CN109694602A - A kind of fireproof flame-retardant coating - Google Patents
A kind of fireproof flame-retardant coating Download PDFInfo
- Publication number
- CN109694602A CN109694602A CN201710989850.2A CN201710989850A CN109694602A CN 109694602 A CN109694602 A CN 109694602A CN 201710989850 A CN201710989850 A CN 201710989850A CN 109694602 A CN109694602 A CN 109694602A
- Authority
- CN
- China
- Prior art keywords
- fire
- flame
- agent
- retardant coating
- fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of fireproof flame-retardant coating, and the group of the weight percent of the fire-proof flame-retarded agent is divided into water 55%-70%, ammonium polyphosphate 10%-15%, ammonium chloride 10%-15%, dispersing agent 5%-6%, catalyst 4%-6%, defoaming agent 1%-3%.The fire-proof flame-retarded agent has the function of outstanding fire protection flame retarding, and the object for coating the fire-proof flame-retarded agent is made also to have fireproof flame-retardant effect, greatly reduces the generation of fire, protects the safety of people.
Description
Technical field
The present invention relates to a kind of fire-proofing preparation, in particular to a kind of fireproof flame-retardant coating.
Background technique
Fireproof agent is also known as fire-proofing chemical and fire retardant, with the development of China's synthetic material industry and constantly opening up for application field
Exhibition, fire retardant are each in chemical building material, electronic apparatus, communications and transportation, space flight and aviation, household furniture, interior decoration, clothing, food, lodging and transportion -- basic necessities of life etc.
It is had a vast market foreground in a field.In addition, the fields such as coalfield, oil field, forest extinguishing also promote, China is fire-retardant, puts out a fire
The faster development of agent production.China's fire retardant has evolved into the second macromolecular material modified additive for being only second to plasticizer.
Although current fireproof agent is applied in large quantities, the fire protecting performance of current fireproof agent is more general, Bu Nengman
High request of the sufficient people to flameproof effect.
Summary of the invention
It is an object of the invention to solve above-mentioned shortcoming and defect existing in the prior art, a kind of fire protection flame retarding painting is provided
Material, makes the object for coating the fire-proof flame-retarded agent also have fireproof flame-retardant effect, greatly reduces the generation of fire, protect the peace of people
Entirely.
Realize the technical solution adopted by the present invention to solve the technical problems are as follows: a kind of fireproof flame-retardant coating, the fire prevention
The group of the weight percent of fire retardant is divided into water 55%-70%, ammonium polyphosphate 10%-15%, ammonium chloride 10%-15%, dispersing agent 5%-
6%, catalyst 4%-6%, defoaming agent 1%-3%.
Further, the catalyst is silicic acid.
Further, the dispersing agent is polypropylene or polystyrene.
Further, the group of the weight percent of the fire-proof flame-retarded agent is divided into water 70%, ammonium polyphosphate 10%, ammonium chloride
10%, dispersing agent 5%, catalyst 4%, defoaming agent 1%.
In conclusion making to coat the invention has the benefit that the fire-proof flame-retarded agent has the function of outstanding fire protection flame retarding
The object of the fire-proof flame-retarded agent also has fireproof flame-retardant effect, greatly reduces the generation of fire, protects the safety of people.
Specific embodiment
Embodiment 1
A kind of fireproof flame-retardant coating described in the present embodiment 1, the group of the weight percent of the fire-proof flame-retarded agent are divided into water
70%, ammonium polyphosphate 10%, ammonium chloride 10%, dispersing agent 5%, catalyst 4%, defoaming agent 1%.
Further, the catalyst is silicic acid.
Further, the dispersing agent is polypropylene or polystyrene.
The above described is only a preferred embodiment of the present invention, not making in any form to structure of the invention
Limitation.Any simple modification, equivalent change and modification to the above embodiments according to the technical essence of the invention,
In the range of still falling within the technical solution of invention.
Claims (4)
1. a kind of fireproof flame-retardant coating, which is characterized in that the group of the weight percent of the fire-proof flame-retarded agent is divided into water 55%-
70%, ammonium polyphosphate 10%-15%, ammonium chloride 10%-15%, dispersing agent 5%-6%, catalyst 4%-6%, defoaming agent 1%-3%.
2. a kind of fireproof flame-retardant coating according to claim 1, which is characterized in that the catalyst is silicic acid.
3. a kind of fireproof flame-retardant coating according to claim 1, which is characterized in that the dispersing agent is polypropylene or polyphenyl
Ethylene.
4. a kind of fireproof flame-retardant coating according to claim 1, which is characterized in that the weight percent of the fire-proof flame-retarded agent
The group of ratio is divided into water 70%, ammonium polyphosphate 10%, ammonium chloride 10%, dispersing agent 5%, catalyst 4%, defoaming agent 1%.