CN107954654A - The diatomite paint and preparation method of a kind of formaldehyde adsorption - Google Patents
The diatomite paint and preparation method of a kind of formaldehyde adsorption Download PDFInfo
- Publication number
- CN107954654A CN107954654A CN201711367449.1A CN201711367449A CN107954654A CN 107954654 A CN107954654 A CN 107954654A CN 201711367449 A CN201711367449 A CN 201711367449A CN 107954654 A CN107954654 A CN 107954654A
- Authority
- CN
- China
- Prior art keywords
- parts
- diatomite
- paint
- formaldehyde adsorption
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the diatomite paint and preparation method of a kind of formaldehyde adsorption.Coating of the present invention includes parts by weight and distinguishes following component：25 50 parts of diatomite, 25 parts of glass fibre, 0.5 2.0 parts of dispersant, 20 30 parts of adhesive, 5 35 parts of Nano titanium dioxide, 5 35 parts of Nano-class zinc oxide, 25 parts of plant fiber；SiO2 weight percentage >=90% contained in the diatomite, the diatomite particle diameter are 60 150 mesh.Diatomite material of the present invention has larger specific surface area, and adsorption capacity is strong, with reference to a variety of nano materials of mixing, glass fibre increases light reflection, the absorption of absorption and formaldehyde of the plant fiber enhancing to humidity is added, indoor air pollutants matter is greatly reduced, actively improves indoor environment；Diatomite has penetrating aperture, and it is possessed extremely strong heat insulating ability, sound absorption properties, and diatom ooze has the electrostatic eliminated in room air, and has killing effect to parasite and microorganism, prevents the mouldy discoloration of metope, while significantly reduce foreign flavor indoors.
Description
Technical field
The present invention relates to field of nanometer material technology, the diatomite paint and preparation method of specifically a kind of formaldehyde adsorption.
Background technology
Formaldehyde adsorption coating is the active material of indoor hardware fitting in recent years.Expanding economy promotes people's environmental protection meaning
The raising of knowledge, environmental quality issues receive the extensive concern of people, and the research and development success of anti-methanal paint effectively relieves consumption
Puzzlement, worry to interior decoration selection.Consumer also results in while the use of a large amount of finishing materials improves quality of the life
The continuous deterioration of indoor air quality, the harm to human body, the danger of old man particularly poor to resistance, children and pregnant woman
Evil, it has also become the hot issue of concern.Anti- methanal paint is the environment-friendly materials of indoor internal wall finishing, can effectively reduce Interior Space
The main pollution of gas, reduces finishing and brings our harm.
At present, in anti-formaldehyde powder and coating research and development, most of enterprise is devoted to the research and development of environment-friendly building materials, interior wall city
In, also there is new product release.Wherein, diatomite material is exactly bright spot maximum in these new products.Diatomite material is multinomial with its
Excellent performance（Decompose free formaldehyde, breathing damping, sterilization etc.）) and abundant skin texture show power, one puts goods on the market, and is just subject to
The trust of designer and consumer and like.
Diatom ooze, diatom ooze material, diatomite material, diatom ooze coating are a kind of brand-new rooms all referring to same thing
Interior health wall finishes material.It is reasonably combined according to the clay pits such as different qualities diatomite, coordinates nano material to make production
Product have stronger selection adsorption capacity, excellent ion exchangeable and molecular sieve function；Improve to moisture and organic steam
Adsorption capacity, especially PARA FORMALDEHYDE PRILLS(91,95), benzene, the organic solution of VOC one kind and harmful metal ion are provided with bigger adsorption capacity.
But diatomite material made from current diatomite, dehumidifying, heat-insulating property are poor, and in terms of decomposition function not
It is preferable.It is then desired to be improved to obtain the diatomite material improved with capacity of decomposition, meet the needs in market.
The content of the invention
The present invention proposes a kind of diatomite paint and preparation method of formaldehyde adsorption, for current interior wall diatomite material point
The problem of harmful substance performances such as solution formaldehyde are low, and a kind of novel environment friendly diatomite material researched and developed, this new diatomite material
Material is made of natural material, and without any harmful material, its generation thoroughly solves indoor environmental pollution pair
The injury of occupant, while built an original, honest, natural living environment for us；And in absorption, decomposition and sterilization
Functionally there is very strong effect.
To achieve the above object, the diatomite paint of a kind of formaldehyde adsorption of the present invention, including parts by weight are respectively such as
Under component：25-50 parts of diatomite, 2-5 parts of glass fibre, 0.5-2.0 parts of dispersant, 20-30 parts of adhesive, nanoscale dioxy
Change 5-35 parts of titanium, 5-35 parts of Nano-class zinc oxide, 2-5 parts of plant fiber；The SiO contained in the diatomite2Weight percent contains
Amount >=90%, the diatomite particle diameter is 60-150 mesh.
The coating weight number distinguishes following component：45-50 parts of diatomite, 4-5 parts of glass fibre, dispersant 0.5-
2.0 parts, 25-30 parts of adhesive, 25-35 parts of Nano titanium dioxide, 25-35 parts of Nano-class zinc oxide, 4-5 parts of plant fiber；
The SiO contained in the diatomite2Weight percentage >=90%, the diatomite particle diameter are 60 mesh.
The particle diameter of the Nano titanium dioxide is 10nm；The particle diameter of the Nano-class zinc oxide is 10nm；The plant
Particle diameter is 300 mesh after the crushing of fiber.
The dispersant is quartz, one kind in tourmaline or combination.
The adhesive is inorganic gel powder.
A kind of preparation method of the diatomite paint of formaldehyde adsorption, including procedure below：
1）Various composition is weighed according to aforementioned proportion, glass fibre, dispersant, plant fiber are mixed 5 minutes, after stirring evenly
Adding Nano-class zinc oxide and Nano titanium dioxide, then stirring 10 minutes adds adhesive and stirs 10 minutes to uniform,
Diatomite is added after last, is mixed 5 minutes, that is, the diatomite paint of formaldehyde adsorption is made.
A kind of construction technology of the diatomite paint of formaldehyde adsorption, the diatomite paint and water by formaldehyde adsorption
By weight 1：1 mixes, and stirs into paste；Then first pass blade coating is carried out on the basal plane that need to be smeared, treats the base once scratched
Face is completely dried, then carries out secondary blade coating, secondary blade coating, you can.
The diatomite paint and preparation method of a kind of formaldehyde adsorption of the present invention, its advantage are：The present invention adopts
Mixed with a variety of inorganic building materials such as diatomite, Nano titanium dioxide, Nano-class zinc oxide, obtained diatomite material
Material has larger specific surface area, so as to have very strong adsorption capacity, with reference to a variety of nano materials of mixing, glass fibre increase
Light reflection, the absorption of absorption and formaldehyde of the addition plant fiber enhancing to humidity, is greatly reduced indoor air pollutants matter, right
The harmful chemicals such as formaldehyde, benzene, ammonia, VOC are decomposed, and actively improve indoor environment；Diatomite has penetrating aperture, makes
It, which possesses extremely strong heat insulating ability, sound absorption properties, and diatom ooze, has anti-static function, can eliminate the electrostatic in room air, avoid
Electrostatic dust sticks, due also to diatomaceous lattice structure has killing effect to parasite and microorganism, prevents metope from sending out
Go mouldy color, while significantly reduces foreign flavor indoors.
Embodiment
Embodiment 1
A kind of diatomite paint of formaldehyde adsorption of the present invention, including parts by weight distinguish following component：45 parts of diatomite,
4 parts of glass fibre, 0.5 part of dispersant, 25 parts of adhesive, 25 parts of Nano titanium dioxide, 25 parts of Nano-class zinc oxide, plant are fine
4 parts of dimension；The SiO contained in the diatomite2Weight percentage >=90%, the diatomite particle diameter are 60 mesh；The nanoscale
The particle diameter of titanium dioxide is 10nm；The particle diameter of the Nano-class zinc oxide is 10nm；Particle diameter is after the crushing of the plant fiber
300 mesh；The dispersant is quartz；The adhesive is inorganic gel powder.
A kind of preparation method of the diatomite paint of formaldehyde adsorption, including procedure below：Weighed according to aforementioned proportion
Various composition, glass fibre, dispersant, plant fiber are mixed 5 minutes, Nano-class zinc oxide and nanometer are added after stirring evenly
Then grade titanium dioxide, stirring add adhesive and stir 10 minutes to uniform for 10 minutes, diatomite, mixing are added after last
Stirring 5 minutes, that is, be made the diatomite paint of formaldehyde adsorption.
A kind of construction technology of the diatomite paint of formaldehyde adsorption, the diatomite paint and water by formaldehyde adsorption
By weight 1：1 mixes, and stirs into paste；Then first pass blade coating is carried out on the basal plane that need to be smeared, treats the base once scratched
Face is completely dried, then carries out secondary blade coating, secondary blade coating, you can.
Embodiment 2
A kind of diatomite paint of formaldehyde adsorption of the present invention, including parts by weight distinguish following component：50 parts of diatomite,
5 parts of glass fibre, 2.0 parts of dispersant, 30 parts of adhesive, 35 parts of Nano titanium dioxide, 35 parts of Nano-class zinc oxide, plant are fine
5 parts of dimension；The SiO contained in the diatomite2Weight percentage >=90%, the diatomite particle diameter are 60 mesh；The nanoscale
The particle diameter of titanium dioxide is 10nm；The particle diameter of the Nano-class zinc oxide is 10nm；Particle diameter is after the crushing of the plant fiber
300 mesh；The dispersant is tourmaline；The adhesive is inorganic gel powder.
A kind of preparation method of the diatomite paint of formaldehyde adsorption, including procedure below：Weighed according to aforementioned proportion
Various composition, glass fibre, dispersant, plant fiber are mixed 5 minutes, Nano-class zinc oxide and nanometer are added after stirring evenly
Then grade titanium dioxide, stirring add adhesive and stir 10 minutes to uniform for 10 minutes, diatomite, mixing are added after last
Stirring 5 minutes, that is, be made the diatomite paint of formaldehyde adsorption.
A kind of construction technology of the diatomite paint of formaldehyde adsorption, the diatomite paint and water by formaldehyde adsorption
By weight 1：1 mixes, and stirs into paste；Then first pass blade coating is carried out on the basal plane that need to be smeared, treats the base once scratched
Face is completely dried, then carries out secondary blade coating, secondary blade coating, you can.
Embodiment 3
A kind of diatomite paint of formaldehyde adsorption of the present invention, including parts by weight distinguish following component：25 parts of diatomite,
2 parts of glass fibre, 0.5 part of dispersant, 20 parts of adhesive, 5 parts of Nano titanium dioxide, 5 parts of Nano-class zinc oxide, plant fiber
2 parts；The SiO contained in the diatomite2Weight percentage >=90%, the diatomite particle diameter are 150 mesh；The nanoscale
The particle diameter of titanium dioxide is 10nm；The particle diameter of the Nano-class zinc oxide is 10nm；Particle diameter is after the crushing of the plant fiber
300 mesh；The dispersant is quartz, tourmaline with parts by weight 1:1 combination；The adhesive is inorganic gel powder.
A kind of preparation method of the diatomite paint of formaldehyde adsorption, including procedure below：Weighed according to aforementioned proportion
Various composition, glass fibre, dispersant, plant fiber are mixed 5 minutes, Nano-class zinc oxide and nanometer are added after stirring evenly
Then grade titanium dioxide, stirring add adhesive and stir 10 minutes to uniform for 10 minutes, diatomite, mixing are added after last
Stirring 5 minutes, that is, be made the diatomite paint of formaldehyde adsorption.
A kind of construction technology of the diatomite paint of formaldehyde adsorption, the diatomite paint and water by formaldehyde adsorption
By weight 1：1 mixes, and stirs into paste；Then first pass blade coating is carried out on the basal plane that need to be smeared, treats the base once scratched
Face is completely dried, then carries out secondary blade coating, secondary blade coating, you can.
Basic principle, main feature and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appended claims and its
Equivalent defines.
Claims (7)
- A kind of 1. diatomite paint of formaldehyde adsorption, it is characterised in that：Following component is distinguished including parts by weight：Diatomite 25-50 parts, 2-5 parts of glass fibre, 0.5-2.0 parts of dispersant, 20-30 parts of adhesive, 5-35 parts of Nano titanium dioxide, nanometer 5-35 parts of zinc oxide of level, 2-5 parts of plant fiber；The SiO contained in the diatomite2Weight percentage >=90%, the diatom Grogs footpath is 60-150 mesh.
- A kind of 2. diatomite paint of formaldehyde adsorption as claimed in claim 1, it is characterised in that：The coating weight number difference Following component：45-50 parts of diatomite, 4-5 parts of glass fibre, 0.5-2.0 parts of dispersant, 25-30 parts of adhesive, nanoscale two 25-35 parts of titanium oxide, 25-35 parts of Nano-class zinc oxide, 4-5 parts of plant fiber；The SiO contained in the diatomite2Weight hundred Divide content >=90%, the diatomite particle diameter is 60 mesh.
- A kind of 3. diatomite paint of formaldehyde adsorption as claimed in claim 2, it is characterised in that：The Nano titanium dioxide Particle diameter is 10nm；The particle diameter of the Nano-class zinc oxide is 10nm；Particle diameter is 300 mesh after the crushing of the plant fiber.
- A kind of 4. diatomite paint of formaldehyde adsorption as claimed in claim 2, it is characterised in that：The dispersant is quartz, electricity One kind or combination in gas stone.
- A kind of 5. diatomite paint of formaldehyde adsorption as claimed in claim 2, it is characterised in that：The adhesive is inorganic gel Powder.
- A kind of 6. preparation method of the diatomite paint of formaldehyde adsorption as any one of claim 1-5, it is characterised in that： Including procedure below：1）Various composition is weighed according to aforementioned proportion, glass fibre, dispersant, plant fiber are mixed 5 minutes, after stirring evenly Adding Nano-class zinc oxide and Nano titanium dioxide, then stirring 10 minutes adds adhesive and stirs 10 minutes to uniform, Diatomite is added after last, is mixed 5 minutes, that is, the diatomite paint of formaldehyde adsorption is made.
- A kind of 7. construction technology of the diatomite paint of formaldehyde adsorption as described in claim 1-5, it is characterised in that：It is described to inhale The diatomite paint of attached formaldehyde is with water by weight 1：1 mixes, and stirs into paste；Then first is carried out on the basal plane that need to be smeared All over blade coating, the basal plane for treating once to scratch is completely dried, then carries out secondary blade coating, secondary blade coating, you can.