CN109679383A - A kind of diatom ooze coating except formaldehyde - Google Patents
A kind of diatom ooze coating except formaldehyde Download PDFInfo
- Publication number
- CN109679383A CN109679383A CN201811630765.8A CN201811630765A CN109679383A CN 109679383 A CN109679383 A CN 109679383A CN 201811630765 A CN201811630765 A CN 201811630765A CN 109679383 A CN109679383 A CN 109679383A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatom ooze
- diatom
- titanium dioxide
- formaldehyde
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of diatom ooze coating and preparation method except formaldehyde, it is made of the raw material of following weight parts: 25-35 parts of diatom, 8-10 parts of aqueous polyurethane, 10-15 parts of lime stone, 5-8 parts of kaolin, active 10-15 parts of powdered carbon, 2-3 parts of dispersing agent, 5-10 parts of titanium dioxide and 25-35 parts of water, diatom ooze has natural porous structure, the characteristics of large specific surface area, it can be by formaldehyde absorbing in hole, titanium dioxide can decompose the harmful substances such as formaldehyde under the action of illumination simultaneously, can continuous and effective and environmental protection removal indoor formaldehyde, avoid to human body generate harm.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of diatom ooze coatings and preparation method except formaldehyde.
Background technique
In recent years, with the improvement of people's living standards, requirement of the people to interior decoration standard is also higher and higher, household
Decoration modernizes increasingly, but Formaldehyde Pollution of Indoor Air problem is following due to material and caused by fitting up.Formaldehyde is a kind of nothing
Color has the gas of intense irritation smell, the highly volatile in room temperature, as the rising evaporation rate of temperature is accelerated.Often at present
The interior seen is to divulge information or removed for a long time using air cleaning unit, but efficiency is lower except carbaldehyde Method, at high cost.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the deficiencies in the prior art, providing one kind can continue to inhale
Receive and decomposing formaldehyde except formaldehyde diatom ooze coating and preparation method.
The present invention is to be achieved by the following technical programs:
A kind of diatom ooze coating except formaldehyde, which is characterized in that be made of the raw material of following weight parts: 25-35 parts of diatom,
8-10 parts of aqueous polyurethane, 10-15 parts of lime stone, 5-8 parts of kaolin, active 10-15 parts of powdered carbon, 2-3 parts of dispersing agent, titanium dioxide
5-10 parts and 25-35 parts of water.
A kind of preparation method of the diatom ooze coating except formaldehyde, which comprises the following steps:
A. 25-35 parts of diatom is weighed by weight, 8-10 parts of aqueous polyurethane, 10-15 parts of lime stone, 5-8 parts of kaolin, is lived
10-15 parts of powdered carbon of property, 2-3 parts of dispersing agent, 5-10 parts of titanium dioxide and 25-35 parts of water；
B: diatom ooze weighed in step a, lime stone, kaolin, active powdered carbon, dispersing agent, titanium dioxide and water are put into
It is stirred 10-15 minutes in agitating device, aqueous polyurethane is then added, continue stirring 5-10 minutes, diatom ooze coating is made.
The beneficial effects of the present invention are:
Diatom ooze has the characteristics of natural porous structure, large specific surface area, can be by formaldehyde absorbing in hole, simultaneously
Titanium dioxide can decompose the harmful substances such as formaldehyde under the action of illumination, being capable of continuous and effective and environmentally friendly removal interior first
Aldehyde avoids generating harm to human body.
Specific embodiment
In order to make those skilled in the art more fully understand technical solution of the present invention, implement below with reference to best
The present invention is described in further detail for example.
Embodiment 1
A kind of diatom ooze coating except formaldehyde, which is characterized in that be made of the raw material of following weight parts: 25 parts of diatom, water
Property 8 parts of polyurethane, 10 parts of lime stone, 5 parts of kaolin, active 10 parts of powdered carbon, 2 parts of dispersing agent, 5 parts of titanium dioxide and 25 parts of water.
A kind of preparation method of the diatom ooze coating except formaldehyde, which comprises the following steps:
A. 25 parts of diatom, 8 parts of aqueous polyurethane, 10 parts of lime stone, 5 parts of kaolin, active powdered carbon 10 are weighed by weight
Part, 2 parts of dispersing agent, 5 parts of titanium dioxide and 25 parts of water；
B: diatom ooze weighed in step a, lime stone, kaolin, active powdered carbon, dispersing agent, titanium dioxide and water are put into
It is stirred 10 minutes in agitating device, aqueous polyurethane is then added, continue stirring 5 minutes, diatom ooze coating is made.
Embodiment 2
A kind of diatom ooze coating except formaldehyde, which is characterized in that be made of the raw material of following weight parts: diatom 30, aqueous
9 parts of polyurethane, 12 parts of lime stone, 6 parts of kaolin, active 13 parts of powdered carbon, 2 parts of dispersing agent, 8 parts of titanium dioxide and 30 parts of water.
A kind of preparation method of the diatom ooze coating except formaldehyde, which comprises the following steps:
A. weigh by weight diatom 30,9 parts of aqueous polyurethane, 12 parts of lime stone, 6 parts of kaolin, active 13 parts of powdered carbon,
2 parts of dispersing agent, 8 parts of titanium dioxide and 30 parts of water；
B: diatom ooze weighed in step a, lime stone, kaolin, active powdered carbon, dispersing agent, titanium dioxide and water are put into
It is stirred 13 minutes in agitating device, aqueous polyurethane is then added, continue stirring 8 minutes, diatom ooze coating is made.
Embodiment 3
A kind of diatom ooze coating except formaldehyde, which is characterized in that be made of the raw material of following weight parts: 35 parts of diatom, water
Property 10 parts of polyurethane, 15 parts of lime stone, 8 parts of kaolin, active 15 parts of powdered carbon, 3 parts of dispersing agent, 10 parts of titanium dioxide and 35 parts of water.
A kind of preparation method of the diatom ooze coating except formaldehyde, which comprises the following steps:
A. 35 parts of diatom, 10 parts of aqueous polyurethane, 15 parts of lime stone, 8 parts of kaolin, active powdered carbon 15 are weighed by weight
Part, 3 parts of dispersing agent, 10 parts of titanium dioxide and 35 parts of water；
B: diatom ooze weighed in step a, lime stone, kaolin, active powdered carbon, dispersing agent, titanium dioxide and water are put into
It is stirred 15 minutes in agitating device, aqueous polyurethane is then added, continue stirring 10 minutes, diatom ooze coating is made.
The foregoing is only a preferred embodiment of the present invention, is not intended to restrict the invention, for the skill of this field
For art personnel, the invention may be variously modified and varied.All within the spirits and principles of the present invention, made any to repair
Change, equivalent replacement, improvement etc., should all be included in the protection scope of the present invention.
Claims (2)
1. a kind of diatom ooze coating except formaldehyde, which is characterized in that be made of the raw material of following weight parts: 25-35 parts of diatom, water
Property 8-10 parts of polyurethane, 10-15 parts of lime stone, 5-8 parts of kaolin, active 10-15 parts of powdered carbon, 2-3 parts of dispersing agent, titanium dioxide 5-
10 parts and 25-35 parts of water.
2. a kind of preparation method of the diatom ooze coating except formaldehyde, which comprises the following steps:
A. 25-35 parts of diatom, 8-10 parts of aqueous polyurethane, 10-15 parts of lime stone, 5-8 parts of kaolin, active carbon are weighed by weight
10-15 parts of powder, 2-3 parts of dispersing agent, 5-10 parts of titanium dioxide and 25-35 parts of water；
B: diatom ooze weighed in step a, lime stone, kaolin, active powdered carbon, dispersing agent, titanium dioxide and water are put into stirring
It is stirred 10-15 minutes in device, aqueous polyurethane is then added, continue stirring 5-10 minutes, diatom ooze coating is made.