CN109694640A - A kind of wear-resisting floor wearing floor - Google Patents
A kind of wear-resisting floor wearing floor Download PDFInfo
- Publication number
- CN109694640A CN109694640A CN201711002259.XA CN201711002259A CN109694640A CN 109694640 A CN109694640 A CN 109694640A CN 201711002259 A CN201711002259 A CN 201711002259A CN 109694640 A CN109694640 A CN 109694640A
- Authority
- CN
- China
- Prior art keywords
- parts
- wear
- floor
- resisting
- diluent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of wear-resisting floor wearing floors, including substrate and the wear-resistant coating for being coated on the substrate surface.The component of the wear-resistant coating is as follows according to parts by weight: 30-40 parts of ricinoleyl alcohol acid resin, 7-10 parts of alkyd resin, 10-15 parts of plasticizer, 10-15 parts of butyl acetate, 10-15 parts of aromatic urethane acrylate, 15-20 parts of dimethylaminoethyl acrylate, 0.2-0.4 parts of propylene glycol methyl ether acetate, 35-45 parts of diluent.Floor manufacture craft provided by the invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and intensity is high, and abrasion resistant effect is good, has broad application prospects.
Description
Technical field
The present invention relates to building material technical field more particularly to a kind of wear-resisting floor wearing floors.
Background technique
Floor is for the common ornament materials in Indoor environment ground.Current floor is due to stress mistake after its curing of coating
Greatly, flexibility is bad, and paint film is caused to be easy to wear, and influences product quality and usage experience.
Summary of the invention
To solve the above problems, the present invention provides a kind of wear-resisting floor wearing floors.
Technical scheme is as follows:
A kind of wear-resisting floor wearing floor, including substrate and the wear-resistant coating for being coated on the substrate surface.
Further, the component of the wear-resistant coating is as follows according to parts by weight: 30-40 parts of ricinoleyl alcohol acid resin,
7-10 parts of alkyd resin, 10-15 parts of plasticizer, 10-15 parts of butyl acetate, 10-15 parts of aromatic urethane acrylate, propylene
Sour dimethylaminoethyl 15-20 parts, 0.2-0.4 parts of propylene glycol methyl ether acetate, 35-45 parts of diluent.
Further, the plasticizer is phthalic acid two (2- ethyl hexyl) ester.
Further, the diluent is 1,6- hexylene glycol double methacrylate (HDDA).
Further, a kind of wear-resisting floor wearing floor preparation method, it is characterised in that:
S1: by ricinoleyl alcohol acid resin, alkyd resin, butyl acetate, aromatic urethane acrylate, acrylic acid diformazan
Amino ethyl ester, propylene glycol methyl ether acetate, diluent are placed in reaction kettle, then first high-speed stirred 30min stirs at low speed 1h.
S2: reaction kettle is warming up to 40-60 DEG C of stirring 15min, then water cooling to room temperature, is added after stirring at low speed 30min
Plasticizer the reaction was continued 2h;
S3: by the raw material after being reacted in step S2 by being uniformly coated on substrate surface, substrate after 80 mesh net filtrations
It is dried at 40-60 DEG C for 24 hours, obtains finished product.
According to the above aspect of the present invention, the present invention at least has the advantages that
Floor manufacture craft provided by the invention is simple, and raw material is easy to buy, and cost of manufacture is cheap, and intensity is high, wear-resisting effect
Fruit is good, has broad application prospects.
Specific embodiment
Technical solution of the present invention is described in detail as follows below with reference to embodiment.
Embodiment 1
A kind of wear-resisting floor wearing floor, including substrate and the wear-resistant coating for being coated on the substrate surface.
Further, the component of the wear-resistant coating is as follows according to parts by weight: 40 parts of ricinoleyl alcohol acid resin, alkyd
10 parts of resin, 15 parts of ester of phthalic acid two (2- ethyl hexyl), 10 parts of butyl acetate, 15 parts of aromatic urethane acrylate,
18 parts of dimethylaminoethyl acrylate, 0.3 part of propylene glycol methyl ether acetate, 1,6- 35 parts of hexylene glycol double methacrylate (HDDA).
Preparation method the following steps are included:
S1: by ricinoleyl alcohol acid resin, alkyd resin, butyl acetate, aromatic urethane acrylate, acrylic acid diformazan
Amino ethyl ester, propylene glycol methyl ether acetate, diluent are placed in reaction kettle, then first high-speed stirred 30min stirs at low speed 1h.
S2: reaction kettle is warming up to 40-60 DEG C of stirring 15min, then water cooling to room temperature, is added after stirring at low speed 30min
Plasticizer the reaction was continued 2h;
S3: by the raw material after being reacted in step S2 by being uniformly coated on substrate surface, substrate after 80 mesh net filtrations
It is dried at 40-60 DEG C for 24 hours, obtains finished product.
Embodiment 2
A kind of wear-resisting floor wearing floor, including substrate and the wear-resistant coating for being coated on the substrate surface.
Further, the component of the wear-resistant coating is as follows according to parts by weight: 31 parts of ricinoleyl alcohol acid resin, alkyd
7 parts of resin, 13 parts of ester of phthalic acid two (2- ethyl hexyl), 14 parts of butyl acetate, 11 parts of aromatic urethane acrylate, third
16 parts of olefin(e) acid dimethylaminoethyl, 0.4 part of propylene glycol methyl ether acetate, 1,6- 41 parts of hexylene glycol double methacrylate (HDDA).
Preparation method the following steps are included:
S1: by ricinoleyl alcohol acid resin, alkyd resin, butyl acetate, aromatic urethane acrylate, acrylic acid diformazan
Amino ethyl ester, propylene glycol methyl ether acetate, diluent are placed in reaction kettle, then first high-speed stirred 30min stirs at low speed 1h.
S2: reaction kettle is warming up to 40-60 DEG C of stirring 15min, then water cooling to room temperature, is added after stirring at low speed 30min
Plasticizer the reaction was continued 2h;
S3: by the raw material after being reacted in step S2 by being uniformly coated on substrate surface, substrate after 80 mesh net filtrations
It is dried at 40-60 DEG C for 24 hours, obtains finished product.
Embodiment 3
A kind of wear-resisting floor wearing floor, including substrate and the wear-resistant coating for being coated on the substrate surface.
Further, the component of the wear-resistant coating is as follows according to parts by weight: 37 parts of ricinoleyl alcohol acid resin, alkyd
9 parts of resin, 12 parts of ester of phthalic acid two (2- ethyl hexyl), 11 parts of butyl acetate, 13 parts of aromatic urethane acrylate, third
19 parts of olefin(e) acid dimethylaminoethyl, 0.2 part of propylene glycol methyl ether acetate, 1,6- 41 parts of hexylene glycol double methacrylate (HDDA).
Preparation method includes the following steps:
S1: by ricinoleyl alcohol acid resin, alkyd resin, butyl acetate, aromatic urethane acrylate, acrylic acid diformazan
Amino ethyl ester, propylene glycol methyl ether acetate, diluent are placed in reaction kettle, then first high-speed stirred 30min stirs at low speed 1h.
S2: reaction kettle is warming up to 40-60 DEG C of stirring 15min, then water cooling to room temperature, is added after stirring at low speed 30min
Plasticizer the reaction was continued 2h;
S3: by the raw material after being reacted in step S2 by being uniformly coated on substrate surface, substrate after 80 mesh net filtrations
It is dried at 40-60 DEG C for 24 hours, obtains finished product.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (5)
1. a kind of wear-resisting floor wearing floor, it is characterised in that: including substrate and the wear-resistant coating for being coated on the substrate surface.
2. a kind of wear-resisting floor wearing floor according to claim 1, it is characterised in that: the component of the wear-resistant coating is according to parts by weight
It is as follows: 30-40 parts of ricinoleyl alcohol acid resin, 7-10 parts of alkyd resin, 10-15 parts of plasticizer, 10-15 parts of butyl acetate,
10-15 parts of aromatic urethane acrylate, 15-20 parts of dimethylaminoethyl acrylate, propylene glycol methyl ether acetate 0.2-0.4
Part, 35-45 parts of diluent.
3. a kind of wear-resisting floor wearing floor according to claim 1, it is characterised in that: the plasticizer is two (2- of phthalic acid
Ethyl hexyl) ester.
4. a kind of wear-resisting floor wearing floor according to claim 1, it is characterised in that: the diluent is 1,6- hexylene glycol double third
Olefin(e) acid ester (HDDA).
5. a kind of wear-resisting floor wearing floor preparation method according to claim 1, it is characterised in that:
S1: by ricinoleyl alcohol acid resin, alkyd resin, butyl acetate, aromatic urethane acrylate, acrylate
Ethyl ester, propylene glycol methyl ether acetate, diluent are placed in reaction kettle, then first high-speed stirred 30min stirs at low speed 1h.
S2: being warming up to 40-60 DEG C of stirring 15min for reaction kettle, then water cooling to room temperature, and plasticising is added after stirring at low speed 30min
Agent the reaction was continued 2h;
S3: by the raw material after reacting in step S2 by being uniformly coated on substrate surface after 80 mesh net filtrations, substrate is in 40-
It is dried at 60 DEG C for 24 hours, obtains finished product.