of the difference of temperature, solubility, dye-uptake etc. in dyeing.When therefore carrying out colorant match, it is necessary to
Dyestuff similar in performance is selected, and more more close better, the control of process conditions, the stabilization of dyeing quality can be conducive in this way.
Select dyestuff due to dyeing machinery difference according to dyeing machinery performance, the property and requirement to dyestuff is not also identical.If be used for
Dye gigging should select direct higher dyestuff;For pad dyeing, then direct lower dyestuff should be selected, before otherwise will generating
The undesirable product such as shallow, uneven shade after depth.
Traditional cloth dyestuff does not have corrosion resistant function, is used for a long time or easily corrodes under corrosive environment
Damage, service life is extremely short, while color fastness is also poor, the serious curtailment service life of cloth.
Summary of the invention
The purpose of the present invention is to provide a kind of anti-corrosion cloth dye formulations, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme: a kind of anti-corrosion cloth dye formulation, including such as
Lower constituent and its mass fraction are as follows: calcium carbonate 6-12%, ethyl alcohol 4-9%, polyamide 20-35%, Sodium Polyacrylate 1-
5%, deionized water 8-21%, defoaming agent 1-2%, dye leveller 4-8%, pigment 15-25%, glacial acetic acid 1-2%, thickener 1-3%, emulsification
Agent 1-4%, paraffin 3-5%, aluminium powder 5-9%, filler 4-8%, antibacterial agent 1-2%, soda acid agent 2-4%, antioxidant 2-4% and yin from
Sub- antistatic agent 0.5-1.5%;
Steps are as follows for the mixed method of the dye formulation:
Step 1: calcium carbonate 6-12%, ethyl alcohol 4-9%, polyamide 20-35%, Sodium Polyacrylate are added in Xiang Hengwen agitator tank
1-5% and deionized water 8-21%, controlled at 45-75 degrees Celsius, control speed of agitator be 1200-1800r/min, stirring
0.5-1h;
Step 2: defoaming agent 1-2%, dye leveller 4-8%, pigment 15-25%, glacial acetic acid 1-2%, thickening are added in Xiang Hengwen agitator tank
Agent 1-3%, emulsifier 1-4% and paraffin 3-5%, controlled at 60-80 degrees Celsius, control speed of agitator is 1000-1500r/
Min stirs 1-1.5h;
Step 3: aluminium powder 5-9%, filler 4-8%, antibacterial agent 1-2%, antioxidant 2-4% and yin are added in Xiang Hengwen agitator tank
Ionic antistatic agent 0.5-1.5%, controlled at 45-60 degrees Celsius, control speed of agitator is 1300-1800r/min, stirring
0.5-1.5h;
Step 4: being slowly added to soda acid agent 2-4% in Xiang Hengwen agitator tank, controlled at 50-65 degrees Celsius, control stirring turns
Speed is 300-800r/min, stirs 0.5-1h, adjusts PH to 6.5-7.5.
Preferably, the diameter of the aluminium powder is 1-10 microns.
Preferably, the thickener is one of casein, guar gum and chitosan.
Preferably, the antibacterial agent is one of zinc oxide, copper oxide, ammonium dihydrogen phosphate and lithium carbonate.
Preferably, the soda acid agent is using one of sodium hydroxide, potassium hydroxide and saleratus.
Preferably, the emulsifier is butyl acrylate, methyl methacrylate, lauryl sodium sulfate and poly alkyl alcohol
One of oxyethylene group ether.
Preferably, the filler is anhydrous sodium sulphate.
Preferably, the dye leveller is paregal O.
Preferably, the antioxidant is one of titanium dioxide, carbon black and silica flour.
Preferably, the defoaming agent is emulsification silicon.
Compared with prior art, beneficial effects of the present invention are as follows:
1, the present invention has reached oxidation resistant effect, it is easy to oxidize when permanent to avoid cloth by the addition of antioxidant
The situation of aging to solve the problems, such as that traditional cloth dyestuff does not have corrosion resistance, and then extends the use of cloth
Service life is suitble to promote the use of.
2, the present invention can be greatly improved the antistatic property of cloth, in turn by the addition of anionic antistatic agents
So that the cloth is used in some particular surroundings, substantially increases the applicability of the cloth.
3, the present invention can be improved the antibacterial effect of the cloth by the addition of antibacterial agent, can be avoided cloth growth
On the one hand germ avoids the situation that germ causes people to infect, on the other hand avoid germ secretion corrosive substance and cause cloth
The situation for expecting damage, to improve the safety of the cloth and extend the service life of the cloth.
Specific embodiment
Below in conjunction with the embodiment in the present invention, technical solution in the embodiment of the present invention is carried out clearly and completely
Description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based on this hair
Embodiment in bright, every other implementation obtained by those of ordinary skill in the art without making creative efforts
Example, shall fall within the protection scope of the present invention.
Embodiment one:
A kind of anti-corrosion cloth dye formulation, including following constituent and its mass fraction are as follows: calcium carbonate 8%, ethyl alcohol 5%,
Polyamide 23%, Sodium Polyacrylate 3%, deionized water 14%, emulsification silicon 1.3%, paregal O 5%, pigment 18%, glacial acetic acid
1.3%, casein 2%, methyl methacrylate 2.4%, paraffin 3.8%, aluminium powder 6%, anhydrous sodium sulphate 5%, zinc oxide 1.2%, titanium dioxide
2.3%, anionic antistatic agents 0.8% and saleratus 1.2%;
Steps are as follows for the mixed method of above-mentioned mass fraction ratio dye formulation:
Step 1: in Xiang Hengwen agitator tank be added calcium carbonate 8%, ethyl alcohol 5%, polyamide 23%, Sodium Polyacrylate 3% and go from
Sub- water 14%, controlled at 60 degrees Celsius, control speed of agitator is 1400r/min, stirs 0.8h;
Step 2: emulsification silicon 1.3%, paregal O 5%, pigment 18%, glacial acetic acid 1.3%, casein are added in Xiang Hengwen agitator tank
2%, methyl methacrylate 2.4% and paraffin 3.8%, controlled at 75 degrees Celsius, control speed of agitator is 1400r/min, is stirred
Mix 1.2h;
Step 3: it is anti-that aluminium powder 6%, anhydrous sodium sulphate 5%, zinc oxide 1.2%, titanium dioxide 2.3% and anion are added in Xiang Hengwen agitator tank
Electrostatic agent 0.8%, controlled at 50 degrees Celsius, control speed of agitator is 1500r/min, stirs 0.9h;
Step 4: being slowly added to saleratus 1.2% in Xiang Hengwen agitator tank, controlled at 55 degrees Celsius, controls speed of agitator
For 500r/min, 0.6h is stirred, adjusts PH to 7.0.
Embodiment two: the difference of the present embodiment and above-described embodiment is:
A kind of anti-corrosion cloth dye formulation, including following constituent and its mass fraction are as follows: calcium carbonate 9%, ethyl alcohol 4%,
Polyamide 26%, Sodium Polyacrylate 2%, deionized water 13%, emulsification silicon 1.5%, paregal O 6%, pigment 19%, glacial acetic acid 1%,
Guar gum 2.2%, butyl acrylate 2.4%, paraffin 3.8%, aluminium powder 7%, anhydrous sodium sulphate 5%, copper oxide 1.5%, titanium dioxide 2.5%, yin from
Sub- antistatic agent 0.9% and saleratus 1.5%;
Steps are as follows for the mixed method of above-mentioned mass fraction dye formulation:
Step 1: in Xiang Hengwen agitator tank be added calcium carbonate 9%, ethyl alcohol 4%, polyamide 26%, Sodium Polyacrylate 2% and go from
Sub- water 13%, controlled at 55 degrees Celsius, control speed of agitator is 1400r/min, stirs 0.8h;
Step 2: emulsification silicon 1.5%, paregal O 6%, pigment 19%, glacial acetic acid 1%, guar gum are added in Xiang Hengwen agitator tank
2.2%, butyl acrylate 2.4% and paraffin 3.8%, controlled at 70 degrees Celsius, control speed of agitator is 1500r/min, stirring
1.5h;
Step 3: it is anti-that aluminium powder 7%, anhydrous sodium sulphate 5%, copper oxide 1.5%, titanium dioxide 2.5% and anion are added in Xiang Hengwen agitator tank
Electrostatic agent 0.9%, controlled at 60 degrees Celsius, control speed of agitator is 1300r/min, stirs 0.9h;
Step 4: being slowly added to saleratus 1.5% in Xiang Hengwen agitator tank, controlled at 50 degrees Celsius, controls speed of agitator
For 550r/min, 0.7h is stirred, adjusts PH to 7.0.
Embodiment three: the difference of the present embodiment and above-described embodiment is:
A kind of anti-corrosion cloth dye formulation, including following constituent and its mass fraction are as follows: calcium carbonate 7%, ethyl alcohol 5%,
Polyamide 20%, Sodium Polyacrylate 5%, deionized water 15%, emulsification silicon 1.5%, paregal O 5.2%, pigment 17%, glacial acetic acid
1.8%, chitosan 2.1%, lauryl sodium sulfate 2.1%, paraffin 3.5%, aluminium powder 8%, anhydrous sodium sulphate 4%, ammonium dihydrogen phosphate 1.4%, titanium
White powder 2.5%, anionic antistatic agents 1% and saleratus 1.5%;
Steps are as follows for the mixed method of above-mentioned mass fraction ratio dye formulation:
Step 1: in Xiang Hengwen agitator tank be added calcium carbonate 7%, ethyl alcohol 5%, polyamide 20%, Sodium Polyacrylate 5% and go from
Sub- water 15%, controlled at 70 degrees Celsius, control speed of agitator is 1300r/min, stirs 1.3h;
Step 2: emulsification silicon 1.5%, paregal O 5.2%, pigment 17%, glacial acetic acid 1.8%, chitosan are added in Xiang Hengwen agitator tank
2.1%, lauryl sodium sulfate 2.1% and paraffin 3.5%, controlled at 70 degrees Celsius, control speed of agitator is 1550r/min,
Stir 1.5h;
Step 3: in Xiang Hengwen agitator tank be added aluminium powder 8%, anhydrous sodium sulphate 4%, ammonium dihydrogen phosphate 1.4%, titanium dioxide 2.5% and yin from
Sub- 1 % of antistatic agent, controlled at 55 degrees Celsius, control speed of agitator is 1600r/min, stirs 0.7h;
Step 4: being slowly added to saleratus 1.5% in Xiang Hengwen agitator tank, controlled at 45 degrees Celsius, controls speed of agitator
For 600r/min, 0.5h is stirred, adjusts PH to 7.0.
In summary: the anti-corrosion cloth dye formulation has reached oxidation resistant effect by the addition of antioxidant
Fruit, avoids the situation of cloth aging easy to oxidize when permanent, thus solve traditional cloth dyestuff do not have it is corrosion-resistant
Property the problem of, and then extend the service life of cloth, be suitble to promote the use of, can by the addition of anionic antistatic agents
The antistatic property of cloth is substantially increased, and then the cloth is enable to use in some particular surroundings, substantially increases the cloth
The applicability of material can be improved the antibacterial effect of the cloth by the addition of antibacterial agent, can be avoided cloth and breeds germ,
On the one hand the situation that germ causes people to infect is avoided, germ secretion corrosive substance is on the other hand avoided and cloth is caused to damage
Situation, to improve the safety of the cloth and extend the service life of the cloth.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (10)
1. a kind of anti-corrosion cloth dye formulation, it is characterised in that: including following constituent and its mass fraction are as follows: carbonic acid
Calcium 6-12%, ethyl alcohol 4-9%, polyamide 20-35%, Sodium Polyacrylate 1-5%, deionized water 8-21%, defoaming agent 1-2%,
Stain 4-8%, pigment 15-25%, glacial acetic acid 1-2%, thickener 1-3%, emulsifier 1-4%, paraffin 3-5%, aluminium powder 5-9%, filler
4-8%, antibacterial agent 1-2%, soda acid agent 2-4%, antioxidant 2-4% and anionic antistatic agents 0.5-1.5%;
Steps are as follows for the mixed method of the dye formulation:
Step 1: calcium carbonate 6-12%, ethyl alcohol 4-9%, polyamide 20-35%, Sodium Polyacrylate are added in Xiang Hengwen agitator tank
1-5% and deionized water 8-21%, controlled at 45-75 degrees Celsius, control speed of agitator be 1200-1800r/min, stirring
0.5-1h;
Step 2: defoaming agent 1-2%, dye leveller 4-8%, pigment 15-25%, glacial acetic acid 1-2%, thickening are added in Xiang Hengwen agitator tank
Agent 1-3%, emulsifier 1-4% and paraffin 3-5%, controlled at 60-80 degrees Celsius, control speed of agitator is 1000-1500r/
Min stirs 1-1.5h;
Step 3: aluminium powder 5-9%, filler 4-8%, antibacterial agent 1-2%, antioxidant 2-4% and yin are added in Xiang Hengwen agitator tank
Ionic antistatic agent 0.5-1.5%, controlled at 45-60 degrees Celsius, control speed of agitator is 1300-1800r/min, stirring
0.5-1.5h;
Step 4: being slowly added to soda acid agent 2-4% in Xiang Hengwen agitator tank, controlled at 50-65 degrees Celsius, control stirring turns
Speed is 300-800r/min, stirs 0.5-1h, adjusts PH to 6.5-7.5.
2. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the diameter of the aluminium powder is
1-10 microns.
3. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the thickener is cheese
One of element, guar gum and chitosan.
4. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the antibacterial agent is oxidation
One of zinc, copper oxide, ammonium dihydrogen phosphate and lithium carbonate.
5. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the soda acid agent uses hydrogen
One of sodium oxide molybdena, potassium hydroxide and saleratus.
6. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the emulsifier is propylene
One of acid butyl ester, methyl methacrylate, lauryl sodium sulfate and fatty alcohol polyoxyethylene ether.
7. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the filler is that member is bright
Powder.
8. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the dye leveller is average
Add O.
9. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the antioxidant is titanium
One of white powder, carbon black and silica flour.
10. a kind of anti-corrosion cloth dye formulation according to claim 1, it is characterised in that: the defoaming agent is cream
SiClx.