CN109704671A - 一种建筑用砌筑干混风积沙砂浆及其制备方法 - Google Patents
一种建筑用砌筑干混风积沙砂浆及其制备方法 Download PDFInfo
- Publication number
- CN109704671A CN109704671A CN201811428906.8A CN201811428906A CN109704671A CN 109704671 A CN109704671 A CN 109704671A CN 201811428906 A CN201811428906 A CN 201811428906A CN 109704671 A CN109704671 A CN 109704671A
- Authority
- CN
- China
- Prior art keywords
- sand
- drift
- mixed
- dry
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种建筑用砌筑干混风积沙砂浆,由以下质量百分比的原料组成:水泥18%‑22%,粉煤灰3%‑6%,风积沙65%‑75%,保水剂0.0l%‑0.2%,抗裂剂0.0l%‑1%。有效解决了长久以来因风积沙颗粒较细而无法满足建筑用沙的难点,以及现今所存一在大量风积沙的利用问题,且为干混砌筑砂浆的制造开辟了一种新途径,改变了建筑用沙资源缺乏的现状,同时其生产土艺简单,操作方便。本发明还公开了一种建筑用砌筑干混风积沙砂浆的制备方法,包括:(1)风积沙的预处理;(2)粉煤灰干燥和筛分;(3)配料;(4)混合搅拌。该制备方法所生产的干混砌筑砂浆强度、保水率、抗冻性均符合建筑用砌筑干混砂浆规范要求。
Description
技术领域
本发明涉及建筑工程技术领域,具体地说,特别涉及一种建筑用砌筑干混 风积沙砂浆及其制备方法。
背景技术
随着建筑业的发展,建筑用砂浆量急剧增加。砂浆的制造通常是采用河沙 或机制砂配合其他成分制造而成,但是国家己经限制对河沙的无度开采,而采 用机制制沙不仅耗能高,而且会对矿山环境造成污染,同时有限的河沙或机制 沙已经无法满足庞大的建筑市场的需要,因而形成了建筑用沙的资源紧张。
风积沙是沙被风沙流搬移到冲积平原地区形成沙丘而产生的,具有结构松 散、级配不良、孔隙率大等特点。风积沙资源在我国西部分布广泛,储量丰富。
发明内容
为了解决现有技术的问题,本发明实施例提供了一种建筑用砌筑干混风积 沙砂浆及其制备方法。所述技术方案如下:
一方面,提供了一种建筑用砌筑干混风积沙砂浆,由以下质量百分比的原 料组成:水泥18%-22%,粉煤灰3%-6%,风积沙65%-75%,保水剂0.0l%-0.2%, 抗裂剂0.0l%-1%。
进一步的,所述水泥为普通硅酸盐42.5水泥。
进一步的,所述粉煤灰为I级粉煤灰。
进一步的,所述保水剂为纤维素醚。
进一步的,所述抗裂剂为可再分散乳胶粉。
另一方面,提供了一种建筑用砌筑干混风积沙砂浆的制备方法,包括:
(1)风积沙的预处理:
首先将风积沙进行水洗1-3遍,接着通过烘干箱进行烘干,然后通过筛网进 行筛分,筛分后的颗粒细度大于0.075mm;
(2)粉煤灰干燥和筛分:
将粉煤灰进行干燥,使得干燥后的粉煤灰含水率按质量百分比计小于3%, 再进行筛分,筛分后的颗粒细度不大于于0.075mm;
(3)配料:
将水泥、保水剂、抗裂剂、以及步骤(1)经筛分后的风积沙和步骤(2)经筛 分后的粉煤灰按照质量百分比计量;
(4)混合搅拌,搅拌过程如下:
计量好的水泥、粉煤灰加入砂浆生产系统混合,搅拌均匀;
将计量好的保水剂、抗裂剂、同时加入砂浆生产系统,并与水泥、粉煤灰 一起搅拌均匀,得到混合砂浆胶凝助剂;
将计量好的风积沙,加入砂浆生产系统中,并与混合砂浆胶凝助剂共同混 合搅拌均匀,制得成品。
本发明实施例提供的技术方案带来的有益效果是:
本发明通过提供了一种建筑用砌筑干混风积沙砂浆,有效解决了长久以来 因风积沙颗粒较细而无法满足建筑用沙的难点,以及现今所存一在大量风积沙 的利用问题,且为干混砌筑砂浆的制造开辟了一种新途径,改变了建筑用沙资 源缺乏的现状,同时其生产土艺简单,操作方便。
本发明通过提供一种建筑用砌筑干混风积沙砂浆的制造方法,有效解决了 长久以来因沙漠沙子颗粒较细、含泥量高而无法满足建筑用沙的难点,以及现 今所存在大量沙漠沙子的利用问题,所生产的干混砌筑砂浆强度、保水率、抗 冻性均符合建筑用砌筑干混砂浆规范要求。本发明为干混砌筑砂浆的制造开辟 了一种新途径,改变了建筑用沙资源缺乏的现状。
与此同时,系统的研究风积沙制备干混砂浆,对利用西部丰富的风积沙资 源进行西部开发建设有重要的意义,同时,也可避免西部在开发建设过程中过 度开采天然河砂和矿山,保护西部的生态环境。
具体实施方式
为使本发明的目的、技术方案和优点更加清楚,下面将对本发明实施方式 作进一步地详细描述。
本发明提供了一种建筑用砌筑干混风积沙砂浆,由以下质量百分比的原料 组成:水泥18%-22%,粉煤灰3%-6%,风积沙65%-75%,保水剂0.0l%-0.2%, 抗裂剂0.0l%-1%。
进一步的,所述水泥为普通硅酸盐42.5水泥。
进一步的,所述粉煤灰为I级粉煤灰。
进一步的,所述保水剂为纤维素醚。
进一步的,所述抗裂剂为可再分散乳胶粉。
本实施例中,风积沙干混砌筑砂浆强度等级分为:
M2.4\M5\M7.5\M10\M15\M20。
另一方面,提供了一种建筑用砌筑干混风积沙砂浆的制备方法,包括:
(1)风积沙的预处理:
首先将风积沙进行水洗1-3遍,接着通过烘干箱进行烘干,然后通过筛网进 行筛分,筛分后的颗粒细度大于0.075mm;
(2)粉煤灰干燥和筛分:
将粉煤灰进行干燥,使得干燥后的粉煤灰含水率按质量百分比计小于3%, 再进行筛分,筛分后的颗粒细度不大于于0.075mm;
(3)配料:
将水泥、保水剂、抗裂剂、以及步骤(1)经筛分后的风积沙和步骤(2)经筛 分后的粉煤灰按照质量百分比计量;
(4)混合搅拌,搅拌过程如下:
计量好的水泥、粉煤灰加入砂浆生产系统混合,搅拌均匀;
将计量好的保水剂、抗裂剂、同时加入砂浆生产系统,并与水泥、粉煤灰 一起搅拌均匀,得到混合砂浆胶凝助剂;
将计量好的风积沙,加入砂浆生产系统中,并与混合砂浆胶凝助剂共同混 合搅拌均匀,制得成品。
以上仅为本发明的较佳实施例,并不用以限制本发明,凡在本发明的精神 和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护 范围之内。
Claims (6)
1.一种建筑用砌筑干混风积沙砂浆,其特征在于,由以下质量百分比的原料组成:水泥18%-22%,粉煤灰3%-6%,风积沙65%-75%,保水剂0.0l%-0.2%,抗裂剂0.0l%-1%。
2.如权利要求1所述的建筑用砌筑干混风积沙砂浆,其特征在于,所述水泥为普通硅酸盐42.5水泥。
3.如权利要求1所述的建筑用砌筑干混风积沙砂浆,其特征在于,所述粉煤灰为I级粉煤灰。
4.如权利要求1所述的建筑用砌筑干混风积沙砂浆,其特征在于,所述保水剂为纤维素醚。
5.如权利要求1所述的建筑用砌筑干混风积沙砂浆,其特征在于,所述抗裂剂为可再分散乳胶粉。
6.一种建筑用砌筑干混风积沙砂浆的制备方法,其特征在于,包括:
(1)风积沙的预处理:
首先将风积沙进行水洗1-3遍,接着通过烘干箱进行烘干,然后通过筛网进行筛分,筛分后的颗粒细度大于0.075mm;
(2)粉煤灰干燥和筛分:
将粉煤灰进行干燥,使得干燥后的粉煤灰含水率按质量百分比计小于3%,再进行筛分,筛分后的颗粒细度不大于于0.075mm;
(3)配料:
将水泥、保水剂、抗裂剂、以及步骤(1)经筛分后的风积沙和步骤(2)经筛分后的粉煤灰按照质量百分比计量;
(4)混合搅拌,搅拌过程如下:
计量好的水泥、粉煤灰加入砂浆生产系统混合,搅拌均匀;
将计量好的保水剂、抗裂剂、同时加入砂浆生产系统,并与水泥、粉煤灰一起搅拌均匀,得到混合砂浆胶凝助剂;
将计量好的风积沙,加入砂浆生产系统中,并与混合砂浆胶凝助剂共同混合搅拌均匀,制得成品。